BS EN ISO 11339-2010 Adhesives - T-peel test for flexible-to-flexible bonded assemblies《粘合剂 挠性材料-挠性材料粘合组件的T-剥离试验》.pdf

《BS EN ISO 11339-2010 Adhesives - T-peel test for flexible-to-flexible bonded assemblies《粘合剂 挠性材料-挠性材料粘合组件的T-剥离试验》.pdf》由会员分享，可在线阅读，更多相关《BS EN ISO 11339-2010 Adhesives - T-peel test for flexible-to-flexible bonded assemblies《粘合剂 挠性材料-挠性材料粘合组件的T-剥离试验》.pdf（12页珍藏版）》请在麦多课文档分享上搜索。

1、BS EN ISO11339:2010ICS 83.180NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBRITISH STANDARDAdhesives T-peel testfor flexible-to-flexiblebonded assembliesThis British Standardwas published under theauthority of the StandardsPolicy and StrategyCommittee on 31 May2010. BSI 2010I

2、SBN 978 0 580 65169 4Amendments/corrigenda issued since publicationDate CommentsBS EN ISO 11339:2010National forewordThis British Standard is the UK implementation of EN ISO 11339:2010.It supersedes BS EN ISO 11339:2005 which is withdrawn.The UK participation in its preparation was entrusted to Tech

3、nicalCommittee PRI/52, Adhesives.A list of organizations represented on this committee can be obtained onrequest to its secretary.This publication does not purport to include all the necessary provisionsof a contract. Users are responsible for its correct application.Compliance with a British Standa

4、rd cannot confer immunityfrom legal obligations.EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN ISO 11339 February 2010 ICS 83.180 Supersedes EN ISO 11339:2005English Version Adhesives - T-peel test for flexible-to-flexible bonded assemblies (ISO 11339:2010) Adhsifs - Essai de pelage en T dasse

5、mblages colls flexible sur flexible (ISO 11339:2010) Klebstoffe - T-Schlprfung fr geklebte Verbindungen aus flexiblen Fgeteilen (ISO 11339:2010) This European Standard was approved by CEN on 11 February 2010. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate t

6、he conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN Management Centre or to any CEN member. This European Standard exists

7、 in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as the official versions. CEN members are the national standards bod

8、ies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Ki

9、ngdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG Management Centre: Avenue Marnix 17, B-1000 Brussels 2010 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN ISO 11339:2010: E

10、BS EN ISO 11339:2010EN ISO 11339:2010 (E) 3 Foreword This document (EN ISO 11339:2010) has been prepared by Technical Committee ISO/TC 61 “Plastics“ in collaboration with Technical Committee CEN/TC 193 “Adhesives” the secretariat of which is held by AENOR. This European Standard shall be given the s

11、tatus of a national standard, either by publication of an identical text or by endorsement, at the latest by August 2010, and conflicting national standards shall be withdrawn at the latest by August 2010. Attention is drawn to the possibility that some of the elements of this document may be the su

12、bject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN ISO 11339:2005. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implemen

13、t this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switze

14、rland and the United Kingdom. Endorsement notice The text of ISO 11339:2010 has been approved by CEN as a EN ISO 11339:2010 without any modification. BS EN ISO 11339:2010INTERNATIONAL STANDARD ISO 11339:2010(E) ISO 2010 All rights reserved 1Adhesives T-peel test for flexible-to-flexible bonded assem

15、blies SAFETY STATEMENT Persons using this document should be familiar with normal laboratory practice, if applicable. This document does not purport to address all of the safety problems, if any, associated with its use. It is the responsibility of the user to establish appropriate safety and health

16、 practices and to ensure compliance with any regulatory conditions. It is recognized that some of the materials permitted in this document may have a negative environmental impact. As technological advances lead to more acceptable alternatives for such materials, they will be eliminated to the great

17、est extent possible. At the end of the test, care should be taken to dispose of all waste in an appropriate manner in accordance with local regulations. 1 Scope This International Standard specifies a T-peel test for the determination of the peel strength of an adhesive by measuring the peeling forc

18、e of a T-shaped bonded assembly of two flexible adherends. This test procedure does not provide design information. NOTE This method was originally developed for use with metal adherends but other, flexible, adherends may also be used. 2 Normative references The following referenced documents are in

