NACE NO 3-1994 Joint Surface Preparation Standard Commercial Blast Cleaning (Item No 21067 SSPC-SP 6).pdf

《NACE NO 3-1994 Joint Surface Preparation Standard Commercial Blast Cleaning (Item No 21067 SSPC-SP 6).pdf》由会员分享，可在线阅读，更多相关《NACE NO 3-1994 Joint Surface Preparation Standard Commercial Blast Cleaning (Item No 21067 SSPC-SP 6).pdf（9页珍藏版）》请在麦多课文档分享上搜索。

1、 Item No. 21067 Joint Surface Preparation Standard NACE No. 3/SSPC-SP 6 Commercial Blast Cleaning This NACE International (NACE)/The Society for Protective Coatings (SSPC) standard represents a consensus of those individual members who have reviewed this document, its scope, and provisions. It is in

2、tended to aid the manufacturer, the consumer, and the general public. Its acceptance does not in any respect preclude anyone, whether he or she has adopted the standard or not, from manufacturing, marketing, purchasing, or using products, processes, or procedures not addressed in this standard. Noth

3、ing contained in this NACE/SSPC standard is to be construed as granting any right, by implication or otherwise, to manufacture, sell, or use in connection with any method, apparatus, or product covered by Letters Patent, or as indemnifying or protecting anyone against liability for infringement of L

4、etters Patent. This standard represents current technology and should in no way be interpreted as a restriction on the use of better procedures or materials. Neither is this standard intended to apply in all cases relating to the subject. Unpredictable circumstances may negate the usefulness of this

5、 standard in specific instances. NACE and SSPC assume no responsibility for the interpretation or use of this standard by other parties and accept responsibility for only those official interpretations issued by NACE or SSPC in accordance with their governing procedures and policies which preclude t

6、he issuance of interpretations by individual volunteers. Users of this NACE/SSPC standard are responsible for reviewing appropriate health, safety, environmental, and regulatory documents and for determining their applicability in relation to this standard prior to its use. This NACE/SSPC standard m

7、ay not necessarily address all potential health and safety problems or environmental hazards associated with the use of materials, equipment, and/or operations detailed or referred to within this standard. Users of this NACE/SSPC standard are also responsible for establishing appropriate health, saf

8、ety, and environmental protection practices, in consultation with appropriate regulatory authorities if necessary, to achieve compliance with any existing applicable regulatory requirements prior to the use of this standard. CAUTIONARY NOTICE: NACE/SSPC standards are subject to periodic review, and

9、may be revised or withdrawn at any time in accordance with technical committee procedures. The user is cautioned to obtain the latest edition. NACE and SSPC require that action be taken to reaffirm, revise, or withdraw this standard no later than five years from the date of initial publication. Reaf

10、firmed 2006-09-13 Reaffirmed 1999-09-07 Approved October 1994 ISBN 1-57590-109-9 2006, SSPC: The Society for Protective Coatings and NACE International NACE International 1440 South Creek Dr. Houston, TX 77084-4906 (telephone +1 281/228-6200) SSPC: The Society for Protective Coatings 40 24th Street,

11、 Sixth Floor Pittsburgh, PA 15222 (telephone +1 412/281-2331) Printed by NACE InternationalNACE No. 3/SSPC-SP 6 NACE International i _ Foreword This joint standard covers the use of blast cleaning abrasives to achieve a defined degree of cleaning of steel surfaces prior to the application of a prote

12、ctive coating or lining system. This standard is intended for use by coating or lining specifiers, applicators, inspectors, or others who may be responsible for defining a standard degree of surface cleanliness. The focus of this standard is commercial blast cleaning. White metal blast cleaning, nea

13、r-white metal blast cleaning, industrial blast cleaning, and brush-off blast cleaning are addressed in separate standards. Commercial blast cleaning provides a greater degree of cleaning than industrial blast cleaning (NACE No. 8/SSPC-SP 141) but less than near-white metal blast cleaning (NACE No. 2

14、/SSPC-SP 102). Commercial blast cleaning is used when the objective is to remove all visible oil, grease, dust, dirt, mill scale, rust, coating, oxides, corrosion products, and other foreign matter, leaving staining or shadows on no more than 33 percent of each unit area of surface. The difference b

15、etween a commercial blast cleaning and a near-white metal blast cleaning is in the amount of staining permitted to remain on the surface. Commercial blast cleaning allows stains or shadows on 33 percent of each unit area of surface. Near-white metal blast cleaning allows staining or shadows on only

