FORD ESE-M1C171-A-2010 GREASE - SILICONE TO BE USED WITH FORD WSS-M99P1111-A 《润滑脂 硅胶 与福特WSS-M99P1111-A 一起使用》.pdf

《FORD ESE-M1C171-A-2010 GREASE - SILICONE TO BE USED WITH FORD WSS-M99P1111-A 《润滑脂 硅胶 与福特WSS-M99P1111-A 一起使用》.pdf》由会员分享，可在线阅读，更多相关《FORD ESE-M1C171-A-2010 GREASE - SILICONE TO BE USED WITH FORD WSS-M99P1111-A 《润滑脂 硅胶 与福特WSS-M99P1111-A 一起使用》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2010 11 29 A - Revised See Summary of Revisions C. Mracna, NA 2008 10 20 A2 - N-STATUS A2 - Replaced by WSS-M13P14-A L. Schmalz, FNA 1976 08 17 Released CE3F-NC 774993-E1 Printed copies are uncontrolled Copyright 2010, Ford Global Technologies

2、, LLC Page 1 of 2 GREASE - SILICONE ESE-M1C171-A GREASE - SILICONE, CONTAINS FLUORESCENT DYE ESE-M1C171-A2 NOT TO BE USED FOR NEW DESIGN 1. SCOPE The materials defined by these specifications are non-melting, stiff, smooth homogeneous, heat stable silicone compounds for use in high tension electrica

3、l connections, ignition systems and electronics equipment. 2. APPLICATION These specifications were released originally for materials used in lubricating and giving an electrical sealant for spark plug and distributor boots in the ignition systems. 3. REQUIREMENTS 3.1 STANDARD REQUIRMENTS FOR PRODUC

4、TION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirments For Production Materials (WSS-M99P1111-A). 3.2 COLOR Light Gray A fluorescent dye shall be added to the ESE-M1C171-A2 (0.3% by weight, max). The dye shall fluoresce under ultraviolet light and shal

5、l be sufficiently intense to permit inspection in the plant. 3.3 BLEED 0.5% max (MIL-S-8660 B, para 3.12) 3.4 EVAPORATION 2.0% max (MIL-S-8660B, Fed-STD-791, Method 321.1) 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of t

6、hese specifications. Grease approved to these specifications should have the following typical properties. 4.1 UNWORKED PENETRATION, tenths of a millimeter See FMD* (ASTM D 217, DIN ISO 2137) *The ESE-M1C171-A specification has two approved sources with unique ranges. 4.2 VOLUME RESISTIVITY (MIL-S-8

7、660 B, para 3.7) At 177 C, min 1E11 OHM-cm ENGINEERING MATERIAL SPECIFICATIONESE-M1C171-A / A2Printed copies are uncontrolled Copyright 2010, Ford Global Technologies, LLC Page 2 of 2 4.3 DIELECTRIC CONSTANT (MIL-S-8660 B, para 3.8) At 1E3 Hz 3.1 max At 1E9 Hz 3.1 max 4.4 INTERFACE COMPATIBILITY (Re

8、quired by all 3 performance specs) 4.4.1 Chemical Attack to Painted Surfaces (FLTM BJ 126-01) Note: Not tested for initial application of this grease. Grease must be tested for chemical attack to painted surfaces for applications that come in contact with paint surfaces, ex. E-coat and powder coat.

9、4.4.2 Resistance to Stress Cracking (FLTM BO 127-03) Note: Not tested for initial application of this grease. Grease must be tested for resistance to stress cracking when used for additional applications that come in contact with polymers such as PC, ABS, PC+ABS, ASA or acrylic 4.4.3 Elastomer Compa

10、tibility (ASTM D 4289, 70 h, 100 C, DIN 53505, DIN 53504) Volume change Hardness change, max Tensile Strength change Note: Not tested for initial application of this grease. Grease must be tested for elastomer compatibility when used for additional applications that come in contact with elastomers.

11、Application specific elastomer should be used for testing instead of a reference elastomer. 5. SUMMARY OF REVISIONS 2010 11 29 Lot certification tests moved to requirements, all other requirements moved to general information. Added information on interface compatibility which are requirements in WSS-M13P13-A.