SAE AMS 5911B-2009 Steel Corrosion-Resistant Sheet and Strip 19Cr - 9 2Ni (SAE 30304) Cold Rolled 1 2 Hard 150 ksi (1034 MPa) Tensile Strength (UNS S30400)《19Cr 9 2Ni(SAE 30304)冷轧 .pdf

《SAE AMS 5911B-2009 Steel Corrosion-Resistant Sheet and Strip 19Cr - 9 2Ni (SAE 30304) Cold Rolled 1 2 Hard 150 ksi (1034 MPa) Tensile Strength (UNS S30400)《19Cr 9 2Ni(SAE 30304)冷轧 .pdf》由会员分享，可在线阅读，更多相关《SAE AMS 5911B-2009 Steel Corrosion-Resistant Sheet and Strip 19Cr - 9 2Ni (SAE 30304) Cold Rolled 1 2 Hard 150 ksi (1034 MPa) Tensile Strength (UNS S30400)《19Cr 9 2Ni(SAE 30304)冷轧 .pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、_ SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising there

2、from, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be revised, reaffirmed, stabilized, or cancelled. SAE invites your written comments and suggestions. Copyright 2014 SAE International All rights reserved. No part of this p

3、ublication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-497

4、0 (outside USA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/www.sae.org/technical/standards/AMS5911B AEROSPACE MATERIAL SPECIFICATION AMS5911 REV. B Issued 1992-01 Revised 2

5、009-04 Reaffirmed 2014-06 Superseding AMS5911A Steel, Corrosion-Resistant, Sheet and Strip 19Cr - 9.2Ni (SAE 30304) Cold Rolled, 1/2 Hard, 150 ksi (1034 MPa) Tensile Strength (Composition similar to UNS S30400) RATIONALE This document has been reaffirmed to comply with the SAE five-year review polic

6、y. 1. SCOPE 1.1 Form This specification covers a corrosion-resistant steel in the form of sheet and strip. 1.2 Application These products have been used typically for applications requiring moderate forming and bending, but usage is not limited to such applications. 1.2.1 Mechanical properties speci

7、fied herein are obtained by cold working (strain hardening), and not by heat treatment. Therefore, the cold-worked product should not be heated to a temperature which adversely affects the mechanical properties or corrosion-resistance before, during, or after fabrication. 2. APPLICABLE DOCUMENTS The

8、 issue of the following documents in effect on the date of the purchase order forms a part of this specification to the extent specified herein. The supplier may work to a subsequent revision of a document unless a specific document issue is specified. When the referenced document has been cancelled

9、 and no superseding document has been specified, the last published issue of that document shall apply. 2.1 SAE Publications Available from SAE International, 400 Commonwealth Drive, Warrendale, PA 15096-0001, Tel: 877-606-7323 (inside USA and Canada) or 724-776-4970 (outside USA), www.sae.org. AMS2

10、242 Tolerances, Corrosion and Heat-Resistant Steel, Iron Alloy, Titanium, and Titanium Alloy Sheet, Strip, and Plate AMS2248 Chemical Check Analysis Limits, Corrosion and Heat-Resistant Steels and Alloys, Maraging and Other Highly-Alloyed Steels, and Iron Alloys AMS2371 Quality Assurance Sampling an

11、d Testing, Corrosion and Heat-Resistant Steels and Alloys, Wrought Products and Forging Stock AMS2807 Identification, Carbon and Low-Alloy Steels, Corrosion and Heat-Resistant Steels and Alloys, Sheet, Strip, Plate, and Aircraft Tubing SAE INTERNATIONAL AMS5911B Page 2 of 5 2.2 ASTM Publications Ava

12、ilable from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-9585, www.astm.org. ASTM A 370 Mechanical Testing of Steel Products ASTM E 290 Bend Testing of Material for Ductility ASTM E 353 Chemical Analysis of Stainless, Heat-Resisting, Maragi

13、ng, and Other Similar Chromium-Nickel-Iron Alloys ASTM E 384 Microindentation Hardness of Materials 3. TECHNICAL REQUIREMENTS 3.1 Composition Shall conform to the percentages by weight shown in Table 1, determined by wet chemical methods in accordance with ASTM E 353, by spectrochemical methods, or

14、by other analytical methods acceptable to purchaser. TABLE 1 - COMPOSITION Element min max Carbon - 0.08 Manganese - 2.00Silicon - 1.00 Phosphorus - 0.040 Sulfur - 0.030Chromium 18.00 20.00 Nickel 8.00 10.50Molybdenum - 0.75 Copper - 0.75 3.1.1 Check Analysis Composition variations shall meet the ap

15、plicable requirements of AMS2248. 3.2 Condition Solution heat treated, descaled unless solution heat treatment is performed in an atmosphere yielding a bright finish, and cold rolled. 3.3 Properties The product shall conform to the following requirements; tensile and hardness properties shall be det

