ASTM D3623-1978a(2012) Standard Test Method for Testing Antifouling Panels in Shallow Submergence《在浅浸状态下防污板的标准试验方法》.pdf

《ASTM D3623-1978a(2012) Standard Test Method for Testing Antifouling Panels in Shallow Submergence《在浅浸状态下防污板的标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM D3623-1978a(2012) Standard Test Method for Testing Antifouling Panels in Shallow Submergence《在浅浸状态下防污板的标准试验方法》.pdf（8页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D3623 78a (Reapproved 2012)Standard Test Method for TestingAntifouling Panels in Shallow Submergence1This standard is issued under the fixed designation D3623; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year o

2、f last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 This test method covers a procedure

3、 for testing antifoul-ing compositions in shallow marine environments and astandard antifouling panel of known performance to serve as acontrol in antifouling studies.NOTE 1Subcommittee D01.45 has a revised rating procedure nowbeing evaluated by round robin.1.2 The values stated in SI units are to b

4、e regarded as thestandard. The values given in parentheses are for informationonly.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and

5、determine the applica-tion of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2A569/A569M Specification for Steel, Carbon (0.15 Maxi-mum, Percent), Hot-Rolled Sheet and Strip Commercial(Withdrawn 2000)3D2200 Practice for Use of Pictorial Surface PreparationStandards and

6、 Guides for Painting Steel Surfaces2.2 U.S. Military Specifications (See also Annex A1):MIL-P-15328D Primer Pretreatment (Formula 117 for Met-als)4MIL-P-15929C Primer Coating, Shipboard, Vinyl-Red Lead(Formula 119For Hot Spray)4MIL-P-15931B Paint, Antifouling, Vinyl, Red (Formula121/63)4MIL-S-22698A

7、 Steel Plate, Carbon, Structural43. Terminology3.1 Definitions:3.1.1 shallow submergencean immersion to depths be-tween 0.3 and 3.0 m (1 and 10 ft).3.2 Abbreviations:3.2.1 The following abbreviations are used in reporting testresults:Al algaeBarn barnaclesE.B. encrusting bryozoansHyd hydroidsSl slim

8、eTun tunicatesC.F. completely fouledF.R. fouling resistance ratingA.F. antifouling ratingA.C. anticorrosive ratingO.P. overall performance ratingCO coelenteratesF.B. filamentous bryozoansMol molluscsPC polychaetes3.2.2 Algal Mups may be delineated by classification nota-tion by phyllum as follows:Al

9、-b Phaeophyta (brown)Al-bg Cyanophyta (blue-green)Al-g Chlorophyta (green)Al-r Rhodophyta (red)4. Significance and Use4.1 This method is designed as a screening test in evaluatingantifouling coating systems. Results of the standard system ina specific marine environment are included to assist in int

10、er-preting results (see Annex A2).4.2 Antifouling systems providing positive comparisonswith the standard system should be considered acceptable foruse in protecting underwater marine structures.4.3 The degree and type of fouling will vary depending onthe environment. Hence, differences in geographi

11、c location oftest sites, in time of year when panels are exposed, and inweather conditions from 1 year to the next can affect results.Therefore, a fouling census on a nontoxic surface is taken. For1This test method is under the jurisdiction of ASTM Committee D01 on Paintand Related Coatings, Materia

12、ls, and Applications and is the direct responsibility ofSubcommittee D01.45 on Marine Coatings.Current edition approved June 1, 2012. Published August 2012. Originallyapproved in 1978. Last previous edition approved in 2004 as D3623 78a (2004).DOI: 10.1520/D3623-78AR12.2For referenced ASTM standards

13、, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3The last approved version of this historical standard is referenced onwww.astm.org.4Availa

14、ble from Standardization Documents Order Desk, DODSSP, Bldg. 4,Section D, 700 Robbins Ave., Philadelphia, PA 19111-5098, http:/dodssp.daps.dla.mil.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1the exposure to be valid the nontoxic s

15、urface should showheavy fouling, and the standard system should show signifi-cantly less fouling than the nontoxic surface (see Annex A3and Annex A4).5. Apparatus5.1 Blast Cleaning Apparatus capable of preparing panels incompliance with 8.1.5.2 Application Equipment consisting of brush, roller, con-

16、ventional spray, or airless spray. Usually the equipment isdictated by the physical properties of the coating and the filmthickness desired.5.3 Exposure Rack to provide firm positioning of the speci-men panels such that they are held vertically in place in spiteof the current and are electrically in

17、sulated from metalliccontact with the rack or other panels. The rack should bepositioned such that the prevailing tidal currents will moveparallel to the panel face, and the panels will be immersed to adepth of a minimum of 0.3 m (1 ft) and a maximum of 3 m (10ft). In a rack where the panels are sta

18、cked front to back, theyshould be spaced at least 60 mm (212 in.) apart, with the twoend positions filled with blank panels. In a rack where thepanels are mounted side by side, the distance between adjacentpanels should be a minimum 1.5 mm (12 in.).6. Materials6.1 Test PanelThe substrate for the sta

