《EN 60684-3-228-2004 en Flexible insulating sleeving Part 3 Specifications for individual types of sleeving Sheet 228 Heat-shrinkable semi-rigid polyvinylidene fluoride sleeving fla.pdf》由会员分享，可在线阅读，更多相关《EN 60684-3-228-2004 en Flexible insulating sleeving Part 3 Specifications for individual types of sleeving Sheet 228 Heat-shrinkable semi-rigid polyvinylidene fluoride sleeving fla.pdf（12页珍藏版）》请在麦多课文档分享上搜索。

1、BRITISH STANDARD BS EN 60684-3-228:2004 Flexible insulating sleeving Part 3: Specifications for individual types of sleeving Sheet 228: Heat-shrinkable, semi-rigid polyvinylidene fluoride sleeving, flame retarded, fluid resistant, shrink ratio 2:1 The European Standard EN 60684-3-228:2004 has the st

2、atus of a British Standard ICS 29.035.20 BS EN 60684-3-228:2004 This British Standard was published under the authority of the Standards Policy and Strategy Committee on 24 September 2004 BSI 24 September 2004 ISBN 0 580 44485 6 National foreword This British Standard is the official English languag

3、e version of EN 60684-3-228:2004. It is identical with IEC 60684-3-228:2004. It supersedes BS EN 60684-3-228:1998 which is withdrawn. The UK participation in its preparation was entrusted by Technical Committee GEL/15, Insulating material, to Subcommittee GEL/15/3, Material specifications, which has

4、 the responsibility to: A list of organizations represented on this subcommittee can be obtained on request to its secretary. Cross-references The British Standards which implement international or European publications referred to in this document may be found in the BSI Catalogue under the section

5、 entitled “International Standards Correspondence Index”, or by using the “Search” facility of the BSI Electronic Catalogue or of British Standards Online. This publication does not purport to include all the necessary provisions of a contract. Users are responsible for its correct application. Comp

6、liance with a British Standard does not of itself confer immunity from legal obligations. aid enquirers to understand the text; present to the responsible European committee any enquiries on the interpretation, or proposals for change, and keep the UK interests informed; monitor related internationa

7、l and European developments and promulgate them in the UK. Summary of pages This document comprises a front cover, an inside front cover, the EN title page, pages 2 to 9 and a back cover. The BSI copyright notice displayed in this document indicates when the document was last issued. Amendments issu

8、ed since publication Amd. No. Date CommentsEUROPEAN STANDARD EN 60684-3-228 NORME EUROPENNE EUROPISCHE NORM August 2004 CENELEC European Committee for Electrotechnical Standardization Comit Europen de Normalisation Electrotechnique Europisches Komitee fr Elektrotechnische Normung Central Secretariat

9、: rue de Stassart 35, B - 1050 Brussels 2004 CENELEC - All rights of exploitation in any form and by any means reserved worldwide for CENELEC members. Ref. No. EN 60684-3-228:2004 E ICS 29.035.20 Supersedes EN 60684-3-228:1998English version Flexible insulating sleeving Part 3: Specifications for in

10、dividual types of sleeving Sheet 228: Heat-shrinkable, semi-rigid polyvinylidene fluoride sleeving, flame retarded, fluid resistant, shrink ratio 2:1 (IEC 60684-3-228:2004) Gaines isolantes souples Partie 3: Spcifications pour types particuliers de gaines Feuille 228: Gaines thermortractables semi-r

11、igides en fluorure de polyvinylidne, retardes la flamme, rsistant aux fluides, rapport de rtreint 2:1 (CEI 60684-3-228:2004) Isolierschluche Teil 3: Anforderungen fr einzelne Schlauchtypen Blatt 228: Wrmeschrumpfende Polyvinylidenefluoridschluche, halbsteif, flammwidrig, flssigkeitsbestndig, Schrump

12、fverhltnis 2:1 (IEC 60684-3-228:2004) This European Standard was approved by CENELEC on 2004-07-01. CENELEC members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration.

13、 Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the Central Secretariat or to any CENELEC member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translat

14、ion under the responsibility of a CENELEC member into its own language and notified to the Central Secretariat has the same status as the official versions. CENELEC members are the national electrotechnical committees of Austria, Belgium, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Ge

15、rmany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. EN 68604-3-22:80024 - - 2 Foreword The text of document 15C/1599/FDIS, future edition 2 of IEC 60684-3-228,

16、 prepared by SC 15C, Specifications, of IEC TC 15, Insulating materials, was submitted to the IEC-CENELEC parallel vote and was approved by CENELEC as EN 60684-3-228 on 2004-07-01. This European Standard supersedes EN 60684-3-228:1998. The significant technical change with regard to EN 60684-2-228:1

17、998 is: - Replacement of the thermal endurance test method according to EN 60216 with a long term ageing test, i.e. 3 000 h at the recommended maximum temperature found suitable for use, in order to provide safe thermal test data within a workable time scale. The following dates were fixed: latest d

