ASTM A844 A844M-2009 Standard Specification for Steel Plates 9 % Nickel Alloy for Pressure Vessels Produced by the Direct-Quenching Process《钢板、9％镍合金、压力容器、由直接淬火工艺生产的标准规范》.pdf

《ASTM A844 A844M-2009 Standard Specification for Steel Plates 9 % Nickel Alloy for Pressure Vessels Produced by the Direct-Quenching Process《钢板、9％镍合金、压力容器、由直接淬火工艺生产的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM A844 A844M-2009 Standard Specification for Steel Plates 9 % Nickel Alloy for Pressure Vessels Produced by the Direct-Quenching Process《钢板、9％镍合金、压力容器、由直接淬火工艺生产的标准规范》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A844/A844M 09Standard Specification forSteel Plates, 9 % Nickel Alloy, for Pressure Vessels,Produced by the Direct-Quenching Process1This standard is issued under the fixed designation A844/A844M; the number immediately following the designation indicates the yearof original adoption or

2、, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers 9 % nickel-alloy steel platesproduced by the direct-

3、quenching process. The plates areintended primarily for use in welded pressure vessels.1.2 The direct-quenching process consists of quenching theplates directly after rolling, without permitting the plates tocool below the critical temperature prior to initiation of thequenching operation, and subse

4、quently tempering the plates.(This differs from the “conventional” process in which theplates are permitted to cool to a temperature significantlybelow the critical temperature, usually to ambient temperature,prior to reheating to a temperature above the upper criticaltemperature, then quenching, an

5、d subsequently tempering.)1.3 The maximum nominal thickness of plates furnishedunder this specification shall not exceed 2 in. 50 mm.1.4 This material is susceptible to magnetization. Use ofmagnets in handling after heat treatment should be avoided ifresidual magnetism would be detrimental to subseq

6、uent fabri-cation or service.1.5 The values stated in either inch-pound or SI units are tobe regarded separately as standard. Within the text, the SI unitsare shown in brackets. The values stated in each system are notexact equivalents; therefore each system must be used inde-pendently of the other.

7、 Combining values from the two systemsmay result in nonconformance with the specification.2. Referenced Documents2.1 ASTM Standards:2A20/A20M Specification for General Requirements forSteel Plates for Pressure VesselsA435/A435M Specification for Straight-Beam UltrasonicExamination of Steel PlatesA57

8、7/A577M Specification for Ultrasonic Angle-Beam Ex-amination of Steel PlatesA578/A578M Specification for Straight-Beam UltrasonicExamination of Rolled Steel Plates for Special Applica-tions3. General Requirements and Ordering Information3.1 Material supplied to this material specification shallconfo

9、rm to Specification A20/A20M. These requirements out-line the testing and retesting methods and procedures, permit-ted variations in dimensions, quality and repair of defects,marking, loading, and ordering information.3.2 In addition to the basic requirements of this specifica-tion, certain suppleme

10、ntary requirements are available whenadditional control, testing, or examination is required to meetend use requirements. The purchaser is referred to the listedsupplementary requirements in this specification and to thedetailed requirements in Specification A20/A20M.3.3 If the requirements of this

11、specification are in conflictwith the requirements of SpecificationA20/A20M, the require-ments of this specification shall prevail.4. Manufacture4.1 Steelmaking PracticeThe steel shall be killed andshall conform to the fine austenitic grain size requirement ofSpecification A20/A20M.4.2 Heat Treatmen

12、t:4.2.1 The plates shall be quenched directly after rolling,without being allowed to cool below 1205F 650C. Thequenching shall be initiated from a temperature within therange from 1205 to 1670F 650 to 910C. (The temperatureshall be reported in accordance with 19.2 of SpecificationA20/A20M.)4.2.2 Sub

13、sequent to quenching, the plates shall be temperedwithin the range from 1050 to 1175F 565 to 635C, holdingat that temperature for a minimum of 30 min/in. 1.2 min/mmof thickness but for not less than 15 min., and then cooling ata rate of not less than 300F/h 165C/h, either in air or byquenching in wa

14、ter, to ambient temperature.4.2.2.1 Prior to the tempering treatment, the plates may besubjected to an intermediate heat treatment consisting ofheating to a temperature in the range from 1165 to 1290F 6301This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and

15、 Related Alloys and is the direct responsibility of SubcommitteeA01.11 on Steel Plates for Boilers and Pressure Vessels.Current edition approved Oct. 1, 2009. Published October 2009. Originallyapproved in 1985. Last previous edition approved in 2004 as A844/A844M 04).DOI: 10.1520/A0844_A0844M-09.2Fo

16、r referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1*A Summary of Changes section appears at the end of this standa

17、rd.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.to 700C, holding at that temperature for a minimum of 1 h/in.(2.4 min/mm of thickness, but in no case less than 15 min, andthen water-quenching to below 300F 150C in the case ofplate

18、thicknesses of more than58 in. 16 mm or cooling in airor water-quenching to below 300F 150C in the case of platethicknesses of58 in. 16 mm and under.NOTE 1The intermediate heat treatment is for the purpose of enhanc-ing elongation and notch-toughness and for reducing susceptibility tostrain-aging em

19、brittlement and temper embrittlement. It may be per-formed at the option of the material manufacturer or may be specified bythe purchaser.5. Chemical Composition5.1 The steel shall conform to the chemical requirementsshown in Table 1 unless otherwise modified in accordance withSupplementary Requirem

