1、I INCHPOUND I 23 August 2000 SUPERSEDING 7 Aprll 1993 A-A-55192A A-A-55 192 COMMERCIAL ITEM DESCRIPTION CASE, MAP The General Services Administration has authorized the use of this Commercial Item Description for all federal agencies. 1. SCOPE. This commercial item description covers map cases to be

2、 used to protect maps in the field. 2. CLASSIFICATION. There shall be one type of map case in the following sizes as specified Size 1 - 22 inches long by 30 inches wide (+l; -0 inches) Size 2 - 38-1/2 inches long by 52-3/4 inches wide (+l; -0 inches) 3. SALIENT CHARACTERISTICS. The map cases shall b

3、e constructed of two clear pieces of vinyl film and a clear vinyl zipper with an aluminum slide closure The film used in fabricating all map cases shall be flexible, for use in a temperature range from O degrees F to 130 degrees F (-17 degrees C to 54.4 degrees C) and shall be 0.014 inch thick vinyl

4、 chloride or polyvinyl chloride. The Map Case shall have a dull-matte finish. The vinyl cases shall have a minimum of 1/8 inch heat sealed seams on three sides, the two long sides and one short side. The open end of the case shall be fitted with a clear vinyl zipper with an aluminum slide of appropr

5、iate length, heat-sealed to the case. One part of the zipper shall be heat sealed to the back of the case and the other part heat sealed to the front part of the case. The ends of the zipper shall be heat sealed to prevent the sides from becoming disengaged. Beneficial comments (recommendations, add

6、itions, deletions) and any pertinent data which may be of use in improving this document should be addressed to: Defense Supply Center Philadelphia, Clothing and Textiles Directorate, Attn: DSCP-COET, 700 Robbins Ave., Philadelphia, PA 191 11-5092. AMSC N/A FSC 8460 DISTRIBUTION STATEMENT A: APPROVE

7、D FOR PUBLIC RELEASE: DISTRIBUTION IS UNLIMITED. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-A-A-55192A Size 1 2 3.1 .Material The flexiblelnon-rigid vinyl chloride plastic film can be calendered, extruded or cast film. The contractor shall ident

8、ify the type of film used on the contract or purchase order. Film shall meet all the requirements listed in accordance with ASTM D 1593. The zipper closure shall be made of a clear compound of vinyl chloride or polyvinyl chloride conforming to the resin material requirements specified in ASTM D 1593

9、. The zipper shall have a slider and pull made of aluminum. Length Width (inches) Tolerance Zipper Size Heat Sealed (inches) (inches) (inches) Seam (inches) 22 30 +1, -0 22 118 38-112 52-314 +1, -0 38-112 ll8 + 036,-O 3.2 Finish. The film shall have a smooth, dull-matte finish on both sides unless o

10、therwise specified by the contract or purchase order. 3.3 Label. The case shall be labeled with the following: Item Description Contract Number Stock Number Size Contractors Name The size and the characters shall be approximately ?A inch high. A white marking medium shall be used. The label shall be

11、 clearly legible after being subjected to the ink adhesion test. The label shall be located midway (+I- 2 inches) between the sealed seams and the opening. 3.4 Bar CodeLabel Tag. Each item shall be individually bar-coded with a paper tag, standard bleach sulfate with a basis weight of 100 lbs. The b

12、ar code shall be a 13 digit national stock number (NSN). The bar code shall be used with a medium to high density and shall be human- readible interpretation (HRI). The labelltag shall be located so that it is completely visible on the item when it is completely folded andor packaged as specified an

13、d shall cause no damage to the item. 3.5 Sizes and Measurements. The finished case shall conform to the measurements below. Table I. Sizes and Measurements 2 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-A-A-55192A 3.6 Performance. 3.6.1 Sealed Sea

14、ms. AU heat sealed seams shall be a minimum of 1/8 inch wide, cleanly trimmed, with no unsealed film beyond permitted sealed area. The breaking strength of the heat sealed seams shall be not less than 16 pounds when tested in accordance with Method A of ASTM D 882. See Figure 1. 3.6.2 Leakage. The c

15、over shall not leak or separate at the seam when tested as specified. 3.7 Workmanship. The finished map case shall be thoroughly clean, well finished, free from gels, pinholes, holes, cracks and blisters, fish eyes, mottling, particles of foreign matter and undispersed raw material. Raw edges shall

16、be free from nicks and cuts. 4 Redatow Requirements. The offeror/contractor is encouraged to use recovered materials to the maximum extent practicable, in accordance with paragraph 23.403 of the Federal Acquisition Regulation (FAR). 5 Product Conformance Provisions 5.1 Product Conformance. The contr

17、actor shall certify and maintain substantiating evidence that the product offered meets the salient characteristics and requirements of this Commercial Item Description and that the product conforms to the producers own drawings, specifications, standards and quality assurance practices. The governm

18、ent reserves the right to require proof of such conformance prior to the first delivery and thereafter as may be otherwise provided for, under the provisions of the contract. Reliance on contractor QA systems shall not relieve the contractor of the responsibility of ensuring that all products or sup

