ASTM D2860 D2860M-2004(2010) Standard Test Method for Adhesion of Pressure-Sensitive Tape to Fiberboard at 90&176 Angle and Constant Stress《在90角度和恒定应力下纤维板上压敏胶纸带粘合性的标准试验方法》.pdf

《ASTM D2860 D2860M-2004(2010) Standard Test Method for Adhesion of Pressure-Sensitive Tape to Fiberboard at 90&176 Angle and Constant Stress《在90角度和恒定应力下纤维板上压敏胶纸带粘合性的标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM D2860 D2860M-2004(2010) Standard Test Method for Adhesion of Pressure-Sensitive Tape to Fiberboard at 90&176 Angle and Constant Stress《在90角度和恒定应力下纤维板上压敏胶纸带粘合性的标准试验方法》.pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D2860/D2860M 04 (Reapproved 2010)Standard Test Method forAdhesion of Pressure-Sensitive Tape to Fiberboard at 90Angle and Constant Stress1This standard is issued under the fixed designation D2860/D2860M; the number immediately following the designation indicates theyear of original adop

2、tion or, in the case of revision, the year of last revision. A number in parentheses indicates the year of lastreapproval. A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1.

3、Scope1.1 This test method covers the determination of the prop-erty of adhesion of pressure-sensitive tape to a fiber-boardsurface. The user of this test method has the option of choosingthe paper surface for the test. The test surface may be thestandard linerboard, another linerboard (or paper) of

4、individualinterest, or a specific fiberboard.1.2 The values stated in either SI or inch-pound units are tobe regarded separately as standard. The values stated in eachsystem are not exact equivalents; therefore, each system mustbe used independently, without combining values in any way.1.3 This stan

5、dard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 A

6、STM Standards:2D996 Terminology of Packaging and Distribution Environ-mentsD2904 Practice for Interlaboratory Testing of a Textile TestMethod that Produces Normally Distributed DataD2906 Practice for Statements on Precision and Bias forTextiles3D4332 Practice for Conditioning Containers, Packages, o

7、rPackaging Components for Testing3. Terminology3.1 Definitions: Terminology found in Terminology D996shall apply.4. Summary of Test Method4.1 Procedure AThe pressure-sensitive tape is mountedon a rigid panel. The adhesive side is exposed. A strip oflinerboard, which represents the fiberboard, is pla

8、ced againstthe tape adhesive with controlled pressure. The area of contactis specified. The panel is mounted in a horizontal position. Aspecified mass is fastened to one end of the linerboard. Themass acts to peel the linerboard away from the adhesive at anangle of 90. The time required to peel the

9、linerboard from thetape is measured.4.2 Procedure BIn this procedure, the fiberboard or thelinerboard representing it is adhered to a rigid panel and thetape peeled from it. In all other respects, the procedure is thesame as Procedure A.5. Significance and Use5.1 This test method is designed to show

10、 the adhesion of apressure-sensitive tape to fiberboard when the tape is under aconstant stress. Test data from this test method for some typesof packaging tape relates to tape performance on fiberboardbox closure.5.2 ProcedureAshould be used when comparing tapes to anestablished requirement. The re

11、quirement may be establishedusing either the standard linerboard or another linerboardrepresenting a specific fiberboard.5.3 Procedure B should be used to rank tapes as to theirability to adhere to fiberboard.6. Apparatus and Materials6.1 Tape, pressure-sensitive, double-coated, 48-mm 2-in.width. Th

12、e tape shall exhibit sufficient adhesion to the paneland test specimen or fiberboard to avoid the failures cited in10.1.9 and 10.2.14.6.2 PanelAny steel piece at least 50 by 125 mm 2 by 5in. and no less than 1.1 mm 0.043 in. thick, having one face(2 by 5 in.) that does not deviate from a plane by mo

13、re than0.050 mm 0.002 in.6.3 Stop Watch.6.4 Razor Blade, single-edge.6.5 MaskAny paper no more than 0.050 mm 0.002 in.thick formed to a rectangle approximately 125 by 60 mm 5 by2.5 in. with a rectangular hole exactly 24 6 0.25 1.0 6 0.011This test method is under the jurisdiction of ASTM Committee D

14、10 onPackaging and is the direct responsibility of Subcommittee D10.14 on Tape andLabels.Current edition approved April 1, 2010. Published May 2010. Originallyapproved in 1970. Last previous edition approved in 2004 as D2860/D2860M 04.DOI: 10.1520/D2860_D2860M-04R10.2For referenced ASTM standards, v

15、isit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Withdrawn. The last approved version of this historical standard is referencedon www.astm.org

16、.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.by 32 mm 1.25 in. centered in the piece. The 24-mm 1-in.hole dimension shall be in the 125-mm 5-in. direction (seeFig. 1 and Fig. 2).6.6 Cutter, for preparing fiberboard or linerboard

