ASTM A1022 A1022M-2007 Standard Specification for Deformed and Plain Stainless Steel Wire and Welded Wire for Concrete Reinforcement《混凝土加筋用刻痕和普通不锈钢丝和焊接钢丝的标准规范》.pdf

《ASTM A1022 A1022M-2007 Standard Specification for Deformed and Plain Stainless Steel Wire and Welded Wire for Concrete Reinforcement《混凝土加筋用刻痕和普通不锈钢丝和焊接钢丝的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM A1022 A1022M-2007 Standard Specification for Deformed and Plain Stainless Steel Wire and Welded Wire for Concrete Reinforcement《混凝土加筋用刻痕和普通不锈钢丝和焊接钢丝的标准规范》.pdf（9页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A 1022/A 1022M 07Standard Specification forDeformed and Plain Stainless Steel Wire and Welded Wirefor Concrete Reinforcement1This standard is issued under the fixed designation A 1022/A 1022M; the number immediately following the designation indicates theyear of original adoption or, in

2、 the case of revision, the year of last revision. A number in parentheses indicates the year of lastreapproval. A superscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers stainless steel wire and weldedwire reinforcement produ

3、ced from hot-rolled stainless steelrod. The stainless steel wire is cold-worked, drawn or rolled,plain (non-deformed) or deformed or a combination of de-formed and plain. It is used as concrete reinforcement forapplications requiring resistance to corrosion and/or controlledmagnetic permeability. Co

4、mmon wire sizes and dimensions arefound in this specification. Actual wire sizes are not restrictedto those shown in the tables.1.2 Supplement S1 describes high strength wire, which shallbe furnished when specifically ordered. It shall be permissibleto furnish high strength wire in place of regular

5、wire ifmutually agreed to by the purchaser and supplier.1.2.1 A supplementary requirement (S2) of an optionalnature is provided. It shall apply only when specified by thepurchaser. In order to obtain a corrosion tested or controlledmagnetic permeability product, steel conforming to Supple-mentary Re

6、quirement S2 should be ordered.1.3 The chemical composition of the steel (stainless grade)shall be selected for suitability to the application involved byagreement between the manufacturer and the purchaser. UseSpecification A 276 for chemical requirements. The UNSdesignations are to be included wit

7、h the type number and notedin brackets, i.e. austenitic stainless steels as Type 304S30400, 304L S30403, 316 S31600, 316L S31603,316N S31651, 316LN S31653 and duplex stainless steels,Types 2205 S32205 and 329 S32900.NOTE 1Only austenitic and duplex stainless steels are usually recom-mended for use a

8、s reinforcement in concrete because of their highcorrosion resistance. Austenitic stainless steels have good general corro-sion resistance, strength characteristics which can be improved by coldworking, good toughness and ductility properties at low temperatures, andlow magnetic permeability. Duplex

9、 stainless steels have generally acorrosion resistance greater than that of most austenitic steels and aremagnetic. Other stainless steels with different chemical compositions thanthe series and types mentioned above, may be used for less restrictiveapplications.1.4 Wire for welded wire reinforcemen

10、t is generally manu-factured at 520 MPa 75 ksi yield strength level. Otherstrength levels shall be by agreement between the purchaserand manufacturer.NOTE 2The term used to refer to yield strength levels are the same asthose in ASTM Standards for welded wire reinforcement.1.5 The values stated in ei

11、ther SI units or inch-pound unitsare to be regarded separately as standard. The values stated ineach system may not be exact equivalents; therefore, eachsystem shall be used independently of the other. Combiningvalues from the two systems may result in non-conformancewith the standard.2. Referenced

12、Documents2.1 ASTM Standards:2A 82/A 82M Specification for Steel Wire, Plain, for Con-crete ReinforcementA 185/A 185M Specification for Steel Welded Wire Rein-forcement, Plain, for ConcreteA 276 Specification for Stainless Steel Bars and ShapesA 342/A 342M Test Methods for Permeability of FeeblyMagne

