ASTM D6098-2016 4638 Standard Classification System and Basis for Specification for Extruded and Compression Molded Shapes Made from Polycarbonate (PC)《利用聚碳酸酯 (PC) 制得挤制和模压成型型材的标准分类.pdf

《ASTM D6098-2016 4638 Standard Classification System and Basis for Specification for Extruded and Compression Molded Shapes Made from Polycarbonate (PC)《利用聚碳酸酯 (PC) 制得挤制和模压成型型材的标准分类.pdf》由会员分享，可在线阅读，更多相关《ASTM D6098-2016 4638 Standard Classification System and Basis for Specification for Extruded and Compression Molded Shapes Made from Polycarbonate (PC)《利用聚碳酸酯 (PC) 制得挤制和模压成型型材的标准分类.pdf（6页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D6098 16Standard Classification System and Basis for Specification forExtruded and Compression Molded Shapes Made fromPolycarbonate (PC)1This standard is issued under the fixed designation D6098; the number immediately following the designation indicates the year oforiginal adoption or,

2、 in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.INTRODUCTIONThis classification system is intended to be a means of calling out mechanical g

3、rade plastic productused in the fabrication of end items or parts.1. Scope*1.1 This classification system covers requirements and testmethods for the material, dimensions, and workmanship, andthe properties of extruded and compression molded plate, rod,and tubular bar manufactured from polycarbonate

4、. This clas-sification system allows for the use of recycled materialsprovided that all specifications are met.1.2 This standard is not intended to cover materials used inglazing and signage as defined in 3.1.2 and 3.1.8. It is intendedto be a means of calling out mechanical grade plastic productsus

5、ed for fabrication of end items or parts as defined in 3.1.3.1.3 The properties included in this standard are thoserequired for the compositions covered. Other requirementsnecessary to identify particular characteristics important tospecialized applications are to be described by using the calloutsy

6、stem given in Section 4.1.4 The values stated in inch-pound units are to be regardedas the standard in all property and dimensional tables. Forreference purposes, SI units are also included in Table S-PCand Table 1 only.1.5 The following precautionary caveat pertains only to thetest method portions,

7、 Section 12, of this standard. This stan-dard does not purport to address all of the safety concerns, ifany, associated with its use. It is the responsibility of the userof this standard to establish appropriate safety and healthpractices and determine the applicability of regulatory limita-tions pr

8、ior to use.NOTE 1There is no known ISO equivalent to this standard.2. Referenced Documents2.1 ASTM Standards:2D256 Test Methods for Determining the Izod PendulumImpact Resistance of PlasticsD618 Practice for Conditioning Plastics for TestingD638 Test Method for Tensile Properties of PlasticsD790 Tes

9、t Methods for Flexural Properties of Unreinforcedand Reinforced Plastics and Electrical Insulating Materi-alsD883 Terminology Relating to PlasticsD1600 Terminology forAbbreviated Terms Relating to Plas-ticsD3892 Practice for Packaging/Packing of PlasticsD3935 Classification System and Basis for Spec

10、ification forPolycarbonate (PC) Unfilled and Reinforced MaterialD4000 Classification System for Specifying Plastic Materi-als2.2 ANSI Standard:Z1.4-1993 Sampling Procedures and Tables for Inspectionby Attributes33. Terminology3.1 Definitions:3.1.1 Except for the terms defined below, the terminologyu

11、sed in this classification system is in accordance with Termi-nologies D883 and D1600.3.1.2 glazing product, na finished product which is glazedor set in frame or sash and not held by mechanical fastenerswhich pass through the product.1This classification system is under the jurisdiction ofASTM Comm

12、ittee D20 onPlastics and is the direct responsibility of Subcommittee D20.15 on ThermoplasticMaterials.Current edition approved Sept. 1, 2016. Published September 2016. Originallyapproved in 1997. Last previous edition approved in 2010 as D6098 - 10. DOI:10.1520/D6098-16.2For referenced ASTM standar

