ASTM D6298-2013 3125 Standard Specification for Fiberglass Reinforced Styrene-Butadiene-Styrene (SBS) Modified Bituminous Sheets with a Factory Applied Metal Surface《带工厂涂敷金属表面的纤维玻璃.pdf

《ASTM D6298-2013 3125 Standard Specification for Fiberglass Reinforced Styrene-Butadiene-Styrene (SBS) Modified Bituminous Sheets with a Factory Applied Metal Surface《带工厂涂敷金属表面的纤维玻璃.pdf》由会员分享，可在线阅读，更多相关《ASTM D6298-2013 3125 Standard Specification for Fiberglass Reinforced Styrene-Butadiene-Styrene (SBS) Modified Bituminous Sheets with a Factory Applied Metal Surface《带工厂涂敷金属表面的纤维玻璃.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D6298 13Standard Specification forFiberglass Reinforced Styrene-Butadiene-Styrene (SBS)Modified Bituminous Sheets with a Factory Applied MetalSurface1This standard is issued under the fixed designation D6298; the number immediately following the designation indicates the year oforiginal

2、 adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers fiberglass reinforced modifiedbituminous

3、sheet materials that use styrene-butadiene-styrene(SBS) thermoplastic elastomer as the primary modifier and aresurfaced with a factory applied continuous metal foil. Thesematerials are intended for use in the fabrication of multiple plyroofing and waterproofing membranes and flashings.1.2 This speci

4、fication is intended as a material specificationonly. Questions regarding the suitability of the specific roofconstructions or application techniques are beyond the scope ofthis specification.1.3 The specified tests and property limits are intended toestablish minimum properties. In place roof syste

5、m designcriteria such as fire resistance, field strength, impact/punctureresistance, material compatibility, uplift resistance, and others,are factors beyond the scope of this specification.1.4 The values stated in SI units are to be regarded as thestandard. The inch-pound units given in parentheses

6、 are forinformation only.1.5 The following precautionary statement pertains to thetest method portion only, Section 8 of this Specification: Thisstandard does not purport to address all of the safety concerns,if any, associated with its use. It is the responsibility of the userof this standard to es

7、tablish appropriate safety and healthpractices and determine the applicability of regulatory limita-tions prior to use.2. Referenced Documents2.1 ASTM Standards:2D1079 Terminology Relating to Roofing and WaterproofingD5147 Test Methods for Sampling and Testing ModifiedBituminous Sheet MaterialD7051

8、Test Method for Cyclic Thermal Shock of SBS-Modified Bituminous Roofing Sheets with Factory-Applied Metal Surface3. Terminology3.1 Definitions For definitions of terms used in thisspecification, refer to Terminology D1079.4. Materials and Manufacture4.1 In the process of manufacture, the fiberglass

9、reinforce-ment is impregnated and coated on both sides with a SBSmodified bituminous coating. The sheet is surfaced with acontinuous metal foil except for any selvage. The SBS modi-fied bituminous coating shall be permitted to be compoundedwith a mineral stabilizer.4.2 The metal surfacing shall be o

10、mitted on any selvage. Toprevent sticking in the roll, the reverse side and any selvageshall be permitted to be covered with a fine mineral surfacingor any other surfacing that will not interfere with adhesion orbonding of the lap during application.4.3 Foil-faced products intended for use where the

11、 applica-tion is to be by heat welding (torching) shall meet the minimumback surface coating requirement found in Table 1.5. Physical Properties5.1 The sheet material shall conform to the physical prop-erties prescribed in Table 1.5.2 The finished product shall not crack nor be so sticky asto cause

12、other material damage upon being unrolled at producttemperatures between 4 and 60C (40 and 140F).1This specification is under the jurisdiction of ASTM Committee D08 onRoofing and Waterproofing and is the direct responsibility of Subcommittee D08.04on Felts, Fabrics and Bituminous Sheet Materials.Cur