19、plies submitted to the government for acceptance comply with all requirements of the contract 5.2 Visual Examination. Case lots shall be inspected in accordance with Sampling Procedures and Tables for Inspection by Attributes, ANSUASQC 21.4, published by the American Society for Quality Control. The

20、 cases shall be examined for the defects listed below. 5.2.1 Defects. The case shall be examined for the following defects: not uniformly colorless and clear; not dull matte finish; objectionable odor; any blister or fish eye or unfused resin particles; seam not continuous, not uniform; poor heat se

21、al resulting in inadequate fusion; corners not rounded; any hole, crack, wrinkle, tear, sharp crease or cut; any spot, stain, or other discoloration which requires a cleaning agent for removal; not clean, evidence of dirt, grit, oil, or other foreign matter on or in map case; zipper does not work pr

22、operly; any rough or sharp edge; label missing, incorrect, or illegible; not constructed as specified. Labeytag omitted or not readible by scanner; human readible interpretation (HRI) omitted or illegible; not visible on folded packaged item; or causes damage to the item. 3 Provided by IHSNot for Re

23、saleNo reproduction or networking permitted without license from IHS-,-,-A-A-55192A 5.2.2 Dimensional Examination. The finished case shall conform to the dimensions specified. Any dimension that is not within the established tolerance (+i inch, -0 inch) shall be classified as a defect. 5.3 End Item

24、Performance Testing. The end items shall be tested for odor, label adhesion, seam strength, crease strength and leakage. 5.3.1 Requirement for Odor . Determination of odor shall be made on samples freely exposed to circulating air at 75 degrees F +/- 5 degrees F (24 degrees C +/- 3 degrees C) for no

25、t less than 24 hours. 5.3.2 Requirement for label adhesion. Each case shall have a label that is directly printed, stamped or stenciled on the case. The contents, size and characters of the inscription, and the format shall be as follows; ITEM DESCRIPTION CONTRACT NUMBER STOCK NUMBER SIZE - minimum

26、of 18 points (approximately ?A inch) - minimum of 18 points (approximately ?A inch) - minimum of 18 points (approximately ?A inch) - minimum of 18 points (approximately ?A inch) CONTRACTORS NAME (bottom of label) - maximum of 18 points (approximately ?A inch 5.3.3. Seam Strength Requirement. Each sp

27、ecimen shall be cut 1 inch by 6 inches with the seam approximately in the middle and parallel to the short sides of the specimen. If the average breaking strength for any sample unit falls to meet the requirements specified, the lot shall be rejected. 5.3.4. Requirement for Leakage. The case shall n

28、ot leak or separate at the seam when tested as specified. 5.3.5 Odor test. Determination of odor shall be made on samples freely exposed to circulating air at 75 degrees F +/- 5 degrees F (24 degrees C +/- 3 degrees C) for not less than 24 hours. 5.3.6 Ink adhesion label test. The ink adhesion shall

29、 be determined in accordance with ASTM F 1842 except that the test shall be performed on the label of a finished case. The test area of the label shall be visually examined for legibility. 4 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-A-A-55192A

30、5.3.7 Seam strena test. The breaking strength of the heat sealed seams shall be not less than 16 pounds when tested in accordance with Method A of ASTM D 882. Each specimen shall be cut 1 inch by 6 inches from a finished case with the seam approximately in the middle and parallel to the short sides

31、of the specimen. The gage marks need not be applied and the elongation need not be measured. The initial separation between the grips of the apparatus shall be 2 inches and the specimen shall be placed in grips with the seam equidistant between the grips. The strength of the seam reported in pounds

32、to the nearest 0.1 pound shall be the average of 5 determinations per sample unit. 5.3.8 Leakage Test. The case shall be marked 5 inches from the inside of the seam and filled with water to the mark. The temperature of the water shall be 73.5 +/- 2 degrees F. The case shall then be suspended over a

33、dry receptacle for a period of 3 hours. At the end of the 3 hour period, the case shall be examined for seam separation and leakage of the water into the receptacle. 6.0 Packaging. Preservation, Packaging and Marking. Cases of one size only shall be packed in accordance with ASTM D 3951 except that

34、twenty (20) size 1 or ten (10) size 2 cases in each container. 7. Notes. Sources of Non-government Documents ANSUASQC 21.4 - Sampling Procedures and Tables For Inspection By Attributes (Applications for copies should be addressed to American National Standards Institute, 11 West 42nd Street, New Yor

35、k, NY 10036.) ASTM D 882 - Tensile Properties of Thin Plastic Sheeting ASTM D 1593 - Standard Specification for Non-rigid Vinyl Chloride Plastic Film and Sheeting ASTM-D 395 1 - Standard Practice for Commercial Packaging ASTM F 1842 - Standard Test Method for Determining Ink or Coating Adhesion on P

36、lastic Substrate for Membrane Switch Applications (Applications for copies should be addressed to American Society For Testing and Materials, 100Barr Harbor Drive, West Conshohocken, PA 19428) 5 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-Custodi

37、ans: Navy-MC Amiy-GL A-A-55192A Civil Agency Coordinating Activity: GSA - FSS Preparing Activity: DLA- CT Project No. 8460-0098 6 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-A-A-55192A b 3 4 Figure 1 - Case, Map 7 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-