13、ds, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Available from American National Standards Institute (ANSI), 25 W. 43rd St.,4th Floor, N

14、ew York, NY 10036, http:/www.ansi.org.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States13.1.3 mechanical grade plastic product, nextruded orcompression molded shapes made

15、from polycarbonate used forfabrication of end items or parts.3.1.4 plate, nflat stock greater than14 in.3.1.5 recycled-plastic shape, na product made from up to100 % recycled plastic.3.1.6 regrind plastic, na product or scrap such as spruesand runners and edge trim that have been reclaimed byshreddi

16、ng and granulating for use in-house.3.1.7 rod, nan extruded solid cylindrical shape with aminimum diameter of18 in.3.1.8 signage product, na fabricated sign or outdoor/indoor structure, consisting of any letter, figure, character,mark, point, plane, marquee sign, design, poster, pictorial,picture, s

17、tripe, line, trademark, reading matter or illuminatingdevice, which is constructed, attached, erected, fastened, ormanufactured in any manner so that the same shall be used forthe attraction of the public to any place, subject, person, firm,corporation, public performance, article, machine ormerchan

18、dise, and displayed in any manner for recognizedadvertising purposes.3.1.9 tubular bar, nan extruded annular shape with mini-mum inside diameter of38 in. and minimum wall thickness of116 in.4. Classification and Material4.1 Product shape and size as defined in the applicablepurchase order.4.2 This c

19、lassification system covers product extruded andcompression molded as listed in Table 1 S-PC. Productsincluded in the designations refer to specification callouts fromD3935 where applicable.4.2.1 The polycarbonate shape product is categorized bytype, class, and grade depending on resin and filler co

20、mposi-tions as defined in Table 1 S-PC.4.2.2 Each polycarbonate shape is categorized into one ofseveral grades:4.2.2.1 Grade 1General PurposeExtruded or compres-sion molded product made using only 100 % virgin polycar-bonate resin.4.2.2.2 Grade 2RecycledExtruded or compressionmolded product made usi

21、ng any amount up to 100 % recycledpolycarbonate plastics.4.3 The type, class and grade is further differentiated basedon dimensional stability (elevated temperature excursion test),Table 1 S-PC, and dimensional requirements, Table 2 A-1,Table 3 B-1, and Table 4 B-2.4.4 Property Tables:4.4.1 Table 1

22、S-PC is used to describe both extruded andcompression molded products.4.4.2 Table 5 is used to describe extruded or compressionmolded products not included in Table 1 S-PC via a cell calloutthat includes the applicable Table 1 S-PC polycarbonate typeand specific properties (Designations 1-7).4.4.3 T

23、o facilitate the incorporation of future or specialmaterials not covered by Table 1 S-PC, the “as specified”category (00) for type, class and grade is shown in the tablewith the basic properties to be obtained from Table 5, as theyapply.4.4.4 Reinforcements and Additive MaterialsA symbol(single-lett

24、er) is used for the major reinforcement orcombination, or both, along with two numbers that indicate thepercentage of reinforcement and/or additive by mass with thetolerances as tabulated below. This must be included in allTable 5 callouts (Specifications).TABLE 1 S-PC Requirements for Polycarbonate

25、 (PC) ShapesType Description Class Description Grade Resin TypeADescriptionUltimateTensileStrength,min, psi(MPa)TensileElongation,% at break,minTensile Modulus,min, psi (MPa)DimensionalStability, max,%01 Polycarbonate 1 Unfilled 1 PC111,BPC112,BPC113,BPC114,BPC115,BPC116,BPC117,BorPC110B34720BGenera

26、lPurpose8000 (55) 50 300 000 (2070) 0.42 As SpecifiedCRecycled . . . . . . . . . . . .0 As SpecifiedCAs Specified . . . . . . . . . . . .2 UV Stabilized 1 PC0135BorPC0136GeneralPurpose8000 (55) 50 300 000 (2070) 0.42 As SpecifiedCRecycled . . . . . . . . . . . .0 As Specified 0 As SpecifiedCAs Speci

