ASTM D6358-2011 7500 Standard Classification System and Basis for Specification for Poly (Phenylene Sulfide) (PPS) Injection Molding and Extrusion Materials Using ISO Methods《用ISO方.pdf

《ASTM D6358-2011 7500 Standard Classification System and Basis for Specification for Poly (Phenylene Sulfide) (PPS) Injection Molding and Extrusion Materials Using ISO Methods《用ISO方.pdf》由会员分享，可在线阅读，更多相关《ASTM D6358-2011 7500 Standard Classification System and Basis for Specification for Poly (Phenylene Sulfide) (PPS) Injection Molding and Extrusion Materials Using ISO Methods《用ISO方.pdf（7页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D6358 11Standard Classification System and Basis for Specification forPoly (Phenylene Sulfide) (PPS) Injection Molding andExtrusion Materials Using ISO Methods1This standard is issued under the fixed designation D6358; the number immediately following the designation indicates the year

2、oforiginal adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This classification system covers unfilled, reinforcedan

3、d filled materials suitable for injection molding and extrusionusing ISO methods. The system allows for the use of poly(phenylene sulfide) (PPS) plastic materials that are recycled,reconstituted recycled-regrind, recovered or reprocessed, orboth, provided that the requirements as stated in this spec

4、ifi-cation are met. It is the responsibility of the supplier and thebuyer of recycled, reconstituted, recycled-regrind, recovered orreprocessed, or both, poly (phenylene sulfide) plastic materialsto ensure compliance (see Guide D7209).1.2 The properties included in this classification are thoserequi

5、red to identify the compositions covered. It is possiblethat other requirements are necessary to identify particularcharacteristics important to specialized applications. The use ofsuffixes as shown in Section 5 is one way of specifying theserequirements.1.3 This classification system and subsequent

6、 line callout(specification) are intended to provide a means of calling outplastic materials used in the fabrication of end items or parts.It is not intended for the selection of materials. Materialselection needs to be made by those having expertise in theplastic field after careful consideration o

7、f the design and theperformance required of the part, the environment to which itwill be exposed, the fabrication process to be employed, thecosts involved, and the inherent properties of the material otherthan those covered by this classification.1.4 The following precautionary caveat pertains only

8、 to thetest method portion, Section 11, of this classification system:This standard does not purport to address all of the safetyconcerns, if any, associated with its use. It is the responsibilityof the user of this standard to establish appropriate safety andhealth practices and determine the appli

9、cability of regulatorylimitations prior to use.NOTE 1This standard and ISO 28078 address the same subject matter,but differ in technical content.NOTE 2ASTM D4067 for PPS uses ASTM test methods.2. Referenced Documents2.1 ASTM Standards:2D618 Practice for Conditioning Plastics for TestingD883 Terminol

10、ogy Relating to PlasticsD1600 Terminology for Abbreviated Terms Relating toPlasticsD3641 Practice for Injection Molding Test Specimens ofThermoplastic Molding and Extrusion MaterialsD3892 Practice for Packaging/Packing of PlasticsD4000 Classification System for Specifying Plastic Materi-alsD4067 Cla

11、ssification System for and Basis for Specificationfor Reinforced and Filled Poly(Phenylene Sulfide) (PPS)Injection Molding and Extrusion Materials Using ASTMMethodsD7209 Guide for Waste Reduction, Resource Recovery, andUse of Recycled Polymeric Materials and ProductsE29 Practice for Using Significan

12、t Digits in Test Data toDetermine Conformance with Specifications2.2 IEC and ISO Standards:3IEC 60112 Recommended Methods for Determining theComparative Tracking Index of Solid Insulation MaterialsIEC 60243 Recommended Methods for Electric Strength ofSolid Insulating Materials at Power FrequenciesIS

13、O 62 Plastics-Determination of Water AbsorptionISO 178 PlasticsDetermination of Flexural Properties ofRigid PlasticsISO 180/1A PlasticsDetermination of Izod ImpactStrength of Rigid MaterialsISO 294-1 PlasticsInjection Moulding Test Specimens ofThermoplastic MaterialsISO 527 PlasticsDetermination of

14、Tensile PropertiesISO 604 PlasticsDetermination of Compressive Proper-tiesISO 1133 PlasticsDetermination of Mass Flow Rate and1This classification system is under the jurisdiction ofASTM Committee D20 onPlastics and is the direct responsibility of Subcommittee D20.15 on ThermoplasticMaterials (Secti

15、on D20.15.17).Current edition approved Dec. 1, 2011. Published January 2012. Originallyapproved in 1998. Last previous edition approved in 2006 as D6358 - 06. DOI:10.1520/D6358-11.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org

16、. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3ISO and IEC Selected Standards for the Plastics Industry, 2nd Edition, ASTM,Stock#: ISOPLAS2.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM Inter