18、ate by which the EN has to be implemented at national level by publication of an identical national standard or by endorsement (dop) 2005-04-01 latest date by which the national standards conflicting with the EN have to be withdrawn (dow) 2007-07-01 Annex ZA has been added by CENELEC. _ Endorsement

19、notice The text of the International Standard IEC 60684-3-228:2004 was approved by CENELEC as a European Standard without any modification. _ Page2 EN606843228:2004066-48-3228 IE2:C 400 3 INTRODUCTION This International Standard is part of a series which deals with flexible insulating sleeving for e

20、lectrical purposes. The series consists of three parts: Part 1: Definitions and general requirements (IEC 60684-1) Part 2: Methods of test (IEC 60684-2) Part 3: Specifications for individual types of sleeving (IEC 60684-3) This standard is one of the sheets comprising Part 3, as follows: Sheet 228:

21、Heat-shrinkable, semi-rigid polyvinylidene fluoride sleeving, flame retarded, fluid resistant, shrink ratio 2:1. Page3 EN606843228:2004066-48-3228 IE2:C 400 4 FLEXIBLE INSULATING SLEEVING Part 3: Specifications for individual types of sleeving Sheet 228: Heat-shrinkable, semi-rigid polyvinylidene fl

22、uoride sleeving, flame retarded, fluid resistant, shrink ratio 2:1 1 Scope This standard gives the requirements for one type of heat-shrinkable, flame retarded, with a nominal shrink ratio 2:1, fluid resistant polyvinylidene fluoride sleeving for use at temperatures up to 175 C. This sleeving is nor

23、mally supplied with an internal diameter up to 25,4 mm, and the standard colour is transparent. Sizes or colours other than those specifically listed in this standard may be available as custom items. These items are considered to comply with this standard if they comply with the property requiremen

24、ts listed in Tables 2, 3, 4 and 5, with the exception of dimensions and mass. Materials which conform to this specification meet established levels of performance. However, the selection of a material by a user for a specific application should be based on the actual requirements necessary for adequ

25、ate performance in that application and not based on this specification alone. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the ref

26、erenced document (including any amendments) applies. IEC 60684-1:2003, Flexible insulating sleeving Part 1: Definitions and general requirements IEC 60684-2:1997, Flexible insulating sleeving Part 2: Methods of test Amendment 1(2003) IEC 60757:1983, Code for designation of colours ISO 846:1978, Plas

27、tics Evaluation of the action of micro-organisms ISO 1817:1999, Rubber, vulcanized Determination of the effect of liquids Page4 EN606843228:2004066-48-3228 IE2:C 400 5 3 Designation The sleeving shall be identified by the following designation: Description IEC publication number IEC part number IEC

28、sheet number Size (expanded/ recovered internal diameter, in mm) Colour Sleeving IEC 60684 - 3 - 228 - 12,7/6,4 - TT *Any colour abbreviation shall comply with IEC 60757. Where no abbreviation is given, the colour shall be written in full. 4 Conditions of test Unless otherwise specified, the sleevin

29、g shall be shrunk in a forced air circulation oven for (5 1) min at 200 C 5 K prior to testing. 5 Requirements In addition to the general requirements given in IEC 60684-1, the sleeving shall comply with the requirements set out in Tables 1, 2, 3, 4 and 5. 6 Sleeving conformance Conformance with the

30、 requirements of this specification shall normally be based on the results from size 12,7/6,4 mm transparent sleeving. The colour fastness to light shall be determined for all colours. Table 1 Dimensional and mass requirements Internal diameter mm Size code Expanded Min. Recovered Max. Recovered wal

31、l thickness mm Mass per unit length Max. g/m 1,2/0,6 1,2 0,6 0,25 0,05 1,5 1,6/0,8 1,6 0,8 0,25 0,05 1,9 2,4/1,2 2,4 1,2 0,25 0,05 2,5 3,2/1,6 3,2 1,6 0,25 0,05 3,2 4,8/2,4 4,8 2,4 0,25 0,05 4,6 6,4/3,2 6,4 3,2 0,30 0,10 8,1 9,5/4,8 9,5 4,8 0,30 0,10 11,8 12,7/6,4 12,7 6,4 0,30 0,10 15,4 19,0/9,5 19

32、,0 9,5 0,45 0,10 31,2 25,4/12,7 25,4 12,7 0,50 0,10 45,1 *TT designates transparent sleeving. Page5 EN606843228:2004066-48-3228 IE2:C 400 6 Table 2 Property requirements Property IEC 60684-2 Clause or subclause Units Max. or min. Requirements Remarks Dimensions internal diameter wall thickness conce

33、ntricity expanded recovered 3 3.1.2 3.3.2 3.3.3 mm mm % Min. Table 1 Table 1 65 85 Heat shock Tensile strength Elongation at break 6 19.1 and 19.2 19.1 and 19.2 MPa % Min. Min. 15 75 Heat at 250 C 5 K Longitudinal change 9 % Max. +0 10 Heat the expanded sleeving at 200 C 5 K for (5 1) min Bending at

