《ASTM D2860 D2860M-2018 Standard Test Method for Adhesion of Pressure-Sensitive Tape to Fiberboard at 90&xb0 Angle and Constant Stress《在90&xb0下压敏胶带与纤维板粘合的标准试验方法 角度和恒定应力》.pdf》由会员分享,可在线阅读,更多相关《ASTM D2860 D2860M-2018 Standard Test Method for Adhesion of Pressure-Sensitive Tape to Fiberboard at 90&xb0 Angle and Constant Stress《在90&xb0下压敏胶带与纤维板粘合的标准试验方法 角度和恒定应力》.pdf(5页珍藏版)》请在麦多课文档分享上搜索。
1、Designation: D2860/D2860M 18Standard Test Method forAdhesion of Pressure-Sensitive Tape to Fiberboard at 90Angle and Constant Stress1This standard is issued under the fixed designation D2860/D2860M; the number immediately following the designation indicates theyear of original adoption or, in the ca
2、se of revision, the year of last revision. A number in parentheses indicates the year of lastreapproval. A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope1.1 This
3、 test method covers the determination of the prop-erty of adhesion of pressure-sensitive tape to a fiber-boardsurface. The user of this test method has the option of choosingthe paper surface for the test. The test surface may be thestandard linerboard, another linerboard (or paper) of individualint
4、erest, or a specific fiberboard.1.2 The values stated in either SI or inch-pound units are tobe regarded separately as standard. The values stated in eachsystem are not exact equivalents; therefore, each system mustbe used independently, without combining values in any way.1.3 This standard does not
5、 purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety, health, and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.4 This international st
6、andard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade (TBT) Committee.2.
7、 Referenced Documents2.1 ASTM Standards:2D996 Terminology of Packaging and Distribution Environ-mentsD2904 Practice for Interlaboratory Testing of a Textile TestMethod that Produces Normally Distributed Data (With-drawn 2008)3D2906 Practice for Statements on Precision and Bias forTextiles (Withdrawn
8、 2008)3D3715/D3715M Practice for Quality Assurance of Pressure-Sensitive TapesD4332 Practice for Conditioning Containers, Packages, orPackaging Components for Testing3. Terminology3.1 DefinitionsTerminology found in Terminology D996shall apply.4. Summary of Test Method4.1 Procedure AThe pressure-sen
9、sitive tape is mounted ona rigid panel. The adhesive side is exposed. A strip oflinerboard, which represents the fiberboard, is placed againstthe tape adhesive with controlled pressure. The area of contactis specified. The panel is mounted in a horizontal position. Aspecified mass is fastened to one
10、 end of the linerboard. Themass acts to peel the linerboard away from the adhesive at anangle of 90. The time required to peel the linerboard from thetape is measured.4.2 Procedure BIn this procedure, the fiberboard or thelinerboard representing it is adhered to a rigid panel and thetape peeled from
11、 it. In all other respects, the procedure is thesame as Procedure A.5. Significance and Use5.1 This test method is designed to show the adhesion of apressure-sensitive tape to fiberboard when the tape is under aconstant stress. Test data from this test method for some typesof packaging tape relates
12、to tape performance on fiberboardbox closure.1This test method is under the jurisdiction of ASTM Committee D10 onPackaging and is the direct responsibility of Subcommittee D10.14 on Tape andLabels.Current edition approved March 1, 2018. Published April 2018. Originallyapproved in 1970. Last previous
13、 edition approved in 2017 as D2860/D2860M 17.DOI: 10.1520/D2860_D2860M-18.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe
14、ASTM website.3The last approved version of this historical standard is referenced onwww.astm.org.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesThis international standard was developed in accordance with internationally recognized pr
15、inciples on standardization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.15.2 ProcedureAshould be used when comparing tapes to anestablished requi
16、rement. The requirement may be establishedusing either the standard linerboard or another linerboardrepresenting a specific fiberboard.5.3 Procedure B should be used to rank tapes as to theirability to adhere to fiberboard.6. Apparatus and Materials6.1 Tape, pressure-sensitive, double-coated, 48-mm
17、2-in.width. The tape shall exhibit sufficient adhesion to the paneland test specimen or fiberboard to avoid the failures cited in10.1.9 and 10.2.14.6.2 PanelAny steel piece at least 50 by 125 mm 2 by 5in. and no less than 1.1 mm 0.043 in. thick, having one face(2 by 5 in.) that does not deviate from
18、 a plane by more than0.050 mm 0.002 in.6.3 Stop Watch.6.4 Razor Blade, single-edge.6.5 MaskAny paper no more than 0.050 mm 0.002 in.thick formed to a rectangle approximately 125 by 60 mm 5 by2.5 in. with a rectangular hole exactly 24 6 0.25 1.0 6 0.01by 32 mm 1.25 in. centered in the piece. The 24-m
19、m 1-in.hole dimension shall be in the 125-mm 5-in. direction (seeFig. 1 and Fig. 2).6.6 Cutter, for preparing fiberboard or linerboard and tapespecimens.6.7 Paperboard Piece, approximately 25 by 25 mm 1 by 1in., for reinforcement.NOTE 1Chipboard pads constructed from 0.030-in. thick fiberboardare ty
20、pically used.6.8 Paper Punch, single-hole.6.9 Fiberboard or Linerboard Surface,4against which thetest is made.6.9.1 For Procedure A, cut a rectangle exactly 24 6 0.25mm 1.0 6 0.01 in. wide by at least 125 mm 5 in. in length,from the linerboard representing the fiberboard on which thetape will be use
21、d. The long dimension shall lie at a right angleto the machine direction of the linerboard. Reinforce one endof the strip with a chipboard piece adhered with double-coatedtape. Punch a hole at the center of the reinforcement.6.9.2 For Procedure B, cut a rectangle, preferably 125 by 50mm 5 by 2 in.,
22、but no less than 50 by 50 mm 2 by 2 in., fromthe fiberboard on which the tape will be used (or linerboardrepresenting it). The long test dimension shall lie at a rightangle to the machine direction of the linerboard.6.9.3 For either procedure, prepare the linerboard or fiber-board in advance of test
23、ing and mark it to show which side touse. When comparing one roll of tape to another or one lot oftape to another, the linerboard or fiberboard should be from asingle lot.6.10 Steel Roller, 82.5 6 2.5 mm 3.25 6 0.1 in. indiameter and 45 6 1.5 mm 1.75 6 0.05 in. in width, coveredwith rubber approxima
24、tely 6 mm 0.25 in. in thickness havinga Shore A durometer hardness of 80 6 5. The surface shall bea true cylinder void of any convex or concave deviations. Themass of the roller shall be 2040 6 45 g 4.5 6 0.1 lb. Themass of the handle shall not add to the mass of the roller duringuse.NOTE 2A simple
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ASTMD2860D2860M2018STANDARDTESTMETHODFORADHESIONOFPRESSURESENSITIVETAPETOFIBERBOARDAT90XB0ANGLEANDCONSTANTSTRESS

链接地址:http://www.mydoc123.com/p-513656.html