BS EN 61249-2-22-2005 Materials for printed boards and other interconnecting structures - Reinforced base materials clad and unclad - Modified non-halogenated epoxide woven E-glassc.pdf

《BS EN 61249-2-22-2005 Materials for printed boards and other interconnecting structures - Reinforced base materials clad and unclad - Modified non-halogenated epoxide woven E-glassc.pdf》由会员分享，可在线阅读，更多相关《BS EN 61249-2-22-2005 Materials for printed boards and other interconnecting structures - Reinforced base materials clad and unclad - Modified non-halogenated epoxide woven E-glassc.pdf（28页珍藏版）》请在麦多课文档分享上搜索。

1、 g49g50g3g38g50g51g60g44g49g42g3g58g44g55g43g50g56g55g3g37g54g44g3g51g40g53g48g44g54g54g44g50g49g3g40g59g38g40g51g55g3g36g54g3g51g40g53g48g44g55g55g40g39g3g37g60g3g38g50g51g60g53g44g42g43g55g3g47g36g58structures Part 2-22: Reinforced base materials, clad and unclad Modified non-halogenated epoxide w

2、oven E-glass laminated sheets of defined flammability (vertical burning test), copper-clad The European Standard EN 61249-2-22:2005 has the status of a British StandardICS 31.180Materials for printed boards and other interconnecting BRITISH STANDARDBS EN 61249-2-22: 2005BS EN 61249-2-22:2005This Bri

3、tish Standard was published under the authority of the Standards Policy and Strategy Committee on 24 August 2005 BSI 24 August 2005ISBN 0 580 45928 4Cross-referencesThe British Standards which implement international or European publications referred to in this document may be found in the BSI Catal

4、ogue under the section entitled “International Standards Correspondence Index”, or by using the “Search” facility of the BSI Electronic Catalogue or of British Standards Online.This publication does not purport to include all the necessary provisions of a contract. Users are responsible for its corr

5、ect application.Compliance with a British Standard does not of itself confer immunity from legal obligations.Summary of pagesThis document comprises a front cover, an inside front cover, the EN title page, pages 2 to 24, an inside back cover and a back cover.The BSI copyright notice displayed in thi

6、s document indicates when the document was last issued.Amendments issued since publicationAmd. No. Date CommentsA list of organizations represented on this committee can be obtained on request to its secretary.enquiries on the interpretation, or proposals for change, and keep UK interests informed;

7、monitor related international and European developments and promulgate them in the UK.National forewordThis British Standard is the official English language version of EN 61249-2-22:2005. It is identical with IEC 61249-2-22:2005.The UK participation in its preparation was entrusted to Technical Com

8、mittee EPL/501, Electronic assembly technology, which has the responsibility to: aid enquirers to understand the text; present to the responsible international/European committee any EUROPEAN STANDARD EN 61249-2-22 NORME EUROPENNE EUROPISCHE NORM March 2005 CENELEC European Committee for Electrotech

9、nical Standardization Comit Europen de Normalisation Electrotechnique Europisches Komitee fr Elektrotechnische Normung Central Secretariat: rue de Stassart 35, B - 1050 Brussels ICS 31.180 English version Materials for printed boards and other interconnecting structures Part 2-22: Reinforced base ma

10、terials, clad and unclad Modified non-halogenated epoxide woven E-glass laminated sheets of defined flammability (vertical burning test), copper-clad (IEC 61249-2-22:2005) Matriaux pour circuits imprims et autres structures dinterconnexion Partie 2-22: Matriaux de base renforcs, plaqus et non plaqus

11、 Feuilles stratifies en tissu de verre de type E poxyde non halogn modifi, dinflammabilit dfinie (essai de combustion verticale), plaques cuivre (CEI 61249-2-22:2005) Materialien fr Leiterplatten und andere Verbindungsstrukturen Teil 2-22: Kaschierte und unkaschierte verstrkte Basismaterialien Kupfe

12、rkaschierte mit E-Glasgewebe verstrkte Laminattafeln auf der Basis von modifiziertem halogenfreien Epoxidharz mit definierter Brennbarkeit (Brennprfung mit vertikaler Prflingslage)(IEC 61249-2-22:2005) This European Standard was approved by CENELEC on 2005-02-01. CENELEC members are bound to comply

13、with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the Central Secret

14、ariat or to any CENELEC member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CENELEC member into its own language and notified to the Central Secretariat has the same status as th

15、e official versions. CENELEC members are the national electrotechnical committees of Austria, Belgium, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Slovakia,

16、Slovenia, Spain, Sweden, Switzerland and United Kingdom. 2005 CENELEC - All rights of exploitation in any form and by any means reserved worldwide for CENELEC members. Ref. No. EN 61249-2-22:2005 E EN 61249-2-22:2005 - 2 - Foreword The text of document 91/494/FDIS, future edition 1 of IEC 61249-2-22

