ASTM D5665 D5665M-1999a(2014)e1 3124 Standard Specification for Thermoplastic Fabrics Used in Cold-Applied Roofing and Waterproofing《冷应用屋面覆盖和防水用热塑性织物的标准规范》.pdf

《ASTM D5665 D5665M-1999a(2014)e1 3124 Standard Specification for Thermoplastic Fabrics Used in Cold-Applied Roofing and Waterproofing《冷应用屋面覆盖和防水用热塑性织物的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM D5665 D5665M-1999a(2014)e1 3124 Standard Specification for Thermoplastic Fabrics Used in Cold-Applied Roofing and Waterproofing《冷应用屋面覆盖和防水用热塑性织物的标准规范》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D5665/D5665M 99a (Reapproved 2014)1Standard Specification forThermoplastic Fabrics Used in Cold-Applied Roofing andWaterproofing1This standard is issued under the fixed designation D5665/D5665M; the number immediately following the designation indicates theyear of original adoption or,

2、in the case of revision, the year of last revision. A number in parentheses indicates the year of lastreapproval. A superscript epsilon () indicates an editorial change since the last revision or reapproval.1NOTEUnits information was editorially corrected in May 2014.1. Scope1.1 This specification c

3、overs thermoplastic fabrics such aspolyester, polyester/polyamide bicomponent, or compositeswith fiberglass or polyester scrims that can be used during theconstruction of cold-applied roofing and waterproofing.1.2 This specification is intended as a material specification.Issues regarding the suitab

4、ility of specific roof constructions orapplication techniques are beyond the scope of this specifica-tion.1.3 The specified tests and property values used to charac-terize the respective fabrics are intended to establish minimumproperties. In-place system design criteria or performanceattributes are

5、 factors beyond the scope of this material speci-fication.1.4 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard. The values stated ineach system may not be exact equivalents; therefore, eachsystem shall be used independently of the other. Combiningvalu

6、es from the two systems may result in non-conformancewith the standard.2. Referenced Documents2.1 ASTM Standards:2D123 Terminology Relating to TextilesD1079 Terminology Relating to Roofing and WaterproofingD1117 Guide for Evaluating Nonwoven Fabrics (Withdrawn2009)3D1776 Practice for Conditioning an

7、d Testing TextilesD1777 Test Method for Thickness of Textile MaterialsD4830 Test Methods for Characterizing Thermoplastic Fab-rics Used in Roofing and WaterproofingD5035 Test Method for Breaking Force and Elongation ofTextile Fabrics (Strip Method)D5733 Test Method for Tearing Strength of NonwovenFa

8、brics by the Trapezoid Procedure (Withdrawn 2008)33. Terminology3.1 DefinitionsFor definitions of terms used in thisspecification, refer to Terminologies D123 and D1079.4. Classification4.1 The thermoplastic fabrics covered by this specificationare of the following general constructions and composit

9、ions.Each is a separate class or type differentiated by the polymertype, combination of polymers, manufacturing process, orsome combination thereof.4.1.1 Type IPolyester spunbonded without resin, un-needled;4.1.2 Type IIPolyester spunbonded without resin, needled;4.1.3 Type IIIPolyester mat plus fib

10、er glass scrim withresin;4.1.4 Type IVPolyester core/polyamide sheath bicompo-nent spunbonded;4.1.5 Type VPolyester mat with polyester stitching; and4.1.6 Type VIPolyester mat plus polyester scrim withresin.4.1.7 Type VIIPolyester scrim fabric with resin.5. Materials and Manufacture5.1 The fabric sh

11、all be a uniform, thin, porous mat of theprimary thermoplastic polymer, with or without the addition ofreinforcing stranded glass or thermoplastic yarns. Chemicallybonding with a water-resistant resin or thermally bonding withother thermoplastic polymers shall be permitted.6. Physical Properties, Th

12、ickness, and Mass6.1 Fabrics shall conform to the thickness, mass, andphysical properties presented in Table 1.1This specification is under the jurisdiction of ASTM Committee D08 onRoofing and Waterproofing and is the direct responsibility of Subcommittee D08.04on Felts, Fabrics and Bituminous Sheet

