1、Designation: D4072 98 (Reapproved 2013)Standard Test Method forToluene-Insoluble (TI) Content of Tar and Pitch1This standard is issued under the fixed designation D4072; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of l

2、ast revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method covers the determination of toluene-insoluble matter (TI) in tar and pitch.1.2 Since this test method

3、is empirical, strict adherence toall details of the procedure is necessary.1.3 The values stated in SI units are to be regarded asstandard. No other units of measurement are included in thisstandard.1.4 This standard does not purport to address all of thesafety concerns, if any, associated with its

4、use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use. For specific hazardinformation, see Section 7.2. Referenced Documents2.1 ASTM Standards:2D95 Test Method for Water

5、in Petroleum Products andBituminous Materials by DistillationD362 Specification for Industrial Grade Toluene (Withdrawn1989)3D850 Test Method for Distillation of Industrial AromaticHydrocarbons and Related MaterialsD4296 Practice for Sampling PitchE11 Specification for Woven Wire Test Sieve Cloth an

6、d TestSieves3. Summary of Test Method3.1 The sample is digested, then extracted with hot toluenein an alundum thimble. The insoluble matter is dried andweighed.4. Significance and Use4.1 This test method is useful for evaluating and character-izing tars and pitches and as one element in establishing

7、 theuniformity of shipments or sources of supply.5. Apparatus5.1 Extraction Apparatus, Flask with metal cap condenseras shown in Fig. 1.5.2 Extraction Thimble, Alundum AN 485 coarse (formerlyRA 98), 30 mm in diameter by 80 mm in height with flatbottom.5.3 Thimble Cover, Paper cone, made by wetting w

8、ith watera 70-mm filter paper normally folded in a small glass funnel,and drying the funnel in an oven with the paper cone in place.5.4 Sieves, U.S. Standard 600-m (No. 30) and 250-m (No.60), conforming to Specification E11.5.5 Heater, having a minimum capacity of 300 W per unit.6. Reagents6.1 Tolue

9、ne, Industrial Pure, meeting Specification D362.(WarningFlammable.)6.2 Concentrated Hydrochloric Acid. (WarningCorrosive.)7. Hazards7.1 Since toluene is a toxic and flammable substance, allworking areas should be efficiently hooded and kept free ofsparks and flames.7.2 Observe proper laboratory proc

10、edures for handling anddiluting hydrochloric acid.8. Bulk Sampling8.1 Samples from shipments shall be taken in accordancewith Practice D4296, and shall be free of foreign substances.Thoroughly mix the sample immediately before removing arepresentative portion for the determination or for dehydration

11、.9. Dehydration of Sample9.1 Hard PitchIf the solid bulk sample contains freewater, air-dry a representative portion in a forced draft oven at50C.1This test method is under the jurisdiction of ASTM Committee D02 onPetroleum Products and Lubricants and is the direct responsibility of SubcommitteeD02.

12、05 on Properties of Fuels, Petroleum Coke and Carbon Material.Current edition approved May 1, 2013. Published August 2013. Originallyapproved in 1981. Last previous edition approved in 2008 as D4072 98 (2008).DOI: 10.1520/D4072-98R13.2For referenced ASTM standards, visit the ASTM website, www.astm.o

13、rg, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3The last approved version of this historical standard is referenced onwww.astm.org.Copyright ASTM International, 100 Barr Harb

14、or Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States19.2 Soft PitchIf the presence of water is indicated bysurface foam on heating, maintain a representative portion ofthe bulk sample of a temperature between 125 and 150C in anopen container until the surface is free of foam. Take

15、care notto overheat, and remove heat source immediately when foamsubsides.9.3 TarDehydrate a representative portion of the bulksample at atmospheric pressure using a simple sidearm distil-lation apparatus similar to the one in Test Method D850 andstop the distillation when the temperature reaches 17

16、0C.Separate any oil from the water that has distilled over (ifcrystals are present, warm sufficiently to ensure their solution)and thoroughly mix the oil with the residual tar in the still afterthe latter has cooled to a moderate temperature.9.3.1 As an alternative to dehydration, the water content

17、ofthe tar is determined by Test Method D95 and, if the watercontent is less than 10 mass percent, the TI content is correctedto a dry-tar basis (see 13.2). This alternative method appliesonly to stable emulsions of water in tar, that is, no waterseparates when the tar sample is left undisturbed for

18、24 h atroom temperature.10. Preparation of Working Sample10.1 Hard PitchIf the pitch can be crushed at roomtemperature, prepare a 20-g working sample by suitablecrushing, mixing, and quartering of a representative portion ofthe dry sample. The crushing can be done with a small jawcrusher and a mulli

19、te mortar and pestle. No particle in therepresentative sample shall be larger than 5 mm in anydimension. Crush this sample so that all of it will pass the250-m (No. 60) sieve. Store the sieved working sample in atightly closed container and use within 24 h (see 10.4).10.2 Soft PitchIf the pitch is t

20、oo soft to grind and toosticky to mix, heat a representative portion of the dry sample tothe lowest temperature that will permit passage through the600-m (No. 30) sieve. Do not exceed 10 min for this meltingperiod. Pass the heated sample through the 600-m sieve toremove foreign matter.10.3 TarHeat a

21、 representative portion of the tar to thelowest temperature that will permit passage through the600-m (No. 30) sieve: then filter through this sieve to removeforeign matter.10.4 Discard working samples 24 h after crushing andsieving as changes in composition sometimes occur in pulver-ized pitch.11.

