BS 3592-1-1986 Steel wire for hose reinforcement - Specification for coated round and flat steel wire for rubber hose reinforcement《软管增强钢丝 第1部分 橡胶软管增强用镀覆圆和扁钢丝规范》.pdf

《BS 3592-1-1986 Steel wire for hose reinforcement - Specification for coated round and flat steel wire for rubber hose reinforcement《软管增强钢丝 第1部分 橡胶软管增强用镀覆圆和扁钢丝规范》.pdf》由会员分享，可在线阅读，更多相关《BS 3592-1-1986 Steel wire for hose reinforcement - Specification for coated round and flat steel wire for rubber hose reinforcement《软管增强钢丝 第1部分 橡胶软管增强用镀覆圆和扁钢丝规范》.pdf（10页珍藏版）》请在麦多课文档分享上搜索。

1、BRITISH STANDARD BS3592-1: 1986 Incorporating Amendment No. 1 Steel wire for hose reinforcement Part 1: Specification for coated round and flat steel wire for rubber hose reinforcement UDC 669.14.0569426:621.643.33:678.4.029.4BS3592-1:1986 This British Standard, having been prepared under the direct

2、ionof the Iron and Steel Standards Committee, was published under the authority ofthe Board of BSI and comes intoeffect on 31 March1986 BSI 03-1999 First published April1963 First revision July1972 Second revision March1986 The following BSI references relate to the work on this standard: Committee

3、reference ISM/26 Draft for comment85/38163 DC ISBN 0 580 15010 0 Committees responsible for this British Standard The preparation of this British Standard was entrusted by the Iron and Steel Standards Committee (ISM/-) to Technical Committee ISM/26, upon which the following bodies were represented:

4、British Steel Industry British Steel Industry (Wire Section) British Wire Netting Association Fencing Contractors Association Institute of Quality Assurance Society of Chain Link Fencing Manufacturers Welding Manufacturers Association (BEAMA Ltd.) The following body was also represented in the draft

5、ing of the standard, through subcommittees and panels: British Rubber Manufacturers Association Amendments issued since publication Amd. No. Date of issue Comments 7283 October 1992 Indicated by a sideline in the marginBS3592-1:1986 BSI 03-1999 i Contents Page Committees responsible Inside front cov

6、er Foreword ii 1 Scope 1 2 Manufacture 1 3 Condition of finished wire 1 4 Properties 1 5 Selection of test pieces 3 6 Test methods 3 7 Retests 3 8 Documentation, identification and packing 3 Table 1 Coated round wire diameters and tolerances 2 Table 2 Coated flat wire sizes and tolerances 2 Table 3

7、Tensile strength grades 2 Table 4 Ductility wrap test 2 Table 5 Reverse bend test 3 Publications referred to Inside back coverBS3592-1:1986 ii BSI 03-1999 Foreword This Part of BS3592 has been prepared under the direction of the Iron and Steel Standards Committee and is a revision of the1972 edition

8、 which is withdrawn. As a consequence of the detailed review, the scope of the two Parts of BS3592 has been changed. This revision of Part1 combines, with additions and amendments, the requirements of the previous Part1 for round and flat mild steel wire and those of the previous Part2 for carbon st

9、eel round wires of2.0mm diameter and larger. Part2 is now restricted to metallic coated patented cold drawn carbon steel wire, in diameters0.20mm to0.71mm, for the bonded reinforcement of hydraulic hoses. A British Standard does not purport to include all the necessary provisions of a contract. User

10、s of British Standards are responsible for their correct application. Compliance with a British Standard does not of itself confer immunity from legal obligations. Summary of pages This document comprises a front cover, an inside front cover, pagesi andii, pages1 to4, an inside back cover and a back

11、 cover. This standard has been updated (see copyright date) and may have had amendments incorporated. This will be indicated in the amendment table on theinside front cover.BS3592-1:1986 BSI 03-1999 1 1 Scope This Part of BS3592 specifies requirements for wire used for rubber hose reinforcement. Two

12、 tensile strength grades are specified for round and flat wires in low carbon steel (mild steel) and five tensile strength grades are specified for round wires in carbon steel, depending upon wire diameter. The round wire diameter range specified is1.60mm to14.22mm and the flat wire dimensions speci

13、fied range from2.18mm 1.63mmto15.9mm 4.76mm. Various types of coating are specified. NOTEThe titles of the publications referred to in this standard are listed on the inside back cover. 2 Manufacture 2.1 Steel rod The rod used for the manufacture of the wire shall be produced from steel made by any

14、process, except the air or air/oxygen bottom blown processes. The rod quality shall be of a grade typical of standard steel making and rod rolling practice. NOTEStandard practice can be taken to mean the following guidelines according to the type of steel. a) Low carbon steel (mild steel). This has

15、an absence of pipe and an inclusion content commensurate with balanced or killed steels of low carbon content. The maximum surface defect depth in the rod should be generally not more than3.5% of the rod diameter. b) Carbon steel. This has an absence of pipe and an inclusion content commensurate wit