13、tic MaterialsA 370 Test Methods and Definitions for Mechanical Testingof Steel ProductsA 496/A 496M Specification for Steel Wire, Deformed, forConcrete ReinforcementA 497/A 497M Specification for Steel Welded Wire Rein-forcement, Deformed, for ConcreteA 700 Practices for Packaging, Marking, and Load

14、ingMethods for Steel Products for ShipmentE83 Practice for Verification and Classification of Exten-someter Systems2.2 Military Standards:3MIL-STD-129 Marking for Shipment and Storage2.3 Federal Standard:1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and

15、 Related Alloys and is the direct responsibility of SubcommitteeA01.05 on Steel Reinforcement.Current edition approved Sept. 1, 2007. Published October 2007. Originallyapproved in 2001. Last previous edition approved in 2006 as A 1022/A 1022M06.2For referenced ASTM standards, visit the ASTM website,

16、 www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Available from Standardization Documents Order Desk, DODSSP, Bldg. 4,Section D, 700 Robbins Ave., Philadelphia, PA

17、19111-5098, http:/www.dodssp.daps.mil.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.Fed. Std. No. 123 Marking for Shipments (Civil Agencies)32.4 ACI Standard:ACI 318

18、 Building Code Requirements for Structural Con-crete43. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 stainless steel plain wire and welded plain wirereinforcementas used within the scope and intent of thisspecification, designates a material composed of cold-workedstainless st

19、eel wire, as cold-drawn or cold-rolled from stainlesssteel hot-rolled rod. The welded intersections provide the bondstrength for shear resistance.3.1.2 stainless steel deformed wire and welded deformedwire reinforcementas used within the scope and intent of thisspecification, designates a material c

20、omposed of cold- workeddeformed stainless steel wire as cold-drawn or cold-rolled fromstainless steel hot-rolled rod. Deformations shall be permittedto be indented or raised rib (protrusion) types. As with plainstainless steel welded wire, the welded intersections providebond strength for shear resi

21、stance and the deformations add tothe bond strength.3.1.3 convoluted wirewhen wire for welded wire rein-forcement is formed into a sinusoidal wave shape, it iscommonly referred to as convoluted wire. The wire is used inthe manufacture of cages for certain applications of concretepipe reinforcement.

22、Only plain wire is normally subject toconvolution.4. Ordering Information4.1 It shall be the responsibility of the purchaser to specifyall requirements that are necessary for material ordered to thisspecification. Such requirement shall include but are notlimited to the following:4.1.1 Quantitymass

23、(weight) or square area.4.1.2 Name of material (Ex: stainless steel welded wire forconcrete reinforcement).4.1.3 Wire spacing and wire sizes.4.1.4 Exclusion of over-steeling or using a larger area ofsteel than specified.4.1.5 Length and width of sheets or rolls.4.1.6 ASTM designation and year of iss

24、ue.4.1.7 Application (corrosion resistance or magnetic perme-ability).4.1.8 Grade (strength level).4.1.9 Chemical composition (stainless steel grade).4.1.10 Heat treatment condition.4.1.11 Supplementary requirements (if desired).NOTE 3A typical ordering description is as follows: For metric units:10

25、,000 square meters of welded wire for concrete reinforcement,3053305-MW653MW65, in flat sheets 2438 mm wide by 4.6 mm longin secured bundles for crane or forklift truck lifts. For in-lbs units:(100,000 square feet of welded wire for concrete reinforcement, 12312-W103W10 in flat sheets 96 in. wide by

26、 15 ft long) in secured bundles forcrane or forklift truck lifts. Testing shall be in accordance with TestMethods A 370.NOTE 4Longitudinal wires can be variably spaced. (Ex: 3053305-MW653MW65,12312-W103W10 or V3305-MD653MD65 or V312-D103D10). See the Tables 1 and 2 for wire sizes.5. Materials5.1 Sta