22、Preparation of Extraction Thimble11.1 Dry the clean thimble in an oven at 105 6 5C for 45min, cool in a desiccator, and weigh to the nearest 0.5 mg.Record the mass.11.1.1 After each use, ignite the thimble at 700 to 800C fora few hours. Cool the thimble slowly by placing in a dryingoven for 1 h afte

23、r removal from the furnace to preventcracking. Before reuse, condition the thimble as described in11.1.11.1.2 After repeated use, boil the thimble in 1 + 1 hydro-chloric acid. (Add equal volume of concentrated hydrochloricacid to distilled water.) to remove residual ash from the pores.Then boil the

24、thimble in distilled water and wash with water.After drying at 105C, ignite and condition the thimble asdescribed in 11.1 and 11.1.1.12. Procedure12.1 The mass of sample taken for analysis shall yieldbetween 150 and 250 mg of matter insoluble in toluene (TI),unless this would require less than the m

25、inimum acceptablesample mass of 1 g, in which case 1 g shall be used.12.2 Place the required amount of sample in a tared 150-mLbeaker and weigh to the nearest 0.5 mg. Pour 60 mL of tolueneinto the beaker, stirring continuously while introducing thetoluene, to ensure complete mixture of the sample an

26、d tolueneand thorough dispersion of the insoluble matter (see 7.1). Placethe beaker on an electric hot plate or on a steam or water bathand heat the contents to a temperature of 95 6 5C. Maintainthis temperature for 25 min. Stir occasionally with a stirringrod during this period to ensure that the s

27、ample is completelydispersed in the toluene. Check for completeness of dispersionby inspecting the bottom of the beaker for undigested material.12.3 Place the tared extraction thimble in a filter tubesupported over a beaker or flask. Wet the thimble completelywith toluene. After digestion, carefully

28、 decant portions of thehot mixture into the wetted thimble (see 7.1). Do not permit thelevel of the toluene to rise higher than 20 mm from the top ofthe thimble. It is advisable while filtering to retain the majorpart of the insoluble matter in the beaker. Finally transfer theinsoluble matter from t

29、he beaker to the thimble with smallportions of toluene. Wash the beaker with toluene until it isclean, using a suitable brush or policeman to detach anyparticles adhering to the beaker. Transfer all washings to thethimble.12.4 When almost all toluene has drained from the thimble,wash the thimble and

30、 its contents once with a small quantity oftoluene. Allow the toluene to drain from the thimble.12.5 While the extraction thimble is still moist with toluene,remove it from the filter tube and place it in the wire supportFIG. 1 Extraction ApparatusD4072 98 (2013)2of the extraction apparatus. Cover t

31、he thimble with the papercone, point down. Assemble the extraction apparatus on a hotplate, with a felt gasket between the top of the extraction flaskand condenser cover, and with fresh toluene in the bottom ofthe extraction flask. Add three to six small lumps of pumicestone to the flask to promote

32、smooth boiling, thereby prevent-ing bumping and spattering during extraction. The surface ofthe toluene in the flask shall be about 25 mm below the bottomof the thimble (see 7.1).12.6 Conduct the extraction at such a rate of heating thatcondensed toluene falls continuously from the condenser at arat

33、e of not less than 1 nor more than 2 drops/s. Continue theextraction at this rate for a period of 18 h (Note 1).NOTE 1The reflux rate can be affected by the ambient temperature,especially when the apparatus is operating overnight unattended (forexample, the temperature of the laboratory is reduced a

34、t night and thereflux rate slows or ceases). One way to alleviate this condition is to placea metal shield around the heater and extraction apparatus which wouldprevent the colder air entering the hood from excessively cooling theextraction apparatus. The shield can be as simple as a can with the en

35、dscut out.12.7 At the end of this period, remove the heat source andallow the toluene to drain from the thimble, then remove thethimble from the extraction apparatus. Remove the paper coneand gently lay the thimble on its side, with the open end tiltedup, on a watch glass in the fume hood so that th

36、e toluene canevaporate. Leave it for 30 min. Place the air-dried thimble in adrying oven at 105 6 5C for 60 min. Remove the dry thimblefrom the oven and place it immediately in a desiccator. Whencool, weigh the thimble and contents to the nearest 0.5 mg, andrecord the mass (see 12.8).12.8 If the mas

37、s of matter insoluble in toluene is less than150 mg or more than 250 mg, repeat the determination with anadjusted sample weight of not less than 1 g (see 11.1).13. Calculation13.1 Calculate the toluene-insoluble (TI) content as follows:TI,%5 B 2 A!/C# 3100 (1)where:A = mass of alundum thimble withou

38、t cone,B = mass of alundum thimble plus toluene-insolublematerial, andC = mass of sample.13.2 If the TI was determined on a wet tar sample (see9.3.1), correct the TI value determined in 13.1 to a dry-tar basisas follows:TI mass% dry basis! 5TI mass% wet basis!100 2 water content of tar, mass%!3100(2

39、)14. Report14.1 Report the toluene-insoluble (TI) content to the nearest0.1 %.15. Precision and Bias15.1 The following criteria shall be used for judging theacceptability of results (95 % probability):15.1.1 RepeatabilityDuplicate values by the same opera-tor shall not be considered suspect unless t

40、he determinedpercentages differ by more than 0.9.15.1.2 ReproducibilityThe values reported by each of twolaboratories, representing the arithmetic average of duplicatedeterminations, shall not be considered suspect unless thereported percentages differ by more than 2.0.15.2 Bias This procedure has n

41、o bias because the value oftoluene insoluble is defined in terms of this test method.16. Keywords16.1 extraction; pitch; tar; toluene-insolublesASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of t

42、his standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five y

43、ears andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical comm

44、ittee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19

45、428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).D4072 98 (2013)3