ASTM D2559-2010 Standard Specification for Adhesives for Structural Laminated Wood Products for Use Under Exterior (Wet Use) Exposure Conditions《室外潮湿条件下用结构层压木材制品用胶粘剂标准规范》.pdf

《ASTM D2559-2010 Standard Specification for Adhesives for Structural Laminated Wood Products for Use Under Exterior (Wet Use) Exposure Conditions《室外潮湿条件下用结构层压木材制品用胶粘剂标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM D2559-2010 Standard Specification for Adhesives for Structural Laminated Wood Products for Use Under Exterior (Wet Use) Exposure Conditions《室外潮湿条件下用结构层压木材制品用胶粘剂标准规范》.pdf（17页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D2559 10Standard Specification forAdhesives for Structural Laminated Wood Products for UseUnder Exterior (Wet Use) Exposure Conditions1This standard is issued under the fixed designation D2559; the number immediately following the designation indicates the year oforiginal adoption or, i

2、n the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.INTRODUCTIONT

3、his specification, which was initially approved in 1966, was developed to ensure that adhesivesdeveloped and used in structural glued laminated timber (glulam) are considered suitable for theintended application. This would include, as a maximum level of severity in the case of moistureeffects, full

4、 and continuous exposure to the weather in a salt water marine environment.The use of adhesives for structural wood products (that is, Engineered Wood Products) hasexpanded beyond Glulam to include products such as Structural Composite Lumber, wood I-Joists andvarious composites adhesively bonded us

5、ing a variety of materials. Although most structural gluedwood products have traditionally specified an adhesive suitable for exterior exposure, the actualexposure of glued wood products to exterior conditions may range from exposure to the weather forbrief periods of time, to continuous exposure to

6、 a marine environment. The wide range of possibleexterior exposures of the adhesively bonded structural wood product requires consideration ofdiffering performance requirements for the adhesive.A distinction between adhesive certification and product performance requirements is necessary toensure th

7、e broadest possible acceptance of adhesive systems to the engineered wood products industry.The suitability of adhesive systems for use in the manufacture of engineered wood products forexterior applications is dependent on both the adhesive certification test requirements specified inSpecification

8、D2559, and performance requirements provided in specific product standards.1. Scope1.1 This specification covers adhesives suitable for thebonding of wood, including treated wood, into structurallaminated wood products for general construction, for marineuse, or for other uses where a high-strength,

9、 waterproofadhesive bond is required.1.2 The requirements of the adhesive are based on theperformance of the adhesive in laminated wood as measuredby:1.2.1 Resistance to shear by compression loading,1.2.2 Resistance to delamination during accelerated expo-sure to wetting and drying, and1.2.3 Resista

10、nce to deformation under static load.1.3 The values stated in SI units are to be regarded as thestandard. The values in parentheses are for information only.1.4 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user o

11、f this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2D9 Terminology Relating to Wood and Wood-Based Prod-uctsD143 Test Methods for Small Clear Specimens of TimberD905 T

12、est Method for Strength Properties of AdhesiveBonds in Shear by Compression LoadingD907 Terminology of AdhesivesD1165 Nomenclature of Commercial Hardwoods and Soft-woods1This specification is under the jurisdiction of ASTM Committee D14 onAdhesives and is the direct responsibility of Subcommittee D1

13、4.30 on WoodAdhesives.Current edition approved May 1, 2010. Published August 2010. Originallyapproved in 1966. Last previous edition approved in 2009 as D2559 09. DOI:10.1520/D2559-10.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm

14、.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.D1583 Test Method for Hydrogen Ion Concentration of DryAdhesiv

15、e FilmsD2555 Practice for Establishing Clear Wood Strength Val-uesD3434 Test Method for Multiple-Cycle Accelerated AgingTest (Automatic Boil Test) for Exterior Wet Use WoodAdhesivesD3535 Test Method for Resistance to Creep Under StaticLoading for Structural Wood Laminating Adhesives UsedUnder Exteri

