EN 2434-003-2010 en Aerospace series - Paints and varnishes - Two component cold curing polyurethane finish - Part 003 Flexible and high fluid resistance for interior《航空航天系列 涂料和清漆 .pdf

《EN 2434-003-2010 en Aerospace series - Paints and varnishes - Two component cold curing polyurethane finish - Part 003 Flexible and high fluid resistance for interior《航空航天系列 涂料和清漆 .pdf》由会员分享，可在线阅读，更多相关《EN 2434-003-2010 en Aerospace series - Paints and varnishes - Two component cold curing polyurethane finish - Part 003 Flexible and high fluid resistance for interior《航空航天系列 涂料和清漆 .pdf（14页珍藏版）》请在麦多课文档分享上搜索。

1、raising standards worldwideNO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBSI Standards PublicationBS EN 2434-003:2010Aerospace series Paints andvarnishes Two componentcold curing polyurethane finishPart 003: Flexible and high fluid resistancefor interiorBS EN 2434-003:2010 BR

2、ITISH STANDARDNational forewordThis British Standard is the UK implementation of EN 2434-003:2010.The UK participation in its preparation was entrusted to TechnicalCommittee ACE/65/-/3, Paints for Aerospace Purposes.A list of organizations represented on this committee can beobtained on request to i

3、ts secretary.This publication does not purport to include all the necessaryprovisions of a contract. Users are responsible for its correctapplication. BSI 2010ISBN 978 0 580 69556 8ICS 49.040Compliance with a British Standard cannot confer immunity fromlegal obligations.This British Standard was pub

4、lished under the authority of theStandards Policy and Strategy Committee on 30 November 2010.Amendments issued since publicationDate Text affectedBS EN 2434-003:2010EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 2434-003 September 2010 ICS 49.040 English Version Aerospace series - Paints and v

5、arnishes - Two component cold curing polyurethane finish - Part 003: Flexible and high fluid resistance for interior Srie arospatiale - Peintures et vernis - Peinture de finition polyurthane, deux composants polymrisant temprature ambiante - Partie 003: Flexibilit et haute rsistance aux fluides pour

6、 application en intrieur Luft- und Raumfahrt - Beschichtungsstoffe - Zweikomponenten- Polyurethan-Decklack, kalthrtend - Teil 003: Elastisch und medienbestndig fr Innen This European Standard was approved by CEN on 6 February 2010. CEN members are bound to comply with the CEN/CENELEC Internal Regula

7、tions which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN Management Centre or to any CEN member. This E

8、uropean Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as the official versions. CEN members are the

9、 national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Sw

10、itzerland and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG Management Centre: Avenue Marnix 17, B-1000 Brussels 2010 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. N

11、o. EN 2434-003:2010: EBS EN 2434-003:2010EN 2434-003:2010 (E) 2 Contents Page Foreword 3Introduction .41 Scope 42 Normative references 43 Terms and definitions .54 Classification 55 Batch release and qualification testing .55.1 Batch release testing .55.2 Qualification tests 5BS EN 2434-003:2010EN 2

12、434-003:2010 (E) 3 Foreword This document (EN 2434-003:2010) has been prepared by the Aerospace and Defence Industries Association of Europe - Standardization (ASD-STAN). After enquiries and votes carried out in accordance with the rules of this Association, this Standard has received the approval o

13、f the National Associations and the Official Services of the member countries of ASD, prior to its presentation to CEN. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by March 2011, and conflicting

14、national standards shall be withdrawn at the latest by March 2011. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. According to the CE

15、N/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Li

16、thuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. BS EN 2434-003:2010EN 2434-003:2010 (E) 4 Introduction This European Standard is part of a series of EN non-metallic materials standards for aerospace ap

17、plications. The general organisation of this series is described in EN 4385. This European Standard is a level 3 document as defined in EN 4385. Definition for subcase numbering in Table 2 to Table 5, is given in EN 7000-9. 1 Scope This European Standard specifies the requirements for a two componen

18、t polyurethane finish, in a limited range of colours, to be applied over a primer for interior aerospace applications, offering flexibility and high resistance to fluid attack. The properties specified in this European Standard are obtained on defined aluminium alloy test pieces prepared in accordan

19、ce with EN 3837 and EN 23270 and painted with primer to EN 2435-003. The ability of the material to be used for a specific application (e.g. alternative substrate, alternative primer, specific drying conditions etc.) shall be determined by supplementary tests to confirm that the requirements of this

20、 standard are met. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 2334

21、, Aerospace series Chromic-sulphuric acid pickle of aluminium and aluminium alloys EN 2435-003, Aerospace series Paints and varnishes Corrosion resistant chromated two component cold curing primer Part 003: High corrosion and fluid resistance EN 2379, Aerospace series Fluids for assessment of non-me

22、tallic materials 1)EN 3837, Aerospace series Paints and varnishes Nature and method for surface preparation of test pieces in aluminium alloys 1)EN 3840, Aerospace series Pieces paints and varnishes Technical specification EN 4385, Aerospace series Non-metallic materials General organisation of stan