27、inless steel wire for welded wire reinforcement shallbe cold worked, either drawn or rolled from steel rod, which isrolled from properly identified heats of mold or strand caststeel.5.2 Cold worked wire or rod used in the manufacture ofstainless steel welded reinforcement shall follow the chemicalan

28、d physical requirements of Specification A 276.6. Manufacture6.1 The wire or rod shall be assembled by automaticmachines or by other suitable mechanical means which willassure accurate spacing and alignment of all wires of thefinished welded wire reinforcement. The finished welded wirereinforcement

29、shall be furnished in flat or bent sheets or in rollsas specified by the purchaser.6.2 Longitudinal and transverse wires shall be securelyconnected at every intersection by a process of electrical-resistance welding which employs the principle of fusioncombined with pressure.6.3 Wire of proper grade

30、 and quality when fabricated in themanner herein required shall result in a strong, serviceableproduct having substantially square or rectangular openings. Itshall be fabricated and finished in a quality manner andconform to this specification.6.4 General Requirements for Plain Wire:6.4.1 Plain Wire

31、 Criteria:4Available from American Concrete Institute (ACI), P.O. Box 9094, FarmingtonHills, MI 48333-9094, http:/www.aci-int.org.TABLE 1 Dimensional Requirements for Plain WireSI UnitsSizeNumberANominal Diameter,mmNominal Area,mm2MW 5 2.50 5MW 10 3.60 10MW 15 4.40 15MW 20 5.00 20MW 25 5.60 25MW 30

32、6.20 30MW 35 6.70 35MW 40 7.10 40MW 45 7.60 45MW 50 8.00 50MW 55 8.40 55MW 60 8.70 60MW 65 9.10 65MW 70 9.40 70MW 80 10.10 80MW 90 10.70 90MW 100 11.30 100MW 120 12.40 120MW 130 12.90 130MW 200 15.95 200MW 290 19.22 290AThis table represents a hard metrication of the most readily available sizes int

33、he welded wire reinforcement industry. Table 1 shall be used in projects that aredesigned using SI units: Table 2 shall be used on projects designed usinginch-pound units.Areas of wire shall be checked with the most efficient and readilyavailable material from producers. Other wire sizes are availab

34、le and manymanufacturers can produce them in 1-mm2increments.A 1022/A 1022M 0726.4.1.1 When plain wire is ordered by size number, therelation between size number, diameter, and area shown inTables 1 and 2 shall apply.6.4.2 Testing:6.4.2.1 Specimens for mechanical properties testing shall befull wire

35、 sections and shall be obtained from ends of wire coilsas drawn. The specimens shall be of sufficient length toperform testing described in Test Methods A 370.6.4.2.2 Test specimens for determining weld-shear proper-ties shall be obtained by cutting from the finished welded wire,a full width section

36、 of sufficient length to perform testingdescribed in Specification A 185/A 185Mor SpecificationA 497/A 497M.6.4.2.3 Measurements for conformance to dimensionalcharacteristics shall be made on full sheets or rolls.6.4.2.4 If any test specimen exhibits obvious isolated im-perfections not representativ

37、e of the product, it shall bediscarded and another specimen substituted.6.4.2.5 Reduction of AreaShall be determined as de-scribed in Test Methods and Definitions A 370. The wire shallconform to the reduction of area requirements in Tables 5 and6.6.4.2.6 One tension and one bend test shall be made f

38、romeach 9000 kg 10 tons or less of each size of wire or fractionthereof.6.5 General Requirements for Deformed Wire:6.5.1 Deformation Criteria:6.5.1.1 Deformations shall be spaced along the wire at asubstantially uniform distance and shall be symmetricallydisposed around the perimeter. The deformatio

39、ns on all longi-tudinal lines of the wire shall be similar in size and shape. Aminimum of 25 % of the total surface area shall be deformedby measurable deformations.6.5.1.2 Deformed wire shall have two or more lines ofdeformations.6.5.1.3 The average longitudinal spacing of deformationsshall be not

