FORD ESB-M5G30-A2-2000 DEADENER MASTIC SHEET - HEAT EXPANDING《热膨胀型乳香脂板减声材料》.pdf

《FORD ESB-M5G30-A2-2000 DEADENER MASTIC SHEET - HEAT EXPANDING《热膨胀型乳香脂板减声材料》.pdf》由会员分享，可在线阅读，更多相关《FORD ESB-M5G30-A2-2000 DEADENER MASTIC SHEET - HEAT EXPANDING《热膨胀型乳香脂板减声材料》.pdf（6页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revision 2000 12 01 Revised Removed ESB-M5G30-A, updated & renumbered B. Xu 1985 03 14 AQ1-6000-2 Released ESB-M5G30-A2 1982 09 15 Released ESB-M5G30-A E83-S-734-S1-A1/CSM1 PR 904475-1 Printed copies are uncontrolled

2、Page 1 of 6 Copyright 2000, Ford Global Technologies, Inc. DEADENER, MASTIC SHEET - HEAT EXPANDING ESB-M5G30-A2 1. SCOPE The materials defined by this specification is heat expanding mastic sheet deadeners. 2. APPLICATION: ESB-M5G30-A2 specification was originally released for 1987 program applicati

3、ons that do not require testing per the flammability lot sampling plan. This material should be installed over electrocoated or primed metal surfaces before guide coat is applied. Proper expansion and bonding occurs during guide coat and enamel oven exposure at metal temperatures between 135 and 163

4、 C. To attain good adhesion, the exposure time must be greater than 8 minutes for the lower 135 C metal temperature. 3. REQUIREMENTS: Material specification requirements are to be used for initial qualification of materials. 3.1 QUALITY SYSTEM REQUIREMENTS Material suppliers and part producers must

5、conform to the Companys Quality System Requirements. 3.2 INFRARED SPECTROPHOTOMETRY AND/OR THERMAL ANALYSIS IR spectra and thermograms established for initial approval shall constitute the reference standard and shall be kept on file at the designated material laboratory. All samples shall produce I

6、R spectra and thermograms that correspond to the reference standard when tested under the same conditions. 3.3 CONDITIONING AND TEST CONDITIONS All test values indicated herein are based on material conditioned in a controlled atmosphere of 23 +/- 2 C and 50 +/- 5 % relative humidity for not less th

7、an 24 h prior to testing and tested under the same conditions unless otherwise specified. ENGINEERING MATERIAL SPECIFICATION ESB-M5G30-A2 Page 2 of 6 Copyright 2000, Ford Global Technologies, Inc. 3.4 UNCURED MATERIAL PROPERTIES 3.4.1 Thickness As specified on (ASTM D 461, 454 g load, drawing engine

8、ering 25 mm diameter foot) 3.4.2 Density 880-1440 kg/m3 (ASTM D 816) The density tolerance for any one supplier shall be +/- 16 kg/m3 based on the recorded density of his originally approved material. 3.4.3 Hardness, Durometer “A“ 75 - 90 (ASTM D 2240) 3.4.4 Specific Strength, min 2.2 MPa (ASTM D 46

9、1, Avg. of 5) 3.4.5 Tear Strength, min 26 kN/m (ASTM D 624, Die “C“, Avg. of 5) 3.4.6 Resistance to Blocking (SAE J912, 454 g wt. 15 min at 60 +/- 1 C) The material shall exhibit no blocking, and the specimens shall be easily separated by hand. 3.4.7 Flexibility No cracking 3.4.7.1 Test at 23 +/- 2

10、C 3.4.7.2 Test at -29 +/ -2 C Test Method: Condition two 50 x 150 x 1.8 mm samples at the temperatures specified for a minimum of 4 h. Slowly bend the sample 180 around a temperature conditioned 50 mm mandrel. 3.5 CURED MATERIAL PROPERTIES 3.5.1 Hardness, Durometer “A“ 60 - 75 (ASTM D 2240, heat cur

11、e material at 163 +/- 2 C metal temperature for 8 min) Save sample for weight loss test, para 3.4.3. ENGINEERING MATERIAL SPECIFICATION ESB-M5G30-A2 Page 3 of 6 Copyright 2000, Ford Global Technologies, Inc. 3.5.2 Volume Expansion (ASTM D 471) 3.5.2.1 Heat cured at 135 +/- 2 C 65 % metal temperature

