ASTM D7395-2007(2012) 5625 Standard Test Method for Cone Plate Viscosity at a 500 s-1 Shear Rate《在500 s-1 剪切率下的锥 板粘度的标准试验方法》.pdf
《ASTM D7395-2007(2012) 5625 Standard Test Method for Cone Plate Viscosity at a 500 s-1 Shear Rate《在500 s-1 剪切率下的锥 板粘度的标准试验方法》.pdf》由会员分享,可在线阅读,更多相关《ASTM D7395-2007(2012) 5625 Standard Test Method for Cone Plate Viscosity at a 500 s-1 Shear Rate《在500 s-1 剪切率下的锥 板粘度的标准试验方法》.pdf(3页珍藏版)》请在麦多课文档分享上搜索。
1、Designation: D7395 07 (Reapproved 2012)Standard Test Method forCone/Plate Viscosity at a 500 s-1Shear Rate1This standard is issued under the fixed designation D7395; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last
2、revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method covers the determination of the viscos-ity of paints and related products using a cone/plate viscometerat
3、a shear rate of 500 s-1.1.2 Viscosity values obtained by this method may be used asan alternative to results from No. 4 Ford cup measurements.The values from this method do not replicate Ford cup results,but can be used for quality control, producer-user specifica-tions and viscosity reduction in th
4、e same manner that Ford cupsare used.1.3 If viscosity at a higher shear rate is needed, Test MethodD4287, which describes viscosity measurement at 10 000 to 12000 s-1may be used.1.4 The values stated in SI units are to be regarded asstandard. No other units of measurement are included in thisstandar
5、d.1.5 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced
6、 Documents2.1 ASTM Standards:2D3925 Practice for Sampling Liquid Paints and RelatedPigmented CoatingsD4287 Test Method for High-Shear Viscosity Using aCone/Plate Viscometer3. Summary of Test Method3.1 The material to be tested is placed between the cone andplate of a cone/plate viscometer set at 25C
7、, a solvent trap islowered, and the specimen is subjected to a shear rate of 500 s-1while the viscosity is measured.4. Significance and Use4.1 This test has been used to measure viscosities ofautomotive topcoats in place of No. 4 Ford cup measurementsand has provided an equivalent ability to evaluat
8、e whether thepaint meets specifications and is sprayable.4.2 The method could be considered as an alternative to No.4 Ford cup and other efflux cup measurements for otherproducts as well.4.3 The type of viscometer described in this method givesbetter temperature control than Ford and other efflux cu
9、ps andis expected to give better precision.4.4 This test method is suitable for all paints and relatedmaterials whether they are Newtonian in behavior or not.5. Apparatus5.1 Cone/Plate Type Viscometer with cone/speed combina-tion producing a shear rate of 500 s-1and fitted with a solventtrap that co
10、vers the cone. For automotive topcoats, the viscom-eter must provide a viscosity measurement range that includes20 to 200 cP (= mPa.s) at the above-mentioned shear rate. ABrookfield CAP1000+ or CAP2000+ with a #10 cone at 100rpm shaft speed has worked well.6. Reagents and Materials6.1 Water or Solve
11、ntIf the viscometer allows manualzeroing, this should be done in accordance with the manufac-turers directions. Zeroing procedures that require liquids maybe satisfied with water or a low-viscosity solvent such asxylene or mineral spirits.6.2 Mineral OilsOne to three standard mineral oils withknown
12、viscosities (certified by an approved laboratory) lyingbetween 10 and 90 % full scale to be used for calibrating theinstrument. If a single oil is used, its viscosity should be similarto that of the materials being tested.NOTE 1Silicone oils should be avoided because of their tendency tocontaminate
13、instruments, containers and other equipment.7. Sampling7.1 Take a representative sample of the product to be testedin accordance with Practice D3925. If the sample has atendency to settle or separate on standing, then it must bestirred or shaken until homogeneous before a test specimen istaken from
14、it. However, it is appropriate to directly test a1This test method is under the jurisdiction of ASTM Committee D01 on Paintand Related Coatings, Materials, and Applications and is the direct responsibility ofSubcommittee D01.24 on Physical Properties of Liquid Paints and Paint Materials.Current edit
15、ion approved Feb. 1, 2012. Published February 2012. Originallyapproved in 2007. Last previous edition approved in 2007 as D7395 - 07. DOI:10.1520/D7395-07R12.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of A
16、STMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.sample that has been under constant circulation and shear in apaint system. The specimen
17、 must be free of any foreign matteror air bubbles, and its volume must be sufficient to cover theportion of the viscometer plate under the cone when the latteris brought into contact with the plate.8. Preparation of Apparatus8.1 The viscometer must be zeroed on a daily basis orotherwise before use,
18、in accordance with the operating manualfor the instrument. It may need to be re-zeroed at other timesin accordance with the manufacturers instructions.8.2 Verify the calibration of the apparatus by following theprocedure in Section 9, but using a standard refined mineral oilhaving Newtonian characte
19、ristics and a known viscosity. If theviscometer reads the correct viscosity (or within 5 % of thatvalue) with an oil whose viscosity is similar to that of thespecimens to be tested, then the viscometer readings may beused as is. If the viscometer does not give the correct viscosityfor the oil, then
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
5000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ASTMD7395200720125625STANDARDTESTMETHODFORCONEPLATEVISCOSITYATA500S1SHEARRATE 500 S1 剪切 粘度 标准 试验 方法 PDF

链接地址:http://www.mydoc123.com/p-525356.html