ASTM C1729-2017 Standard Specification for Aluminum Jacketing for Insulation《绝缘铝护套的标准规格》.pdf

《ASTM C1729-2017 Standard Specification for Aluminum Jacketing for Insulation《绝缘铝护套的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM C1729-2017 Standard Specification for Aluminum Jacketing for Insulation《绝缘铝护套的标准规格》.pdf（9页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: C1729 16aC1729 17Standard Specification forAluminum Jacketing for Insulation1This standard is issued under the fixed designation C1729; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A numbe

2、r in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers aluminum jacketing for thermal and acoustical insulation operating at either above or belowambient temperatures an

3、d in both indoor and outdoor locations. It does not cover insulation jacketing made from other materialssuch as mastics, fiber reinforced plastic, PVC, or stainless steel nor does it cover the details of thermal or acoustical insulationsystems.1.2 This specification provides physical requirements fo

4、r aluminum jacketing for thermal and acoustical insulation. GuideC1423 provides guidance in selecting jacketing materials and their safe use.1.3 This is a material specification and does not imply any performance of the installed system using the materials specifiedherein. For information about inst

5、allation of aluminum jacketing, see (1).21.4 The values stated in inch-pound units are to be regarded as standard. No other units of measurement are included in thisstandard.NOTE 1A version of this specification in SI units is available as C1729M.1.5 This standard does not purport to address all of

6、the safety concerns, if any, associated with its use. It is the responsibilityof the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatorylimitations prior to use.1.6 This international standard was developed in accordance with inter

7、nationally recognized principles on standardizationestablished in the Decision on Principles for the Development of International Standards, Guides and Recommendations issuedby the World Trade Organization Technical Barriers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:3B209 Sp

8、ecification for Aluminum and Aluminum-Alloy Sheet and PlateB487 Test Method for Measurement of Metal and Oxide Coating Thickness by Microscopical Examination of Cross SectionC168 Terminology Relating to Thermal InsulationC450 Practice for Fabrication of Thermal Insulating Fitting Covers for NPS Pipi

9、ng, and Vessel LaggingC585 Practice for Inner and Outer Diameters of Thermal Insulation for Nominal Sizes of Pipe and TubingC835 Test Method for Total Hemispherical Emittance of Surfaces up to 1400CC1371 Test Method for Determination of Emittance of Materials Near Room Temperature Using Portable Emi

10、ssometersC1423 Guide for Selecting Jacketing Materials for Thermal InsulationC1729M Specification for Aluminum Jacketing for InsulationC1785 Test Method for Concentration of Pinhole Detections in Moisture Barriers on Metal JacketingD3363 Test Method for Film Hardness by Pencil TestE84 Test Method fo

11、r Surface Burning Characteristics of Building MaterialsF1249 Test Method for Water Vapor Transmission Rate Through Plastic Film and Sheeting Using a Modulated Infrared Sensor1 This specification is under the jurisdiction of ASTM Committee C16 on Thermal Insulation and is the direct responsibility of

12、 Subcommittee C16.40 on InsulationSystems.Current edition approved Sept. 1, 2016May 1, 2017. Published September 2016May 2017. Originally approved in 2010. Last previous edition approved in 2016 asC1729 16.C1729 16a. DOI: 10.1520/C1729-16A.10.1520/C1729-17.2 The boldface numbers in parentheses refer

13、 to a list of references at the end of this standard.3 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM website.This doc

14、ument is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as

15、 appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States12.2 AAMA Standard:4AAMA 2605 Specification, Performance

16、Requirements and Test Procedures for Superior Performing Organic Coatings onAluminum Extrusions and Panels (with Coil Coating Appendix)2.3 ANSI Standard:5ANSI H35.2/H35.2(M) Dimensional Tolerances for Aluminum Mill Products3. Terminology3.1 DefinitionsDefinitions in Terminology C168 apply to terms u

17、sed in this specification.3.2 Definitions of Terms Specific to This Standard:3.2.1 box ribaluminum sheet formed to have alternating parallel grooves and ridges with a cross section approximating asquare wave.3.2.2 cladding (as related to insulation jacketing)synonymous with jacketing.3.2.2.1 Discuss

18、ionThe three terms “jacketing,” “lagging,” and “cladding” are considered synonymous in most metal jacket related applications andgeographies. However, in some cases in the power industry in North America the term “lagging” has a different meaning than“jacketing” or “cladding” and refers specifically

19、 to a heavier gauge of jacketing.3.2.3 crevice corrosionlocalized corrosion of metal jacketing surface at, or immediately adjacent to, an area that is shieldedfrom full exposure to the environment because of close proximity between the metal and the surface of another material.3.2.4 cross crimpedsyn

20、onymous with 316 in. corrugated.3.2.5 deep corrugatedaluminum sheet formed to have alternating parallel grooves and ridges with a cross sectionapproximating a sine wave.3.2.6 finishthe texture of the aluminum surface.3.2.7 gorejacketing for elbows, fittings, or other non-straight portions of the pip