19、dispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. ISO 291, Plastics Standard atmospheres for conditioning and testing ISO 10365, Adhesives D

20、esignation of main failure patterns ISO 17212, Structural adhesives Guidelines for the surface preparation of metals and plastics prior to adhesive bonding 3 Terms and definitions For the purposes of this document, the following terms and definitions apply. 3.1 peel strength force per unit width nec

21、essary to bring an adhesive joint to the point of failure and/or maintain a specified rate of failure by means of a stress applied in a peeling mode ISO 472:1999 BS EN ISO 11339:2010ISO 11339:2010(E) 2 ISO 2010 All rights reserved3.2 flexible adherend adherend having dimensions and physical properti

22、es that permit bending through any angle up to 90 without breaking or cracking 4 Principle For the T-peel test for a flexible-to-flexible assembly, the force is applied to the unbonded ends of the specimen. The angle between the bond line and the direction of the applied force is not fixed. Adherend

23、s are separated at an approximately steady rate from an open edge of a prepared bond so that separation occurs progressively along the bond line. 5 Apparatus 5.1 Tensile-testing machine1), capable of maintaining a predetermined constant crosshead rate (preferred rate 100 mm/min). It shall be provide

24、d with a suitable self-aligning grip to hold the specimen. Each set of jaws of the grip shall firmly engage the outer 25 mm of the unbonded ends of the flexible adherends. The grip and attachments shall be constructed in such a way that they will move into alignment with the specimen as soon as the

25、force is applied. The machine shall produce a chart that can be read in terms of millimetres of crosshead movement as a function of the applied force. The machine shall permit the measurement and recording of the applied force with an accuracy of 2 %. All equipment shall be calibrated regularly. It

26、is recommended that a clamping device with low inertia be used. 5.2 Device for measuring thickness, with an accuracy of 0,01 mm, or a means of checking the thickness to that tolerance. 6 Test specimens 6.1 Test specimens of the dimensions shown in Figure 1 shall be prepared, either individually or c

27、ut from bonded laminates. Test specimens shall consist of two flexible adherends properly prepared and bonded together. 6.2 Surface treatment shall be such as to obtain optimum strength in the bonded assembly. The preparation of the surface shall be in accordance with ISO 17212, and details of the p

28、reparation shall be stated in the test report. The adhesive shall be applied in accordance with the manufacturers instructions to obtain an optimum bond with minimum variation; the procedure used shall be reported in the test report. NOTE Direct comparison of different adhesives can be made only whe

29、n specimen construction, adherend materials and dimensions, and test conditions are identical. 6.3 The thickness of the flexible adherends shall be reported. The preferred thicknesses are 0,5 mm 0,02 mm for steel (type XES)2)and 0,7 mm 0,02 mm or 0,5 mm 0,02 mm for aluminium (type 5754, H111)3)unles

30、s otherwise specified. 1) See for instance ISO 58934. 2) XES = low-carbon steel: composition (in mass %) C = 0,05, Cr 0,01, Cu = 0,013, Mn = 0,018, Al = 0,064, Ni = 0,02; Youngs modulus E = 210 GPa; initial yield stress y= 150 MPa; strain-hardening coefficient = 0,4. 3) See ISO 2091and ISO 21073. BS

31、 EN ISO 11339:2010ISO 11339:2010(E) ISO 2010 All rights reserved 36.4 Test specimens shall be cut from the bonded panels (see Figure 1) by a method that is not deleterious to the bond. The width shall be either a) 25 mm (preferred width) or b) any other convenient width, provided that the test equip

32、ment is suitably adapted and the width is stated in the test report. NOTE The method of cutting the specimens is dependent upon the adherend and adhesive compositions and the specimen width tolerance specified in Figure 1. Milling and bandsawing are two methods commonly used for this purpose. 6.5 Be

33、fore the test is carried out, the test specimen shall be bent in a manner that does not affect the bonded joint. The two unbonded ends of the flexible adherends shall be bent in opposite directions until each end is perpendicular to the bonded assembly, to form a T-shaped specimen (see Figure 1) for

