1、 MIL-DTL-1608J 3 July, 2001 SUPERSEDING MIL-H-1608H 25 November, 1991 DETAILED SPECIFICATION HOOKS, TENT This specification is approved for use by all Departments and Agencies of the Department of Defense. 1. SCOPE 1.1 Scope. This specification covers steel wire tent hooks. 1.2 Classification. (see

2、6.2) Type I Triangle eye (hook in line with center of eye). Size 1 - 1 inch Size 2 - 1 inch Type III - Square eye size 1 inch Type IV - Trapezoid eye size 1 inch Type V - Diamond eye size 1 inch Type VI - Diamond eye, shackle type size 1 inch Beneficial comments (recommendations, additions, deletion

3、s, clarifications) and any pertinent data which may be of use in improving this document should be addressed to: Defense Supply Center Philadelphia, Clothing and Textiles Directorate, Attn: DSCP-CNR, 700 Robbins Ave., Philadelphia, PA 19111-5096 by using the Standardization Document Improvement Prop

4、osal (DD Form 1426) appearing at the end of this document or by letter. AMSC N/A FSC 8340 INCH-POUND Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-DTL-1608J 2 2. APPLICABLE DOCUMENTS *2.1 General. The documents listed in this section are specif

5、ied in sections 3 and 4 of this specification. This section does not include documents cited in other sections of this specification or recommended for additional information or as examples. While every effort has been made to ensure the completeness of this list, document users are cautioned that t

6、hey must meet all specified requirements documents cited in sections 3 and 4 of this specification, whether or not they are listed. 2.2 Government documents. 2.2.1 Specifications, standards, and handbooks. The following specifications, standards, and handbooks form a part of this document to the ext

7、ent specified herein. Unless otherwise specified, the issues of these documents are those listed in the issue of the Department of Defense Index of Specifications and Standards (DODISS) and supplement thereto, cited in the solicitation (see 6.2). SPECIFICATIONS FEDERAL TT-E-485 - Enamel, Semigloss,

8、Rust Inhibiting STANDARDS FEDERAL FED-STD-595 - Colors (Unless otherwise indicated. copies of federal and military specifications, standards, and handbooks are available from the Defense Automated Printing Service, Bldg. 4D (DPM-DODSSP), 700 Robbins Avenue, Philadelphia, PA 19111-5094.) *2.2.2 Other

9、 Government documents, drawings, and publications. The following other Government documents, drawings, and publications form a part of this document to the extent specified herein. Unless otherwise specified, the issues are those cited in the solicitation. DRAWINGS U.S. ARMY BIOLOGICAL & CHEMICAL CO

10、MMAND 5-4-166 - Hooks, Tent, Assembly and Details 5-4-355 - Hooks, Tent (Copies of drawings are available from the U. S. Army Biological and Chemical Command, ATTN: SSCNC-EMSS, NATICK, MA 01760-5017.) *2.3 Non-Government publications. The following document(s) form a part of this document to the ext

11、ent specified herein. Unless otherwise specified the issues of the documents which are DoD adopted are those listed in the issue of the DODISS cited in the solicitation. Unless otherwise specified, the issues of documents not listed in the DODISS are the issues of the documents cited in the solicita

12、tion (see 6.2). Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-DTL-1608J 3 AMERICAN SOCIETY FOR TESTING AND MATERIALS (ASTM) ASTM-A-153 - Zinc Coating (Hot Dip) on Iron and Steel Hardware ASTM-A-575 - Merchant Quality Hot Rolled, Carbon Steel Ba

13、rs ASTM-A-853 - Steel Wire, Carbon, for General Use ASTM-B-633 - Electrodeposited Coatings of Zinc on Iron and Steel ASTM-D-1005 - Measurement of Dry Film Thickness of Organic Coatings ASTM-D-2092 - Preparation of Zinc-Coated Steel Surfaces for Painting (Applications for copies of referenced documen

14、ts should be addressed to the American Society for Testing and Materials, 100 Barr Harbor Drive, West Conshohocken, PA 19426-2959.) *2.4 Order of precedence. In the event of a conflict between the text of this specification and the references cited herein, the text of this specification takes preced

15、ence. Nothing in this specification, however, supersedes applicable laws and regulations unless a specific exemption has been obtained. 3. REQUIREMENTS *3.1 First article. When specified (see 6.2), a sample shall be subjected to first article inspection (see 4.2 and 6.2). *3.2 Materials and componen

