FORD WSB-M3G209-A-2006 TAPE BUTYL PRESSURE SENSITIVE EXTRUDED TO BE USED WITH FORD WSS-M99P1111-A 《挤塑压敏丁基胶带 与标准FORD WSS-M99P1111-A一起使用 》.pdf

《FORD WSB-M3G209-A-2006 TAPE BUTYL PRESSURE SENSITIVE EXTRUDED TO BE USED WITH FORD WSS-M99P1111-A 《挤塑压敏丁基胶带 与标准FORD WSS-M99P1111-A一起使用 》.pdf》由会员分享，可在线阅读，更多相关《FORD WSB-M3G209-A-2006 TAPE BUTYL PRESSURE SENSITIVE EXTRUDED TO BE USED WITH FORD WSS-M99P1111-A 《挤塑压敏丁基胶带 与标准FORD WSS-M99P1111-A一起使用 》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 02 08 Revised Inserted 3.0; Deleted 3.1, 3.2, 3.3, 3.14, 4 1992 08 06 Released NBOOI10043054196 D. Henrickson K. Minnich B. Ferns Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 1 of 2 TAPE, BUTYL, PRESS

2、URE SENSITIVE, EXTRUDED WSB-M3G209-A 1. SCOPE The material defined by this specification is a pressure sensitive, extruded, elastomeric butyl tape with a release liner or specified laminate film on either side. 2. APPLICATION This specification was released originally for material used to bond plast

3、ic mesh to an instrument panel defroster grille. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 SPECIFIC GRAVITY 1.40 +/- 0.25 (ASTM D 792) 3.5

4、SOLIDS, min 95% (ASTM D 2834, except use 100 C for 3 h) (by weight) 3.6 ODOR, max 2 Rating (SAE J1351) 3.7 NEEDLE PENETRATION 10 - 90 1/10 mm (ASTM D 5, 100 g total load) 3.8 COLD FLEXIBILITY No cracking or delamination Test Method: Condition a 150 x 10 x 10 mm strip of material for 4 h at -20 +/- 2

5、 C and bend 180 around a 25 mm mandrel conditioned at the same temperature. 3.9 HEAT STABILITY No sagging or delamination Test Method: Bond a 150 x 150 mm sample of the material to each of two 300 x 300 mm production painted steel panels by applying a 1.5 kg load over the sample surface for 15 s. Su

6、spend one panel vertically and one inverted in an oven maintained at 120 +/- 2 C for 24 h. 3.10 ADHESION, min 3.6 N/cm Test specimens exposed to the following conditions shall meet the above minimum requirement or demonstrate cohesive failure of the tape material. ENGINEERING MATERIAL SPECIFICATIONW

7、SB-M3G209-APrinted copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 2 3.10.1 Original - 1 h after bonding 3.10.2 Original - 24 h after bonding 3.10.3 7 days at 90 +/- 2 C 3.10.4 7 days at 38 +/- 2 C and 95 - 100% relative humidity 3.10.5 2 cycles: 4 h at 90 +/- 2 C 4 h

8、 at 38 +/- 2 C and 95 - 100% relative humidity 16 h at 30 +/- 2 C 4 h at 90 +/- 2 C 16 h at 30 +/- 2 C Test Method: Bond 25 x 125 mm samples to production substrate materials by rolling once with a 2.2 kg roller (leaving a 25 mm length unbonded for attaching to test fixture). The material should be

9、backed with release paper or other specified film. Pull 90 to surface at a crosshead speed of 305 mm/minute within 1 h from completion of exposure. Condition samples for para 3.10.3 - 3.10.5 for 24 h at 23 +/- 2 C before exposing to environmental conditions. 3.11 BLOCKING RESISTANCE The material sha

10、ll separate easily with no tearing. Test Method: Ply 5 layers of material, with release liner, 100 x 100 mm and cover with an aluminum plate of the same size. Apply a load of 6 kg and place in an oven for 14 days at 35 +/- 2 C. Remove the weight and cover plate and examine plied samples for blocking

11、. 3.12 FOGGING (FLTM BO 116-03, 3 h at 100 C) Fog Number, min 60 The formation of droplets or coalescence into a clear film is cause for rejection. 3.13 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, max 100 mm/minute 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 STORAGE STABILITY This material shall maintain specification performance for 180 days when stored at temperatures not exceeding 35 C.