17、and tapespecimens.6.7 Paperboard Piece, approximately 25 by 25 mm 1 by 1in., for reinforcement.6.8 Paper Punch, single-hole.6.9 Fiberboard or Linerboard Surface,4against which thetest is made.6.9.1 For Procedure A, cut a rectangle exactly 24 6 0.25mm 1.0 6 0.01 in. wide by at least 125 mm 5 in. in l

18、ength,from the linerboard representing the fiberboard on which thetape will be used. The long dimension shall lie at a right angleto the machine direction of the linerboard. Reinforce one endof the strip with a chipboard piece adhered with double-coatedtape. Punch a hole at the center of the reinfor

19、cement.6.9.2 For Procedure B, cut a rectangle, preferably 125 by 50mm 5 by 2 in., but no less than 50 by 50 mm 2 by 2 in., fromthe fiberboard on which the tape will be used (or linerboardrepresenting it). The long test dimension shall lie at a rightangle to the machine direction of the linerboard.6.

20、9.3 For either procedure, prepare the linerboard or fiber-board in advance of testing and mark it to show which side touse. When comparing one roll of tape to another or one lot oftape to another, the linerboard or fiberboard should be from asingle lot.6.10 Steel Roller, 82.5 6 2.5 mm 3.25 6 0.1 in.

21、 indiameter and 45 6 1.5 mm 1.75 6 0.05 in. in width, coveredwith rubber approximately 6 mm 0.25 in. in thickness havinga Shore A durometer hardness of 80 6 5. The surface shall bea true cylinder void of any convex or concave deviations. Themass of the roller shall be 2040 6 45 g 4.5 6 0.1 lb. Thema

22、ss of the handle shall not add to the mass of the roller duringuse.NOTE 1A simple check to determine if the rubber surface is cylindri-cal is to wrap the roller in a very thin paper (onionskin) and drag it acrossa flat glass plate on which is placed a carbon paper, face up. The carbonrubs off onto t

23、he thin paper wrapper to reveal high spots or hollows on therubber surface.6.11 Test Stand, to support the panel securely in a horizontalplane during the test period.6.12 Mass, 200 6 0.2 g, with a hook.6.13 Timing System, for measuring test time in minutes.6.14 Paper, clean, unprinted, and without a

24、 coating of anykind, for use in adhering linerboard or fiberboard to the panel(Procedure B).7. Sampling7.1 Sampling shall be in accordance with Practice D4332.8. Test Specimens8.1 A roll or rolls of tape for testing must be at least 36 mm1.5 in. in width.8.2 Unwind and discard at least three, but no

25、 more than six,outer wraps from the sample roll before taking specimens fortesting.8.3 Test five specimens from each roll of tape.9. Conditioning9.1 Condition sample rolls of tape and linerboard or fiber-board in the standard conditioning atmosphere as described inPractice D4332 for a period of not

26、less than 24 h. Test at theseconditions.10. Procedure10.1 Procedure A:4The linerboard accepted as the standard test surface, Standard ReferenceMaterial 1810A, is available form the Office of Standard Reference Materials,National Institute of Standards and Technology, Washington, DC 20234.NOTE 1Fix p

27、anel securely in a horizontal plane.FIG. 1 Test Assembly for Procedure AD2860/D2860M 04 (2010)210.1.1 Adhere the double-coated tape to the firm fingerpressure and remove the liner.10.1.2 Lightly sand the backing of the test tape on the rollfor approximately 250 mm 10 in. with 300-grit sandpaper tore

28、move the easy unwind treatment. Start timing with the stopwatch. Immediately unwind 300 to 450 mm 12 to 18 in. oftape from a freely rotating roll at a rate of 500 to 750 mm 20to 30 in./s.10.1.3 Center the sanded area of this strip, adhesive side up,on the panel, aligning the long edges parallel with

29、 the panellong edges. Trim it to the panel dimensions. Do not allow anyobject to contact the adhesive.10.1.4 Place a mask at the center of the specimen so that the24-mm 1-in. dimension of the hole in the mask lies parallel tothe long dimension of the specimen edges (see Fig. 1). Rubagainst the mask

30、to assure that the tape specimen is welladhered to the double-coated tape on the panel. Avoid touchingthe adhesive.10.1.5 At 90 6 5 s, position the linerboard strip (endopposite the hole) to span the mask and enter it lengthwise onthe specimen adhesive. Ensure that the correct side of thelinerboard

31、is placed against the specimen adhesive. Do notapply any finger pressure to the specimen. Continue timing.10.1.6 Roll the linerboard against the specimen lengthwisetwice each way at a rate of 10 6 0.5 mm/s 24 6 0.5 in./minusing the rubber-covered roller.10.1.7 Immediately set the panel, specimen sid

32、e down, intothe test stand, assuring that it will remain in a horizontal planethroughout the test.10.1.8 At 180 6 5 s (3 min from unwinding the tape fromthe roll), add the 200-g mass so that no shock load is impartedto the linerboard, and immediately start the time.Allow the testto continue until th

