BS EN 10209-2013 Cold rolled low carbon steel flat products for vitreous enameling Technical delivery conditions《搪瓷加工用的冷轧低碳钢平板产品 交付技术条件》.pdf

《BS EN 10209-2013 Cold rolled low carbon steel flat products for vitreous enameling Technical delivery conditions《搪瓷加工用的冷轧低碳钢平板产品 交付技术条件》.pdf》由会员分享，可在线阅读，更多相关《BS EN 10209-2013 Cold rolled low carbon steel flat products for vitreous enameling Technical delivery conditions《搪瓷加工用的冷轧低碳钢平板产品 交付技术条件》.pdf（30页珍藏版）》请在麦多课文档分享上搜索。

1、BSI Standards PublicationBS EN 10209:2013Cold rolled low carbon steelflat products for vitreousenamelling Technicaldelivery conditionsBS EN 10209:2013 BRITISH STANDARDNational forewordThis British Standard is the UK implementation of EN 10209:2013. Itsupersedes BS EN 10209:1996 which is withdrawn.Th

2、e UK participation in its preparation was entrusted to TechnicalCommittee ISE/109, Coated and Uncoated Flat Products to be Usedfor Cold Forming.A list of organizations represented on this committee can beobtained on request to its secretary.This publication does not purport to include all the necess

3、aryprovisions of a contract. Users are responsible for its correctapplication. The British Standards Institution 2013. Published by BSI StandardsLimited 2013ISBN 978 0 580 71517 4ICS 77.140.50Compliance with a British Standard cannot confer immunity fromlegal obligations.This British Standard was pu

4、blished under the authority of theStandards Policy and Strategy Committee on 31 July 2013.Amendments issued since publicationDate Text affectedBS EN 10209:2013EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 10209 June 2013 ICS 77.140.50 Supersedes EN 10209:1996English Version Cold rolled low ca

5、rbon steel flat products for vitreous enamelling - Technical delivery conditions Produits plats lamins froid, en acier doux pour maillage par vitrification - Conditions techniques de livraison Kaltgewalzte Flacherzeugnisse aus weichen Sthlen zum Emaillieren - Technische Lieferbedingungen This Europe

6、an Standard was approved by CEN on 11 April 2013. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references conce

7、rning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member int

8、o its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, G

9、ermany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE

10、 FR NORMUNG Management Centre: Avenue Marnix 17, B-1000 Brussels 2013 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 10209:2013: EBS EN 10209:2013EN 10209:2013 (E) 2 Contents Page Foreword 3 1 Scope 4 2 Normative references 4 3 Te

11、rms and definitions .5 4 Designation 5 5 Requirements .5 6 Tests 8 7 Identification .9 8 Packaging .9 9 Disputes 9 10 Information to be supplied by the purchaser at the time of ordering 9 Annex A (normative) Methods for determining the resistance to fish scaling of a steel sheet for enamelling . 13

12、Annex B (normative) Method for determining mass loss (iron loss) due to pickling for steel grades for direct enamelling in accordance with 5.4.2 17 Annex C (normative) Method for determining the adherence level of enamel applied to a steel sheet . 20 Annex D (informative) Characteristics for the sel

13、ection of enamelling steel grades 25 BS EN 10209:2013EN 10209:2013 (E) 3 Foreword This document (EN 10209:2013) has been prepared by Technical Committee ECISS/TC 109 “Flat products for cold working - Qualities, dimensions, tolerances and specific test”, the secretariat of which is held by AFNOR. Thi

14、s European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by December 2013, and conflicting national standards shall be withdrawn at the latest by December 2013. Attention is drawn to the possibility that some of

15、 the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 10209:1996. According to the CEN-CENELEC Internal Regulations, the national standards organizations of the f

16、ollowing countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherland

17、s, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. BS EN 10209:2013EN 10209:2013 (E) 4 1 Scope This European Standard applies to cold rolled non-coated low carbon steel flat products in rolled widths equal to or over 600 mm and in thi

18、cknesses equal to or less than 3 mm, delivered in sheet, wide strip, slit wide strip or cut lengths obtained from slit wide strip or sheet. It does not apply to cold rolled narrow strip (rolling width 1,6 m 5.9 Stretcher strain marks All the products are generally subjected to a light skin-pass afte

19、r annealing at the manufacturers works to avoid the formation of stretcher strain marks during subsequent forming. The tendency to form such marks may reappear a certain time after the skin-pass. It is therefore in the purchasers interest to form the products as soon as possible. Quality DC06EK and