27、fied . . . . . . . . . . . .00 OtherPolycarbonates0 As Specified 1 As Specified GeneralPurpose. . . .2 As Specified Recycled . . . . . . . . . . . .0 As SpecifiedCAs Specified . . . . . . . . . . . .AIn accordance with Classification System D3935.BApplicable D3935 resin type to be specified on purch

28、ase order.CAlphanumeric sequence indicating filler type and quantity must precede Table 5 callouts for modified products (see 4.4.4).D6098 162Symbol MaterialTolerance(Based on the Total Mass)C Carbon and graphite fiber 2 %reinforcedG Glass-reinforced15 % glass content 3 %L Lubricants (for example, D

29、epends upon material andPTFE, graphite, and silicone) processto be specifiedM Mineral 2 %R Combinations of reinforcements 3 % for the total reinforcementor fillers, or both4.5 Callout DesignationAone-line system shall be used tospecify polycarbonate materials covered by this classificationsystem. Th

30、e system uses pre-defined cells to refer to specificaspects of this classification system as illustrated below:4.5.1 Examples:4.5.1.1 Example 1Product made from general purposepolycarbonate:CELL CALLOUT: S-PC0111S-PC01 = Product made from PC in accordance with Table 1 S-PC1 = Unfilled class1 = Gener

31、al purpose grade product4.5.1.2 Example 2Product made from 20 % glass rein-forced general purpose polycarbonate:CELL CALLOUT: S-PC0100G2053454430TABLE 2 A-1 Dimensional Requirements for Polycarbonate RodASize, in. Diameter Tolerance, in.RoundnessTIR, in.Camber, in./ft18 to78 +0.002/-0.001 0.002 212

32、/81 +0.005/-0 0.002 114 /8118 to 114 +0.005/-0 0.004 114 /8138 to 178 +0.005/-0 0.005 114 /82 +0.005/-0 0.010 114 /8218 to 212 +0.030/-0 0.025 114 /8258 to 6 +0.250/-0 0.05014 /4ATo convert inches to millimetres multiply by 25.40.TABLE 3 B-1 Dimensional Requirements for Extruded Polycarbonate Plates

33、 (Grade 1)ASize, in.ThicknessTolerances, in.Length Camber,in./ftWidth Bow, in./ft14 to 2 +0.025/-034 /4316 /2218 to 3 +0.050/-014 /4116 /2318 and over +0.050/-014 /4116 /1ATo convert inches to millimetres multiply by 25.40.TABLE 4 B-2 Dimensional Requirements for Compression Molded Polycarbonate Pla

34、tesA,BSize, in. Thickness Tolerance, in.Length Camber,in./ftWidth Bow,in./ft38 to78 +0.090/-038 /4332 /21 and over +0.090/-018 /4364 /2ATo convert inches to millimetres multiply by 25.40.BCompression molded plate is supplied sufficiently oversize to finish to nominal dimension listed.TABLE 5 Additio

35、nal Detail RequirementsReinforced/Unreinforced Extruded and Compression Molded PolycarbonatesNOTE 1The applicable table polycarbonate type (including fillers in accordance with 4.4.4 ) must precede this table designation.Designa-tion OrderNumberProperty 0 123456 7 8 91 Tensile strength, Test Method

36、Unspecified 6000 8000 10 000 12 000 14 000 16 000 20 000 25 000 SpecifyD638, min, psi (MPa) (41) (55) (69) (83) (97) (110) (138) (172) Value2 Elongation at Break Unspecified 1 3 5 10 20 50 100 200 SpecifyTest Method D638,%,min Value3 Tensile Modulus, min, Test Method Unspecified 100 000 200 000 300

37、000 400 000 500 000 600 000 800 000 1 000 000 SpecifyD638 min, psi (MPa) (690) (1379) (2073) (2760) (3448) (4137) (5516) (6895) Value4 Dimensional Stability, % max, Unspecified 0.1 0.2 0.3 0.4 0.6 0.8 1.0 1.5 Specifyper 12.2 Value5 Flexural Modulus, Unspecified 250 000 350 000 450 000 550 000 650 00

