《ASTM D7932-2014 6073 Standard Specification for Printed Pressure-Sensitive Adhesive Labels for Use in Extreme Distribution Environments《极值分布环境中使用的印刷和压力敏感性粘结标签的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM D7932-2014 6073 Standard Specification for Printed Pressure-Sensitive Adhesive Labels for Use in Extreme Distribution Environments《极值分布环境中使用的印刷和压力敏感性粘结标签的标准规格》.pdf（7页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D7932 14Standard Specification forPrinted, Pressure-Sensitive Adhesive Labels for Use inExtreme Distribution Environments1This standard is issued under the fixed designation D7932; the number immediately following the designation indicates the year oforiginal adoption or, in the case of

2、 revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification provides a standard means to test andmeasure performance characteristics of

3、printed, pressure-sensitive adhesive labels for containers, particularly containersto be used in extreme distribution environments (for example,hazardous materials labels, aerospace, military containers). Forthe purposes of this specification, an extreme distributionenvironment is one in which it ca

4、n be reasonably expected toexperience direct exposure to deteriorating chemicals, weather,elevated/cold temperatures, and other environmental andphysical elements for an extended period of time.1.2 UnitsThe values stated in either SI units or inch-pound units are to be regarded separately as standar

5、d. Thevalues stated in each system may not be exact equivalents;therefore, each system shall be used independently of the other.Combining values from the two systems may result in non-conformance with the standard.1.3 This standard does not purport to address all of thesafety concerns, if any, assoc

6、iated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2A666 Specification for Annealed or Cold-Worked AusteniticS

7、tainless Steel Sheet, Strip, Plate, and Flat BarD374 Test Methods for Thickness of Solid Electrical Insu-lation (Withdrawn 2013)3D975 Specification for Diesel Fuel OilsD996 Terminology of Packaging and Distribution Environ-mentsD1000 Test Methods for Pressure-Sensitive Adhesive-Coated Tapes Used for

8、 Electrical and Electronic Applica-tionsD3611 Practice for Accelerated Aging of Pressure-SensitiveTapesD3951 Practice for Commercial PackagingD4332 Practice for Conditioning Containers, Packages, orPackaging Components for TestingD4814 Specification for Automotive Spark-Ignition EngineFuelD6210 Spec

9、ification for Fully-Formulated Glycol Base En-gine Coolant for Heavy-Duty EnginesD6252/D6252M Test Method for PeelAdhesion of Pressure-Sensitive Label Stocks at a 90 AngleG195 Guide for Conducting Wear Tests Using a RotaryPlatform Abraser2.2 Department of Defense Standards:4MIL-STD-810 Environmental

10、 Engineering Considerationsand Laboratory TestsMIL-STD-2073 Standard Practice for Military PackagingMIL-DTL-83133 Turbine Fuel, Aviation, Kerosene Type,JP-8 (NATO F-34), NATO F-35, and JP-8+100 (NATOF-37)2.3 Society of Automotive Engineers Standards:5SAE J183 Engine Oil Performance and Engine Servic

11、eClassificationSAE J300 Engine Oil Classification2.4 Other:ISO/IEC 15415 Information Technology Automatic Iden-tification and Data Capture Techniques Bar Code PrintQuality Test Specification Two Dimensional Symbols6ISO/IEC 15416 Information Technology Automatic Iden-tification and Data Capture Techn

12、iques Bar Code PrintQuality Test Specification Linear Symbols61This specification is under the jurisdiction of ASTM Committee D10 onPackaging and is the direct responsibility of Subcommittee D10.14 on Tape andLabels.Current edition approved Sept. 1, 2014. Published October 2014. DOI: 10.1520/D793214

13、2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3The last approved version of this historical standard is ref

14、erenced onwww.astm.org.4Copies of these documents are available online at http:/quicksearch.dla.mil orfrom the Standardization Document Order Desk, 700 Robbins Avenue, Building4/D, Philadelphia, PA 19111-5094.5Copies of these documents are available from Society ofAutomotive Engineers(SAE), 400 Comm

15、onwealth Dr., Warrendale, PA 15096-0001.6Copies of these documents are available at www.iso.org or www.ansi.org orfrom theAmerican National Standards Institute, 25 West 43rd Street, 4th Floor, NewYork, NY 10036.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 1

16、9428-2959. United States1ISO/IEC 15426-1 Information Technology AutomaticIdentification and Data Capture Techniques Bar CodeVerifier Conformance Specification Part 1: Linear Sym-bols6ISO/IEC 15426-2 Information Technology AutomaticIdentification and Data Capture Techniques Bar CodeVerifier Conforman

17、ce Specification Part 2: Two-Dimensional Symbols6ANSI MH10.8.1 Linear Bar Code then subtract to obtain the label thicknessonly.11.5 Abrasion ResistanceExposure to abrasion shall beconducted as specified in Guide G195. Label samples shall beattached to the test plates such that maximum barcode printe

18、darea will be in the abrasion path. Label samples do not have tobe adhered to test plates using adhesive for the purposes of thistest. Label samples shall be abraded at a speed of 60 cycles/minusing the CS-10 or CS-10F abrading wheel and a 500 g weighton each wheel. Vacuum level shall be set to 100

19、%. Durationshall be 500 cycles for Type I and 100 cycles for Type II labels.Following completion, label samples shall meet the minimumprint quality requirements of 11.2.11.5.1 Hot and Cold ConditioningFor the purpose ofdetermining abrasion resistance at hot and cold atmosphericconditions, label samp