20、DC06ED products do not exhibit stretcher strain marks after deformation. For the other qualities the absence of stretcher strain marks may be guaranteed for six months after the products are made available. 5.10 Weldability The material is specified as suitable for normal welding procedures as long

21、as the products are degreased beforehand. The welding procedure shall be specified at the time of ordering (see 10 h). 5.11 Tolerances on dimensions and shape Tolerances on dimensions and shape are given in EN 10131. BS EN 10209:2013EN 10209:2013 (E) 8 6 Tests 6.1 General 6.1.1 The purchaser shall s

22、pecify at the time of ordering his requirements for: type of inspection and testing: specific or non-specific, see EN 10021; type of inspection document, see EN 10204. 6.1.2 Specific inspection and testing shall be carried out in accordance with 6.2, 6.3, 6.4, 6.5 and 6.6. 6.1.3 Specific inspection

23、and testing may not be specified either for the product analysis or the surface finish. 6.2 Inspection units The inspection unit is 30 t or a fraction of 30 t products of the same grade and nominal thickness. When a wide coil exceeds 30 t, it constitutes a single inspection unit, as do its products.

24、 6.3 Number of tests For each inspection unit a tensile test shall be carried out, and if required, a determination of r and of the suitability for enamelling shall be performed (see Table 2 and Annex A, Annex B and Annex C). 6.4 Sampling The requirements of EN ISO 377 and EN 10021 are supplemented

25、by the following specific requirements. For sheet and cut lengths the selection of products to be tested and the position of the samples in the products is left to the discretion of the inspection representative. In the case of wide strip and slit wide strip, the sample should preferably be taken fr

26、om the outer end. If the width of the product permits, the test pieces for the tensile test shall be taken perpendicular to the direction of rolling at a distance of at least 50 mm from the edge of the product. 6.5 Test methods 6.5.1 The products shall be tested in the as-delivered condition. The te

27、sts shall be carried out at ambient temperature. 6.5.2 The tensile test shall be carried out as specified in EN ISO 6892-1 using type 2 test pieces (initial gauge length Lo= 80 mm, width b = 20 mm). 6.5.3 Surface roughness shall be measured in accordance with EN 10049. 6.5.4 The determination of the

28、 plastic strain ratio r shall be carried out in accordance with ISO 10113. 6.5.5 The tests for suitability for enamelling (see 5.4.3) shall be carried out in accordance with Annex A for the fish scaling resistance test; Annex B for the mass loss due to pickling test; Annex C for the adherence test.

29、BS EN 10209:2013EN 10209:2013 (E) 9 6.5.6 For the determination of the chemical composition the corresponding European Standards shall apply in cases of dispute. 6.6 Retests The requirements of EN 10021 shall apply. For coils, in the event of the test results giving rise to dispute, the samples for

30、retests shall be taken at intervals of at least one lap but also at a maximum distance of 20 m from the appropriate end. 6.7 Inspection documents If agreed at the time of ordering, an inspection document chosen from those given in EN 10204 shall be supplied (see also 6.1.1). 7 Identification All mat

31、erials shall be identified with at least the following information: the conventional designation as described in Clause 4; the coil or bundle number; the suppliers mark. Typically, the identification is applied by either a label or using an easily removable non-corrosive ink on the inspected surface

32、. Other identification requirements shall be agreed at the time of ordering. 8 Packaging The packaging requirements shall be agreed at the time of ordering. 9 Disputes With regard to any claims and actions, EN 10021 shall apply. 10 Information to be supplied by the purchaser at the time of ordering

33、To permit the manufacturer to supply products conforming to this standard, the following information should be given in the order: a) the full designation as given in Clause 4; b) nominal dimensions and quantities; c) if the products are to be supplied non skin-passed, d) if the products are to be d

34、elivered with mill edges or sheared edges; e) limits on mass and sizes of coils and individual bundles; f) intended application for the products; g) enamelling process used (see Annex D); BS EN 10209:2013EN 10209:2013 (E) 10 h) if the products are to be welded, indication of the method to be used; i

35、) if the products are to be supplied as suitable for making a specific part; j) if inspection documents are requested and type; k) if an external inspection is to be carried out at the manufacturers works; l) if oiling is not required; m) detailed description of all other special requirements; n) an

36、y special requirements for packaging and marking; o) the position of the surface of better surface finish quality. BS EN 10209:2013EN 10209:2013 (E) 11 Table 2 Characteristics a iDesignation in accordance with EN 100271 Designation in accordance with EN 100272 Method of deoxidation Validity of mecha

