1、BRITISH STANDARD BS 7585-3: 1992 ISO 4386-3: 1992 Metallic multilayer plain bearings Part 3: Method for non-destructive die penetrant testingBS7585-3:1992 This British Standard, having been prepared under the directionof the Machinery and Components Standards Policy Committee, was published under th
2、e authority of the Standards Board and comes into effect on 15 July 1992 BSI 09-1999 The following BSI references relate to the work on this standard: Committee reference MCE/12 Draft for comment 88/78717 DC ISBN 0 580 20992 X Committees responsible for this British Standard The preparation of this
3、British Standard was entrusted by the Machinery and Components Standards Policy Committee (MCE/-) to Technical Committee MCE/12, upon which the following bodies were represented: Association of Bronze and Brass Founders British Plastics Federation British Powder Metal Federation Copper Development A
4、ssociation Institution of Diesel and Gas Turbine Engineers Institution of Mechanical Engineers Society of Motor Manufacturers and Traders Ltd. Amendments issued since publication Amd. No. Date CommentsBS7585-3:1992 BSI 09-1999 i Contents Page Committees responsible Inside front cover National forewo
5、rd ii 1 Scope 1 2 Normative reference 1 3 Safety precautions 1 4 Preparation of test surface 1 5 Application of penetrant 1 6 Removal of excess penetrant 2 7 Application of the developer 2 8 Inspection 2 9 Subsequent cleaning 2 10 Test report 2 Annex A (normative) Designation classes and acceptance
6、criteria 3 Annex B (informative) Bibliography 8 Figure A.1 Marks 3 Figure A.2 Shape and location of marks Class A 4 Figure A.3 Shape and location of marks Class B 5 Figure A.4 Shape and location of marks Class C 6 Figure A.5 Shape and location of marks Class D 7 Figure A.6 Shape and location of mark
7、s Class E 8 List of references Inside back coverBS7585-3:1992 ii BSI 09-1999 National foreword This Part of BS 7585 has been prepared under the direction of the Machinery and Components Standard Policy Committee. It is identical with ISO4386-3:1992 Plain bearings Metallic multilayer plain bearings P
8、art 3: Non-destructive penetrant testing, published by the International Organization for Standardization (ISO). NOTEFor the purposes of this standard, any reference in the text to penetrant should be taken to mean die penetrant. A British Standard does not purport to include all the necessary provi
9、sions of a contract. Users of British Standards are responsible for their correct application. Compliance with a British Standard does not of itself confer immunity from legal obligations. Cross-reference International Standard Corresponding British Standard ISO 4386-1:1992 BS 7585 Metallic multilay
10、er plain bearings Part 1:1992 Method for non-destructive ultrasonic testing of bond (Identical) Summary of pages This document comprises a front cover, an inside front cover, pages i and ii, pages1 to 8, an inside back cover and a back cover. This standard has been updated (see copyright date) and m
11、ay have had amendments incorporated. This will be indicated in the amendment table on the inside front cover.BS7585-3:1992 BSI 09-1999 1 1 Scope This part of ISO 4386 specifies a non-destructive penetrant testing for determining bond defects and discontinuities in the sliding surface of the bearing.
12、 The penetration method is used to detect a) bond defects in the transitional area between the bearing backing/bearing material on the end faces and joint faces of multilayer plain bearings which cannot be detected by the ultrasonic testing method specified in ISO4386-1; b) discontinuities in the sl
13、iding surface of the bearing. The penetration method is applicable, in principle, to finished multilayer plain bearings. The bond test can be carried out only on cast multilayer plain bearings, with a backing consisting of steel, cast steel or cast bronze. Bearing backings which cannot be tin-plated
14、, or only with difficulty, such as perlitic cast iron, rust-resistant steel and cast aluminium, cannot be tested since no bond is possible between the bearing material and bearing backing. 2 Normative reference The following standard contains provisions which, through reference in this text, constit
15、ute provisions of this part of ISO4386. At the time of publication, the edition indicated was valid. All standards are subject to revision, and parties to agreements based on this part of ISO4386 are encouraged to investigate the possibility of applying the most recent edition of the standard indica
16、ted below. Members of IEC and ISO maintain registers of currently valid International Standards. ISO 4386-1:1992, Plain bearings Metallic multilayer plain bearings Pert 1: Non-destructive ultrasonic testing of bond. 3 Safety precautions As penetrant inspection techniques often require the use of dan
17、gerous, flammable and/or volatile materials, the relevant accident prevention, handling of dangerous substances and environmental protection regulations shall be observed. 4 Preparation of test surface 4.1 General The surfaces to be tested shall be free from residual matter to allow the penetrant to
18、 ingress in any discontinuity. Adherent metal splinters and chips caused by machining shall be removed mechanically, and adherent oil and grease removed chemically. Finally, the surface shall be thoroughly dried, at a maximum temperature of55 C. The test surface shall have a surface roughness of R a
19、 u 54m. 4.2 Mechanical pre-cleaning Rust etc. shall be removed by brushing, by grinding using an abrasive blasting process, or by similar methods. Care shall be taken to ensure that the defects are not sealed by the pre-cleaning process, if necessary, etching is recommended after the use of any mech
20、anical method. The surface shall then be thoroughly rinsed and dried. 4.3 Chemical pre-cleaning Residual matter shall be removed by means of suitable cleaning materials, e.g. by degreasing solvents, etchants or paint strippers. After use, all traces of cleaning materials shall be removed completely
21、from the test surface and from the discontinuities, e.g. by rinsing the test surface. 4.4 Drying At the end of the pre-cleaning process, the surfaces to be examined shall be dried so that no water or cleaning material remains in the discontinuities. 5 Application of penetrant 5.1 A penetrant which i
22、s removable by water or solvent shall be used for the test. The test temperature, i.e. the temperature of the test surface, shall be between10 C and50 C. NOTE 1A very viscous penetrant increases the safety of the interim cleaning. 5.2 The penetrant shall be applied by immersing the bearing, or by me
23、ans of a brush, or by spraying. The penetration time shall be10min to 60min. With very viscous penetrants it shall be at least20min. The surfaces to be examined shall be wetted continuously during this time.BS7585-3:1992 2 BSI 09-1999 6 Removal of excess penetrant The penetrant shall be removed from
24、 the surface by rinsing or spraying with water (without detergents) using a handspray with hydrostatic pressure of less than2bar, or by wiping with a cloth lightly moistened with a solvent appropriate to the penetrant system. Excess washing is to be avoided by prechecking the procedure on a standard
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- BS758531992METALLICMULTILAYERPLAINBEARINGSMETHODFORNONDESTRUCTIVEDIEPENETRANTTESTING 多层 金属 滑动 轴承 部分 渗透
链接地址:http://www.mydoc123.com/p-546905.html