16、5 percent of each unit area of surface. The difference between a commercial blast cleaning and an industrial blast cleaning is that a commercial blast cleaning removes all visible oil, grease, dust, dirt, mill scale, rust, coating, oxides, corrosion products, and other foreign matter from all surfac

17、es and allows stains to remain on 33 percent of each unit area of surface, while industrial blast cleaning allows defined mill scale, coating, and rust to remain on less than 10 percent of each unit area of surface and allows defined stains to remain on all surfaces. This joint standard was original

18、ly prepared in 1994 and reaffirmed in 1999 by the SSPC/NACE Task Group (TG) A on Surface Preparation by Abrasive Blast Cleaning. This joint TG includes members of both the SSPC Surface Preparation Committee and the NACE Unit Committee T-6G on Surface Preparation. It was reaffirmed in 2006 by NACE Sp

19、ecific Technology Group (STG) 04, Protective Coatings and Linings: Surface Preparation, and the SSPC Surface Preparation Committee. In NACE/SSPC standards, the terms shall, must, should, and may are used in accordance with Paragraph 2.2.1.8 of the Agreement Between NACE International and SSPC: The S

20、ociety for Protective Coatings. The terms shall and must are used to state mandatory requirements. The term should is used to state something considered good and is recommended but is not mandatory. The term may is used to state something considered optional. _ NACE No. 3/SSPC-SP 6 ii NACE Internati

21、onal _ Joint Surface Preparation Standard NACE No. 3/SSPC-SP 6 Commercial Blast Cleaning Contents 1. General 1 2. Definitions 1 3. Associated Documents 1 4. Procedures Before Cleaning 1 5. Blast Cleaning Methods and Operation . 2 6. Blast Cleaning Abrasives . 2 7. Procedures Following Blast Cleaning

22、 and Immediately Prior to Coating 2 8. Inspection . 3 9. Safety and Environmental Requirements 3 10. Comments (Nonmandatory) 3 References 3 Appendix A: Explanatory Notes (Nonmandatory). 4 _ NACE No. 3/SSPC-SP 6 NACE International 1 _ Section 1: General 1.1 This joint standard covers the requirements

23、 for commercial blast cleaning of uncoated or coated steel surfaces by the use of abrasives. These requirements include the end condition of the surface and materials and procedures necessary to achieve and verify the end condition. 1.2 The mandatory requirements are described in Sections 1 to 9. Se

24、ction 10, “Comments,” and Appendix A,“Explanatory Notes,” are not mandatory requirements of this standard. 1.3 Information about the function of commercial blast cleaning is in Paragraph A1 of Appendix A. 1.4 Information about use of this standard in maintenance coating work is in Paragraph A2 of Ap

25、pendix A. _ Section 2: Definitions 2.1 Commercial Blast Cleaned Surface: A commercial blast cleaned surface, when viewed without magnification, shall be free of all visible oil, grease, dust, dirt, mill scale, rust, coating, oxides, corrosion products, and other foreign matter. Random staining shall

26、 be limited to no more than 33 percent of each unit area of surface (approximately 5,800 mm29.0 in.2) (i.e., a square 76 mm x 76 mm 3.0 in. x 3.0 in.) and may consist of light shadows, slight streaks, or minor discolorations caused by stains of rust, stains of mill scale, or stains of previously app

27、lied coating. 2.1.1 Acceptable variations in appearance that do not affect surface cleanliness as defined in Paragraph2.1 include variations caused by type of steel, original surface condition, thickness of the steel, weld metal, mill or fabrication marks, heat treating, heat-affected zones, blastin

28、g abrasives, and differences because of blasting technique. 2.1.2 SSPC-VIS 13may be specified to supplement the written definition. In any dispute, the written definition set forth in this standard shall take precedence over reference photographs and comparators. Additional information on reference

29、photographs and comparators is in Paragraph A3 of Appendix A. _ Section 3: Associated Documents 3.1 The latest issue, revision, or amendment of the documents listed in Paragraph 3.3 in effect on the date of invitation to bid shall govern unless otherwise specified. 3.2 If there is a conflict between

30、 the requirements of any of the documents listed in Paragraph 3.3 and this standard, the requirements of this standard shall prevail. 3.3 Documents cited in the mandatory sections of this standard include: Document Title SSPC-AB 14Mineral and Slag Abrasives SSPC-AB 25Cleanliness of Recycled Ferrous

31、Metallic Abrasives SSPC-AB 36Ferrous Metallic Abrasives SSPC-SP 17Solvent Cleaning SSPC-VIS 1 Guide and Reference Photographs for Steel Surfaces Prepared by Dry Abrasive Blast Cleaning _ Section 4: Procedures Before Cleaning 4.1 Before blast cleaning, visible deposits of oil, grease, or other contam