17、, prepared by IEC TC 91, Electronics assembly technology, was submitted to the IEC-CENELEC parallel vote and was approved by CENELEC as EN 61249-2-22 on 2005-02-01. The following dates were fixed: latest date by which the EN has to be implemented at national level by publication of an identical nati

18、onal standard or by endorsement (dop) 2005-11-01 latest date by which the national standards conflicting with the EN have to be withdrawn (dow) 2008-02-01 Annex ZA has been added by CENELEC. _ Endorsement notice The text of the International Standard IEC 61249-2-22:2005 was approved by CENELEC as a

19、European Standard without any modification. _ 3 EN 61249-2-22:2005 CONTENTS 1 Scope 5 2 Normative references .5 3 Materials and construction6 3.1 Resin system.6 3.2 Metal foil .6 3.3 Reinforcement.6 4 Internal marking .6 5 Electrical properties .6 6 Non-electrical properties of the copper-clad lamin

20、ate7 6.1 Appearance of the copper-clad sheet.7 6.2 Appearance of the unclad face 9 6.3 Laminate thickness9 6.4 Bow and twist9 6.5 Properties related to the copper foil bond.10 6.6 Punching and machining11 6.7 Dimensional stability11 6.8 Sheet sizes .12 6.9 Cut panels.12 7 Non-electrical properties o

21、f the base material after complete removal of the copper foil 13 7.1 Appearance of the dielectric base material.13 7.2 Flexural strength .13 7.3 Flammability14 7.4 Water absorption.14 7.5 Measling .15 7.6 Glass transition temperature and cure factor15 8 Quality assurance 16 8.1 Quality system.16 8.2

22、 Responsibility for inspection 16 8.3 Qualification inspection .16 8.4 Quality conformance inspection .16 8.5 Certificate of conformance.16 8.6 Safety data sheet 16 9 Packaging and marking 17 10 Ordering information.17 Annex A (informative) Engineering information.18 A.1 Chemical properties 18 A.2 E

23、lectrical properties.18 A.3 Flammability properties .18 A.4 Mechanical properties .18 A.5 Physical properties19 A.6 Thermal properties 19 Annex B (informative) Common laminate constructions 20 Annex C (informative) Guideline for qualification and conformance inspection 22 EN 61249-2-22:2005 4 Annex

24、ZA (normative) Normative references to international publications with their corresponding European publications .23 Bibliography .24 Table 1 Electrical properties 7 Table 2 Nominal thickness and tolerance of metal-clad laminate 9 Table 3 Bow and twist requirements.10 Table 4 Pull-off and peel stren

25、gth requirements .11 Table 5 Dimensional stability .12 Table 6 Size tolerances for cut panels12 Table 7 Rectangularity of cut panels 13 Table 8 Flexural strength requirements 14 Table 9 Flammability requirements.14 Table 10 Water absorption requirements.15 Table 11 Measling requirements 15 Table 12

26、Glass transition temperature and cure factor requirements.15 5 EN 61249-2-22:2005 MATERIALS FOR PRINTED BOARDS AND OTHER INTERCONNECTING STRUCTURES Part 2-22: Reinforced base materials clad and unclad Modified non-halogenated epoxide woven E-glass laminated sheets of defined flammability (vertical b

27、urning test), copper-clad 1 Scope This part of IEC 61249 gives requirements for properties of modified non-halogenated epoxide woven E-glass laminated sheet 0,05 mm up to 3,2 mm, of defined flammability (vertical burning test), copper-clad. The flammability rating is achieved through the use of phos

28、phorus compounds and/or aluminium hydroxide fire retardants contained as part of the polymeric structure. The glass transition temperature is defined to be between 150 C to 190 C. Some property requirements may have several classes of performance. The class desired should be specified on the purchas

29、e order, otherwise the default class of material will be supplied. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced docu

30、ment (including any amendments) applies. IEC 60194:1999, Printed board design, manufacture and assembly Terms and definitions IEC 61189-2:1997,Test methods for electrical materials, printed boards and interconnection structures and assemblies Part 2: Test method for materials for interconnection str

31、uctures IEC 61249-5-1:1995, Materials for interconnection structures Part 5: Sectional specification set for conductive foils and films with and without coatings Section 1: Copper foils (for the manufacture of copper-clad base materials) ISO 9000:2000, Quality management systems Fundamentals and voc

32、abulary ISO 11014-1:1994, Safety data sheet for chemical products Part 1: Content and order of sections ISO 14001:1996, Environmental management systems Specification with guidance for use EN 61249-2-22:2005 6 3 Materials and construction The sheet consists of an insulating base with metal-foil bond

33、ed to one side or both. Refer to IEC 60194 for terms and definitions. 3.1 Resin system Majority di-functional non-halogenated epoxide, modified non-halogenated epoxide, woven E-glass laminate with a glass transition temperature of 150 C to 190 C. The maximum total halogens contained in the resin plu