37、nical properties and absence of stretcher strain marks ReMPa max b c lRmMPa lA80% min d l_ r average min e lChemical composition (ladle analysis) % max C content (product analysis) % max C Ti Mn P S DC01EK 1.0390 Fully killed f6 months f270 270/390 30 0.08 0.60 0,045 0,050 DC04EK 1.0392 Fully killed

38、 6 months 220k270/350 36 0.08 0,50 0,030 0,050 DC05EK 1.0386 Fully killed 6 months 220k270/350 36 1.5 0.08 0,50 0,025 0,050 DC06EK 1.0869 Fully killed 6 months 190 270/350 38 1.6 0.02 0.30h0,50 0,020 0,050 DC03ED 1.0399 Fully killed f6 months f240 270/370 34 j 0,40 0,035 0,050 0,004 DC04ED 1.0394 Fu

39、lly killed 6 months 210g270/350 38 j 0,40 0,030 0,050 0,004 DC06ED 1.0872 Fully killed 6 months 190 270/350 38 1.6 0.02 0.30h0,35 0,020 0,050 aThe mechanical properties apply only to skin-passed product. bThe value for yield stress is the Rp0,2 % for products which do not present a definite yield po

40、int and the lower yield stress (Rel,) for the others. When the thickness is less than or equal to 0,7 mm and greater than 0,5 mm, the value for yield stress is increased by 20 MPa. For thicknesses less than or equal to 0,5 mm, the value is increased by 40 MPa. cFor design purposes, the lower limit o

41、f Refor qualities DCO1EK, DC04EK, DC05EK, DC03ED and DC04ED may be assumed to be 140 MPa and for qualities DC06EK and DC06ED as 120 MPa. dWhen the thickness is less than or equal to 0,7 mm, and greater than 0,5 mm, the minimum elongation value after fracture is reduced by 2 units. For thicknesses eq

42、ual to or less than 0,5 mm, the minimum value is reduced by 4 units. eThe value of r average only applies to products of thicknesses equal to or greater than 0,5 mm. When the thickness is over 2,0 mm, the value of r average is reduced by 0,2 units. fSubject to agreement at the time of ordering, othe

43、r deoxidation methods may be used. If so, the periods for validity of the mechanical properties and the absence of stretcher strain marks shall be agreed at the time of ordering. BS EN 10209:2013EN 10209:2013 (E) 12 gIf the thickness is greater than or equal to 1,5 mm, the maximum value for the yiel

44、d stress may reach 225 MPa. hTitanium may be replaced by niobium if agreed upon at the time of ordering. Carbon and nitrogen shall be completely bound. iSubject to agreement at the time of ordering, other steels may be supplied which have the same mechanical properties. If so, the chemical compositi

45、on of these steels shall be agreed at the time of ordering. jThe decarburisation of qualities DC03ED and DC04ED can take place in the solid or the liquid phase. The carbon content, determined by product analysis after decarburisation shall be 0,004 % maximum. If agreed at the time of ordering, quali

46、ties DC03ED and DC04ED may contain for example titanium, niobium or boron. kAt the request of the purchaser, the DC04EK and DC05EK qualities may be supplied with Re 210 MPa and A80 38 % in the 0,7 mm to 1,5 mm thicknesses. It is therefore for the manufacturer to select the surface roughness within t

47、he range of normal roughness options. l The mechanical property values refer to the perpendicular testing direction. BS EN 10209:2013EN 10209:2013 (E) 13 Annex A (normative) Methods for determining the resistance to fish scaling of a steel sheet for enamelling A.1 Hydrogen permeation test A.1.1 Fiel

48、d of application The test pieces shall be 0,5 mm to 3 mm thick. A.1.2 Principle Generate hydrogen electrolytically on one side of a degreased sheet. The time between the start of electrolysis and the determination of hydrogen having passed to the other side of the sheet shall be defined as the hydro

49、gen permeation time. A long permeation time shall indicate good resistance to fish scaling. A.1.3 Apparatus E. Buchel and L. Leontaritis measuring apparatus. Electrolyte made up of 6 % (volume fraction) by volume of H2S04(60 ml of H2S04concentrated in 940 ml of distilled water) with 0,25 g/l of HgCl2and 0,5 g/l of As203. The solution shall be freshly made for each test (the chemical products being of analytical quality). Highly alkaline degreasing agent, suitable for steel sheets, containing silicates. Deionised water. 10 - 15 % (mass frac