BS 5S 82-1976 Specification - 4% nickel-chromium-molybdenum case-hardening steel billets bars forgings and parts (1320-1520 MPa)《含4%镍铬钼表面硬化钢方坯、棒材、锻件和零件规范(1320-1520MPa)》.pdf

《BS 5S 82-1976 Specification - 4% nickel-chromium-molybdenum case-hardening steel billets bars forgings and parts (1320-1520 MPa)《含4%镍铬钼表面硬化钢方坯、棒材、锻件和零件规范(1320-1520MPa)》.pdf》由会员分享，可在线阅读，更多相关《BS 5S 82-1976 Specification - 4% nickel-chromium-molybdenum case-hardening steel billets bars forgings and parts (1320-1520 MPa)《含4%镍铬钼表面硬化钢方坯、棒材、锻件和零件规范(1320-1520MPa)》.pdf（8页珍藏版）》请在麦多课文档分享上搜索。

1、BRITISH STANDARD AEROSPACE SERIES BS 5S 82:1976 (Superseding BS 4S 82) Incorporating Amendment Nos. 1, 2 and 3 Specification for 4%ni cke l-ch ro miu m- molybdenum case-hardening steel billets, bars, forgings and parts (1 3201 520 MPa) UDC 629.7:669.15 24 26 28:669.14.018.298.2 BS 5S 82:1976 This Br

2、itish Standard, having been prepared under the direction of the Aerospace Industry Standards Committee, was published under the authority of the Executive Board on 31 March 1976 BSI 30 May 2003 The following BSI references relate to the work on this standard: Committee reference ACE 15 Draft for com

3、ment 74/74367 DC and draft for approval ISBN 0 580 08799 9 Amendments issued since publication Amd. No. Date Comments 2217 February 1977 3532 August 1981 14161 30 May 2003 Indicated by a sidelineBS 5S 82:1976 BSI 30 May 2003 i Contents Page Foreword ii 1 Inspection and testing procedure 1 2 Manufact

4、ure 1 3 Chemical composition 1 4 Surface dressing 1 5 Condition 1 6 Heat treatment 2 7 Mechanical properties 2BS 5S 82:1976 ii BSI 30 May 2003 Foreword This publication does not purport to include all the necessary provisions of a contract. Users are responsible for its correct application. Complian

5、ce with a British Standard does not of itself confer immunity from legal obligations. Summary of pages This document comprises a front cover, an inside front cover, pages i and ii, pages 1 and 2, an inside back cover and a back cover. The BSI copyright notice displayed in this document indicates whe

6、n the document was last issued. Sidelining in this document indicates the most recent changes by amendment.BS 5S 82:1976 BSI 30 May 2003 1 NOTE The specified chemical composition, heat treatment and tensile properties comply with AECMA Recommendation FE-PL79 (for material heat treated to a tensile s

7、trength of 1 3201 520 MPa). 1 Inspection and testing procedure 1.1 General. This British Standard shall be used in conjunction with the relevant sections of the latest issue of BS S 100 as follows: 1.2 Sulphur printing or deep etching tests. One sample shall be taken from each ingot for sulphur prin

8、ting or deep etching tests. 1.3 Ultrasonic examination. The material shall be ultrasonically tested in accordance with BS S 100, Annex B. 2 Manufacture The material shall be manufactured by an electric process. 3 Chemical composition The steel shall contain: 4 Surface dressing The material shall be

9、overall dressed. 5 Condition 5.1 The material shall be supplied in the appropriate condition stated below: 5.2 Parts shall be supplied finally heat treated. Bars for machining delivered in other than the finally heat treated condition sections 1 and 2 Forging stock and billets and bars for subsequen

10、t working sections 1 and 5 Forgings sections 1 and 6 Parts finally heat treated after machining sections 1 and 7 Element % min. max. Carbon 0.14 0.18 Silicon 0.15 0.40 Manganese 0.25 0.55 Phosphorus 0.025 Sulphur 0.020 Chromium 1.0 1.4 Molybdenum 0.20 0.30 Nickel 3.8 4.3 Designation Form Condition o

11、f supply S82B Black bars for machining Normalized and softened S82D Bright bars for machining Normalized and softened and subsequently cold drawn, cold rolled, machined or ground S82A Forging stock and billets and bars for subsequent working Softened S82C Forgings Normalized and softenedBS 5S 82:197