16、ts. Materials and components shall be as specified herein and on the applicable drawings. Materials and components not definitely specified shall be of the quality normally used by the manufacturer provided the completed item complies with all the provisions of this document. 3.2.1 Wire, steel, carb

17、on. Carbon steel wire shall conform to steel number 1010-1020, bare finish, annealed in process, of ASTM-A-853. 3.2.2 Steel bar, carbon. Carbon steel wire shall conform to grade M 1010-M 1020 of ASTM-A-575. *3.2.3 Enamel. Enamel shall conform to type I or II, composition G or L, as applicable, olive

18、 drab color No. 24087 of TT-E-485. 3.3 Construction. Construction of the tent hooks shall conform to Drawings 5-4-166 and 5-4-355 and as specified herein. 3.3.1 Fabrication. 3.3.1.1 Type I, III, IV and V tent hooks. The body for the type I, III, IV and V tent hooks shall be fabricated from steel wir

19、e specified in 3.2.1. The ends of the formed wire body shall be securely welded as shown on Drawing 5-4-355 and all welds shall be complete, sound and uniform. The type I, size 1 tent hook shall be capable of withstanding a load of 125 pounds minimum in tension without any evidence of cracked or fra

20、ctured weld or permanent distortion of the wire body when tested as specified in 4.4.5. The type I, size 2 and types III, IV and V tent hooks shall be capable of withstanding a load of 500 pounds minimum in tension without any evidence of cracked or fractured weld or permanent distortion of the wire

21、 body when tested as specified in 4.4.5. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-DTL-1608J 4 3.3.1.2 Type VI tent hook. The hook portion shall be fabricated of steel wire specified in 3.2.1. The upper and lower shackles shall be fabricate

22、d of steel bar specified in 3.2.2. The welding of the hook to the upper shackle shall be complete, sound and uniform. After enameling, the tent hook shall be assembled with bolt and the self locking nut shall be drawn up finger-tight. 3.3.2 Deburring. All burrs, sharp edges, and rough spots shall be

23、 removed prior to application of the finish. 3.4 Finish. 3.4.1 Zinc coating. After complete fabrication of the tent hooks and prior to assembly of the type VI tent hook, all tent hooks and components (except bolt and nut) shall be zinc coated. The zinc coating shall conform to either ASTM A 153 with

24、 preparation for painting in accordance with method A, crystalline zinc phosphate conversion treatment of ASTM D 2092 or to type IV, thickness classification Fe/Zn12 of ASTM B 633. As an alternate, use chromate conversion type II of ASTM B 633. 3.4.2 Enameling. All zinc coated surfaces of tent hooks

25、 and components (except bolt and nut) shall be completely coated with enamel specified in 3.2.3. The coating shall be a smooth, uniform, dry film without runs, blisters, wrinkles, area of thin or no film, scratch or scuff, foreign matter imbedded in finish, and wet or tacky paint. 3.4.3 Epoxy powder

26、 coating. As an alternate to the zinc coating and enameling specified in 3.4.1 and 3.4.2 the surfaces shall be prepared and coated as follows: a. The tent hooks shall be prepared for coating by mechanical means. The surfaces shall be thoroughly cleaned and uniformly textured by blasting using 80 gri

27、t aluminum oxide. Prepared surfaces shall be kept clean during subsequent handling. Handling shall be conducted by clean gloved hands or by clean implements. The surfaces shall be epoxy coated within 8 hours after sand blasting. b. The finished coating shall be camouflage green 483 conforming to col

28、or chip 34094 of FED-STD-595 and finished with an electrodeposited epoxy powder coating. The epoxy coating shall conform to epoxy coatings produced by H. B. Fuller Co., or the OBrien corporation, or equal (see 6.6 and 6.8). c. The electrodeposited epoxy powder coating shall be baked on in accordance

29、 with commercial practices. The thickness of the coating shall be .003 + .001 inch. d. The final coating shall be smooth and uniform in appearance and shall be free from wrinkles, streaks, corrosion, blistering, peels, cracks or sags. 3.5 Marking for identification. The hooks shall be marked with th

30、e manufacturers identification in accordance with industry practice. 3.6 Workmanship. All welding shall be free from , pits, slag inclusion, porosity, crack, flash and excess flux deposit. The finished tent hooks shall be clean and free of dirt and grease. Threads and finish of bolt and nut shall be

31、 free from damage, i.e., nut shall not bind on bolt. The tent hooks shall conform to the quality of product established by this specification. The occurrence of defects shall not exceed the applicable acceptable quality levels. *3.7 Recycled, recovered, or environmentally preferable materials. Recyc