20、les shall be conditioned in the desert andcryogenic conditioning atmospheres, respectively, described inTable 1 of Practice D4332 for a period of not less than 24 hbefore testing. The abrasion shall be conducted in standardatmospheric conditions as soon as possible after removal of thelabel sample f

21、rom the desert or cryogenic conditioning atmo-sphere. The maximum permissible time from conditioningchamber removal to start of abrasion shall be 3 min.11.6 High TemperatureExposure to high temperature shallbe conducted in accordance with MIL-STD-810, Method501.5, Procedure I, Storage. The temperatu

22、re cycle shall be inaccordance with induced conditions of Table 501.5-III and theexposure duration shall be seven 24-h cycles.11.7 Low TemperatureExposure to low temperature shallbe conducted in accordance with MIL-STD-810, Method502.5, Procedure I, Storage. The temperature shall be inaccordance wit

23、h Design Type C3, Severe Cold, and theexposure duration shall be 4 h. A ramp up and ramp down timeof12 h each, independent of 4 h test time, shall be used totransition the label test specimen from ambient to cold andagain from cold to ambient.11.8 RainExposure to rain shall be conducted in accor-dan

24、ce with MIL-STD-810, Method 506.5, Procedure II, Exag-gerated Rain. Label test specimen standoff distance shall be amaximum of 19 in. (48 cm) and exposure duration shall be 40min. The label test specimen shall be positioned in the verticalY-direction and rain spray shall be in the horizontal X-direc

25、tionto avoid pooling effects.11.9 Salt FogExposure to salt fog shall be conducted inaccordance with MIL-STD-810, Method 509.5. A 5 6 1 % saltsolution shall be used. The label test specimen shall be exposedto alternating 24-h periods of salt fog exposure and dryingconditions for four 24-h cycles.11.1

26、0 Blowing DustExposure to blowing dust shall beconducted in accordance with MIL-STD-810, Method 510.5,Procedure I.11.11 HumidityExposure to humidity shall be performedin accordance with MIL-STD-810, Method 507.5, inducedconstant high humidity Cycle B1. Exposure duration shall be45 days.11.12 Freeze/

27、ThawExposure to a freeze/thaw cycle shallbe conducted in accordance with MIL-STD-810, Method 524,Procedure III, Rapid Temperature Change. The temperaturerange shall be from a minimum of 14F to at least 72F. Theexposure shall consist of three cycles and shall begin and finishin the warm condition.11.

28、13 Accelerated AgingExposure to accelerated agingconditions shall be conducted in accordance with PracticeD3611. The label test specimen shall be exposed to anenvironment of 66C (150F) and 80 % relative humidity for aperiod of 96 h (4 days).11.14 Contamination by FluidsExposure to contamina-tion by

29、fluids (chemical resistance) shall be conducted inaccordance with MIL-STD-810, Method 504.1, Procedure II.The application method shall be by immersion only.11.14.1 The contamination sequence shall be as follows: 1 himmersion time, visual inspection, 7 h immersion time, dryingtime not to exceed 24 h,

30、 examination in accordance with 11.2and 11.3 (see 10.6).11.14.2 Test chemicals and respective adhesion require-ments shall be as described in Table 3.11.14.3 Several test chemicals, such as gasoline, may par-tially or fully evaporate before completion of 8 h immersiontime. In this case do not refill

31、 or reapply any additional testchemical to the label test sample and allow sequence toproceed as specified in 11.14.1.11.15 Solar RadiationExposure to solar radiation (sun-shine) shall be conducted in accordance with MIL-STD-810,D7932 146Method 505.5, Procedure II. Exposure duration shall be fifty-s

32、ix 24-hour cycles. The label test specimen shall be examinedand photographed after every 10 cycles to document anychanges. A solar test system utilizing xenon arc or metal halidebulbs with proper filters is recommended to meet the spectralirradiance requirements.12. Report12.1 Report fully all the s

33、teps taken. At a minimum, thereport should include:12.1.1 Reference to this specification.12.1.2 Description of product (for example, manufacturer,backing material, adhesive, batch/lot number(s), etc.) andshipping unit.12.1.3 Test plan.12.1.4 Assurance levels and rationale.12.1.5 Number of samples t

34、ested.12.1.6 Conditioning used.12.1.7 Acceptance criteria.12.1.8 Variation from recommended procedures.12.2 Military ShipmentsIn addition to 12.1.2 12.1.8, thecomplete report shall include the following:12.2.1 Party, other than contractor, performing testing.12.2.2 Testing facility used, other than

35、contractors.12.2.3 Government representative witnessing testing.13. Certification13.1 When specified in the purchase order or contract (see6.1.7) the purchaser shall be furnished with a certificationstating that the samples representing each lot of labels havebeen tested and inspected as directed in

36、 this specification andthe requirements have been met.14. Rejection14.1 Material that fails to conform to the requirements ofthis specification may be rejected. Rejection shall be reportedto the producer or supplier promptly in writing.15. Preparation for Delivery15.1 Unless otherwise specified in t

37、he purchase order orcontract (see 6.1.9), labels shall be packaged and packed inaccordance with Practice D3951. Such packaging shall ensurearrival at destination in satisfactory conditions and shall beacceptable to the carrier used at the lowest rate.15.2 Military ShipmentsWhen specified (see 6.1.9)

38、 ship-ments to the Department of Defense shall be packaged andpacked in accordance with MIL-STD-2073 at the levelsspecified in the purchase order or contract.16. Keywords16.1 labels; pressure-sensitive adhesives; shipping contain-ers; distribution environmentsASTM International takes no position res

39、pecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This

40、standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM Intern

41、ational Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown be

42、low.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 147