GME 60410-2009 Adhesion of Organic Coatings after Storage in Warm Water - Delamination Test.pdf

《GME 60410-2009 Adhesion of Organic Coatings after Storage in Warm Water - Delamination Test.pdf》由会员分享，可在线阅读，更多相关《GME 60410-2009 Adhesion of Organic Coatings after Storage in Warm Water - Delamination Test.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Issue/Ausgabe: 3Date of Issue/Ausgabedatum: 01/09Prepared/Ausgefertigt: KMAPage ofSeite 1 von 3LBSP GME PVS 2 11/95ENGINEERINGSTANDARDSEUROPETEST SPECIFICATIONPRFVORSCHRIFTAdhesion of Organic Coatings after Storage in Warm Water - Delamination TestHaftung von organischen Beschichtungen nach Warmwass

2、erlagerung -Delaminationstest GME 60410Note: This standard may be applied only for current projects incl. Global Epsilon (37#). It is Supercededfor all future projects and replaced by GMW14704. /Hinweis: Diese Spezifikation darf nur noch fr laufende Projekte einschlielich Global Epsilon (37#)angewen

3、det werden und ist fr alle zuknftigen Projekte ungltig und ersetzt durch GMW14704.Revisions/nderungenDate/Datum Description/Beschreibung Approved/Genehmigt07.10.1996 was issue 1, date of issue 02/95 / clause 2, 3, 4 text reworked /war Ausgabe 1, Ausgabedatum 02/95 / Pos. 2, 3, 4 Text berarbeitet26/J

4、AN/2009 was issue 2, date of issue 10/96 / set to Supersededwar Ausgabe 2, Ausgabedatum 10/96 /Status auf Superseded“ gesetztApproved/GenehmigtJrg Kruse 26/JAN/2009 Gerald Badersbach 16/JAN/2009Adam Opel GmbHGME EngineeringRequirements EngineeringAdam Opel GmbHGME EngineeringDespite spot checks poss

5、ibly performed by the receiver, it is the suppliers responsibility that the delivered parts are in line with thesespecifications. Deliveries of samples, first off-tool parts and parts, the performance of which has been changed, must be accompanied by atest report showing the test results in terms of

6、 figures./Unbeschadet etwaiger durch den Abnehmer erfolgenden Stichprobenprfungen trgt der Lieferant die Verantwortung dafr, da diegelieferte Ware diese Vorschriften erfllt. Ein Prfbericht mit zahlenmigen Ergebnissen aus Prfungen der Lieferung selbst, ist bei jederBemusterung, Erstbelieferung und Au

7、sfhrungsnderung mitzugeben.ENGINEERINGSTANDARDSEUROPETEST SPECIFICATIONPRFVORSCHRIFT GME 60410Issue/Ausgabe: 3Date of Issue/Ausgabedatum: 01/09Prepared/Ausgefertigt: KMAPage ofSeite 2 von 3Reference is made to the following test method and material specification:GME 60401 Cross Hatch Test of Organic

8、 CoatingsB 0400540 Fabric Adhesive Tape, Grey1 Scope and ApplicationThis test method shall be used to determine the adhesion of organic coatings on metallic or non-metallicsubstrate after a storage in warm water.2 Test Piece and ConditioningTwo coated and clean body-sheet panels or plastic parts wit

9、h suitable dimensions without burrs shall beused as test pieces. The edges of the body-sheet panels shall be masked using adhesive tape (e. g. fabricadhesive tape B 0400540).3 ProcedureAt least 24 h after bake of the painting the painted test pieces shall be immersed in a bath of fullydemineralized

10、water. The temperature of the fully demineralized water (conductivity 30 scm-1) during theentire test shall be +63C 2 K.After 24 h the first test piece and after further 24 h the second test piece shall be removed from the bath andshall be dried with a clean cloth.After a regeneration time of 1 h 10

11、 min at +23C 5 K an Andrews Style Cross shall be scratched into thecoated surface until the substrate using a scriber without any auxiliary devices, e. g. ruler or similar. Each legshall be at least 50 mm long.After scratch an adhesion test of adhesive tape to GME 60401, clause 7.5 shall be performe

12、d. Deviatingfrom this test the adhesive tape shall be jerky peeled off twice from down to upwards.4 EvaluationAfter 48 h water storage at +63C 2 K and a regeneration time of 1 h 10 min at +23C 5 K are onlyalong the scratches separation of the painting or the paint coatings of 2 mm max. permissible.