21、ing system made from a multitude of similaroverlapping pieces.3.2.8 lagging (as related to insulation jacketing)synonymous with jacketing.3.2.8.1 DiscussionThe three terms “jacketing”, “lagging”, and “cladding” are considered synonymous in most metal jacket related applications andgeographies. Howev

22、er, in some cases in the power industry in North America the term “lagging” has a different meaning than“jacketing” or “cladding” and refers specifically to a heavier gauge of jacketing.3.2.9 moisture retarder (moister barrier)a layer of plastic film or other material applied to the inner side of me

23、tal jacketingto inhibit jacket corrosion by interfering with the formation of a galvanic cell between the dissimilar metals of the pipe and jacketor by preventing crevice corrosion.3.2.9.1 DiscussionA moisture retarder is not an insulation system water vapor retarder and does not perform the same fu

24、nction.3.2.10 polykrafta multilayer composite film used as a moisture retarder on metal jacketing consisting of at least one layer ofminimum 40 lb kraft paper and one or more layers of plastic film, usually polyethylene at a minimum thickness of 1.5 mils.3.2.11 polyfilmin relation to metal jacketing

25、, a three-layer film used as a moisture retarder on metal jacketing consisting ofone layer of ethylene/methacrylic acid copolymer and two layers of other polymers, usually polyethylene.3.2.12 PVdF based paint systema pigmented paint used on the outer surface of metal jacketing to provide corrosion r

26、esistanceand higher emittance than bare metal consisting of a fairly thin primer paint layer covered by a thicker topcoat paint layer wherethe latter is a polyvinylidene fluoride (PVdF) type paint.3.2.13 PVF filma polymer film consisting of polyvinyl fluoride used on the outer surface of metal jacke

27、ting to providecorrosion resistance and higher emittance than bare metal.3.2.14 safety edgean edge of metal jacketing that has been de-burred or rounded by a rolling operation.4 Available from American Architectural Manufacturers Association (AAMA), 1827 Walden Office Square, Suite 550, Schaumburg,

28、IL 60173-4268, http:/www.aamanet.org.5 Available from American National Standards Institute (ANSI), 25 W. 43rd St., 4th Floor, New York, NY 10036, http:/www.ansi.org.C1729 1723.2.15 safety hema rounded edge of metal jacketing created by folding the edge of sheet jacketing completely back upon itself

29、using a roll former or a brake.3.2.15.1 DiscussionThe fold is typically made toward the underside of the jacketing so that the original edge is hidden and the external appearanceof the jacketing is preserved.3.2.16 splice rollmetal jacketing sold in roll form where the package contains two separate

30、pieces of metal jacketing rolledapproximately end to end.3.2.16.1 DiscussionA splice roll occurs when the metal coil being used to form the roll jacketing reaches its end before the required roll length isobtained.3.2.17 split rollsynonymous with splice roll.4. Significance and Use4.1 This specifica

31、tion is used to specify material by physical property requirements that address the prerequisites in Sections6 to 10. The designer of an insulation system, after determining the system requirements, shall use this specification to specify theappropriate aluminum jacketing.5. Classification5.1 Classi

32、fication of aluminum jacketing is based on three factors:5.1.1 Outer surface treatment and emittance ():5.1.1.1 Type I = Bare surface, 0.1,5.1.1.2 Type II = Painted with pigmented paint, 0.8,5.1.1.3 Type III = Painted with unpigmented paint, 0.5,5.1.1.4 Type IV = Plastic film coated surface, 0.85, a

33、nd5.1.1.5 Type V = Painted with a PVdF based paint system, 0.8.5.1.1.6 PVF film is one kind of plastic film used in Type IV.5.1.1.7 Paint systems for Types II and III must be factory applied and baked on.5.1.1.8 Plastic film for Type IV must be factory applied and heat laminated to the surface.5.1.2

34、 Alloy and Temper per Specification B209:5.1.2.1 Grade 1 = Alloy 3105 or 3003, half hard temper (H14 or H24)5.1.2.2 Grade 2 = Alloy 3105 or 3003, quarter hard temper (H12 - lock forming quality),5.1.2.3 Grade 3 = Alloy 1100, dead soft temper,5.1.2.4 Grade 4 = Alloy 3004,5.1.2.5 Grade 5 = Alloy Alcla

35、d 3004 (alloy 3004 clad both sides with alloy 7072 for improved corrosion resistance), and5.1.2.6 Grade 6 = Alloy 5052.5.1.3 Moisture Retarder:5.1.3.1 Class A = polyfilm, 3 mil thick,5.1.3.2 Class C = polykraft per section 3.2.10,5.1.3.3 Class D = painted, and5.1.3.4 Class E = no moisture retarder.N

