ASTM A838-2002(2013) Standard Specification for Free-Machining Ferritic Stainless Soft Magnetic Alloy Bar for Relay Applications《继电器用易切铁素体不锈软磁合金棒标准规格》.pdf

《ASTM A838-2002(2013) Standard Specification for Free-Machining Ferritic Stainless Soft Magnetic Alloy Bar for Relay Applications《继电器用易切铁素体不锈软磁合金棒标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM A838-2002(2013) Standard Specification for Free-Machining Ferritic Stainless Soft Magnetic Alloy Bar for Relay Applications《继电器用易切铁素体不锈软磁合金棒标准规格》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A838 02 (Reapproved 2013)Standard Specification forFree-Machining Ferritic Stainless Soft Magnetic Alloy Barfor Relay Applications1This standard is issued under the fixed designation A838; the number immediately following the designation indicates the year oforiginal adoption or, in the

2、 case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers free-machining ferritic stain-less soft magnetic alloy produc

3、ed or supplied expressly incold-finished bar form for use in magnetic cores and other partsrequiring a high permeability, low-coercivity stainless steel.1.1.1 This specification does not cover either cast parts orparts produced by powder metallurgy techniques.1.2 Two specific alloy types are covered

4、. The primaryconstituents are shown in Table 1. These types have corrosionresistance similar to AISI Type 430F and Type 430F, Specifi-cation A582/A582M.1.3 This specification covers only these alloy types suppliedin cold-finished bars in cross-sectional shapes such as rounds,squares, hexagons, and o

5、ctagons with diameters (diagonals)greater than or equal to 0.250 in. (6.35 mm) and less than orequal to 1.625 in. (41.28 mm).21.4 Certain cold-finished round bar products are capable ofbeing supplied mill annealed to required magnetic propertiessuch as low coercivity. The size range that can be mill

6、 annealedis from 0.250 to 1.625 in. (6.35 to 41.28 mm). Other productsof these alloys cannot be mill annealed to produce equivalentlylow coercivity; hence, the final machined parts should be heattreated as recommended by the producer.1.5 The values stated in customary (cgs-emu and inch-pound) units

7、are to be regarded as standard. The values givenin parentheses are mathematical conversions to SI units whichare provided for information only and are not consideredstandard.2. Referenced Documents2.1 ASTM Standards:3A34/A34M Practice for Sampling and Procurement Testingof Magnetic MaterialsA340 Ter

8、minology of Symbols and Definitions Relating toMagnetic TestingA341/A341M Test Method for Direct Current MagneticProperties of Materials Using D-C Permeameters and theBallistic Test MethodsA582/A582M Specification for Free-Machining StainlessSteel BarsA596/A596M Test Method for Direct-Current Magnet

9、icProperties of Materials Using the Ballistic Method andRing SpecimensA773/A773M Test Method for dc Magnetic Properties ofMaterials Using Ring and Permeameter Procedures withdc Electronic HysteresigraphsE1019 Test Methods for Determination of Carbon, Sulfur,Nitrogen, and Oxygen in Steel, Iron, Nicke

10、l, and CobaltAlloys by Various Combustion and Fusion Techniques2.2 Other Standard:IEC Publication 60404-7 Methods of Measurement of theCoercivity of Magnetic Materials in an Open MagneticCircuit43. Terminology3.1 The terms and symbols used in this specification aredefined in Terminology A340.4. Clas

11、sification4.1 Two specific alloy types are covered:1This specification is under the jurisdiction of ASTM Committee A06 onMagnetic Properties and is the direct responsibility of Subcommittee A06.02 onMaterial Specifications.Current edition approved May 1, 2013. Published July 2013. Originally approve

12、din 1985. Last previous edition approved in 2007 as A838 02 (2007). DOI:10.1520/A0838-02R13.2Other product forms can be supplied to the chemistries listed in this specifi-cation; however, all other requirements shall be subject to negotiation between theproducer and the user.3For referenced ASTM sta

13、ndards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.4Available from American National Standards Institute (ANSI), 25 W. 43rd St.,4th Floo

14、r, New York, NY 10036, http:/www.ansi.org.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States14.2 Grades, Alloy Type 1The standard grades of this alloytype are distinguished by the as-supplied condition, coercivity,and nominal mechanical

15、hardness and are listed in Table 2.4.3 Grades, Alloy Type 2The standard grades of this alloytype are distinguished by the as-supplied condition, coercivity,and nominal mechanical hardness and are listed in Table 3.5. Ordering Information5.1 Purchase orders for material under this specificationshall

16、include the following information to adequately describethe desired product:5.1.1 Reference to this specification and year of issue/revision.5.1.2 Alloy type and grade (Section 4),5.1.3 Form and condition,5.1.4 Dimensions and tolerances (Section 9),5.1.5 Quantity (weight or number of pieces),5.1.6 M

17、agnetic property requirements if other than shown inthis specification.5.1.7 Certification of analysis or magnetic qualityevaluation, or both, if needed,5.1.8 Marking and packaging, and5.1.9 Exceptions to the specification or special require-ments.6. Chemical Composition6.1 The material shall confor