13、No separationof painting or remaining areas permissible. Furthermore blistering or significant changes of colour tone arenot permissible. Insignificant changes of colour tone are permissible.5 Coding SystemThis test method shall be called up on part drawings, specifications, etc. as follows:“Adhesio

14、n of Organic Coatings to GME 60410“6 DeviationsDeviations from the requirements of this test method shall have been agreed upon. These requirementsshall be specified on component drawings, and defined on test reports etc.ENGINEERINGSTANDARDSEUROPETEST SPECIFICATIONPRFVORSCHRIFT GME 60410Issue/Ausgab

15、e: 3Date of Issue/Ausgabedatum: 01/09Prepared/Ausgefertigt: KMAPage ofSeite 3 von 3Folgendes Prfverfahren und folgende Materialvorschrift kommen in dieser Vorschrift zur Anwendung:GME 60401 Gitterschnittprfung von organischen BeschichtungenB 0400540 Stoffklebeband, grau1 Zweck und AnwendungDieses Pr

16、fverfahren dient der Ermittlung der Haftfhigkeit von organischen Beschichtungen aufmetallischem oder nichtmetallischem Untergrund nach einer Warmwasserlagerung.2 Probekrper und ProbenvorbehandlungAls Probekrper werden zwei beschichtete, gratfreie und saubere Karosseriebleche bzw. Kunststoffteile mit

17、geeigneten Abmessungen verwendet. Die Kanten der Karosseriebleche sind mit einem geeignetenKlebeband (z. B. Textilklebeband B 0400540) abzukleben.3 DurchfhrungDie lackierten Prfteile werden frhestens 24 h nach dem Einbrennen der Lackierung vollstndig in vollentsalztes Wasser (Leitfhigkeit 30 scm-1)

18、eingetaucht und bei +63C 2 K ausgelagert.Nach 24 h wird der erste Probekrper, nach weiteren 24 h der zweite Probekrper aus dem Wasserbadentnommen und mit einem sauberen Tuch trocken gewischt.Nach einer Regenerationszeit von 1 h 10 min bei +23C 5 K wird die Lackierung der Probekrper miteiner Reinadel

19、 bis zum Substrat kreuzfrmig (Andreaskreuz) angeritzt. Das Anritzen erfolgt ohneHilfsmittel, z. B. Lineal o. . Die Anritze sollen mindestens 50 mm lang sein.Nach dem Anritzen wird ein Klebebandhaftungstest entsprechend GME 60401, Pos. 7.5 durchgefhrt.Abweichend von diesem Test wird das Klebeband zwe

20、imal ruckartig von unten nach oben abgezogen.4 AuswertungNach 48 h Wasserlagerung bei +63C 2 K und anschlieender Regenerationszeit von 1 h 10 min bei+23C 5 K darf sich die Lackierung bzw. Lackschichten nur 2 mm max. entlang der Ritzspuren ablsen.Auf den brigen Flchen drfen keine Ablsungen auftreten.

21、 Unzulssig sind weiterhin Blasenbildung sowieein Farbtonumschlag. Leichte Farbtonnderungen sind zulssig.5 Angaben in ZeichnungenIn Zeichnungen, Vorschriften, usw. wird dieses Prfverfahren wie folgt angegeben:“Haftung von organischen Beschichtungen nach GME 60410“6 AbweichungenAbweichungen von den Bedingungen dieses Prfverfahrens mssen vereinbart werden. Diese Bedingungensind auf den Teilzeichnungen vorgeschrieben bzw. mssen in Prfzeugnissen, Berichten und dergl.angegeben werden.