34、 low temperature 14 No cracks shall be visible Condition at 55 C 3 K. For strips, the mandrel shall be no more than 10 times the wall thickness. Full section sleeving is tested unfilled and the mandrel shall be no more than 10 times the outer diameter Dimensional stability during storage 16 The dime

35、nsions shall be as specified in Table 1 Tensile strength Elongation at break 19.1 and 19.2 19.1 and 19.2 MPa % Min. Min. 35 150 Use a jaw separation rate of 100 mm/min. Below 6,5 mm diameter as sleeving; at 6,5 mm diameter and above as dumb-bells Secant modulus at 2 % elongation 19.4 MPa MPa Min. Ma

36、x. 250 750 Breakdown voltage 21 kV Min. Table 3 Volume resistivity at room temperature after damp heat 23 23.4.2 23.4.4 m m Min. Min. 10 910 8Flame propagation Time of burning Length burned 26 Method C s mm Max. Max. 15 75 Transparency 28 Printing shall be legible Transparent only Copper corrosion 3

37、3 % Max. None above the allowable 8 % Heat for (16 0,5) h at 175 C 3 K Page6 EN606843228:2004066-48-3228 IE2:C 400 7 Table 2 (continued) Property IEC 60684-2 Clause or subclause Units Max. or min. Requirements Remarks Colour fastness to light 34 The colour contrast between the exposed and unexposed

38、parts of the specimens shall be equal to or less than that of the fastness standard. After this test, transparent sleeving shall meet the requirements for transparency Fastness standard No. 5 Resistance to selected fluids Tensile strength Elongation at break 36 19.1 and 19.2 19.1 and 19.2 MPa % Min.

39、 Min. 25 150 Use the fluids and test temperatures specified in Table 4 Mass per unit length 38 g/m Max. Table 1 Heat ageing Tensile strength Elongation at break 39 19.1 and 19.2 19.1 and 19.2 MPa % Min. Min. 15 75 Heat at 200 C 3 K Water absorption 40 % Max. 0,5 Long-term ageing Elongation 50 (Amend

40、ment 1) 19.1 and 19.2 % Min. 100 The test to establish failure shall be elongation at break: the ageing temperature shall be 175 C 3 K The breakdown voltage shall be determined by any of the methods described in 21.2, 21.3 or 21.4 of IEC 60684-2. The central value shall comply with the minimum value

41、 in Table 3 below. The rate of application of the voltage shall be 500 V/s. Table 3 Requirements for breakdown voltage Nominal recovered wall thicknessamm Breakdown voltage Min. kV 0,25 0,30 0,45 0,50 5,0 6,0 9,0 10,0 a For non-standard wall thicknesses, the electric strength shall be at least that

42、of the next smaller standard wall thickness. For wall thicknesses smaller than 0,25 mm, the electric strength shall be at least 20,0 kV/mm. Page7 EN606843228:2004066-48-3228 IE2:C 400 8 Table 4 Resistance to selected fluids Fluids Type Standard or symbol Immersion temperature C 2 K Gasoline ISO 1817

43、 Liquid B 23 Fuels Kerosene ISO 1817 Liquid F 70 Phosphate base ISO 1817 Liquid 103 23 Silicone base S-1714* 70 Hydraulic fluids Mineral base H-520* 50 Synthetic base ISO 1817 Liquid 101 70 Mineral base ISO 1817 Oil No. 2 70 Mineral base O-1176* 70 Oils Mineral base O-142* 50 Isopropyl alcohol 23 Pr

44、opanol 25 % White spirit 75 % 23 Cleaning fluids Solvent Methylethylketone 23 Runway de-icers Inhibited potassium acetate in water, 50 % 23 De-icing fluids Aircraft de-icers Ethylene glycol 80 %, water 20 % 23 * These are commercially available fluids which can be identified in aviation fluid guides

45、. NOTE Other fluids and/or temperatures may be specified for customers with specific needs. These additional fluids and/or temperatures should be applicable when incorporated into agreements between the supplier and the customer. Table 5 Additional property requirements Property IEC 60684-2 Subclaus

46、e Units Max. or min. Requirements Remarks Fungus resistance Tensile strength Elongation at break 19.1 and 19.2 19.1 and 19.2 MPa % Min. Min. 35 150 The test method shall be ISO 846, Method B. 56 days exposure Shelf lifeaThe dimensions shall be as specified in Table 1 Condition the sleeving for 60 mo

47、nths at ambient temperature prior to testing; interim measurements are to be made every 12 months aDue to the duration of this test, lack of completion of this test shall not preclude certification of this specification. Additional evidence of compliance with this requirement in the interim shall be

48、 as agreed between the supplier and/or the approval authority and/or the customer. Page8 EN606843228:2004 - - 3 EN 68604-3-22:80024 Annex ZA (normative) Normative references to international publications with their corresponding European publications The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. NOTE Where an international publication has been modified by co