13、rent edition approved May 1, 2013. Published June 2013. Originallyapproved in 1998. Last previous edition approved in 2005 as D6298 05E01. DOI:10.1520/D6298-13.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of

14、 ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States16. Dimensions, Mass, and Permissible Variations6.1 The width of the roll shall be as ag

15、reed between thepurchaser and the seller and shall not vary more than 61%.6.2 The area of the roll shall not be less than as agreed uponbetween the purchaser and seller.6.3 The selvage width shall be within 66.4 mm (14 in.) ofthe nominal value and shall not be less than 57 mm (2.25 in.).7. Workmansh

16、ip, Finish, and Appearance7.1 The finished product shall be completely coated in acontinuous, unbroken film and shall be free of such defects asholes, ragged or untrue edges, breaks, cracks, tears,protrusions, delaminations, and indentations.7.2 The metal surface shall be uniform in surface andtextu

17、re, that is, free from such defects as holes, breaks tears,protrusions, and indentations (except for intended factoryembossing pattern).7.3 The line of demarcation between the metal-surfacedportion of the weather side and any selvage shall be straightand parallel to the edge of the sheet.7.4 When un

18、rolled on a smooth plane, the sheet shall be flat,straight, and true so the lap will mate with the adjacent sheetwithin the tolerance of the lap without wrinkles, buckles, orfishmouths.8. Sampling and Test Methods8.1 Sample the material and determine the properties de-scribed in this specification i

19、n accordance with Test MethodD5147 unless otherwise indicated.8.2 Cyclic Thermal ShockSample and test the material inaccordance with Test Method D7051.9. Inspection9.1 InspectionInspection shall be in accordance with therequirements of this specification.9.2 Inspection AlternativesAlternative inspec

20、tion require-ments shall be determined by and as agreed upon between thepurchaser and supplier.10. Rejection and Resubmittal10.1 Failure to ConformFailure to conform to any of therequirements as stated in this specification constitutes groundsfor rejection.10.2 Rejection RedressThe supplier shall ha

21、ve the right toinspect the rejected materials. The supplier and the purchasershall agree to the quantity of rolls deemed unacceptable. Thesupplier shall then have the right to submit the same number ofnew rolls as replacement.11. Packaging and Package Marking11.1 The finished material shall be furni

22、shed as rolls. Therolls shall be securely wrapped to prevent shifting of materialand to permit normal handling. There shall be no manufactur-ing splices in the roll, and there shall be no more than twopieces.11.2 Unless otherwise agreed upon by the seller andpurchaser, each product package shall be

23、plainly marked withthe suppliers name, the product brand, the ASTM designation,the net coverage area, and the type bitumen if not evident in thelabel name of the product.12. Keywords12.1 glass reinforcement; metal foil surface; modified bitu-minous sheet; styrene-butadiene-styrene (SBS); thermoplast

24、icelastomerTABLE 1 Properties of SBS Modified Bituminous Sheet MaterialsSurfaced With a Factory Applied Metal FoilDescriptionThickness, min 3.4 (134)mm (mils)Net Mass per Unit 3.9 (80)Area, min kg/m2(lb/100 ft2)Back Surface Coating Thickness 1 (40)min, mm (mils)Peak Load, MD and XMD, 18C (0F) 28.0 (

25、160)min, kN/m (lbf/in.) 23C (73F) 14.9 (85)Elongation at Peak Load, 18C (0F) 3MD and XMD, min, % 23C (73F) 5Ultimate Elongation, 23C (73F) 25MD and XMD, min, %Tensile-Tear Strength,MD and XMD, min kN (lbf) 0.53 (120)Low Temperature Flexibility 18 (0)max, C (F)DimensionalStability, max, % 0.2Compound

26、 Stability, 107 (225)min passing, C (F)Cyclic Thermal Shock, 2 (0.2)max, % (mm/m)Water Absorption, 1.0max, %Moisture Content, 0.2max, %D6298 132ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of t

27、his standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five y

28、ears andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical comm

29、ittee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19

30、428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).D6298 133