23、dardisation Links between types of standards 1)EN 7000-9, Aerospace series Non-metallic materials Rules for the drafting and presentation of material standards Part 9: Paints and varnishes 1) EN ISO 1513, Paints and varnishes Examination and preparation of samples for testing (ISO 1513:1992) EN ISO

24、3696, Water for analytical laboratory use Specification and test methods (ISO 3696:1987) 1)Published as ASD-STAN Prestandard at the date of publication of this standard BS EN 2434-003:2010EN 2434-003:2010 (E) 5 EN 23270, Paints, varnishes and their raw materials Temperatures and humidities for condi

25、tioning and testing (ISO 3270:1984) 3 Terms and definitions For the purposes of this document, the following terms and definitions apply. 3.1 Gloss finish 80 units measured at 60 according to EN 3840 test 27 4 Classification Not applicable. 5 Batch release and qualification testing 5.1 Batch release

26、 testing For batch acceptance the tests marked with an * in Table 1 to Table 5 shall be performed. 5.2 Qualification tests For product qualification, all tests mentioned in this standard, in the Table 1 to Table 5, shall be performed. BS EN 2434-003:2010EN 2434-003:2010 (E) 6 Table 1 General Require

27、ments 1.001 Material description Two component cold curing polyurethane coating 1.002 Formulation Base a base containing an hydroxyl functional resin, solvents and pigments. Activator a polyisocyanate activator solution Thinner if required 1.003 Form and method of production These components shall b

28、e mixed in simple whole number proportions, by volume or by weight, in accordance with the manufacturers instructions. 1.004 Technical specification See EN 3840 1.009 Application and use Dry film thickness of (30 5) m 1.010 Storage stability See EN 3840 1.011 Shelf life See EN 3840 1.013 Processing

29、conditions EN 23270 for 7 d before testing unless otherwise specified. Finish is applied to the primer following drying of the primer for 4 h to 16 h. 1.093 Quality assurance See EN 3840 1.094 Designation Polyurethane Finish EN 2434-03 1.095 Packaging See EN 3840 1.096 Identification marking See EN

30、3840 1.097 Flash point See EN 3840 1.098 Health and safety See EN 3840 Table 2 Physical and chemical characteristics 2.014 Condition 1 EN ISO 1513 6 As received in original container * 7 Shall be free from extraneous matter and show no skinning, gelling, hard settlement or other defect which will pr

31、event satisfactory application to produce a defect free film. 2.011 Application properties and finish 1 None 3 EN 3837 A22024-T3 clad4 EN 3837 Process A or B bEN 2334 Pickle or CAA 5 EN 2435-03 primer + finish to this standard * 7 Paint film shall show an opaque even finish, free from runs, sags, wr

32、inkling, pinholing or other defect. 2.034 Sedimentation rating EN 3840 1 Test 5 6 base + activator + thinner 7 ml V = 30 after 4 h 2.012 Pot life EN 3840 1 Test 20 followed by Test 8 aor Test 9 a6 base + activator + thinner * 7 s or Pa s 2 x initial value after 4 h 2.035 Fineness of grind EN 3840 1

33、Test 10 6 base + activator * 7 m Gloss finish 15, other gloss levels 30 (continued) BS EN 2434-003:2010EN 2434-003:2010 (E) 7 Table 2 Physical and chemical characteristics (concluded) 2.029 Viscosity EN 3840 1 Test 8 1or Test 9 16 base + activator + thinner 7 s or Pa s 10 % 2, 32.027 Non volatile ma

34、tter EN 3840 1 Test 1 7 base activator % 2 2,3 2 2, 32.027 Volatile organic compound (VOC) content EN 3840 1 Test 49 6 base + activator + thinner 7 g/l reference value 2,32.057 Density EN 3840 1 Test 3 6 base * 7 g/cm3 2 2,3, 52.057 Density hydrometer EN 3840 1 Test 4 6 activator + thinner 7 activat

35、or thinner * g/cm3 2 2,3 2 2, 32.036 Flash point EN 3840 1 Test 7 7 base activator thinner C reference value 3 reference value 3 reference value 32.041 Surface dry time EN 3840 1 Test 21 3 EN 3837 A22024-T3 clad4 EN 3837 Process A or B 2EN 2334 Pickle or CAA 5 EN 2435-03 primer + finish to this stan

36、dard 6 EN 232707 h 1 42.041 Drying time print-free EN 3840 1 Test 22 3 EN 3837 A22024-T3 clad4 EN 3837 Process A or B 2EN 2334 Pickle or CAA 5 EN 2435-03 primer + finish to this standard 6 EN 23270 7 h 6 2.041 Through dry time EN 38401 Test 23 3 EN 3837 A22024-T3 clad4 EN 3837 Process A or B 2EN 233

37、4 Pickle or CAA 5 EN 2435-03 primer + finish to this standard 6 EN 23270 * 7 h 16 2.999 Notes 1 Test 8 shall be used for non-thixotropic paints and test 9 for thixotropic paints. 2 The deviation is that compared to the reference value. 3 The reference value is that established during qualification.