34、 clamping in the grips of the test machine. 6.6 The number of specimens tested shall be not less than five. 6.7 The specimens shall be conditioned and tested in one of the standard laboratory atmospheres specified in ISO 291, which shall be reported in the test report. 7 Procedure On the at least fi

35、ve specimens, using the device described in 5.2, measure with an accuracy of 0,01 mm the average thickness of the adhesive layer after formation of the bond. Clamp each unbonded end of the T-shaped specimen in the grips of the test machine, taking care that the end is accurately aligned between the

36、grips so that the tension applied is distributed evenly across the width. If one adherend is more flexible than the other, attach the less flexible adherend to the moveable grip. Set the machine in motion at the selected separation rate and record the force applied versus the distance of grip separa

37、tion. NOTE A separation rate of 100 mm/min is generally used for metals and 10 mm/min for other adherends. Continue the test until at least 150 mm of the bonded length is separated. Note the type of failure in accordance with ISO 10365. BS EN ISO 11339:2010ISO 11339:2010(E) 4 ISO 2010 All rights res

38、ervedDimensions in millimetres Key 1 specimen cut at panel edge 2 specimen 3 direction of pull aBonded. bUnbonded. Figure 1 Panel before cutting and individual specimen after cutting 8 Expression of results Determine from the recorded curve, for about 100 mm of peeling (disregarding the first 25 mm

39、and the last 25 mm), the average, maximum and minimum peeling force, in newtons, required to separate the adherends. The average force shall be determined from the curve by drawing the best straight line, or by using other suitable means if a more accurate result is required. Record the average, max

40、imum and minimum peeling forces for each individual specimen. From the peeling forces thus recorded, calculate the average, maximum and minimum peel strengths for each individual specimen, in newtons per 100 mm of specimen width. 9 Precision The precision of this test method is not known because int

41、erlaboratory data are not available. When interlaboratory data are obtained, a precision statement will be added at the following revision. BS EN ISO 11339:2010ISO 11339:2010(E) ISO 2010 All rights reserved 510 Test report The test report shall include the following information: a) a reference to th

42、is International Standard; b) all information necessary for complete identification of the adhesive tested, including type, source, manufacturers code number, batch or lot number, form, etc.; c) all information necessary for complete identification of the adherends, including the nature and the thic

43、kness of the material, the width and the surface preparation; d) a description of the bonding process, including the method of application of the adhesive, the drying or precuring conditions (where applicable) and the curing time, temperature and pressure; e) the average thickness of the adhesive la

44、yer after formation of the bond; f) a complete description of the specimen, whether individual or cut from a panel, including the dimensions and construction of the specimen, the conditions used for cutting out individual specimens, the number of test panels represented and the number of individual

45、specimens (when edge specimens are tested, they shall be designated “edge specimens”); g) the conditioning procedure used prior to testing and the test atmosphere; h) the crosshead separation rate; i) the method for determining the average peeling force; j) the average, maximum and minimum peeling f

46、orce values, in newtons, for each individual specimen (edge specimens shall be reported separately); k) the calculated average, maximum and minimum peel strength values, in newtons per 100 mm of specimen width, for each specimen (edge specimens shall be reported separately); l) the type of failure i

47、n accordance with ISO 10365. BS EN ISO 11339:2010ISO 11339:2010(E) 6 ISO 2010 All rights reservedBibliography 1 ISO 209, Aluminium and aluminium alloys Chemical composition 2 ISO 472:1999, Plastics Vocabulary 3 ISO 2107, Aluminium and aluminium alloys Wrought products Temper designations 4 ISO 5893,

48、 Rubber and plastics test equipment Tensile, flexural and compression types (constant rate of traverse) Specification BS EN ISO 11339:2010This page has been intentionally left blank BS EN ISO11339:2010BSI GroupHeadquarters 389Chiswick High Road,London, W4 4AL, UKTel +44 (0)20 8996 9001Fax +44 (0)20

49、8996 - British Standards InstitutionBSI is the independent national body responsible for preparing BritishStandards. It presents the UK view on standards in Europe and at theinternational level. It is incorporated by Royal Charter.RevisionsBritish Standards are updated by amendment or revision. Users of