19、ndard antifoulingcoating system shall be medium low-carbon steel plate perSpecification A569/A569M,53 mm thick by 150 to 250 mm by250 to 300 mm (18 in. thick by 6 to 10 by 10 to 12 in.) with aminimum area per side of 465 cm2(72 in.2). A 6-mm (14-in.)diameter hole,12 to 1 in. from the top and centere

20、d shall bedrilled for holding the panel while handling and painting. Thetest coating system shall be applied to that substrate for whichit is designed provided there is a minimum area per side of 466cm2(72 in.2).6.2 Standard Coating SystemThe standard antifoulingcoating system shall consist of:6.2.1

21、 Green pretreatment coating conforming to U.S. Mili-tary Specification MIL-P-15328B (Formula 117), B revisiononly.6.2.2 Vinyl red lead primer conforming to U.S. MilitarySpecification MIL-P-15929C (Formula 119), C revision only.6.2.3 Vinyl antifouling coating conforming to U.S. MilitarySpecification

22、MIL-P-15931B (Formula 121/63), B revisiononly.6.3 Test Coating SystemThe test antifouling coating maybe applied to the standard primer system, or to any othersuitable anticorrosive primer system.7. Safety Precautions7.1 WarningAntifouling paints contain toxic materialsthat could cause skin and eye i

23、rritation on contact and adversephysiological effects if ingested or inhaled. In the preparationof panels and the application of various types of antifoulingpaints the use of appropriate protective clothing and equipmentis required consistent with local, state, and federal governmentregulations, and

24、 recognized industrial and technical standards.Spills, overspray, and unused material should not be flusheddown the drain, but should be disposed of as hazardous waste.8. Procedure8.1 Abrasive blast the required number of panels to near-white metal (Sa 212 of Method D2200) to obtain a profile of 25t

25、o 38 m (1 to 1.5 mils).NOTE 2A profile of 25 to 38 m (1 to 1.5 mils) can be obtained withthe following parameters: (1) Type and size of grit, No. 46 (sand); (2)Pressure, 620 kPa (90 psi); (3) Angle, 90 deg; (4) Distance from surface,75 to 125 mm (3 to 5 in.); (5) Nozzle size, 9 mm (38 in.).8.2 On th

26、e clean, dry, uncontaminated, blasted surface applyto each standard panel one coat of pretreatment coatingMIL-P-15328D to give a nominal dry film thickness of 13 m(12 mil).NOTE 3All coating drying times are for a minimum temperature of21C and a maximum relative humidity of 70 %.8.3 Within 24 h of ap

27、plication of the pretreatment coatingapply the first coat of red lead vinyl primer MIL-P-15929C.Apply a total of four coats of red lead vinyl primer to give anominal dry film thickness of 150 m (6 mils ). Allow aminimum of 2 h and a maximum of 24 h drying between coatsof red lead vinyl primer.8.4 Al

28、lowing a minimum of 2 h and a maximum of 24 hdrying after the last coat of red lead vinyl primer, apply the firstcoat of vinyl antifouling coating MIL-P-15931B to the stan-dard panels, and the test coating to the test panels. A 19-mm(34-in.) numbered vinyl tape can be applied before the secondcoat o

29、f antifouling coating for identification. Allowing aminimum of 2 h and a maximum of 24 h drying after the firstcoat, apply a second coat of the respective antifouling coatingto give a nominal dry film thickness for both antifouling coatsof 100 m (4 mils).8.5 Before immersion permit the second coat o

30、f antifoulingcoating to dry a minimum of 4 h and a maximum of 2 weeks,the latter time allowing for shipping the panels to the immer-sion site.8.6 Expose for a minimum period of 1 year at an immersionsite with a high incidence of fouling as indicated by attach-ments on a dark nontoxic surface such as

31、 slate. A monthlyfouling census as well as a yearly accumulation when appro-priate is required.8.7 Evaluate the antifouling panels for surface fouling andphysical condition of the film system at least monthly asfollows using the report form in Table 1.8.7.1 Fouling on SurfacesRate fouling present on

32、 thatportion of the antifouling test surface which is intact at the timeof inspection (see 9.1). Rate both sides of the panel ifappropriate. Ignore fouling present on the substrate or onanticorrosive undercoats. Barnacles, polychaetes, coelenter-ates, etc., that are immature or loosely attached shou

33、ld be soreported in the appropriate space. Report fouling by initial5See also U.S. Military Specification MIL-S-22698, Type 1, Class A.D3623 78a (2012)2algal germination, low-form algae and diatoms as “algalslime.” Report absorbed organic and inorganic chemicals,trapped silt and detritus, and other

34、unidentified slimes as “silt.”8.7.2 Physical ConditionRate the condition of coatingfilms in accordance with 9.2. Record qualitative descriptions offilm deterioration and discoloration in this column, and unlessotherwise specified, refer only to the antifouling test surface.Indicate deterioration of