38、4 Unless otherwise specified. 5 Test could also be used for activator and thinner if required. BS EN 2434-003:2010EN 2434-003:2010 (E) 8 Table 3 Physico - chemical characteristics 3.084 or 3.053 Colour EN 3840 1 Test 30 3 EN 3837 A22024-T3 clad4 EN 3837 Process A or B bEN 2334 Pickle or CAA 5 EN 243

39、5-03 primer + finish to this standard 6 EN 23270 * 7 E shall match the colour specified 3.088 or 3.083 Gloss 60 EN 3840 1 Test 27 3 EN 3837 A22024-T3 clad4 EN 3837 Process A or B bEN 2334 Pickle or CAA 5 EN 2435-03 primer + finish to this standard 6 EN 23270 * 7 Gloss units shall match the gloss spe

40、cified BS EN 2434-003:2010EN 2434-003:2010 (E) 9 Table 4 Mechanical characteristics 4.082 Adhesion EN 3840 1 Test 24 3 EN 3837 A22024-T3 clad4 EN 3837 Process A EN 2334 Pickle 5 EN 2435-03 primer + finish to this standard 6 EN 23270 7 Classification 0 4.076 Scratch resistance EN 3840 1 Test 29 3 EN

41、3837 A22024-T3 clad4 EN 3837 Process A or B bEN 2334 Pickle or CAA 5 EN 2435-03 primer + finish to this standard 6 EN 23270 * 7 1 500 g primer not exposed 4.082 Bend test cylindrical mandrel EN 3840 1 Test 25 6 mm mandrel 3 EN 3837 A62024-T3 clad4 EN 3837 Process A EN 2334 Pickle 5 EN 2435-03 primer

42、 + finish to this standard 6 ( 55 2) C 7 No detachment or cracking (10 x magnification) 4.080 Impact resistance EN 3840 1 Test 26 3,8 mm spacing 3 EN 3837 A22024-T3 clad4 EN 3837 Process A or B bEN 2334 Pickle or CAA 5 EN 2435-03 primer + finish to this standard 6 EN 23270 7 no detachment or crackin

43、g 4.082 Slow deformation EN 3840 1 Test 46 3 EN 3837 A22024-T3 clad4 EN 3837 Process A EN 2334 Pickle 5 EN 2435-03 primer + finish to this standard 6 EN 23270 * 7 4 mm no detachment or cracking BS EN 2434-003:2010EN 2434-003:2010 (E) 10 Table 5 Environmental characteristics 5.102 Heat EN 3840 1 Test

44、 38 3 EN 3837 A22024-T3 clad4 EN 3837 Process A EN 2334 Pickle 5 EN 2435-03 primer + finish to this standard 6 150 C 24 h 7 Test 46 2,5 mm (EN 23270) 5.102 Cold EN 3840 1 Test 38 3 EN 3837 A22024-T3 clad4 EN 3837 Process A EN 2334 Pickle 5 EN 2435-03 primer + finish to this standard 6 40 C 24 h 7 Te

45、st 46 4 mm (EN 23270) 5.100 Humidity EN 3840 1 Test 37 3 EN 3837 A22024-T3 clad4 EN 3837 Process A EN 2334 Pickle 5 EN 2435-03 primer + finish to this standard 6 (40 2) C, (100 5) % r.h. 500 h 7 No blistering, softening, lifting or other film defect Test 24 1 5.101 Resistance to fluids aEN 3840 1 Te

46、st 35 3 EN 3837 A22024-T3 clad4 EN 3837 Process A or B 2EN 2334 Pickle or CAA 5 EN 2435-03 primer + finish to this standard, panel scribed to substrate immediately before testing. 6 A tri-n-butyl phosphate to EN 2379 G2 for 1000h (EN 23270) 1B tri-n-butyl phosphate to EN 2379 G2 for 1000h at (70 2)

47、C 17 No blistering, softening, lifting or other film defect Test 29 1200 g primer not exposed 5.100 Water behaviour EN 3840 1 Test 34 3 EN 3837 A22024-T3 clad4 EN 3837 Process A EN 2334 Pickle 5 EN 2435-03 primer + finish to this standard, panel scribed to substrate immediately before testing. 6 wat

48、er to EN ISO 3696 Grade 2 for 168 h at (40 2) C 7 No blistering, softening, lifting or other film defect Test 24 Classification 1 Test 29 1500 g primer not exposed 5.999 Notes 1 Additional fluids shall be subject of agreement between the manufacturer and the user. 2Pre-treatments specified shall be

49、used for qualification testing. For batch testing pre-treatment shall be the subject of agreement between manufacturer and user.This page deliberately left blankBSI is the independent national body responsible for preparing British Standardsand other standards-related publications, information and services. It presents the UK view on standards in Europe and at the international lev