ASTM D6492-1999(2003) Standard Practice for Detection of Hexavalent Chromium On Zinc and Zinc Aluminum Alloy Coated Steel《锌及锌 铝合金涂覆钢上六价铬检测的标准实施规程》.pdf

《ASTM D6492-1999(2003) Standard Practice for Detection of Hexavalent Chromium On Zinc and Zinc Aluminum Alloy Coated Steel《锌及锌 铝合金涂覆钢上六价铬检测的标准实施规程》.pdf》由会员分享，可在线阅读，更多相关《ASTM D6492-1999(2003) Standard Practice for Detection of Hexavalent Chromium On Zinc and Zinc Aluminum Alloy Coated Steel《锌及锌 铝合金涂覆钢上六价铬检测的标准实施规程》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D 6492 99 (Reapproved 2003)Standard Practice forDetection of Hexavalent Chromium On Zinc and Zinc/Aluminum Alloy Coated Steel1This standard is issued under the fixed designation D 6492; the number immediately following the designation indicates the year oforiginal adoption or, in the ca

2、se of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This practice can be used to detect the presence ofhexavalent chromium on galvanized and

3、zinc/aluminum alloycoated steel surfaces. Hexavalent chromium-bearing treat-ments (passivates) can be applied to coated steels to preventstorage stain. While passivated 55 % aluminum-zinc alloycoated steel is commonly painted, passivated galvanized steelis not. Chrome passivation may interfere with

4、the successfulpretreatment of galvanized steel, as well as contaminatecleaning and pretreatment baths on a coil coating line.1.2 The amount of hexavalent chromium that will cause theindicator to produce a discernible pink color is in the range of0.5 parts per million dissolved in the indicator solut

5、ion. It ispossible that a coated steel surface that produces a negativeresult does have chromium on the surface. If a material thatyields a negative result is suspected of having chromium on thesurface, instrumental methods should be used. Chrome depos-its of 1 mg/ft2can be easily missed by analytic

6、al instrumentssuch as the scanning electron microscope with energy disper-sive x-ray analysis (EDXA) capability. Auger electron spec-troscopy (AES) or electron spectroscopy for chemical analysis(ESCA) can identify chemical species present in the levelsrequired for adequate detection. Stripping the m

7、etallic coatingand analyzing for chrome by atomic absorption or inductivelycoupled plasma can also give reliable results in detecting thepresence of chrome.1.3 This practice is designed to be a qualitative means ofscreening chrome passivated coils from those which are notchrome passivated.1.4 Some c

8、hromium-free passivates are being used com-mercially. Although these products will test negative forhexavalent chromium, they may interfere with cleaning andpretreating. Chromium bearing passivates that contain filmforming constituents such as acrylic resins are also beingcommercially applied. The r

9、eaction of these products to thespot test will vary. Abrading the surface with emery paper willimprove the likelihood of reliable detection. This technique isnot recommended for acrylic resin containing passivationtreatments.1.5 The values stated in SI units are to be regarded as thestandard. The va

10、lues given in parentheses are for informationonly.1.6 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of r

11、egulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2D 2092 Guide for Treatment of Zinc-coated (GalvanizedSteel Surfaces) for PaintingD 5723 Practice for Determination of Chromium TreatmentWeight on Metal Substrates by X-Ray Fluorescence3. Apparatus3.1 The following material

12、s will be required to perform thestripping procedure:3.1.1 Dark colored or Brown Polyethylene Wash Bottle,(500 mL) or brown glass dropper bottle.3.1.2 Test Specimens, which may be cut panels or coil stock.4. Reagents4.1 The following chemical reagents are required to performthis procedure:4.1.1 1,5-

13、Diphenylcarbohydrazide.4.1.2 Acetone.4.1.3 Ethanol, 85 %.4.1.4 Phosphoric Acid.4.1.5 Distilled Water.1This practice is under the jurisdiction of ASTM Committee D01 on Paint andRelated Coatings, Materials, and Applications and is the direct responsibility ofSubcommittee D01.53 on Coal Coated Metal.Cu

14、rrent edition approved Dec. 1, 2003. Published December 2003. Originallyapproved in 1999. Last previous edition approved in 1999 as D 6492 99.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards vol

15、ume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.5. Preparation of Indicator Solution5.1 Combine 25 mL acetone with 25 mL ethanol in asuitable container.

16、 Add 0.5 g 1,5-diphenylcarbohydrazide andallow to dissolve completely. Vigorous agitation may berequired to effect complete dissolution. Slowly add 25 mL85 % phosphoric acid to 25 mL distilled water. Add the dilutedphosphoric acid to the 1,5-diphenylcarbohydrazide solutionand mix well.5.2 The indica

17、tor solution has a shelf life of approximately6 h when exposed to light. Shelf life can be extended to severaldays if the solution is kept refrigerated. Discard the solution ifit becomes discolored.6. Procedure6.1 Remove oil and dirt from the metal surface to be tested.A thorough solvent wipe is gen

18、erally sufficient. Apply severaldrops of the indicator to the material to be tested, or use a washbottle to apply a small amount of solution onto outer and innerwraps of a coil. Samples of non-passivated material should betested side-by-side as controls. Any color change perceived inthe indicator on

19、 the material being tested should be comparedto the controls.7. Evaluation7.1 A pink color will develop if hexavalent chromium ispresent. The color can appear within 30 s for material with apassivation less than 1 week old. For material up to 1 monthold, the reaction time should be extended to 30 mi

20、n. If thematerial is older than 1 month, the reaction time should beextended to 1 h. The color that is achieved and the timerequired for the color change to occur depends upon age of themetal being tested, the amount of chromium on the surface, andthe age of the indicator. Heavier hexavalent chrome

21、concen-trations will give a darker pink color.7.2 Even heavy chrome passivation (greater than 3 mg/ft2chrome ) can yield a light pink color or no color change at all.The detection of hexavalent chrome by this practice requireshexavalent chrome ions to be dissolved by the indicatorsolution. It is com

22、mon for chrome passivation films to declinein hexavalent chrome content over time. The temperature andhumidity conditions under which the coils are stored willgreatly affect the residual hexavalent chrome concentration aswell as its solubility.8. Keywords8.1 diphenylcarbohydrazide; hexavalent chromi

23、um; passi-vate; passivation; steel; zinc; zinc/aluminumASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent

24、rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either

25、for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hear

26、ing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).D 6492 99 (2003)2