18、m to the requirements pre-scribed in Table 4.6.2 Determination of metallic constituents shall be by amethod acceptable to both the producer and the user. Analysisof carbon, nitrogen, sulfur, and oxygen shall be done inaccordance with Test Methods E1019.7. Form and Condition7.1 Cold Finished BarsCold

19、 drawn; cold drawn andcenterless ground; cold drawn and precision ground; millannealed and centerless ground; mill annealed and precisionground.8. Magnetic Property Requirements8.1 GeneralMaterial supplied under terms of this specifi-cation shall be tested using either ring, permeameter, orcoercimet

20、er test methods. Only the coercive field strength (Hc)is subject to specification. Since coercimeters saturate the testspecimen before measurement of the coercive field strength,two different sets of coercive field strength requirements, onefor ring and permeameter testing and one for coercimetertes

21、ting, are given. Unless specified in the purchase order,coercimeter testing shall be the standard test method.8.2 Test SpecimenTest specimen size and shape shall be inaccordance with the requirements listed in Practice A34/A34M. If tests on heat-treated specimens are requested, allmachining operatio

22、ns shall be performed before heat treatment.The cross-sectional area of all specimen types shall be deter-mined by measurement with a micrometer or calipers.8.3 Magnetic Test Specimen Heat TreatmentWhen speci-fied on the purchase order, the annealed magnetic properties(also referred to as the magnet

23、ic capability) rather than theas-supplied magnetic properties shall be determined. The heattreatment to be used to assess the magnetic capability should bespecified by the user. If not, the following heat treatmentprocedure (full anneal) shall be used.8.3.1 AtmosphereHigh vacuum or very dry hydrogen

24、(dew point less than 60C).8.3.2 Soak Temperature (Alloy Type 1)815 6 25C.8.3.3 Soak Temperature (Alloy Type 2)850 6 25C.8.3.4 Soak Time2-h minimum.8.3.5 CoolingFurnace cool (50 to 100C/h) to 400C thencool to room temperature at any convenient rate.8.4 dc Ring and Permeameter Testing :8.4.1 Either ri

25、ng or permeameter test methods may be used.For ring testing, a link-type specimen with its long edgeparallel to the bar axis is preferred. Testing of ring or linkspecimens shall be in accordance with Test Methods A596/A596M or A773/A773M. Testing of bar specimens on apermeameter shall be in accordan

26、ce with either Test MethodsA341/A341M or A773/A773M.8.4.2 RequirementsThe coercive field strength, whenmeasured from a maximum flux density of 10.0 kG (1.00 T),shall meet the requirements listed in Table 5. Full-annealrequirements refer to specimens heat treated in accordancewith 8.3.8.5 Coercimeter

27、 Testing:8.5.1 Coercimeter testing is permitted provided it can bedemonstrated that the maximum flux density induced in thespecimen exceeds 13 kG (1.30 T) and that the equipment andprocedures used satisfy the requirements of IEC Publication60404-7.8.5.2 Any machining before testing shall be done wit

28、h duecare, and only enough material shall be removed to permitinsertion of the test specimen into the coercimeter.8.5.3 Requirements The coercive field strength shall meetthe requirements listed in Table 6. Full-anneal requirementsrefer to specimens heat treated in accordance with 8.3.TABLE 1 Alloy

29、TypesAlloy TypeNominal Composition, Weight PercentCarbon Chromium Silicon Sulfur Iron1 0.05 17.5 0.50 0.30 balance2 0.05 17.5 1.25 0.30 balanceTABLE 2 Grades for Alloy Type 1Grade As-Supplied Condition1 mill annealed2 mill annealed3 unannealed, cold drawnTABLE 3 Grades for Alloy Type 2Grade As-Suppl

30、ied Condition1 mill annealed2 unannealed, cold drawnA838 02 (2013)29. Dimensions and Tolerances9.1 Dimensions and tolerances shall be as mutually agreedupon between the user and the producer.10. Certification10.1 When specified in the purchase order or contract, theuser shall be furnished certificat

31、ion that samples representingeach lot have been either tested or inspected as directed in thisspecification and the requirements have been met. Whenspecified in the purchase order or contract, a report of testresults shall be furnished.11. Packaging and Package Marking11.1 Packaging and package mark

32、ing shall be subject toagreement between the user and the producer.11.2 Material furnished under this specification shall beidentified by the name or symbol of the producer, by alloy typeand grade, or producers brand name, or a combination thereof,heat number, and material size. Each heat supplied o

33、n a givenorder must be identified separately and packaged separately.12. Keywords12.1 coercive field strength; coercivity; ferritic stainlesssteel; free-machining; relayTABLE 4 Chemical RequirementsAlloy Type Carbon, maxManganese,maxSiliconPhosphorus,maxSulfur ChromiumMolybdenum,maxNickel, max Iron1