40、less than 3.5 nor more than 5.5 deformations per 25mm (1 in.) in each line of deformations on the wire.6.5.1.4 The minimum average height of the center of typicaldeformations based on the nominal wire diameters shown inTables 7 and 8 shall be as follows:Wire Sizes Minimum Average Height of Deformati

41、ons,Percent of Nominal Wire DiameterMD 19 D 3 and finer 4Coarser than MD 19 D 3 throughMD 65 D 10412Coarser than MD 65 D 10 56.5.1.5 The deformations shall be placed with respect to theaxis of the wire so that the included angle is not less than 45;or if deformations are curvilinear, the angle forme

42、d by thetransverse axis of the deformation and the wire axis shall be notless than 45. Where the line of deformations forms an includedangle with the axis of the wire from 45 to 70 inclusive, theTABLE 2 Dimensional Requirements for Plain WireInch-poundUnitsSizeNumberANominal Diameter,in.Nominal Area

43、,in2W 0.5 0.080 0.005W 1.2 0.124 0.012W 1.4 0.134 0.014W 2 0.160 0.020W 2.5 0.178 0.025W 2.9 0.192 0.029W 3.5 0.211 0.035W 4 0.226 0.040W 4.5 0.239 0.045W 5 0.252 0.050W 5.5 0.265 0.055W 6 0.276 0.060W 8 0.319 0.080W 10 0.357 0.100W 11 0.374 0.110W 12 0.391 0.120W 14 0.422 0.140W 16 0.451 0.160W 18

44、0.479 0.180W 20 0.505 0.200W 22 0.529 0.220W 24 0.533 0.240W 26 0.575 0.260W 28 0.597 0.280W 30 0.618 0.300W 31 0.628 0.310W 45 0.757 0.450AThis table represents the most readily available sizes in the welded wirereinforcement industry in sizes using inch-pound units. Areas of wire shall bechecked w

45、ith the most efficient and readily available material from producers.Other wire sizes are available and many manufacturers can produce them in0.0015-in.2increments.TABLE 3 Bend Test RequirementsPlain WireSize Number Of Wire Bend TestMW45 W7 and smaller Bend around a pin the diameter that is equal to

46、the diameter of the specimenLarger than MW45 W7 Bend around a pin the diameter that is equal totwice the diameter (2d) of the specimenTABLE 4 Permissible Variation in Wire DiameterPlain WireSize Numbermetric in-lbs.Nominal Diameter,mm in.Permissible VariationPlus and Minus,mm in.Smaller than MW32 W5

47、,MW32 W5 toMW77 W12, inclUnder 6.4 0.2526.4 0.252 to 9.930.391, incl0.08 0.0030.10 0.004Over to MW130 W20,inclOver 9.93 0.391to 12.83 0.505,incl0.15 0.006Over MW130 W20 Over 12.83 0.505 0.20 0.008TABLE 5 Tension Test RequirementPlain WireTensile strength, min, MPa ksi 550 80Yield strength, min, MPa

48、ksi 485 70Reduction of area, min. % 30AAFor material testing over 690 MPa 100 ksi tensile strength, the reduction ofarea shall be not less than 25%.TABLE 6 Tension Test Requirement Plain Wire (Material forWelded Wire)Size MW8 W1.2and LargerSmaller thanSize MW8W1.2Tensile strength, min, MPa ksi 515 7

49、5 485 70Yield strength, min, MPa ksi 450 65 385 56Reduction of area, min. % 30A30AAFor material testing over 690 MPa 100 ksi tensile strength, the reduction ofarea shall be not less than 25%.A 1022/A 1022M 073deformations shall alternately reverse in direction on each side,or those on one side shall be reversed in direction from thoseon the opposite side. Where the included angle is over 70, areversal in direction is not required.6.5.1.6 The average spacing of deform