12、 for 8 min, min 3.5.2.2 Heat cured at 163 +/- 2 C 152% metal temperature for 8 min, max 3.5.3 Weight Loss, max 5 % Test Method: Weight a 25 x 25 mm piece of the sample prepared in para 3.4 1. Determine the percent weight loss after exposure at 232 +/- 2 C for 1 h. 3.5.4 Moldability Must conform with

13、out material separation to all test panel configurations. Test Method: . Prepare two panel assemblies as shown in Figure 1. . Subject one assembly to 135 +/- 1 C metal temperature for 8 min and the other assembly to 163 +/- 1 C metal temperature for 8 min. . After heat exposure, visually examine mat

14、erial for moldability. 3.5.5 Sag Resistance, max 6 mm Test Method: . Clamp a 50 x 100 x 1.8 mm material sample on a 100 x 150 mm electrocoated panel as shown in Figure 2. . Scribe a line indicating the location of the materials bottom edge. . Position the panel in a supporting block at a 60 angle fr

15、om horizontal and expose at 177 +/- 2 C metal temperature for 20 min. . After exposure, permit the sample to reach room temperature and measure the material sag below the scribed line. . Save the sample for Heat Stability test, para 3.4.6. ENGINEERING MATERIAL SPECIFICATION ESB-M5G30-A2 Page 4 of 6

16、Copyright 2000, Ford Global Technologies, Inc. 3.5.6 Heat Stability No evidence of degradation, embrittlement, or excessive blistering after bonding mastic as indicated in para 3.4.5. 3.5.7 Bond Adhesion, min (FLTM BV 1-5) Heat cure sample on E-coated panel at 135 +/- 2 C for 30 min. 3.5.7.1 Origina

17、l 196 N 3.5.7.2 Aged 75 % of original Aging Cycle: . 4 h at 98 +/- 2% R.H. and 38 +/- 2 C . 4 h or overnight at -34 +/- 2 C . 4 h at 82 +/- 2 C . 1 h min at room temperature 3.6 SUPPLIERS RESPONSIBILITY All materials supplied to this specification must be equivalent in all characteristics to the mat

18、erial upon which approval was originally granted. Prior to making any changes to the material originally approved under this specification, whether or not such changes affect the materials ability to meet the specification requirements, the Supplier shall notify the affected Purchasing, and Material

19、s Engineering activities (with reasons) of the proposed changes. Upon notification of the Company, further instructions will be provided. Note: Suppliers should be prepared to provide test data and samples demonstrating compliance to this specification, if requested. Substance restrictions imposed b

20、y regulations or Company direction applies to the materials addressed by this document. The restrictions are identified in Restricted Substance Management Standard WSS-M99P9999-A1. ENGINEERING MATERIAL SPECIFICATION ESB-M5G30-A2 Page 5 of 6 Copyright 2000, Ford Global Technologies, Inc. 4. APPROVAL

21、OF MATERIALS Materials defined by this specification for direct supply to the Company must have prior approval. Certain materials subcontracted by part suppliers may also require prior approval. These include materials critical to the Companys business for regulatory, safety, environmental or compat

22、ibility requirements or contractual agreements. Suppliers desiring approval of their materials shall first obtain an expression of interest from Purchasing, Design or Materials Engineering activity. Upon request, the Supplier shall submit a completed copy of their laboratory test reports, signed by

23、a qualified and authorized representative of the test facility, demonstrating full compliance with all the requirements of this specification. 5. GENERAL INFORMATION: The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 SUBST

24、RATES ESB-M64J19 Electrocoat Primed Steel Panel: Primed per minimum specification requirements, steel nominal thickness 0.89 mm. 5.2 MECHANICAL CONVECTION OVEN The mechanical oven(s) used to cure the material shall be capable of obtaining 163 C metal temperature on body steel (0.89 mm) within 8-10 min. ENGINEERING MATERIAL SPECIFICATION ESB-M5G30-A2 Page 6 of 6 Copyright 2000, Ford Global Technologies, Inc. Figure 1 Figure 2