32、inants shall be removed in accordance with SSPC-SP 1 or other agreed-upon methods. 4.2 Before blast cleaning, surface imperfections such as sharp fins, sharp edges, weld spatter, or burning slag should be removed from the surface to the extent required by the procurement documents (project specifica

33、tion). Additional information on surface imperfections is in Paragraph A4 of Appendix A. 4.3 If reference photographs or comparators are specified to supplement the written standard, the condition of the steel prior to blast cleaning should be determined before the blasting commences. Additional inf

34、ormation on reference photographs and comparators is in Paragraph A3 of Appendix A. NACE No. 3/SSPC-SP 6 2 NACE International _ Section 5: Blast Cleaning Methods and Operation 5.1 Clean, dry compressed air shall be used for nozzle blasting. Moisture separators, oil separators, traps, or other equipm

35、ent may be necessary to achieve this requirement. 5.2 Any of the following methods of surface preparation may be used to achieve a commercial blast cleaned surface: 5.2.1 Dry abrasive blasting using compressed air, blast nozzles, and abrasive. 5.2.2 Dry abrasive blasting using a closed-cycle, recirc

36、ulating abrasive system with compressed air, blast nozzle, and abrasive, with or without vacuum for dust and abrasive recovery. 5.2.3 Dry abrasive blasting using a closed-cycle, recirculating abrasive system with centrifugal wheels and abrasive. 5.3 Other methods of surface preparation (such as wet

37、abrasive blast cleaning) may be used to achieve a commercial blast cleaned surface by mutual agreement between those responsible for establishing the requirements and those responsible for performing the work. Information on the use of inhibitors to prevent the formation of rust immediately after we

38、t abrasive blast cleaning is in Paragraph A5 of Appendix A. _ Section 6: Blast Cleaning Abrasives 6.1 The selection of abrasive size and type shall be based on the type, grade, and surface condition of the steel to be cleaned, the type of blast cleaning system used, the finished surface to be produc

39、ed (cleanliness and surface profile roughness), and whether the abrasive will be recycled. 6.2 The cleanliness and size of recycled abrasives shall be maintained to ensure compliance with this standard. 6.3 The blast cleaning abrasive shall be dry and free of oil, grease, and other contaminants as d

40、etermined by the test methods found in SSPC-AB 1, SSPC-AB 2, and SSPC-AB 3. 6.4 Any limitations on the use of specific abrasives, the quantity of contaminants, or the degree of allowable embedment shall be included in the procurement documents (project specification) covering the work, because abras

41、ive embedment and abrasives containing contaminants may not be acceptable for some service requirements. Additional information on abrasive selection is in Paragraph A6 of Appendix A. 6.5 When a coating is specified, the cleaned surface shall be roughened to a degree suitable for the specified coati

42、ng system. Additional information on surface profile and the film thickness of coating applied over the surface profile is in Paragraphs A7 and A8 of Appendix A. _ Section 7: Procedures Following Blast Cleaning and Immediately Prior to Coating 7.1 Visible deposits of oil, grease, or other contaminan

43、ts shall be removed according to SSPC-SP 1 or another method agreed upon by those parties responsible for establishing the requirements and those responsible for performing the work. 7.2 Dust and loose residues shall be removed from prepared surfaces by brushing; blowing off with clean, dry air; vac

44、uum cleaning; or other methods agreed upon by those responsible for establishing the requirements and those responsible for performing the work. 7.2.1 The presence of toxic metals in the abrasives or coating being removed may place restrictions on the methods of cleaning permitted. The chosen method

45、 shall comply with all applicable regulations. 7.2.2 Moisture separators, oil separators, traps, or other equipment may be necessary to achieve clean, dry air. 7.3 After blast cleaning, any remaining surface imperfections (e.g., sharp fins, sharp edges, weld spatter, burning slag, scabs, slivers) sh

46、all be removed to the extent required by the procurement documents (project specification). Any damage to the surface profile resulting from the removal of surface imperfections shall be corrected to meet the requirements of Paragraph 6.5. Additional information on surface imperfections is in Paragr

47、aph A4 of Appendix A. 7.4 Immediately prior to coating application, the entire surface shall comply with the degree of cleaning specified in this standard. Any visible rust that forms on the surface of NACE No. 3/SSPC-SP 6 NACE International 3 the steel after blast cleaning shall be removed by recleaning the rusted areas before coating. Information on chemical contamination, rust-back (rerusti