12、6 2 BSI 30 May 2003 6 Heat treatment 6.1 Normalizing treatment. The normalizing treatment shall consist of heating uniformly at a temperature between 910 C and 930 C. 6.2 Softening treatment. The softening treatment shall consist of heating uniformly at a temperature of not less than 630 , followed

13、by cooling in air. 6.3 Final heat treatment 6.3.1 Except as provided in 6.3.2, the final heat treatment shall consist of the following: a) Carburizing or blank carburizing. Heat uniformly at a temperature between 880 C and 930 C. b) Hardening. Heat at a temperature of 825 10 C, followed by cooling i

14、n oil. NOTE A sub-zero treatment at 60 C to 80 C is recommended before tempering. c) Tempering. Heat at a temperature of 190 5 C, followed by cooling in air. 6.3.2 Alternatively to 6.3.1, the final heat treatment of parts shall be agreed between the manufacturer and the purchaser. NOTE If an alterna

15、tive heat treatment is used for parts, it may be necessary to agree alternative mechanical properties. 7 Mechanical properties 7.1 Tensile test at room temperature and impact test. The mechanical properties obtained from test pieces, machined from test samples reduced, where applicable, to 20 mm dia

16、meter or square before heat treatment, shall be as follows: 7.2 Hardness test. The hardness of material heat treated in accordance with 6.1 and 6.2, or 6.2, as appropriate, shall be not greater than 277 HB. 0.2 % proof stress Tensile strength Elongation Reduction of area Izod impact min. min. max. m

17、in. min. min. MPa MPa MPa % % ft lbf 1 030 1 320 1 520 8 35 25blankBS 5S 82:1976 BSI 389 Chiswick High Road London W4 4AL BSI British Standards Institution BSI is the independent national body responsible for preparing British Standards. It presents the UK view on standards in Europe and at the inte

18、rnational level. It is incorporated by Royal Charter. Revisions British Standards are updated by amendment or revision. Users of British Standards should make sure that they possess the latest amendments or editions. It is the constant aim of BSI to improve the quality of our products and services.

19、We would be grateful if anyone finding an inaccuracy or ambiguity while using this British Standard would inform the Secretary of the technical committee responsible, the identity of which can be found on the inside front cover. Tel: +44 (0)20 8996 9000. Fax: +44 (0)20 8996 7400. BSI offers members

20、an individual updating service called PLUS which ensures that subscribers automatically receive the latest editions of standards. Buying standards Orders for all BSI, international and foreign standards publications should be addressed to Customer Services. Tel: +44 (0)20 8996 9001. Fax: +44 (0)20 8

21、996 7001. Email: ordersbsi-. Standards are also available from the BSI website at http:/www.bsi-. In response to orders for international standards, it is BSI policy to supply the BSI implementation of those that have been published as British Standards, unless otherwise requested. Information on st

22、andards BSI provides a wide range of information on national, European and international standards through its Library and its Technical Help to Exporters Service. Various BSI electronic information services are also available which give details on all its products and services. Contact the Informat

23、ion Centre. Tel: +44 (0)20 8996 7111. Fax: +44 (0)20 8996 7048. Email: infobsi-. Subscribing members of BSI are kept up to date with standards developments and receive substantial discounts on the purchase price of standards. For details of these and other benefits contact Membership Administration.

24、 Tel: +44 (0)20 8996 7002. Fax: +44 (0)20 8996 7001. Email: membershipbsi-. Information regarding online access to British Standards via British Standards Online can be found at http:/www.bsi- Further information about BSI is available on the BSI website at http:/www.bsi-. Copyright Copyright subsis

25、ts in all BSI publications. BSI also holds the copyright, in the UK, of the publications of the international standardization bodies. Except as permitted under the Copyright, Designs and Patents Act 1988 no extract may be reproduced, stored in a retrieval system or transmitted in any form or by any

26、means electronic, photocopying, recording or otherwise without prior written permission from BSI. This does not preclude the free use, in the course of implementing the standard, of necessary details such as symbols, and size, type or grade designations. If these details are to be used for any other purpose than implementation then the prior written permission of BSI must be obtained. Details and advice can be obtained from the Copyright & Licensing Manager. Tel: +44 (0)20 8996 7070. Fax: +44 (0)20 8996 7553. Email: copyrightbsi-.