20、ent S17, Vacuum Carbon-DeoxidizedSteel, in Specification A20/A20M.6. Finish6.1 The plates shall be descaled by the producer prior toshipment.7. Mechanical Requirements7.1 Tension Test RequirementsThe material as representedby the tension-test specimens shall conform to the require-ments specified in

21、 Table 2.7.1.1 For nominal plate thicknesses of34 in. 20 mm andunder, the 112-in. 40-mm wide rectangular specimen may beused for the tension test and the elongation may be determinedin a 2-in. 50-mm gage length that includes the fracture andshows the greatest elongation.7.2 Impact Test Requirements:

22、7.2.1 Charpy V-notch impact tests shall be made in accor-dance with Specification A20/A20M.7.2.2 Number and Location of Test CouponsTwo impacttests shall be made from each plate-as-heat-treated, with thetest coupons being taken from locations adjacent to the tensiontest coupons.7.2.3 OrientationThe

23、longitudinal axis of the test speci-men shall be transverse to the final rolling direction of theplate.7.2.4 Test TemperatureUnless otherwise specified on theorder, the tests shall be conducted at 320F 195C.7.2.5 Acceptance CriteriaEach test specimen shall have alateral expansion opposite the notch

24、of not less than 0.015 in.0.381 mm.8. Marking8.1 In addition to the marking required in SpecificationA20/A20M, each plate shall be legibly stamped or stenciled,depending upon the ordered thickness, with the letters DQTexcept as otherwise specified in 8.1.1.8.1.1 When the optional heat treatment perm

25、itted in 4.2.2 isperformed, the plates shall be marked with the letters DQTTinstead of DQT.9. Keywords9.1 alloy steel; alloy steel plate; pressure containing parts;pressure vessel steels; steel plates; steel plates for pressurevessel applicationsSUPPLEMENTARY REQUIREMENTSSupplementary requirements s

26、hall not apply unless specified in the order.A list of standard supplementary requirements, for use at the option of the purchaser, are includedin Specification A20/A20M. Several of those that are considered to be suitable for use with thisspecification are listed below by title. Other tests may be

27、performed by agreement between thesupplier and the purchaser.S1. Vacuum Treatment,S2. Product Analysis,S6. Drop Weight Test (for Material 0.625 in. 16 mm andOver in Thickness),S8. Ultrasonic Examination in Accordance with Specifica-tion A435/A435M,S11. Ultrasonic Examination in Accordance with Speci

28、fica-tion A577/A577M,S12. Ultrasonic Examination in Accordance with Specifica-tion A578/A578M,S13. NDT Temperature Determination,S17. Vacuum Carbon-Deoxidized Steel,S18. Unspecified Elements, andS19. Restricted Chemical Requirements.TABLE 1 Chemical RequirementsElement Composition, %Carbon, maxA0.13

29、Manganese, max:Heat analysisProduct analysis0.900.98Phosphorus, maxASulfur, maxASilicon:0.0150.015Heat analysisProduct analysis0.150.40B0.130.45BNickel:Heat analysisProduct analysis8.509.508.409.60AApplies to both heat and product analyses.BThe specified minimum limit does not apply if the total alu

30、minum content is0.030 % or more, or provided that acid soluble aluminum is 0.025 % or more.TABLE 2 Tensile RequirementsTensile strength, ksi MPa 100 to 120 690825Yield strength, min, ksi MPa 85 585Elongation in 2 in. 50 mm, min, %A20.0ASee Specification A20/A20M for elongation adjustments.A844/A844M

31、 092ADDITIONAL SUPPLEMENTARY REQUIREMENTSAlso listed are additional optional Supplementary Requirements S55 and S56 which are suitable forthis specification:S55. Longitudinal Charpy Impact Energy AbsorptionRequirementS55.1 The longitudinal Charpy V-notch impact propertiesshall not be less than 25 ft

32、lbf 34 J at the test temperaturespecified in the order.S55.2 Each impact test value shall constitute the averagevalue of three specimens, with not more than one individualspecimen value below the specified minimum value of 25 ftlbf34 J but in no case below 20 ftlbf 27 J for full-sizespecimens.S56. T

33、ransverse Charpy Impact Energy Absorption Re-quirementS56.1 The transverse Charpy V-notch impact propertiesshall not be less than 20 ftlbf 27 J at the test temperaturespecified in the order.S56.2 Each impact test value shall constitute the averagevalue of three specimens, with not more than one indi

34、vidualspecimen value below the specified minimum average value of20 ftlbf 27 J but in no case below 15 ftlbf 20 J for full-sizespecimens.SUMMARY OF CHANGESCommittee A01 as identified the location of selected changes to this standard since the last issue(A844/A844M 04) that may impact the use of this

35、 standard. (Approved Oct. 1, 2009.)(1) 3.2 and 3.4 deleted and content incorporated into 3.1 and3.2, respectively. 3.3.13.3.4 deleted as redundant. Sectionparagraphs subsequently renumbered.(2) Table 1 revised to reflect modern melting practices.(3) Supplementary Requirement S3 deleted as not approp

36、riatefor this grade of steel (seldom if ever used).ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent righ

37、ts, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for

38、revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing

39、you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).A844/A844M 093