34、 0.065 0.80 0.30/0.70 0.030 0.25/0.40 17.25/18.25 0.50 0.60 bal2 0.065 0.80 1.00/1.50 0.030 0.25/0.40 17.25/18.25 0.50 0.60 balTABLE 5 DC Coercive Field Strength (Hc) RequirementsRing and Permeameter TestingAlloy Type Grade Bar Diameter Range, in. (mm) Hc, max11$0.250 (6.35) #0.6875 (17.46) 2.30 Oe

35、(183 A/m)0.6875 (17.46) #1.625 (41.28) 3.00 Oe (239 A/m)12$0.250 (6.35) #0.6875 (17.46) 4.70 Oe (374 A/m)0.6875 (17.46) #1.625 (41.28) 5.00 Oe (398 A/m)13$0.250 (6.35) #1.625 (41.28) 7.00 Oe (557 A/m)1 full anneal (all grades) $0.250 (6.35) #1.625 (41.28) 2.20 Oe (175 A/m)21$0.250 (6.35) #0.6875 (17

36、.46) 2.60 Oe (207 A/m)0.6875 (17.46) #1.625 (41.28) 2.80 Oe (223 A/m)22$0.250 (6.35) #1.625 (41.28) 7.00 Oe (557 A/m)2 full anneal (all grades) $0.250 (6.35) #1.625 (41.28) 2.60 Oe (207 A/m)TABLE 6 Coercive Field Strength (Hc) RequirementsCoercimeter TestingAlloy Type Grade Bar Diameter Range, in. (

37、mm) Hc, max11$0.250 (6.35) #0.6875 (17.46) 2.90 Oe (231 A/m)0.6875 (17.46) #1.625 (41.28) 3.60 Oe (286 A/m)12$0.250 (6.35) #0.6875 (17.46) 6.00 Oe (477 A/m)0.6875 (17.46) #1.625 (41.28) 6.60 Oe (525 A/m)13$0.250 (6.35) #1.625 (41.28) 8.50 Oe (676 A/m)1 full anneal (all grades) $0.250 (6.35) #1.625 (

38、41.28) 2.80 Oe (223 A/m)21$0.250 (6.35) #0.6875 (17.46) 3.40 Oe (271 A/m)0.6875 (17.46) #1.625 (41.28) 3.60 Oe (286 A/m)22$0.250 (6.35) #1.625 (41.28) 8.50 Oe (676 A/m)2 full anneal (all grades) $0.250 (6.35) #1.625 (41.28) 3.40 Oe (271 A/m)A838 02 (2013)3APPENDIX(Nonmandatory Information)X1. TYPICA

39、L PHYSICAL, MAGNETIC, AND MECHANICAL PROPERTIESX1.1 Typical physical and magnetic properties are listed inTable X1.1 for the two alloy types contained in this specifica-tion. Magnetic property data shown were measured on 0.250-to 0.375-in. (6.35- to 9.52-mm) diameter mill-annealed (Grade1both types)

40、 bar using a Fahy Permeameter in accordancewith Test Method A341/A341M. Larger-diameter bars willyield lower maximum permeabilities and residual inductionsdue to limitations associated with testing large-diameter, rela-tively high-permeability bars on a permeameter. Typical me-chanical property data

41、 other than hardness for Grade 1 of bothalloy types is shown in Table X1.2. Typical hardness ranges aregiven in Table X1.3. The data provided are for informationonly and are not requirements in this specification and need notbe measured.ASTM International takes no position respecting the validity of

42、 any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to

43、revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Y

44、our comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is co

45、pyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.

46、org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).TABLE X1.1 Typical Physical and Magnetic PropertiesProperty Alloy Type 1 Alloy Type 2Density, g/cm3(kg/m3) 7.62 (7620) 7.59 (7590)E

47、lectrical resistivity, -cm (-mm) 60.0 (600) 76.0 (760)Mean coefficient of thermal expansion,(0649C) (m/m/C)(11.9) (11.9)Curie temperature, C 671 660Saturation flux density, kG (T) 15.5 (1.55) 15.2 (1.52)(Relative) maximum permeability 2300 2350Residual induction,AkG (T) 7.54 (0.754) 7.42 (0.742)Coer

48、cive field strength,AOe (A/m) 1.80 (143) 1.64 (130)AResidual induction and coercive field strength are determined from a maximum flux density of 10 kG (1.0 T).TABLE X1.2 Typical Mechanical PropertiesGrade 1Property Alloy Type 1 Alloy Type 20.2 % yield strength, ksi (MPa) 45 (310) 50 (350)Ultimate te

49、nsile strength, ksi (MPa) 75 (520) 78 (540)Percent elongation in 2 in. (50.8 mm) 20 30Percent reduction in area 60 60TABLE X1.3 Typical HardnessAlloy Type Grade Typical Hardness1 1 75 to 82 HRB1 2 82 to 91 HRB1 3 85 HRB at midradius92 HRB at surface2 1 80 to 88 HRB2 2 85 HRB at midradius92 HRB at surfaceA838 02 (2013)4