1、BRITISH STANDARD BS ISO 15987:2003 Plastics Film and sheeting Biaxially oriented polyamide (nylon) films ICS 83.140.10 BS ISO 15987:2003 This British Standard was published under the authority of the Standards Policy and Strategy Committee on 1 June 2003 BSI 1 June 2003 ISBN 0 580 41937 1 National f

2、oreword This British Standard reproduces verbatim ISO 15987:2003 and implements it as the UK national standard. The UK participation in its preparation was entrusted to Technical Committee PRI/75, Plastics films and sheets, which has the responsibility to: A list of organizations represented on this

3、 committee can be obtained on request to its secretary. Cross-references The British Standards which implement international publications referred to in this document may be found in the BSI Catalogue under the section entitled “International Standards Correspondence Index”, or by using the “Search”

4、 facility of the BSI Electronic Catalogue or of British Standards Online. This publication does not purport to include all the necessary provisions of a contract. Users are responsible for its correct application. Compliance with a British Standard does not of itself confer immunity from legal oblig

5、ations. aid enquirers to understand the text; present to the responsible international/European committee any enquiries on the interpretation, or proposals for change, and keep the UK interests informed; monitor related international and European developments and promulgate them in the UK. Summary o

6、f pages This document comprises a front cover, an inside front cover, the ISO title page, pages ii and iii, a blank page, pages 1 to 6, an inside back cover and a back cover. The BSI copyright date displayed in this document indicates when the document was last issued. Amendments issued since public

7、ation Amd. No. Date CommentsINTERNATIONAL STANDARD ISO 15987 First edition 2003-05-15 Reference number ISO 15987:2003(E) OSI 2003 Plastics Film and sheeting Biaxially oriented polyamide (nylon) films Plastiques Film et feuille Films en polyamide (nylon) bi-orientsBSISO15987:2003 ISO :78951(3002)E ii

8、 ISO 3002 All rithgs reresvde id FDPscalimer ThFDP si fam eliy ctnome niat deddebyepfa.sec In cacnadrociw eth sebodA sneciliycilop gn, thf siam elirp eb ytnide or viewb detu llahs ton tide ebed lnuet sst ehyfepcaa hcihw serdebme et desnecil era dedo tsni dnat no dellahpmoc eturep reformign ttide ehi

9、gn. In odt gnidaolnwsih liferap ,tcca seitpe trehnie snopser ehtitiliby fo nto fnirA gnigniycilop gnisnecil sebod. Teh SItneC Olar Seerctraiat catpecs ibail ontily t nih.aera si Aebod t a sirramedak fo AsyS ebodtmeI snocrropta.de teDlias fo tfos ehtwcudorp erats t desutaerc ot esih FDP fb nac elif e

10、t ni dnuoG ehreneI lafnr oleative tt of eh;eli tP ehDF-rctaenoi temaraptpo erew sremizif deorp rinti.gn Evrey t neeb sah eracakt neo rusnee ttah tf ehtius si elibaf elosu re by ISO memdob rebsei. In eht kilnuyle evtne ttah a borplme rtaleit gno it si f,dnuo esaelp ifnrom thtneC erla ceSrteraita ta t

11、eh sserdda vigoleb new. IOS 3002 Alr lithgs reresv.de sselnU toesiwreh sficep,dei rap ont fo thbup silitaciam nocudorper eb yde or tuilidez na nif yorm ro by nam ysnae, tcelerm ro cinocinahcela, tohp gnidulcnicopom dna gniyicrfomli, tiwuoht repsimsi noin wrtif gnirtie mohI reSO ta the asserdd ebwol

12、or ISOmem sreb obyd t nitnuoc ehry fo teh euqertsre. SIc Oopyrigho tfifce saCsop etela 65 -HCG 1121eneva 02 T.le 22 14 + 10 947 11 Fxa + 22 14 0 94774 9 Eam-il ocpyrithgios.ogr Web wwwi.soo.rg BSISO15987:2003 ISO 89513002:7)E( ISO 3002 r llAithgs reservde iii Foreword ISO (the International Organiza

13、tion for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established

14、has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. In

15、ternational Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare International Standards. Draft International Standards adopted by the technical committees are circulated to the member bodies for voting. Publi

16、cation as an International Standard requires approval by at least 75 % of the member bodies casting a vote. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent r

17、ights. ISO 15987 was prepared by Technical Committee ISO/TC 61, Plastics, Subcommittee SC 11, Products. BSISO15987:2003 blank BSISO15987:2003 ANRETNIITOTS LANDNADRA ISO 89513002:7)E( ISO 3002 r llAithgs reservde 1 Plastics Film and sheeting Biaxially oriented polyamide (nylon) films 1S c o p e This