16、h killed carbon steels. The maximum depth of partial decarburization and surface defects should be generally not more than3% of the rod diameter. 2.2 Steel composition The ladle analysis of the steel shall show sulphur and phosphorus contents each not greater than0.040%. 2.3 Wire The wire shall be c

17、old drawn or rolled to the finished dimensions. Where appropriate for the tensile strength grade, an inter-process heat treatment shall be applied. The wire shall have one of the following coatings: a) zinc; b) copper; c) bronze; d) copper lacquer; e) phosphate (chemically bonded). NOTE 1There may b

18、e a limit to the wire diameters or sizes available with a zinc, copper or bronze coating. NOTE 2When copper or bronze coatings are specified, the mass of coating and the method of determination of the mass of coating should be the subject of agreement between the purchaser and the manufacturer at th

19、e time of the enquiry and order. 2.4 Welds For the low carbon steel (mild steel) type it shall be permissible for welds made at any stage before inter-process heat treatment to remain in the finished wire. For the carbon steel type, apart from any welds made between rod coils before drawing, there s

20、hall be no welds in any coil of finished wire. 3 Condition of finished wire The wire shall be free from rust and shall not be oiled. The wire in coil shall be “dead cast”, i.e.when a complete turn of wire is removed from the coil without tension and placed on a smooth horizontal surface without rest

21、raint, the wire circle shall have a diameter approximately that of the coil and any corkscrew set, measured by the deviation of one cut end from the horizontal plane, shall not exceed50mm. 4 Properties 4.1 Sizes and tolerances The wire diameters and dimensions of flat wires shall be as given in Tabl

22、e 1 and Table 2 with the appropriate tolerances. NOTE 1The size range varies according to the tensile strength grade. (See Table 3.) NOTE 2If any intermediate sizes are used they should have the tolerance of the next larger listed size.BS3592-1:1986 2 BSI 03-1999 Table 1 Coated round wire diameters

23、and tolerances Table 2 Coated flat wire sizes and tolerances 4.2 Tensile strength The tensile strength shall be calculated on the actual diameter or dimensions of the wire. The tensile strength shall be one of the grades given in Table 3 according to steel type, wire form or size. Table 3 Tensile st

24、rength grades 4.3 Ductility wrap The wire shall withstand without sign of fracture the wrap test appropriate to the tensile strength grades and wire diameters, as given in Table 4. Table 4 Ductility wrap test 4.4 Reverse bend The wire shall withstand without sign of fracture the reverse bend test ov

25、er the bend radius as given in Table 5 according to tensile strength grade and wire size. The wire shall be bent through90 and then in the reverse direction through180. Flat wire shall be tested with the larger dimension parallel to the axis of the bending mandrel. 4.5 Zinc coating 4.5.1 Flat wire.

26、For flat wire, the mass of zinc coating shall be not less than40g/m 2 . 4.5.2 Round wire. For round wire, the mass of zinc coating shall comply with section 3 of BS443:1982, except that where the wires are to be covered with rubber, there shall be only a thin coating of zinc to a minimum mass of one

27、-third of that specified in section 3 of BS443:1982 (rounded to the nearestg/m 2 ). Nominal diameter Tolerance mm mm 1.60 1.80 2.00 2.36 2.65 3.00 3.25 3.65 4.00 4.50 5.00 5.30 6.00 6.30 7.10 7.50 9.00 9.50 11.20 11.80 12.50 14.22 0.05 0.05 0.05 0.05 0.08 0.08 0.08 0.10 0.10 0.10 0.10 0.10 0.10 0.10

28、 0.10 0.10 0.10 0.10 0.10 0.10 0.10 0.10 Nominal dimensions Tolerance Width Thickness Width Thickness mm mm mm mm 3.18 3.25 3.95 4.75 6.35 6.35 6.35 9.50 9.50 9.50 12.70 12.70 15.90 15.90 1.63 1.42 1.98 1.59 1.63 1.83 3.16 2.38 3.17 4.76 3.17 4.76 3.17 4.76 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.10 0.

29、10 0.10 0.10 0.10 0.10 0.10 0.03 0.03 0.03 0.03 0.03 0.03 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05 Steel type Wire form Size range Tensile strength grade mm N/mm 2 Low carbon steel (mild steel) Round See Table 1 350 to 600 600 to 850 Flat See Table 2 350 to 600 600 to 850 Carbon steel Round 2.0 to 5.