34、s reinforcement matrix is 1 500 106with a maximum chlorine of 900 106and a maximum bromine of 900 106. Contrast agents may be added to enhance processing such as automated optical inspection (AOI). Its flame resistance is defined in terms of the flammability requirements of 7.3. 3.2 Metal foil Coppe

35、r as specified in IEC 61249-5-1.The preferred foils are electro-deposited of defined ductility. 3.3 Reinforcement Woven E-glass as specified in IEC 61249-6-3. 4 Internal marking Not specified. 5 Electrical properties The electrical property requirements are shown in Table 1. 7 EN 61249-2-22:2005 Tab

36、le 1 Electrical properties Property Test method (IEC 61189-2) Requirement Resistance of foil 2E12 As specified in IEC 61249-5-1 Surface resistance after damp heat while in the humidity chamber (optional) 2E03 10 000 M Surface resistance after damp heat and recovery 2E03 50 000 M Volume resistivity a

37、fter damp heat while in the humidity chamber (optional) 2E04 5 000 Mm Volume resistivity after damp heat and recovery 2E04 10 000 Mm Relative permittivity after damp heat and recovery (1 MHz) 2E10 5,4 Dissipation factor after damp heat and recovery (1 MHz) 2E10 0,035 Electric strength (only for mate

38、rial thickness less than 0,5 mm ) 2E11 30 kV/mm Arc resistance 2E14 60 s Dielectric breakdown (only for material thicknesses 0,5 mm) 2E15 40 kV Surface resistance at 125 C 2E07 10 000 M Volume resistivity at 125 C 2E07 10 000 Mm 6 Non-electrical properties of the copper-clad laminate 6.1 Appearance

39、of the copper-clad sheet The copper-clad face shall be substantially free from defects that may have an impact on the materials fitness for use for the intended purpose. For the following specific defects the requirements given shall apply when inspection is made in accordance with IEC 61189-2 metho

40、d 2M18. 6.1.1 Indentations (pits and dents) The size of an indentation, usually the length, shall be determined and given a point value to be used as measure of the quality. Size mm Point value for each indentation 0,13 0,25 1 0,26 0,50 2 0,51 0,75 4 0,76 1,00 7 Over 1,00 30 EN 61249-2-22:2005 8 The

41、 total point count for any 300 mm x 300 mm area shall be calculated to determine the class of the material. Indentation class A: 29 maximum total point count Indentation class B: 17 maximum total point count Indentation class C: 5 maximum total point count Indentation class D: 0 total point count In

42、dentation class X: to be agreed upon by user and supplier. The required class of material shall be specified in the purchase order. Indentation Class A applies unless otherwise specified. 6.1.2 Wrinkles There shall be no wrinkles in the copper surface. 6.1.3 Scratches Scratches deeper than 20 % of t

43、he nominal thickness of the foil thickness are not permitted. Scratches with a depth less than 5 % of the nominal thickness of the foil shall not be counted unless this depth is 10 m or more. Scratches with a depth between 5 % and 20 % of the nominal thickness of the foil are permitted to a total le

44、ngth of 100 mm for a 300 x 300 mm area. 6.1.4 Raised areas Raised areas are usually impressions in the press plates used during manufacture but may also be caused by blisters or inclusions of foreign particles under the foil. Raised areas caused by blisters or inclusions are not permitted. Raised ar

45、eas being impressions of defects in press plates are permitted to the following extent: Indentation class A and X material: maximum height 15 m and max length 15 mm; Indentation class B and C material: maximum height 8 m and max length 15 mm; Indentation class D material : maximum height 5 m and max

46、 length 15 mm. 6.1.5 Surface waviness When examined in accordance to test method 2M12 of IEC 61189-2, the surface waviness in both the machine and cross machine direction shall not exceed 7 m. 9 EN 61249-2-22:2005 6.2 Appearance of the unclad face The unclad face of single side clad sheet shall have

47、 the natural appearance resulting from the curing process. Small irregularities in colour are permitted. The gloss of the unclad face shall be that given by the press plate or release foil used. Variations of gloss due to the impact of pressure of gases released during the curing are permitted. 6.3

48、Laminate thickness The laminate thickness may be ordered to include or exclude the copper foil contribution as specified in the purchase order. As a general rule laminates less than 0,8 mm are measured excluding copper and laminates greater or equal to 0,8 mm are measured including copper. If the co

49、pper-clad laminate is tested in accordance with test method 2D01 of IEC 61189-2, the thickness shall not depart from the nominal thickness by more than the appropriate value shown in table 2. The fine tolerances shall apply unless the other tolerances are ordered. Table 2 Nominal thickness and tolerance of metal-clad laminate Tolerance requirement mm Nominal thickness exc