16、or Exposure ConditionsD4442 Test Methods for Direct Moisture Content Measure-ment of Wood and Wood-Base MaterialsD4300 Test Methods for Ability of Adhesive Films toSupport or Resist the Growth of FungiD5055 Specification for Establishing and Monitoring Struc-tural Capacities of Prefabricated Wood I-

17、JoistsD5266 Practice for Estimating the Percentage of WoodFailure in Adhesive Bonded JointsD5456 Specification for Evaluation of Structural CompositeLumber ProductsE6 Terminology Relating to Methods of Mechanical TestingE41 Terminology Relating To ConditioningE691 Practice for Conducting an Interlab

18、oratory Study toDetermine the Precision of a Test Method3. Terminology3.1 DefinitionsMany terms in this specification are de-fined in Terminology D907.3.2 Definitions of Terms Specific to This Standard:3.2.1 delamination, nthe separation of layers in a lami-nate because of failure of the adhesive, e

19、ither in the adhesiveitself or at the interface between the adhesive and the adherend.3.2.2 glulam, nsynonym for structural-glued-laminatedtimber.NOTE 1The following ASTM standards may be referred to for otherterms used in this specification: Nomenclature D1165, Terminologies D9,E6, and E41.3.2.3 la

20、minated wood product, na fabricated wood assem-bly resulting from the bonding together of two or morelaminations, all with the direction of grain essentially parallel,to form a larger piece such as a structural member.3.2.3.1 DiscussionThe individual laminations themselvesmay be made up of two or mo

21、re pieces both in width andlength.3.2.4 structural-glued-laminated timber, nan engineeredstress-rated product of a timber laminating plant comprisingassemblies of specially selected and prepared wood lamina-tions securely bonded together with adhesives, with the fol-lowing characteristics: (1) the g

22、rain of all laminations isapproximately parallel longitudinally; and (2) the laminationsmay be comprised of pieces end-joined to form any length, ofpieces placed or glued edge-to-edge to make wider ones or ofpieces bent to curved form during gluing. (Synonym: glulam)ANSI/AITC A190.11992. American Na

23、tional Standard forWood ProductsStructural Glued Laminated Timber (edited toconform with ASTM format).4. Significance and Use4.1 Structural design based on strength of material prin-ciples of the structural components, including the adhesive andthe adhesives potential durability, requires that the s

24、uitabilityfor structural wet use exposure be predicted.4.2 Performance of the adhesive for resistance to shear bycompression loading, resistance to delamination during accel-erated aging exposure to wetting and drying, and resistance todeformation under load data developed by this test aid indetermi

25、ning if the adhesive is suitable for structural wet use.5. Classification5.1 The manufacturer shall classify the adhesive as togeneral type. Typical classifications include: resorcinol,phenol-resorcinol, phenol, melamine, etc.5.2 The manufacturer may be considered to be the testingfacility certifyin

26、g the adhesive.6. Ordering Information6.1 The manufacturer will furnish the adhesive in anysuitable form agreeable to the purchaser.7. Fillers and Extenders7.1 If amylaceous or protein fillers and extenders are used,the adhesive must not only pass requirements of this specifi-cation, but in addition

27、, possess sufficient antifungal propertiesto inhibit the growth of selected fungal species when tested inaccordance with Test Method D4300. The adhesive manufac-turer shall state in his bulletin whether such materials arepresent.8. Chemical Requirements8.1 The cured adhesive film shall develop a pH

28、value of notless than 2.5 when tested in accordance with Test MethodD1583.9. Physical Requirements9.1 The adhesive manufacturer shall furnish written instruc-tions stating the general chemical type of adhesive, its storageand mixing procedure, the method of wood preparation, andany other data which

29、is pertinent to the use of the adhesive inthe manufacture of laminated wood products.9.2 The adhesive must pass the tests required by thisspecification for all limiting conditions recommended in themanufacturers bulletin. The information furnished by themanufacturer should include each of the follow

30、ing for eachspecies of wood included in his recommendations:9.2.1 Limits of working life,9.2.2 Minimum and maximum open and closed assemblytimes as dictated by temperature, moisture content of the wood,mix age, etc.,9.2.3 Minimum spread rates for assembly times and useconditions as indicated in 9.2.