35、undercoats, when evident, by thenotation “A.C.” For example, “Peeling, A.F. from A.C.” or“Chipping, A.C. from steel.”9. Calculations:9.1 Fouling Resistance (F.R.)Award each test surface freeof fouling except for the presence of algal spores and otherbiological slimes a rating of 100. Reduce the rati

36、ng to 95 ifonly incipient fouling is present. If mature forms of fouling arepresent, obtain the rating by subtracting from 95 the sum of thenumber of individuals present and percent surface covered bycolonial forms. For example, if the “fouling on surface” is:Barn 6, 3 to 10 mmE.B. NoneOthers Mol 1,

37、20 mmAl-g (green) 10 %then the F.R. percent rating would be 95 (6+1+10)=78.9.2 Physical Condition:9.2.1 Antifouling Film (A.F.)Award an antifouling testsurface having no physical defects a rating of 100. Subtract thepercent surface affected by film defects from 100 to obtain therating for imperfect

38、films.9.2.2 Anticorrosive Film (A.C.)Obtain the rating by thesame procedure as 9.2.1.9.3 Overall Performance (O.P.)For overall performance,award the panel the lowest percent rating of the three precedingvalues.9.4 NormalizationThe rating system described above isbased on a minimum test on one side a

39、rea of 465 cm2(72 in.2).Correct the percent ratings for test surfaces of nonstandarddimensions for the difference between the minimum standardpanel area of 72 in.2(465 cm2) and the area on one side of thetest specimen.10. Report10.1 Report the results of the immersion test in terms offouling resista

40、nce and overall performance for both the mate-rial under test and the standard system.10.2 Other DataReport the place, depth, and date ofimmersion, whether mounted from a dock or a floating raft,date the panels were removed and inspected, panel size, andpanel identification number. A census of fouli

41、ng on a nontoxicsurface taken each month for the period of exposure must beincluded in the report.11. Precision11.1 The precision statements are based on an interlabora-tory study in which seven laboratories prepared pairs of panelscoated with the standard antifouling system, submerged them,and afte

42、r 1 year rated the fouling. The within-laboratorystandard deviation was found to be 2.08. The between-laboratory standard deviation was found to be 4.67. Based onTABLE 1 Behavior Report of Experimental SurfacesOrigin: Place of Immersion:Series: Depth of Immersion:Base: Date Immersed:Size: Date Inspe

43、cted:Inspected by:Test Surface No.Fouling on SurfacesAPhysical ConditionPercent RatingsF.R. A.F. A.C. O.P.Barn:E.B.:Others:Barn:E.B.:Others:Barn:E.B.:Others:Barn:E.B.:Others:Barn:E.B.:Others:Barn:E.B.:Others:Barn:E.B.:Others:AFouling reported as found on the more heavily fouled surface. Solitary for

44、ms reported numerically; colonial forms by percent surface covered, Al: algae; Barn: barnacles;E.B.: encrusting bryozoans; Hyd: hydroids; Tun: tunicates; C.F.: completely fouled; CO: coelenterates; F.B.: filamentous bryozoans; Mol: molluscs; PC: polychaetes.D3623 78a (2012)3these standard deviations

45、, the following criteria should be usedto judge the acceptability of results at the 95 % confidencelevel:11.1.1 RepeatabilityTwo results each the mean of dupli-cates obtained by the same operator should be consideredsuspect if they differ by more than seven units.11.1.2 ReproducibilityTwo results ea

46、ch the mean of du-plicates obtained by operators in different laboratories shouldbe considered suspect if they differ by more than 16 units.12. Keywords12.1 antifouling; antifouling coatings; fouling; immersion;performance; staticANNEXES(Mandatory Information)A1. STANDARD COATING SYSTEM FORMULASTABL

47、E A1.1 Green Pretreatment Coating, MIL-P-15328D (Formula 117)Pounds per 100 galof Mixed MaterialGallons per 100 galof Mixed MaterialIngredients of resin component (80 gal):Polyvinyl-butyral resinA56 6.10Zinc chromate (insoluble type)B54 1.78Magnesium-silicate (Type A or B of Specification MIL-M-1517

48、3) 8 0.34Lampblack (Specification TT-L-70) 0.6 0.04Butyl alcohol, normal (Spec. TT-B-846) 125 18.48Isopropyl alcohol, 99 %C353 53.80Water 15 1.80Ingredients of acid component (20 gal):Phosphoric acid (Class A of Spec. O-P-313) 28 2.0Water 25 3.0Isopropyl alcohol, 99 %C99 15.0AThe resin shall be a po

49、lyvinyl partial butyral resin containing only poly(vinyl butyral), poly(vinyl alcohol), and poly(vinyl acetate) in the molecule. The resin shall contain18.0 to 20.0 % vinyl alcohol, and not more than 1.0 % of vinyl acetate. A 6 % solution of the resin in methanol shall have a viscosity of 12 to 18 cP at 20C. The specificgravity of the resin shall be 1.05 to 1.15.BThe zinc chromate shall be of an insoluble type, showing an analysis of 16 to 19 % CrO3, and 67 to 72 % ZnO, and not more than 1 % water-soluble salts.CIsopropyl alcohol, 99 % shall h