30、0 1200 to 1400 1400 to 1600 1600 to 1800 Over5.0 to 14.22 900 to 1100 1100 to 1300 Tensile strength grade Wire diameter Number of turns on the wire diameter N/mm 2 mm 350 to 600 600 to 850 1.6 to6.3 Wrap on8 turns and unwrap 7 turns 1200 to1400 1400 to1600 1600 to1800 2.0 to4.0 Wrap on8 turns onlyBS

31、3592-1:1986 BSI 03-1999 3 Table 5 Reverse bend test 5 Selection of test pieces A sufficient length of wire for all the mechanical tests shall be taken from representative coils of wire at a frequency not less than two lengths per tonne of wire. 6 Test methods 6.1 Dimensions The micrometer used for m

32、easurements shall be capable of reading to intervals of at least0.002mm. For round wire, pairs of measurements shall be made at right angles to each other at three places along a length of not less than250mm. The reported diameter of the wire shall be the average of the six measurements. For flat wi

33、re, the width and thickness shall be determined by taking three measurements of each dimension along a length of not less than250mm. The separate averages of each group of three measurements shall be the reported dimensions of the wire. 6.2 Mechanical tests Mechanical tests shall be carried out in a

34、ccordance with BS4545. 6.3 Zinc coating The mass of zinc coating shall be determined in accordance with section 2 of BS443:1982. 7 Retests 7.1 If any test piece fails any test, two additional test pieces shall be taken from the same coil of wire and subjected to the test or tests which the original

35、test piece failed. If both additional test pieces pass the test or tests, the coil shall be deemed to comply with this Part of BS3592 but if either of them fails, the coil shall be deemed not to comply. 7.2 If10% or more of the coils in a lot fail to comply, the whole lot shall be deemed not to comp

36、ly with this Part of BS3592. NOTEFurther tests may be carried out by agreement between the purchaser and the manufacturer at the time of the enquiry and order. 8 Documentation, identification and packing 8.1 The manufacturer shall provide for each consignment either: a) a certificate of compliance w

37、ith this Part of BS3592 based on the results of his tests; or b) a test certificate giving the results of all tests identified to each coil number. NOTEWhether type (a) or (b) certificate is to be supplied should be agreed between the purchaser and the manufacturer at the time of the enquiry and ord

38、er. 8.2 Each coil shall be identified with the following information: a) the manufacturers name; b) the number and date of this Part of BS3592, i.e.BS3592-1:1986 1) ; c) the specified, diameter or dimensions and strength; d) the individual coil number; e) the coil mass. NOTEAdditional marking may be

39、 agreed between the purchaser and the manufacturer at the time of the enquiry and order. 8.3 Each coil shall be securely tied and shall have the identification label attached. Tensile strength grade Wire form Wire size Bend radius Over Up to and including N/mm 2 mm mm mm 350 to 600 Round 6.30 14.22

40、12.5 600 to 850 350 to 850 Flat All sizes 5.0 650 to 850 1250 to 1400 Round 4.0 5.0 12.5 1400 to 1600 1600 to 1800 900 to 1100 Round 5.0 8.0 15.0 1100 to 1300 8.0 14.22 25.0 1) Marking BS3592-1:1986 on or in relation to a product is a claim by the manufacturer that the product has been manufactured

41、to the requirements of the standard. The accuracy of such a claim is therefore solely the manufacturers responsibility.4 blankBS3592-1:1986 BSI 03-1999 Publications referred to BS443, Specification for testing zinc coatings on steel wire and for quality requirements. BS4545, Methods for mechanical t

42、esting of steel wire. BS3592, Steel wire for hose reinforcement. BS3592-2, Specification for metallic coated steel wire for the bonded reinforcement of hydraulic hoses 2) . 2) Referred to in the foreword only.BSI 389 Chiswick High Road London W4 4AL | | | | | | | | | | | | | | | | | | | | | | | | |

43、| | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | BSI British Standards Institution BSI is the independent national body responsible for preparing

44、 British Standards. It presents the UK view on standards in Europe and at the international level. It is incorporated by Royal Charter. Revisions British Standards are updated by amendment or revision. Users of British Standards should make sure that they possess the latest amendments or editions. I

45、t is the constant aim of BSI to improve the quality of our products and services. We would be grateful if anyone finding an inaccuracy or ambiguity while using this British Standard would inform the Secretary of the technical committee responsible, the identity of which can be found on the inside fr

46、ont cover. Tel: 020 8996 9000. Fax: 020 8996 7400. BSI offers members an individual updating service called PLUS which ensures that subscribers automatically receive the latest editions of standards. Buying standards Orders for all BSI, international and foreign standards publications should be addr

47、essed to Customer Services. Tel: 020 8996 9001. Fax: 020 8996 7001. In response to orders for international standards, it is BSI policy to supply the BSI implementation of those that have been published as British Standards, unless otherwise requested. Information on standards BSI provides a wide ra

48、nge of information on national, European and international standards through its Library and its Technical Help to Exporters Service. Various BSI electronic information services are also available which give details on all its products and services. Contact the Information Centre. Tel: 020 8996 7111

49、. Fax: 020 8996 7048. Subscribing members of BSI are kept up to date with standards developments and receive substantial discounts on the purchase price of standards. For details of these and other benefits contact Membership Administration. Tel: 020 8996 7002. Fax: 020 8996 7001. Copyright Copyright subsists in all BSI publications. BSI also holds the copyright, in the UK, of the publications of the international standardization bodies. Except as permitted under the Copyright, Designs and Patents Act 1988 no extract may be reproduced, stored in a r