FORD ESB-M2D260-B-2009 POLYURETHANE FOAM SLAB - POLYESTER TYPE HEAT FORMABLE TO BE USED WITH FORD WSS-M99P1111-A 《可热成型的聚酯平板式聚氨酯泡沫 与标准FORD WSS-M99P1111-A一起使用 》.pdf

《FORD ESB-M2D260-B-2009 POLYURETHANE FOAM SLAB - POLYESTER TYPE HEAT FORMABLE TO BE USED WITH FORD WSS-M99P1111-A 《可热成型的聚酯平板式聚氨酯泡沫 与标准FORD WSS-M99P1111-A一起使用 》.pdf》由会员分享，可在线阅读，更多相关《FORD ESB-M2D260-B-2009 POLYURETHANE FOAM SLAB - POLYESTER TYPE HEAT FORMABLE TO BE USED WITH FORD WSS-M99P1111-A 《可热成型的聚酯平板式聚氨酯泡沫 与标准FORD WSS-M99P1111-A一起使用 》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2009 08 21 N-STATUS No Replacement Named C. Mracna, NA 2004 07 21 Revised Para 3.0 inserted; para 3.1, 3.14 & 4 deleted 1982 04 15 Released AN1-6000 3 Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 1 of 2 PO

2、LYURETHANE FOAM, SLAB - POLYESTER TYPE, ESB-M2D260-B HEAT FORMABLE NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a heat formable, slab, polyester type urethane foam. 2. APPLICATION This specification was released originally for material used as an anti-slip bac

3、king for molded carpeted throw-in mats, to prevent slipping. The foam should always be used as a bonded composite. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS

4、-M99P1111-A). 3.2 TENSILE STRENGTH, min 20 psi (ASTM D 1564) (138 kPa) 3.3 ELONGATION, min 280% (ASTM D 1564) 3.4 TEAR STRENGTH, Trapezoid, min 1.5 lb (6.7 N) (ASTM D 5733) 3.5 DENSITY, min 1.5 lb/ft3(ASTM D 1564, sample size 12 x 12 in (24 kg/m3) (300 x 300 mm) x thickness) 3.6 DETERIORATION (FLTM

5、BO 12-1) No crumbling, or evidence of deterioration after autoclave aging. Test Method: A specimen 2 x 8 in (50 x 200 mm) x thickness shall be subjected to steam autoclave aging for 3 h at 2.8 +/- 1.5 psi (19.3 +/- 10.3 kPa) and/or 104 +/- 5 C, then dried 3 h at 104 +/- 3 C in a convection oven foll

6、owed by 2 h conditioning at room temperature. 3.7 MILDEW RESISTANCE No evidence of mildew growth or deterioration after 7 days exposure in a humidity cabinet controlled to 100% relative humidity at 38 C. 3.8 ODOR No offensive odor before, during, or after the deterioration tests of para. 3.6 and 3.7

7、. ENGINEERING MATERIAL SPECIFICATIONESB-M2D260-B Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 2 of 2 3.9 CELL STRUCTURE Homogeneous, fine celled structure, approximately 50 cells/inch (25 mm). 3.10 THICKNESS, min 0.09 in (2.3 mm) or as specified in the drawing 3

8、.11 FLAMMABILITY, max 4 in (101 mm)/min (FLTM BN 24-2, without the lot sampling plan and tested as a bonded composite) In addition, when tested as a bonded composite from a mat assembly, the test specimen shall not exhibit any flashing or sudden flaming on either surface in excess of the above maxim

9、um value. 3.12 FLAMMABILITY TEST PROGRAM Materials, portions of components, and composites governed by this specification must also comply with the requirements of ES-D3AB-11014-AA. 3.13 ADDITIONAL REQUIREMENTS The fabricated mat assemblies employing the ESB-M2D260-B foam must also meet the requirements of the applicable mat performance specification.