FORD WSK-M2P169-A-2008 PAINT PERFORMANCE ENGINE COMPARTMENT HIGH DURABILITY TO BE USED WITH FORD WSS-M99P1111-A 《发动机舱用高耐久性油漆的性能 与标准FORD WSS-M99P1111-A一起使用 [使用 FORD WSS-M2P185-A.pdf

《FORD WSK-M2P169-A-2008 PAINT PERFORMANCE ENGINE COMPARTMENT HIGH DURABILITY TO BE USED WITH FORD WSS-M99P1111-A 《发动机舱用高耐久性油漆的性能 与标准FORD WSS-M99P1111-A一起使用 [使用 FORD WSS-M2P185-A.pdf》由会员分享，可在线阅读，更多相关《FORD WSK-M2P169-A-2008 PAINT PERFORMANCE ENGINE COMPARTMENT HIGH DURABILITY TO BE USED WITH FORD WSS-M99P1111-A 《发动机舱用高耐久性油漆的性能 与标准FORD WSS-M99P1111-A一起使用 [使用 FORD WSS-M2P185-A.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Ver. 4 2008 09 11 N-STATUS Replaced by WSS-M2P185-A2 G. Weber, FNA 2003 08 12 Revised Para 3.0 inserted; Para 3.1, 3.2, 3.12, 4 deleted 1992 09 01 Released EP00E10176304000 K. Wolters Printed copies are uncontrolled Copyright 2008, Ford Globa

2、l Technologies, Inc. Page 1 of 2 PAINT PERFORMANCE, ENGINE COMPARTMENT, HIGH DURABILITY WSK-M2P169-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE This specification defines the performance requirements for paint systems where resistance to corrosion, fuel, hot oil and coolant is required. 2. APPLICATION T

3、his specification was released originally to define paint performance requirements for electrocoated engine accessories, oil pans as well as sheet metal parts within the engine compartment. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must

4、conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.3 SYSTEM COMPONENTS 3.3.1 Substrate Cold rolled steel, pre-coated, electroplated zinc or zinc alloy coated steel as specified on Engineering Drawing. 3.3.2 Pretreatment The surface to be coated must be free fr

5、om oil, rust, dirt, fingerprints, moisture, and other foreign materials. All substrates shall be zinc phosphated and conform to the requirements of WSK-M3P1-C. 3.3.3 Cathodic Electrocoat Suitable to meet the requirements of this specification or as specified on Engineering Drawing. 3.3.4 Ageing Test

6、 panels or test specimens prepared for investigations according to this specification must be aged for at least 2 hours at 23 +/- 2 C or 16 hours at 45 +/- 1 C prior to testing. 3.4 FILM PROPERTIES 3.4.1 Color Black or as specified on (FLTM BI 109-01) Engineering Drawing ENGINEERING MATERIAL SPECIFI

7、CATION WSK-M2P169-A Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, Inc. Page 2 of 2 3.4.2 Gloss Semi-gloss or as specified on (FLTM BI 110-01) Engineering Drawing 3.4.3 Film Thickness, min Suitable to meet the requirements (FLTM BI 117-01) of this specification 3.4.4 Adhes

8、ion Grade Grade 1 (FLTM BI 106-01, Method B) 3.4.5 Initial Hardness The finish shall be sufficiently hard after curing to withstand normal handling without damage. 3.5 SALT SPRAY RESISTANCE 480 h (FLTM BI 103-01) No blistering, no rusting or loss of adhesion more than 3 mm from the scribed line. 3.6

9、 WATER IMMERSION TEST 240 h (FLTM BI 104-01) No loss of adhesion, no loss of gloss and no blistering accepted. 3.7 RESISTANCE TO SCAB CORROSION (FLTM BI 123-01, 10 Cycles) No blistering, rusting or loss of adhesion more than 3 mm from the scribe line. 3.8 HEAT RESISTANCE 24 h at 180 +/- 3 C No loss

10、of adhesion per 3.4.4. No flaking, no cracking and no change of color or gloss accepted. 3.9 RESISTANCE AGAINST HOT OIL (8 h immersion at 180 +/- 2 C) The test panel shall be immersed into current production engine oil as required. Evaluate one hour after test end. No blistering, no loss of adhesion

11、 and not more than slight dulling and softening. 3.10 SOLVENT RESISTANCE (FLTM BI 152-01) No blistering, no loss of adhesion and not more than slight dulling or softening accepted. 3.11 RESISTANCE AGAINST COOLANT (1 h immersion at 70 +/- 2 C) Test panels shall be immersed into a mixture of 50% water and 50% current production coolant. No blistering, no loss of adhesion and not more than slight dulling or softening accepted.