BS 2S 147-1976 Specification for 0 5% nickel-chromium-molybdenum steel bars for the manufacture of forged bolts and forged nuts《锻制螺栓、螺母用的含0 5%镍-铬-钼钢棒规范》.pdf

《BS 2S 147-1976 Specification for 0 5% nickel-chromium-molybdenum steel bars for the manufacture of forged bolts and forged nuts《锻制螺栓、螺母用的含0 5%镍-铬-钼钢棒规范》.pdf》由会员分享，可在线阅读，更多相关《BS 2S 147-1976 Specification for 0 5% nickel-chromium-molybdenum steel bars for the manufacture of forged bolts and forged nuts《锻制螺栓、螺母用的含0 5%镍-铬-钼钢棒规范》.pdf（6页珍藏版）》请在麦多课文档分享上搜索。

1、BRITISH STANDARD AEROSPACE SERIES CONFIRMED AUGUST 1985 BS2S 147:1976 (Superseding BSS147) Incorporating Amendment No. 1 Specification for 0.5% nickel-chromium- molybdenum steel bars for the manufacture of forged bolts and forged nuts UDC 629.7:669.15242628 194 422:621.882.2/.3BS2S147:1976 This Brit

2、ish Standard, having been prepared under the directionof the Aerospace Standards Committee, was published under the authority ofthe Executive Board on 30November 1976 BSI 01-2000 The following BSI references relate to the work on this standard: Committee reference ACE/15 Draft for comment 75/74998DC

3、 ISBN 0 580 09500 2 A British Standard does not purport to include all the necessary provisions of a contract. Users of British Standards are responsible for their correct application. Compliance with a British Standard does not of itself confer immunity from legal obligations. Summary of pages This

4、 document comprises a front cover, an inside front cover, pages i and ii, page1 and a back cover. This standard has been updated (see copyright date) and may have had amendments incorporated. This will be indicated in the amendment table on the inside front cover. Amendments issued since publication

5、 Amd. No. Date of issue Comments 6836 November 1971 Indicated by a sideline in the marginBS2S147:1976 BSI 01-2000 i Contents Page 1 Inspection and testing procedure 1 2 Manufacture 1 3 Chemical composition 1 4 Surface dressing 1 5 Condition 1 6 Heat treatment 1 7 Mechanical properties 1 8 Grain size

6、 1ii blankBS2S147:1976 BSI 01-2000 1 NOTEThe requirements for the finished bolts and nuts are given in the relevant specifications for those products, such as those in the “A” series of British Standards. 1 Inspection and testing procedure 1.1 General. This British Standard shall be used in conjunct

7、ion with sections 1 and 9 of the latest issue of BSS100. 1.2 Sulphur printing or deep etching tests. One sample shall be taken from each ingot for sulphur printing or deep etching tests. 1.3 Ultrasonic examination. Billets shall be subjected to ultrasonic examination. 2 Manufacture The material shal

8、l be manufactured by an electric process. 3 Chemical composition The steel shall contain: 4 Surface dressing The material shall be overall dressed. 5 Condition 5.1 Bar in straight lengths. Bar delivered in straight lengths shall be supplied annealed and either cold drawn or centreless ground. 5.2 Ba

9、r in coil. Bar delivered in coil shall be supplied spheroidized, cold drawn and suitably coated for cold forging. 6 Heat treatment The final heat treatment applicable to bolts and nuts made from this material and to their representative test samples shall consist of the following: a) Hardening. Heat

10、 at a temperature of840 C to870 C, followed by cooling in oil. The tolerance on the chosen temperature shall be 10 C. b) Tempering. Heat uniformly at a temperature between450 C and 660 C, followed by cooling in air. 7 Mechanical properties 7.1 Hardening test. The hardness shall be not less than 500H

11、V. 7.2 Tests in the condition of supply. Material delivered in the condition specified in 5.1 or 5.2, as appropriate, shall comply with the following requirements. NOTEMPa = N/mm 2 . Information on SI units is given in BS3763 “The International System of units (SI)” and BS350“Conversion factors and

12、tables”. 8 Grain size The grain size shall be determined in accordance with BS 4490 “Methods for the determination of the austenitic grain size of steel”, method 3 or method 5. The grain size shall be no. 5 or finer and no grain shall be coarser than no. 3. Element % min. max. Carbon 0.38 0.43 Silic

13、on 0.20 0.35 Manganese 0.75 1.00 Phosphorus 0.025 Sulphur 0.020 Chromium 0.40 0.60 Molybdenum 0.20 0.30 Nickel 0.40 0.70 Bar in straight lengths Bar in coil Tensile strength (max.) (MPa) 770 680 or Hardness (max.) 229 HB BS 2S 147:1976 BSI 389 Chiswick High Road London W4 4AL BSIBritishStandardsInst

14、itution BSI is the independent national body responsible for preparing BritishStandards. It presents the UK view on standards in Europe and at the international level. It is incorporated by Royal Charter. Revisions BritishStandards are updated by amendment or revision. Users of BritishStandards shou

15、ld make sure that they possess the latest amendments or editions. It is the constant aim of BSI to improve the quality of our products and services. We would be grateful if anyone finding an inaccuracy or ambiguity while using this BritishStandard would inform the Secretary of the technical committe

16、e responsible, the identity of which can be found on the inside front cover. Tel:02089969000. Fax:02089967400. BSI offers members an individual updating service called PLUS which ensures that subscribers automatically receive the latest editions of standards. Buying standards Orders for all BSI, int

17、ernational and foreign standards publications should be addressed to Customer Services. Tel:02089969001. Fax:02089967001. In response to orders for international standards, it is BSI policy to supply the BSI implementation of those that have been published as BritishStandards, unless otherwise reque

18、sted. Information on standards BSI provides a wide range of information on national, European and international standards through its Library and its Technical Help to Exporters Service. Various BSI electronic information services are also available which give details on all its products and service

19、s. Contact the Information Centre. Tel:02089967111. Fax:02089967048. Subscribing members of BSI are kept up to date with standards developments and receive substantial discounts on the purchase price of standards. For details of these and other benefits contact Membership Administration. Tel:0208996

20、7002. Fax:02089967001. Copyright Copyright subsists in all BSI publications. BSI also holds the copyright, in the UK, of the publications of the international standardization bodies. Except as permitted under the Copyright, Designs and Patents Act 1988 no extract may be reproduced, stored in a retri

21、eval system or transmitted in any form or by any means electronic, photocopying, recording or otherwise without prior written permission from BSI. This does not preclude the free use, in the course of implementing the standard, of necessary details such as symbols, and size, type or grade designatio

22、ns. If these details are to be used for any other purpose than implementation then the prior written permission of BSI must be obtained. If permission is granted, the terms may include royalty payments or a licensing agreement. Details and advice can be obtained from the Copyright Manager. Tel:02089967070.