33、e linerboard has peeled free from thespecimen adhesive.10.1.9 Void all tests where the tape (test specimen) haspulled away from the panel (either the specimen from thedouble-coated tape or the double-coated tape from the panel).When this occurs, repeat the test assuring that the panel, thedouble-coa

34、ted tape, and the test specimen are well bondedtogether.10.2 Procedure B:10.2.1 Adhere the double-coated tape to the panel with firmfinger pressure and remove the liner.10.2.2 Superimpose the fiberboard (or linerboard) on thedouble-coated tape, exposing the correct side and assuring thatthe machine

35、direction is at a right angle to the long dimensionof the panel. Handle the fiberboard only at the edges andcorners so that an area at least 35 mm 1.5 in. square at itscenter is absolutely free of contamination.10.2.3 Place a clean sheet of paper (6.14) on top of thefiberboard. Rub against this to a

36、ssure that the fiberboard is wellbonded to the double-coated tape on the panel. Do not rub thefiberboard surface with the paper or fingers.10.2.4 Start timing with the stop watch. Immediately un-wind 300 to 450 mm 12 to 18 in. of tape from a freely,rotating roll at a rate of 500 to 750 mm 20 to 30 i

37、n./s.10.2.5 From the center of this strip, cut a specimen 24 60.25 mm 1.0 6 0.01 in. wide and at least 180 mm 7 in. inlength. Handle this strip by its ends only. Do not allowadhesive to contact any object.10.2.6 Lay the specimen, adhesive side up, on the work bench and tape the ends down to hold the

38、 specimen flat.10.2.7 Apply a mask at one end of the specimen so that the24-mm 1-in. dimension of the hole lies parallel to the longedges of the specimen (see Fig. 2).10.2.8 Apply the chipboard square to the exposed adhesiveat the other end of the specimen (see Fig. 2).10.2.9 Cut away the taped ends

39、 of the specimen. Punch ahole for the hook of the mass in the chipboard.10.2.10 At 90 6 5 s, position the specimen lengthwise onthe fiberboard, adhesive down, so that the 1 by 1-in. 24 by24-mm adhesive area is approximately centered on the fiber-board. Do not apply any finger pressure to the specime

40、n.Continue timing.10.2.11 Roll the specimen lengthwise twice each way at arate of 10.0 6 0.2 mm/s 24 6 0.5 in./min, using therubber-covered roller.10.2.12 Immediately set the panel, specimen side down,into the test stand, assuring that it will remain in a horizontalplane throughout the test.10.2.13

41、At 180 6 5 s (a total of 3 min from unwinding thetape from the roll), add the 200-g mass so that no shock loadis imparted to the specimen and start the timer. Allow the testto continue until the specimen has peeled free from thefiberboard (see Fig. 3).10.2.14 Void all tests where the fiberboard has

42、pulled awayfrom the panel (either the fiberboard from the double-coatedtape or the double-coated tape from the panel). When thisoccurs, repeat the test, assuring that the panel, double-coatedtape, and the fiberboard are well bonded together.FIG. 2 Preparation of Specimen for Procedure BD2860/D2860M

43、04 (2010)311. Calculation11.1 To determine the test result for each roll of tape,convert each of the five specimen test results to its logarithm.Obtain the arithmetic mean of all logarithms and then convertthe arithmetic mean logarithm back to time by obtaining itsantilogarithm. This final step give

44、s the test result for the roll oftape under consideration. No single specimen value shall beconsidered as representative of the roll under test.12. Report12.1 The report shall include the following:12.1.1 Astatement that this test method was used, indicatingwhich procedure (A or B), and any deviatio

45、ns from the methodas written,12.1.2 Complete identification of each roll of tape testedincluding type, source, manufacturers code number, and form,12.1.3 Linerboard or fiberboard identification including thetype, source, manufacturers code number, and conditioninghistory prior to the test,12.1.4 Num

46、ber of specimens tested from each roll of tape,12.1.5 Anomalous behavior during the test, that is, adhesivetransfer or splitting paper fiber pulled free from the linerboardor fiberboard, delamination of the linerboard or fiberboard, and12.1.6 Mean time value calculated in 11.1 for each of therolls o

47、f tape under test.13. Precision and Bias13.1 SummaryThe difference between two single obser-vations should not exceed 27.7 % of the average of the twoobservations in transformed units in 95 out of 100 cases whenboth observations are taken by the same well-trained operatorusing the same piece of test

48、 equipment and specimens ran-domly drawn from the same sample of material. Largerdifferences may occur under all other circumstances. The truevalue of adhesion to fiberboard at 90 angle under constantstress can only be defined in terms of a specific test method.Within this limitation, Test Method D2

49、860/D2860M has noknown bias. Sections 13.2 through 13.5 explain the basis forthis summary and for evaluations made under other conditions.The information applies either to comparisons of specimens ofthe same material or to specimens of different materials.NOTE 2This precision statement applies only to Procedure A.13.2 Interlaboratory Test Data5An interlaboratory studywas made in 1980 in which randomly drawn samples of twomaterials were tested in each of four laboratories. Two opera-tors in each labora