36、OTE 2Class B was removed in 2011 because it was not used or produced. The remaining Classes were not renumbered to avoid conflicts withengineering specifications that reference the remaining Classes.6. Materials and Manufacture6.1 Aluminum jacketing materials are composed of a single material or a l

37、amination of several components. The materials aresupplied in the form of rolls or sheets or preformed to fit the surface to which they are to be applied. The materials are appliedin the field or as a factory-applied composite with the insulation.6.2 The primary material shall be aluminum and shall

38、have a finish that is smooth, 316 in. corrugated, or stucco embossed. Thedimensions of corrugations (pitch and depth) must be agreed to by manufacturer and purchaser to achieve interchangeability,constant rigidity, and appearance.6.3 When agreed upon by purchaser and seller, aluminum sheets used as

39、pipe insulation jacketing (see 8.2) shall have a safetyedge or a 38 to 12 in. safety hem along one entire width edge of the sheet. Aluminum jacketing with a safety edge or safety hemmust still meet the length dimensions specified in 8.2.1. A safety hem shall not be specified when the finish is 316 i

40、n. corrugated.C1729 1736.4 In most cases, the inner surface of aluminum jacketing material is coated or covered with a moisture resistant film to retardpossible galvanic or chemical corrosion, or both, of the jacketing.6.5 Polyfilm (Class A) and polykraft (Class C) must be factory applied and heat l

41、aminated to the interior surface of the metaljacketing.6.6 For highly corrosive ambient conditions or to increase emittance, the purchaser shall specify that the outer surface of thealuminum be coated with a pigmented paint (Type II), unpigmented paint (Type III), a plastic film (Type IV), or with a

42、 PVdF basedpaint system (Type V).6.7 Pigmented paint (Type II), unpigmented paint (Type III), and PVdF based paint systems (Type V) must be factory appliedand baked on to the outer surface.6.8 The topcoat of the factory applied PVdF based paint systems (Type V) must contain at least seventy percent

43、(70 %) byweight of polyvinylidene fluoride (PVdF) resin based on the total weight of resins present and at least forty percent (40 %) byweight of PVdF resin based on the total weight of solids present in the coating composition. The full PVdF based paint systemmust meet the application and performan

44、ce requirements of AAMA 2605.6.9 Unless agreed to otherwise by purchaser and seller of the metal jacketing, the primer layer for Type V outer surfacetreatment must have a minimum dry thickness of 0.2 mils and the PVdF topcoat must have a minimum dry thickness of 0.7 mils.NOTE 3It is important to be

45、aware that the minimum 0.7 mil thickness requirement in Table 1 applies to the topcoat of the Type V PVdF based paintsystem and not to the total outer surface paint thickness.6.10 Plastic film (Type IV), including PVF film, must be factory applied to the metal jacketing outer surface using heatlamin

46、ation with a thermally activated adhesive.6.11 Plastic film (Type IV), including PVF film, must be a minimum of 1.5 mils thick.6.12 The aluminum used in this jacketing, with the exception of box rib, shall be manufactured from Specification , alloys 3003,3105, or 1100 with tempers of H14 or H24 (hal

47、f hard), H12 (quarter hard), or dead soft Grades 1, 2, or 3 per 5.1.2.6.13 Aluminum jacketing shall be specified by the thickness of the aluminum layer which shall be in the range from 0.016 to0.050 in.NOTE 4The thickness values mentioned in 6.116.12, 6.136.14, and 6.126.13 are nominal thickness. Th

48、e tolerances shown in Table 2 apply to theselisted nominal values.TABLE 1 Physical PropertiesType I II and V III IVGrade All All All AllClass A C D E A C D E A C D E A C D EEmittance 0.1 0.1 0.1 0.1 0.8 0.8 0.8 0.8 0.5 0.5 0.5 0.5 0.85 0.85 0.85 0.85SurfaceBurning(flame/smoke max)25/50 25/50 25/50 2

49、5/50 25/50 25/50 25/50 25/50 25/50 25/50 25/50 25/50 25/50 25/50 25/50 25/50Moistureretarderpinholedectections(per 50 ft2)#5 #5 #5 n.a. #5 #5 #5 n.a. #5 #5 #5 n.a. #5 #5 #5 n.a.MoistureretarderWVTR(g/100 in2/day)#0.1 #1.1 n.a. n.a. #0.1 #1.1 n.a. n.a. #0.1 #1.1 n.a. n.a. #0.1 #1.1 n.a. n.a.Outer PaintThickness(mils)n.a. n.a. n.a. n.a. 0.7-0.8 0.7-0.8 0.7-0.8 0.7-0.8 0.3-0.4 0.3-0.4 0.3-0.4 0.3-0.4 n.a. n.a. n.a. n.a.Outer PaintPencilHardness(min)n.a. n.a. n.a n.a. H H H H H H H H n.a n.a n.a. n.a.C1729 1746.14 The mea