32、led, recovered, or environmentally preferable materials should be used to the maximum extent possible provided that the material meets or exceeds the operational and maintenance requirements, and promotes economically advantageous life cycle costs. Provided by IHSNot for ResaleNo reproduction or net

33、working permitted without license from IHS-,-,-MIL-DTL-1608J 5 4. VERIFICATION 4.1 Classification of inspections. The inspection requirements specified herein are classified as follows: a. First article inspection (see 4.2). b. Conformance inspection (see 4.3). 4.2 First article inspection. When a f

34、irst article is required (see 6.2) the tent hooks it shall be examined for the defects listed in 4.3.4 and 4.3.5 and tested for the strength characteristic specified in 4.6.1. 4.3 Inspection. 4.3.1 Conformance inspection. Sampling for inspection shall be as specified in the contract or purchase orde

35、r. 4.3.2 Component and material inspection. In accordance with 4.1, components and materials shall be inspected in accordance with all the requirements of referenced documents unless otherwise excluded, amended, modified or qualified in this specification or applicable purchase document. 4.3.3 In-pr

36、ocess inspection. Inspection shall be made of the operations and requirements listed in Table I to establish conformance with the specified requirements. Whenever nonconformance is noted, correction shall be made to the items affected and the operations. Items which cannot be corrected shall be remo

37、ved from production. The government reserves the right to exclude from consideration for acceptance any material for which in-process inspection has indicated nonconformance. Table I. In-process inspection. - Requirement or operation Requirement paragraph - Removal of burrs, sharp edges and rough sp

38、ots prior to finishing 3.3.2 Zinc coating of tent hooks and components (except bolt and nut) prior to enameling 3.4.1 - *4.3.4 End item visual examination. The end item shall be examined for the defects listed in Table II. The lot size shall be expressed in units of frame sections of one type only.

39、The sample unit shall be one completely fabricated frame section. The inspection level shall be II. TABLE II. Classification of defects Classification Examine Defect Major Minor Finish Color of finish is not as specified 201 Not finished 101 Coating not smooth or uniform 202 Finish is not dry, i.e.,

40、 wet or tacky to touch 102 Run, wrinkle or blister 203 Area of no film exposing bare metal 103 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-DTL-1608J 6 TABLE II. Classification of defects Classification Examine Defect Major Minor Finish Area o

41、f thin film exposing zinc coating 204 Any scratch or foreign matter embedded in finish 205 Construction Any component not as specified or missing, e.g., & workman- shackle, bolt or nut 104 ship Type IV tent hook not assembled or the self- locking nut has not been drawn up finger-tight 206 Threads or

42、 finish of bolt or nut is damaged, i.e., nut binds on bolt 207 Not clean, i.e., has dirt or grease 208 Burr, sharp edge, or rough spot 209 Welding Missing where required 105 Not type specified 106 Incomplete or not sound 107 Not uniform 210 Pits, slag inclusion or porous 211 Crack or fracture 108 Fl

43、ash or excess flux deposit has not Been removed 212 Marking for Missing, illegible, incorrect or incomplete 213 identification - *4.3.5 End item dimensional examination. Examination shall be made of the end item for compliance with the dimensions on the drawings. Only those dimensions that can be ev

44、aluated without damaging or disassembling the end items shall be examined. Any dimension not within the specified tolerance shall be classified as a defect. The lot size shall be expressed in units of tent hooks of one type only. The sample unit shall be one tent hook. The inspection level shall be

45、S-2. *4.3.5.1 Epoxy coating thickness examination (when applicable). The end item shall be examined for thickness of the epoxy coating in accordance with ASTM-D-1005. Three observations shall be made per sample unit. Any epoxy coating with a minimum thickness not as specified in 3.4.3 shall be class

46、ified as a defect. The lot size shall be expressed in units of tent hooks of one type offered for inspection at one time. The sample unit shall be one tent hook. The inspection level shall be S-2. *4.4 End item testing. Types I, III, IV and V tent hooks shall be tested for strength as specified in 4

47、.6.1. The inspection level shall be S-2. The requirement shall be applicable to the individual unit. There shall be one determination per sample unit for types I, III and IV hooks and two determinations per sample unit for type V hooks. *4.5 Packaging examination. The fully packaged end items shall be examined for marking, materials, workmanship and content defects. 4.6 Methods of inspection 4.6.1 Strength test. The tent hooks shall be tested as shown on Drawing 5-4-355. The load rate shall not exceed 1000 pounds per minute. T