18、International Standard specifies biaxially oriented transparent polyamide (nylon) films, mainly used for packaging. NOTE Biaxially oriented transparent polyamide (nylon) films are used alone and/or as laminated film with other films. 2 Normative references The following referenced documents are indi

19、spensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. ISO 291:1997, Plastics Standard atmospheres for conditioning and testing ISO 527-3:1995, Pla

20、stics Determination of tensile properties Part 3: Test conditions for films and sheets ISO 4593:1993, Plastics Film and sheeting Determination of thickness by mechanical scanning ISO 8296:1987, Plastics Film and sheeting Determination of wetting tension ISO 14782:1999, Plastics Determination of haze

21、 for transparent materials ISO 15105-1:2002, Plastics Film and sheeting Determination of gas-transmission rate Part1: Differential-pressure method ISO 15105-2:2003, Plastics Film and sheeting Determination of gas-transmission rate Part 2: Equal- pressure method 3 Classification Films are classified

22、into two groups as follows. 1) Film treated with corona discharge. 2) Film not treated with corona discharge. 4 Requirements 4.1 Appearance The films shall be visibly free of flaws, slackness, wrinkles, stains, foreign matter or any marks that impair its serviceability. BSISO15987:2003 ISO :78951(30

23、02)E 2 ISO 3002 All rithgs reresvde The splicing of two films in a roll shall be prominently marked in order to provide a visible indication from the side of the roll. The interested parties shall agree upon the method of marking the splice. NOTE One acceptable method of marking is the use of colour

24、ed adhesive tape. 4.2 Dimensions 4.2.1 General For any individual film selected at random from any delivery, the dimensions listed in 4.2.2 to 4.2.5, including their nominal values, shall be agreed upon among interested parties. 4.2.2 Width The tolerance of film width shall be within of the nominal

25、value. An example of film width with corresponding tolerance is given in Table 1. 4.2.3 Length of film in a roll The tolerance of film length in a roll shall be within of the nominal value. Examples of film length and corresponding tolerance in a roll are shown in Table 2. 4.2.4 Inside diameter of c

26、ore of a roll The inside diameter tolerance of a core of a roll shall be within of the nominal value. Examples of inside diameter of core in a roll, and corresponding tolerance are given in Table 3. 4.2.5 Thickness The thickness tolerance shall be within of the nominal value. Examples of thicknesses

27、 and corresponding tolerances are given in Table 4. Table 1 Example of a film width and its tolerance Width ToleranceNOTE : integer, 0, 1, 2, ., in width steps of . Table 2 Examples of film length in a roll and their tolerances Length of film Tolerance of length of film Nominal length Length in a ro

28、ll 400 0 4 600 0 6 800 0 8of nominal length +4 0 mm mm mm 500+ 40n +4 0 n 40 mm +1 0 % mk mm +40 0 +60 0 +80 0 8 000 81 % +2 0 mm 10 % BSISO15987:2003 ISO 89513002:7)E( ISO 3002 r llAithgs reservde 3 4.3 Physical properties Films shall meet the requirements of physical properties listed in Table 5.

29、4.4 Physiological behaviour For applications involving food contact, the film shall conform to all applicable regulatory requirements. 5 Test methods 5.1 Conditioning and testing of specimens Testing of tensile properties, haze and wetting tension shall be carried out in a standard atmosphere of , i

30、n accordance with ISO 291, after conditioning the specimens for at least under the same conditions. Specimens for the testing of dimensional change on heating shall also be conditioned under these conditions. Table 3 Examples of inside diameters of a core in a roll and their tolerances Inside diamet

31、er of core Tolerance on inside diameter of core 76 152 Table 4 Examples of thicknesses and their tolerances Thickness Tolerance Nominal thickness Thickness No. 12 12 15 15 25 25 Table 5 Properties of film Properties Unit Test method Requirements Testing in accordance with subclause Longitudinal a Tr

32、ansverse b Tensile strength at break ISO 527-3 5.4 Tensile strain at break ISO 527-3 5.4 Dimensional change on heating 5.5 Coefficient of oxygen transmission c ISO 15105-1 or ISO 15105-2 5.6 Haze ISO 14782 5.7 Wetting tension d ISO 8296 5.8 a Longitudinal: direction parallel to extrusion or “machine

33、 direction”. b Transverse: direction perpendicular to extrusion. c , relative humidity. d The wetting tension shall only apply to films treated with corona discharge mm mm +2 0 +2 0 m m 1,2 1,5 2,5 MPa 150 150 % 200 200 % 6,0 6,0 fmol 100 m/ m 2 s Pa 41 % 8,0 mN/m 40 23 C0% (23 2) C (50 5) % 8h BSIS