13、 Materials.Current edition approved May 1, 2014. Published May 2014. Originallyapproved in 1995. Last previous edition approved in 2006 as D5665 99a (2006).DOI: 10.1520/D5665_D5665M-99AR14.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at servic

14、eastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3The last approved version of this historical standard is referenced onwww.astm.org.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA

15、19428-2959. United States17. Unit Mass7.1 Determine the unit mass of the fabric using the proce-dures described in Test Methods D1117.8. Workmanship, Finish, and Appearance8.1 The finished material shall be free of visible defectssuch as ragged or untrue edges, folds, creases, wrinkles, tearsand hol

16、es.9. Sampling9.1 Sample the material and determine the properties enu-merated in this specification in accordance with the testprocedures referenced herein (also see Practice D1776).10. Thickness10.1 Determine the thickness of the fabric using the proce-dures described in Test Methods D1777.11. Bre

17、aking Load and Elongation11.1 Determine the breaking load and elongation by the cutstrip method as described in Test Methods D4830 and D5035.The preferred SI unit for breaking load is kN/m.12. Trapezoid Tearing Strength12.1 Determine the trapezoid tearing strength using theprocedures described in Te

18、st Methods D5733.13. Puncture Strength13.1 Determine the puncture strength using the proceduresdescribed in Test Methods D4830.14. Inspection14.1 InspectionInspection shall be in accordance with therequirements of this specification.14.2 Inspection AlternativesAlternative inspection re-quirements sh

19、all be determined by and as agreed upon betweenthe purchaser and the supplier.15. Rejection and Resubmittal15.1 Failure to ConformFailure to conform to any of therequirements as stated in this specification constitutes groundsfor rejection.15.2 Rejection RedressThe supplier shall have the right toin

20、spect the rejected materials. The supplier and the purchasershall agree to the quantity of rolls deemed unacceptable. Thesupplier shall then have the right to submit the same number ofnew rolls as replacement.16. Packaging and Package Marking16.1 The rolls shall be wrapped or banded securely with as

21、ubstantial grade of paper, plastic wrap, or taping that encirclesthe roll in a manner that will prevent slipping or unraveling.16.2 No roll shall contain more than two pieces, and nomore than 3 % of the rolls in any lot (pallet or shipment) shallcontain two pieces. Pieces represent roll ends that ca

22、n be oneof the following: (1) individual and loose, (2) adhered, or (3)stitched to appear as one continuous piece. These rolls must bemarked clearly with a red tag or other item to identify thelocation of the splice.16.3 Unless otherwise specified, each package shall bemarked plainly with the manufa

23、cturers or suppliers name,product or brand name, or both, and theASTM designation andtype.17. Keywords17.1 cold-applied roofing and waterproofing; fiber glassscrim; polyester/polyamide reinforcement; polyester reinforce-ment; thermoplastic fabricsTABLE 1 Physical Properties of Thermoplastic Fabrics

24、for Use In Cold-Applied Roofing and WaterproofingPropertiesTypesI II III IV V VI VIIUnit mass, nominal, g/m2, oz/yd2 51 1.5 119 3.5 125 3.7 75 2.2 125 3.7 73 2.1 58 1.7lb/100 ft2 1.0 2.4 2.6 1.5 2.6 1.5 1.2Thickness, mm mils, min 0.21 8.3 1.22 48 0.41 16 0.56 22 0.28 11 0.12 4.7 0.10 4.0Breaking loa

25、d, kN/m lbf/in., min, machine direction(MD) and crossmachine direction (CD)1.6 9 4.6 26 20.5 117 4.2 24 5.6 32 7.0 40 6.5 37Elongation, %, min, MD and CD 32 50 3.3 24 17 15 14Trapezoid tearing strength, N lbf, min, MD and CD 71 16 142 32 31 7 125 28 36 8 44 10 76 17Puncture strength, N lbf, min 102

26、23 187 42 53 12 98 22 329 74 49 11 49 11D5665/D5665M 99a (2014)12ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any su

27、ch patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invit

28、ed either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a

29、 fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this

30、 standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).D5665/D5665M 99a (2014)13