17、national, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.Melt Volume Flow RateISO 1183 PlasticsMethods for Determining the Densityand Relative Density of Noncellular PlasticsISO 3167 PlasticsMultipurpose Test SpecimensISO 3451 PlasticsDetermination of AshISO 1144

18、3 PlasticsDetermination of the Fluidity of Plas-tics Using Capillary and Split Die RheometersISO 28078 PlasticsPoly(phenylene sulfide) (PPS) Mould-ing and Extrusion MaterialsPart 1: Designation Systemand Basis for Specifications2.3 UL Standards:4UL 94 Test for Flammability of Plastic Materials for P

19、artsin Devices and Appliances2.4 NTIS Standards:5AD297457 Procedures and Analytical Method for Deter-mining Toxic Gases Produced by Synthetic Compounds2.5 Military Standards:6MIL-M-24519MIL-P-461743. Terminology3.1 DefinitionsThe terminology used in this classificationsystem is in accordance with Te

20、rminology D883 and Termi-nology D1600.4. Classification4.1 Poly(phenylene sulfide) materials are classified accord-ing to their composition. These classes are subdivided intogrades as shown in the Basic Property Table (Table PPS).NOTE 3An example of the use of this classification system forspecifyin

21、g fiberglass reinforced poly(phenylene sulfide) is given asfollows: The line callout PPS011G40 (specification) indicates the follow-ing:PPS = poly(phenylene sulfide) as found in Terminology D1600.01 = general purpose (group),1 = glass reinforced (class), andG40 = nominal 40 % glass with the requirem

22、ents given in TablePPS (grade).4.1.1 To facilitate incorporation of future or special materi-als the “other” category for group (00), class (0), and grade (0)is shown in Table PPS. The basic properties of these materialsare obtained from Table A as they apply.4.2 Reinforced, filled, and unfilled ver

23、sions of poly(phe-nylene sulfide) materials that are not in Table PPS are specifiedin accordance with Tables PPS, A, and B. Table PPS is firstused to identify the group and class of poly(phenylene sulfide).Table A is then used to specify the property requirements afterthe addition or reinforcements,

24、 pigments, fillers, or lubricantsat the nominal level indicated (see 4.2.1) or Table B is used tospecify the property requirements of unfilled/unreinforcedversions of poly(phenylene sulfide).4.2.1 Reinforced versions of the basic materials are identi-fied by a single letter that indicates the reinfo

25、rcement used andtwo digits that indicate the nominal quantity in percent byweight. Thus, a letter designation G for glass-reinforced and 30for percent of reinforcement, G30, specifies a filled materialwith a nominal glass level of 30 %. The reinforcement letterdesignations and associated tolerance l

26、evels are shown asfollows:Symbol Material Tolerance (Based on Total Mass)C carbon and graphite fiber rein-forced62 percentage pointsG glass-reinforced 63 percentage pointsL lubricants (such as PTFE,graphite, silicone)depends upon material and process.to be specified by supplier/useragreement.M miner

27、al-reinforced 63 percentage pointsR combinations of reinforcementsor fillers, or both63 percentage pointsNOTE 4This part of the classification system uses the percent ofreinforcements or additives, or both, in the callout (specification) of themodified basic material. The types and percentages of re

28、inforcements andadditives are usually shown on the suppliers technical data sheet unlessthey are proprietary in nature. If necessary, additional callout of thesereinforcements and additives are to be accompanied by use of the suffixpart of the system (see Section 5).4.2.2 Specific requirements for r

29、einforced, filled, or lubri-cated poly(phenylene sulfide) materials shall be identified byusing a six-character line callout. The specification shallconsist of the letter “A” and the five digits comprising the cellnumber for the property requirements in the order as theyappear in Table A.4.2.2.1 Alt

30、hough the values listed are necessary to includethe range of properties available in existing materials, this doesnot infer that every possible combination of the propertiesexists or can be obtained.4.2.3 When the grade of the basic material is not known, oris not important, the use of the “0” grade

31、 classification shall beused for the reinforced materials in this system.NOTE 5An example of a specification for a reinforced PPS material isgiven as follows. The specification PPS0110G20A31042 indicates thefollowing material requirements:PPS0110 = Glass reinforced poly(phenylene sulfide), from Tabl

32、ePPS,G20 = Glass reinforced at 20 % nominal,A = Table A property requirements,3 = 110 MPa tensile strength, min,1 = 6000 MPa flexural modulus, min,0 = Unspecified Izod strength,4 = 160 MPa flexural strength, min, and2=1.53 103kg/m3density, min.If no properties are specified, the designation would be

33、 PPS010G20A00000.NOTE 6An example of a specification for an unfilled/unreinforcedPPS material is given as follows. The designation PPS0000B32030indicates the following material requirements:PPS0000 = unfilled/unreinforced poly(phenylene sulfide), from TablePPS,B = Table B property requirements,3 = 6