16、ermined in accordance with ASTM A 370: 3.3.1 Tensile Properties Shall be as shown in Table 2 for product over 0.005 inch (0.13 mm) in nominal thickness. SAE INTERNATIONAL AMS5911B Page 3 of 5 TABLE 2A - MINIMUM TENSILE PROPERTIES, INCH/POUND UNITS Property Value Tensile Strength 150 ksi Yield Streng

17、th at 0.2% Offset 110 ksi Elongation in 2 Inches or 4D Nominal Thickness Over 0.005 to 0.015 inch, incl 6% Over 0.015 inch 7% TABLE 2B - MINIMUM TENSILE PROPERTIES, SI UNITS Property Value Tensile Strength 1034 MPa Yield Strength at 0.2% Offset 758 MPa Elongation in 50.8 mm or 4D Nominal Thickness O

18、ver 0.13 to 0.38 mm, inch, incl 6% Over 0.38 mm 7% 3.3.2 Hardness Shall be not lower than 32 HRC, or equivalent (See 8.2). Product shall not be rejected on the basis of hardness if the tensile properties of 3.3.1 are acceptable, determined on specimens taken from the same sample as that with nonconf

19、orming hardness or from another sample with similar nonconforming hardness. 3.3.2.1 Microhardness testing in accordance with ASTM E 384 may be used for thin gages where superficial hardness testing is impractical. 3.3.3 Bending Product shall be tested in accordance with ASTM E 290 using a sample pre

20、pared nominally 0.75 inch (19.0 mm) in width, with the axis of bend parallel to the direction of rolling, and shall withstand, without cracking, when bending at room temperature through the angle indicated in Table 3 around a diameter equal to the bend factor times the nominal thickness of the produ

21、ct. In case of dispute, the results of tests using the guided bend test of ASTM E 290 shall govern. TABLE 3A - BENDING, INCH/POUND UNITS Nominal Thickness Inch Angle degrees, min Bend Factor Up to 0.050, incl 180 2 Over 0.050 to 0.187, incl 90 2 TABLE 3B - BENDING, SI UNITS Nominal Thickness Millime

22、ters Angle degrees, min Bend Factor Up to 1.27, incl 180 2 Over 1.27 to 4.75, incl 90 2 SAE INTERNATIONAL AMS5911B Page 4 of 5 3.4 Quality The product, as received by purchaser, shall be uniform in quality and condition, sound, and free from foreign materials and from imperfections detrimental to us

23、age of the product. 3.5 Tolerances Shall conform to all applicable requirements of AMS2242. 4. QUALITY ASSURANCE PROVISIONS 4.1 Responsibility for Inspection The vendor of the product shall supply all samples for vendors tests and shall be responsible for the performance of all required tests. Purch

24、aser reserves the right to sample and to perform any confirmatory testing deemed necessary to ensure that the product conforms to specified requirements. 4.2 Classification of Tests All technical requirements are acceptance tests and shall be performed on each heat or lot as applicable. 4.3 Sampling

25、 and Testing Shall be in accordance with AMS2371. 4.4 Reports The vendor of the product shall furnish with each shipment a report showing the results of tests for composition of each heat and for tensile, hardness, and bending properties of each lot, and stating that the product conforms to the othe

26、r technical requirements. This report shall include the purchase order number, heat and lot numbers, AMS5911B, size, and quantity. 4.5 Resampling and Retesting Shall be in accordance with AMS2371. 5. PREPARATION FOR DELIVERY 5.1 Identification Shall be in accordance with AMS2807. 5.2 Packaging The p

27、roduct shall be prepared for shipment in accordance with commercial practice and in compliance with applicable rules and regulations pertaining to the handling, packaging, and transportation of the product to ensure carrier acceptance and safe delivery. 6. ACKNOWLEDGMENT A vendor shall mention this

28、specification number and its revision letter in all quotations and when acknowledging purchase orders. 7. REJECTIONS Product not conforming to this specification, or to modifications authorized by purchaser, will be subject to rejection. SAE INTERNATIONAL AMS5911B Page 5 of 5 8. NOTES 8.1 A change b

29、ar (|) located in the left margin is for the convenience of the user in locating areas where technical revisions, not editorial changes, have been made to the previous issue of a document. An (R) symbol to the left of the document title indicates a complete revision of the document, including techni

30、cal revision. Change bars and (R) are not used in original publications, nor in documents that contain editorial changes only. 8.2 Hardness conversion tables for metals are presented in ASTM E 140. 8.3 Terms used in AMS are clarified in ARP1917. 8.4 Dimensions and properties in inch/pound units and

31、the Fahrenheit temperatures are primary: dimensions and properties in SI units and the Celsius temperatures are shown as the approximate equivalents of the primary units and are presented only for information. 8.5 Purchase documents should specify not less than the following: AMS5911B Form and size of product desired Quantity of product desired. 8.6 Similar Specifications MIL-S-5059, Type 304, Condition 1/2 Hard, is listed for information only and shall not be construed as an acceptable alternate unless all requirements of this AMS are met. PREPARED BY AMS COMMITTEE “F“