SAE AMS 2431 8B-2007 Peening Media (AWCH) Conditioned Carbon Steel Cut Wire Shot High Hardness (55 to 62 HRC)《适合高硬度(55～62 HRC)喷丸硬化介质(AWCH)的碳钢切割线射丸》.pdf

《SAE AMS 2431 8B-2007 Peening Media (AWCH) Conditioned Carbon Steel Cut Wire Shot High Hardness (55 to 62 HRC)《适合高硬度(55～62 HRC)喷丸硬化介质(AWCH)的碳钢切割线射丸》.pdf》由会员分享，可在线阅读，更多相关《SAE AMS 2431 8B-2007 Peening Media (AWCH) Conditioned Carbon Steel Cut Wire Shot High Hardness (55 to 62 HRC)《适合高硬度(55～62 HRC)喷丸硬化介质(AWCH)的碳钢切割线射丸》.pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、 SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising theref

2、rom, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invites your written comments and suggestions. Copyright 2007 SAE International All rights reserved. No part of this publication ma

3、y be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: 724-776-4970 (outside USA)

4、Fax: 724-776-0790 Email: custsvcsae.org SAE WEB ADDRESS: http:/www.sae.org AMS 2431/8B AEROSPACE MATERIAL SPECIFICATION Issued SEP 1996 Revised MAY 2007 Superseding AMS 2431/8A Peening Media (AWCH) Conditioned Carbon Steel Cut Wire Shot, High Hardness (55 to 62 HRC) RATIONALE This revision adds Cut

5、Wire Shot sizes 80, 96 and 116; Figures 1, 2 and 3 were changed. 1. SCOPE 1.1 Purpose The complete requirements for procuring the product shall consist of this document and the latest issue of the basic specification, AMS 2431. 1.2 Application Conditioned carbon steel cut wire shot, high hardness, c

6、onforming to this specification is intended for use in peening metal surfaces to impart compressive stresses to these surfaces thereby increasing resistance to fatigue and stress-corrosion cracking. Generally, high hardness conditioned carbon steel cut wire shot is used on parts of hardness 50 HRC o

7、r over. 2. APPLICABLE DOCUMENTS See AMS 2431. 3. TECHNICAL REQUIREMENTS 3.1 Conditioned carbon steel cut wire shot, high hardness, shall conform to AMS 2431 and the requirements specified herein. 3.2 Composition shall conform to the percentages by weight shown in paragraph 5.1 of SAE J441 (For refer

8、ence only, see Table 1), and shall be determined in accordance with ASTM E 350. TABLE 1 - COMPOSITION Element min max Carbon 0.45 0.85 Manganese 0.30 1.30 Silicon 0.15 0.35 Phosphorus - 0.040Sulfur - 0.05 SAE AMS 2431/8B - 2 - 3.3 Hardness Not less than 90% of the readings, using a microhardness tes

9、ter with a minimum 500 gram load, shall fall within the range of 55 to 62 HRC, or equivalent, determined in accordance with ASTM E 384. Hardness testing shall be performed after the shot has been conditioned for shape. 3.4 Wire Quality Shot shall be manufactured from wire that is free from shear cra

10、cks and laps and shall not contain excessive seams or burrs. 3.5 Weight shall conform to Table 3 or Table 4 as determined in accordance with 4.1.3.2. 3.6 Contamination Shot shall be clean and free of dirt, grit, oil, or grease. 3.7 Quality requirements shall conform to 3.7.1, 3.7.2, 3.7.3, and 3.7.4

11、, determined in accordance with 3.9.2. 3.7.1 Shape shall be predominantly spherical as a result of conditioning or rounding. 3.7.2 Acceptable Shapes Shapes conforming to Figure 1 shall be in accordance with Table 2. 3.7.3 Marginal Shapes Shapes conforming to Figure 2 are permissible to the extent sp

12、ecified in Table 2. 3.7.4 Unacceptable Shapes Shapes conforming to Figure 3 are permissible to the extent specified in Table 2. 3.7.5 Conditioning is accomplished by impacting the as-cut wire cylinders against a hardened target until a predominantly round shape (See Figure 1) has been obtained. TABL

13、E 2 - SHAPE REQUIREMENTS Shot Size Area per Field Square Inches (mm2) Number of Fields Viewed Number of Marginal Particles All Fields max(1) Number of Unacceptable Particles All Fields max(2) AWCH 116 1(645) 3 7 2 AWCH 96 1(645) 2 7 2 AWCH 80 1(645) 2 10 3 AWCH 62 1 (645) 9 63 2 AWCH 54 1 (645) 7 66