34、O15987:2003 ISO :78951(3002)E 4 ISO 3002 All rithgs reresvde 5.2 Visual examination The appearance of the film shall be checked with the naked eye. 5.3 Dimensions 5.3.1 Width The width of the film shall be measured using a calibrated metal rule. 5.3.2 Inside diameter of core of roll The Inside diame

35、ter of the core of a roll shall be measured using a vernier calliper. 5.3.3 Thickness The average thickness of films shall be measured to the nearest using a dial gauge or equivalent in accordance with ISO 4593. Five piles of films shall be used for thicknesses over and ten piles of films shall be u

36、sed for film thicknesses not more than . The thickness of films shall be measured at ten equidistant points across the film width. The thickness shall be reported as the arithmetic average of these measurements. 5.4 Tensile strength and tensile strain at break Tensile strength and tensile strain at

37、break shall be determined by tensile testing at least five specimens in accordance with ISO 527-3. The specimen dimensions are shown in Figure 1. The test speed shall be . Width: to Thickness: Gauge length: Initial distance between grips: Overall length: a Gauge marks Figure 1 Tensile test specimen

38、1 m 15 m 15 m (200 20) mm/min b 10 mm 25 mm h 1mm L 0 50 mm 0,5 mm L 100 mm5mm l 3 150 mm BSISO15987:2003 ISO 89513002:7)E( ISO 3002 r llAithgs reservde 5 5.5 Dimensional change on heating 5.5.1 Preparation of specimen Prepare 5 specimens, in width and approximately in length for both the longitudin

39、al direction and the transverse direction. Mark off a gauge length centred on the specimen (each mark approximately from the end). 5.5.2 Procedure Suspend the specimens vertically in a circulating air oven which is kept at for . After removal from the oven, allow them to cool for to room temperature

40、. Measure the length between marks. Calculate an arithmetic mean of 5 specimens using the following equation: where is the numerical value of the dimensional change on heating, expressed as a percentage; is the numerical value of the length between marks before heating, expressed in millimetres; is

41、the numerical value of the length between marks after heating, expressed in millimetres. 5.6 Coefficient of oxygen transmission The coefficient of oxygen transmission shall be determined in accordance with ISO 15105-1 or ISO 15105-2 The result is calculated by the following equation expressed per th

42、ickness. where is the numerical value of the coefficient of oxygen transmission, expressed in per square metre second pascal; is the numerical value of the transmission rate of oxygen, expressed in fmol per square metre second pascal; is the numerical value of the thickness of specimen, expressed in

43、 millimetres. 5.7 Haze Haze shall be determined in accordance with ISO 14782. 5.8 Wetting tension Wetting tension shall be determined in accordance with ISO 8296. 6 Packaging Packaging and size of unit packaging shall be agreed upon between interested parties taking into account conditions of transp

44、ortation and storage. 20 mm 150 mm 100 mm 25 mm (160 3) C 30 min 20 min S = L 1 L 2 L 1 100 S L 1 L 2 100 m P O 2 = O 2 GTR (d/0,1) P O 2 fmol 100 m O 2 GTR d BSISO15987:2003 ISO :78951(3002)E 6 ISO 3002 All rithgs reresvde 7 Marking 7.1 Marking on products If applicable, the surfaces of the film wi

45、th corona discharge shall be clearly identified. 7.2 Marking on packaging The following shall be clearly marked on the package: a) name of products; b) classification, whether treated with corona discharge or not; c) nominal thickness, width and length of a roll; d) year and month of manufacture; e)

46、 name of manufacturer or symbol. BSISO15987:2003 blankBS ISO 15987:2003 BSI 389 Chiswick High Road London W4 4AL BSI British Standards Institution BSI is the independent national body responsible for preparing British Standards. It presents the UK view on standards in Europe and at the international

47、 level. It is incorporated by Royal Charter. Revisions British Standards are updated by amendment or revision. Users of British Standards should make sure that they possess the latest amendments or editions. It is the constant aim of BSI to improve the quality of our products and services. We would

48、be grateful if anyone finding an inaccuracy or ambiguity while using this British Standard would inform the Secretary of the technical committee responsible, the identity of which can be found on the inside front cover. Tel: +44 (0)20 8996 9000. Fax: +44 (0)20 8996 7400. BSI offers members an indivi

49、dual updating service called PLUS which ensures that subscribers automatically receive the latest editions of standards. Buying standards Orders for all BSI, international and foreign standards publications should be addressed to Customer Services. Tel: +44 (0)20 8996 9001. Fax: +44 (0)20 8996 7001. Email: ordersbsi-.