38、0 750 000 1 000 000 1 500 000 SpecifyTest Method D790,min, psi (MPa)(1649) (2400) (3100) (3792) (4482) (5171) (6895) (10 343) Value6 Izod impact, Test Method Unspecified 0.5 0.75 1.0 2.5 5.0 10.0 15.0 18.0 SpecifyD256, min ftlb/in. (27) (40) (53) (133) (266) (533) (800) (960) Value(J/m)7 To be deter

39、mined Unspecified . . . . . . . . . . . . . . . . . . . . . . . . . . .D6098 163S-PC0100 = Product made from PC in accordance with Table 1 S-PCG20 = 20 % glass1=Table 5 properties3 = Tensile strength (10,000 psi)4 = Elongation at break (10 %)5 = Tensile Modulus (500,000 psi)4 = Dimensional stability

40、 (0.4 %)4 = Flexural Modulus (550,000 psi)3 = Izod Impact (1.0 ft-lb/in.)0 = Unspecified4.5.2 These two examples illustrate how a one-line, alpha-numeric sequence can identify (specify) the productcomposition, commercial parameters and physical characteris-tics of extruded or compression molded prod

41、uct. A space mustbe used as a separator between the specification number andthe type designation. No separators are needed between type,class and grade. When special notes are to be included, suchinformation shall be preceded by a comma. Special tolerancesmust be noted at the time of order and are i

42、nserted after thegrade in parenthesis and preceded by a comma.5. Ordering Information5.1 All shapes covered by this standard shall be orderedusing the proper callout designation (see 4.5).6. Physical Property Requirements6.1 The physical property values listed in the tables of thisstandard are to be

43、 considered minimum specification values.Any requirement for specific test data for a given productionlot shall be specified at the time of order. Physical propertiesfor products not yet included in Table 1 S-PC are specifiedusing Table 5 for extruded or compression molded products.7. Dimensional Re

44、quirements7.1 The type, class and grade is differentiated based ondimensional stability (elevated temperature excursion test), asindicated in Table 1 S-PC.7.2 Products shall be produced within commercial toler-ances and with the lowest stress levels for machined parts asdelineated in Table 2 A-1, Ta

45、ble 3 B-1, and Table 4 B-2.7.3 Tubular bar dimensions shall be supplied in the unfin-ished condition, unless otherwise specified at time of order,sufficient to finish to the nominal dimension ordered.7.4 The maximum allowable camber and/or bow shall bewithin the limits referenced in Table 2 A-1, Tab

46、le 3 B-1, andTable 4 B-2.8. Workmanship, Finish, and Appearance8.1 AppearanceThe resin material color is transparentwith water-white or light straw color. Natural resin is alsooffered with various amounts of blue tinting. The product colorshall be as published by the shapes manufacturer. They shall

47、beuniform in color throughout the thickness. Specific colors andcolor matching only as agreed to by order.8.1.1 Physical properties, although unaffected by tinting,can be affected if coloring by other means.8.2 FinishAll products shall be free of blisters, wrinkles,cracks, gouges and defects that re

48、strict commercial use of theproduct. Special surface finish shall be supplied only whenspecified in the purchase order or contract.8.3 DefectsAll products shall be free of voids, dirt,foreign material and embedded particles exceeding 0.040 in.maximum diameter as defined in 8.3.1.8.3.1 The criteria f

49、or determining the internal cleanlinessshall be external visual inspection. A maximum number of twointernal defects per square foot of plate and one foot length ofrod and tubular bar are allowed. Clusters of defects less than0.040 in. diameter are to be counted as a single defect.8.3.2 For compression molded products, four defects up to0.080 in. diameter per square foot of plate are allowed.9. Sampling9.1 Sampling shall be statistically adequate to satisfy therequirements of this classification system as applicable (see