14、 2 AWCH 47 1 (645) 5 68 2 AWCH 41 1 (645) 4 70 2 AWCH 35 AWCH 32 0.25 (161) 0.25 (161) 14 12 67 60 2 2 AWCH 28 0.25 (161) 7 67 2 AWCH 23 0.25 (161) 5 70 2 AWCH 20 0.25 (161) 4 76 2 AWCH 17 0.0625 (40) 11 70 2 AWCH 14 0.0625 (40) 6 60 2 AWCH 12 0.0625 (40) 5 68 2 Notes: (1) Maximum number of marginal

15、 shapes is approximately 3% of the total number of particles viewed. (2) Maximum number of unacceptable shapes is approximately 1% of the total number of particles viewed. SAE AMS 2431/8B - 3 - 3.8 Size shall conform to the requirements of Table 3 and Table 4, determined in accordance with 3.9.1. TA

16、BLE 3 - SIZE REQUIREMENTS, 50 PIECE SAMPLE Shot Size Wire Diameter Inch Wire Diameter Millimeters Weight of 50 pieces Grams AWCH 116 0.116 0.002 2.946 0.05 5.77 to 7.05 AWCH 96 0.096 0.002 2.438 0.05 3.45 to 4.25 AWCH 80 0.080 0.002 2.032 0.05 2.09 to 2.55 AWCH 62 0.0625 0.002 1.588 0.05 0.98 to 1.2

17、0 AWCH 54 0.054 0.002 1.37 0.05 0.65 to 0.79 AWCH 47 0.047 0.002 1.19 0.05 0.43 to 0.52 AWCH 41 0.041 0.002 1.04 0.05 0.28 to 0.35 AWCH 35 0.035 0.001 0.89 0.025 0.18 to 0.22 AWCH 32 0.032 0.001 0.81 0.025 0.12 to 0.16 AWCH 28 0.028 0.001 0.71 0.025 0.09 to 0.11 AWCH 23 0.023 0.001 0.58 0.025 0.045

18、to 0.060 AWCH 20 0.020 0.001 0.51 0.025 0.035 to 0.045 TABLE 4 - SIZE REQUIREMENTS, 100 PIECE SAMPLE Shot Size Wire Diameter Inch Wire Diameter Millimeter Weight of 100 pieces Grams AWCH 17 0.017 0.001 0.43 0.025 0.040 to 0.055 AWCH 14 0.014 0.001 0.36 0.025 0.015 to 0.030 AWCH 12 0.012 0.001 0.30 0

19、.025 0.010 to 0.020 3.9 Test Methods and Procedures 3.9.1 Size The size of shot shall be determined in accordance with 4.1.3.2. 3.9.2 Shape Visual evaluation, at a minimum magnification of 10X for sizes CW 23 and larger and a minimum magnification of 30X for sizes finer than CW 23, shall be performe

20、d using the areas and number of fields specified in Table 2 for each respective shot size. 4. QUALITY ASSURANCE PROVISIONS See AMS 2431 and the following: 4.1 Sampling and Testing Two samples of approximately 800 grams each shall be selected from separate containers chosen at random from each lot. E

21、ach sample shall be split to test quantities as follows: 4.1.1 Composition Not less than two samples from each lot shall be evaluated. 4.1.2 Hardness Not less than 20 microhardness readings shall be made from each sample with no more than one impression on any one shot. SAE AMS 2431/8B - 4 - 4.1.2.1

22、 Samples for microhardness testing shall be prepared by encapsulating a representative sample of each lot in a plastic mount and polishing down to nominal half spheres. 4.1.3 Size Two representative samples of not less than 100 grams each shall be used for size evaluation. 4.1.3.1 Alternative method

23、s for size evaluation may be used provided that they can be correlated to the weight method and are acceptable to purchaser. 4.1.3.2 Fifty pieces of the conditioned media shall meet the weight requirements of Table 3. One hundred pieces of the conditioned media shall meet the weight requirements of

24、Table 4. 4.1.4 Shape A representative sample shall consist of a number of shot, in one layer, which completely fills the areas specified in Table 2. The number of areas, or fields, viewed at 10X or 30X (See 3.9.2) evaluated for each shot size shall be as indicated in Table 2. 4.1.4.1 Alternative met

25、hods of inspection for shape are permitted provided that they can be correlated to the optical method and are acceptable to purchaser. 5. PREPARATION FOR DELIVERY See AMS 2431 and the following: 5.1 Packaging and Identification Steel shot shall be packaged in 40 to 55 pound (18 to 25 kg) units in plastic coated bags or pails. 6. ACKNOWLEDGMENT See AMS 2431. 7. REJECTIONS See AMS 2431. 8. NOTES See AMS 2431. PREPARED BY AMS COMMITTEE “B” SAE AMS 2431/8B - 5 - FIGURE 1 - ACCEPTABLE SHAPES FIGURE 2 - MARGINAL SHAPES FIGURE 3 - UNACCEPTABLE SHAPES