34、0 MPa tensile strength, min,2 = 2000 MPa flexural modulus, min,0 = unspecified Izod strength,3 = 80 MPa flexural strength min, and0 = unspecified.If no properties are specified, the designation would be PPS0000B00000.4Available from Underwriters Laboratories (UL), 2600 N.W. Lake Rd., Camas,WA 98607-

35、8542, http:/.5Available from National Technical Information Service (NTIS), 5301 ShawneeRd., Alexandria, VA 22312, http:/www.ntis.gov.6Available from Standardization Documents Order Desk, DODSSP, Bldg. 4,Section D, 700 Robbins Ave., Philadelphia, PA 19111-5098, http:/dodssp.daps.dla.mil.D6358 1125.

36、Suffixes5.1 When additional requirements are needed that are notcovered by the basic requirements or cell-table requirements,they shall be indicated through the use of suffixes.5.2 A list of suffixes is found in Classification SystemD4000 (Table 3) and shall be used for additional requirementsas app

37、ropriate. Additional suffixes will be added to thatstandard as test methods and requirements are developed andrequested.6. General Requirements6.1 Basic requirements from the property tables or celltables are always in effect unless superseded by specific suffixrequirements, which always take preced

38、ence.6.2 The plastics composition shall be uniform and shallconform to the requirements specified herein.7. Detail Requirements7.1 The materials shall conform to the requirements in TablePPS, A, and B, and suffix requirements as they apply.7.2 For purposes of determining conformance, all specifiedli

39、mits for a specification (line callout) based on this classifica-tion system are absolute limits, as defined in Practice E29. Withthe absolute method, an observed value or a calculated value isnot rounded, but is to be compared directly with the limitingvalue. Conformance or nonconformance is based

40、on thiscomparison.8. Sampling8.1 Sampling shall be adequate statistically to satisfy therequirements of 12.4.8.2 A batch or lot shall be constituted as a unit of manufac-ture as prepared for shipment and may consist of a blend of twoor more “production runs.”9. Specimen Preparation9.1 Test specimens

41、 for relevant test methods shall be basedon the injection molded ISO 3167 Type 1A multipurpose testspecimen. The following specimens are to be used for the listedrelevant test methods (tolerances are found in ISO 3167). Alltest specimens are to be tested as molded and conditioned.Annealing is not al

42、lowed.Test Piece Relevant Test MethodISO 3167 Type 1A bar Tensile strength80 by 10 by 4-mm bar cut from thecenter portion of ISO 3167 Type 1AFlexural modulus, Izod impact,Flexural strengthSpecimen approximately 10 by 10 by4-mm cut from the center portion ofISO 3167 Type 1ADensity9.2 The test specime

43、ns shall be prepared by an injectionmolding process as specified in ISO 294-1 and Practice D3641.Accurate, reproducible settings of the processing parametersare essential to obtain specimens with comparable properties.Processing conditions are:Drying 2 h at 135CPlastic melt temperature 320CMold temp

44、erature 140CAverage injection velocity 275 6 75 mm/s10. Conditioning10.1 Test specimens shall be conditioned for a minimum of4hat236 2C and 50 6 10 % relative humidity beforeperforming the required tests.10.2 Conduct those tests influenced by ambient conditionsin the standard laboratory atmosphere o

45、f 23 6 2C and 50 610 % relative humidity in accordance with Practice D618(4/23/50).11. Test Methods11.1 Determine the properties enumerated in this classifica-tion system in accordance with the test methods in 2.1.11.1.1 The number of tests shall be consistent with therequirements of Sections 8 and

46、12.4.12. Inspection and Certification12.1 Inspection and certification of the material suppliedwith reference to a specification based on this classificationsystem shall be for conformance to the requirements specifiedherein.12.2 Lot-acceptance inspection shall be the basis on whichacceptance or rej

47、ection of the lot is made. The lot-acceptanceinspection shall consist of apparent shear viscosity (TestMethod ISO 11443) or flow rate (Test Method ISO 1133);reinforcement or filler content (reinforced and filled productsonly) (Test Method ISO 3451); and, tensile strength (reinforcedand filled produc

48、ts only) (Test Method ISO 527).12.3 Periodic check inspection with reference to a specifi-cation based upon this classification system shall consist of thetests for all requirements of the material under the specifica-tion. Inspection frequency shall be adequate to ensure thematerial is certifiable

49、in accordance with 12.4.12.4 Certification shall be that the material was manufac-tured by a process in statistical control; sampled, tested, andinspected in accordance with this classification system; andthat the average values for the lot meet the requirements of thespecification (line callout).12.5 A report of test results shall be furnished when re-quested. The report shall consist of results of the lot-acceptanceinspection for the shipment and, if requested, shall include theresults of the most recent periodic-check inspection. If re-quested,