31、2,9.2.4 Minimum cure time and temperature of bondline forcomplete cure,9.2.5 Minimum pressure, and9.2.6 Maximum and minimum allowable moisture contentof the wood.D2559 10210. Selection and Preparation of Wood for Testing ofAdhesives10.1 Test the adhesive on the species of wood to be bondedor for whi

32、ch it is recommended including chemically treatedwood (see Note 2). The wood shall have a maximum slope ofgrain of 1 in 15 on any face or any edge. The wood shallcontain no knots larger than 3 mm (18 in.) in diameter and shallbe free from decay, machining defects (such as chipped grain,dubbed ends,

33、feed roll polish, coarse knife marks, and feed rollcompression), and any drying defects such as case hardening,collapse, splits, or checks. Use only flat-grained wood.NOTE 2Grouping of species is not permitted.10.2 Wood Moisture Content:10.2.1 Ambient Curing AdhesivesCondition the wood at23 6 2C (73

34、.4 6 3.6F) and a relative humidity of 50 to 70 %(preferably 65 %) until a moisture content of 8 to 14 % or,preferably 9 to 12 %, has been attained.10.2.2 Hot Press Curing AdhesivesCondition the wood at23 6 2C (73.4 6 3.6F) and a relative humidity of less than50 % until a moisture content of 3 to 8 %

35、 has been attained.10.3 Freshly surface each lamination before bonding withthe adhesive to be tested. Remove at least 0.4 mm (164 in.)from each face within 24 h of bonding. The machiningtolerances for each lamination used in preparing the testsamples shall be no greater than 60.25 mm (0.01 in.) betw

36、eenlaminations and 60.20 mm (0.008 in.) within laminations.11. Preparation of Laminated Wood Test Members11.1 Ambient-Curing Adhesives:11.1.1 Prepare six pieces of wood of the same species foreach laminated wood member. Each of the six pieces shall havea specific gravity equal to or exceeding the mi

37、nimum require-ment of Table 1. Each piece of wood shall be 19-mm (0.75-in.)thick lumber (see Note 3) at least 140 mm (512 in.) in widthand 1 m (40 in.) long. Orient the direction of the annulargrowth rings when viewed on the end of the laminations in thelaminated wood test member so that they are al

38、ternated.NOTE 3This thickness would normally come from “nominal 1-in.lumber.”11.1.1.1 As an alternative to the preparation of laminatedwood test members 1 m (40 in.) in length, prepare duplicate610-mm (24-in.) laminated wood members to obtain at least anequivalent number of test specimens. This alte

39、rnative includesthe preparation of separate two-ply assemblies for evaluationusing Test Method D905 block shear specimens that may beused as an alternate to stair-step specimens.11.1.2 Apply the adhesive uniformly to the contacting facesof each lamination in accordance with the manufacturersinstruct

40、ions.11.1.3 Place the laminated wood members under pressurefor a period of time and at the bondline temperature specifiedby the manufacturer of the adhesive.11.1.4 ConditioningCondition the laminated wood mem-bers at 23 6 2C (73.4 6 3.6F) and a relative humidity of 50to 70 % (preferably 65 %) for th

41、e minimum time recommendedby the manufacturer for each curing temperature used duringthe pressure period, and test immediately.11.2 Hot-Press Curing Adhesives:11.2.1 Prepare six pieces of wood of the same species foreach laminated test member. Each of the six pieces shall havea specific gravity equa

42、l to or exceeding the minimum require-ment of Table 1. Each piece of wood shall be 19 mm (0.75 in.)thick lumber (see Note 4) at least 140 mm (512 in.) in widthand 1 m (40 in.) long as allowed in 11.1.1.1. Orient theTABLE 1 Required Shear Strength for Structural Laminated Wood ProductsNOTE 1For speci

43、es other than those given, strength values shall be based on 90 % of the value for shear parallel to grain at 12 % moisture content.The use of 90 % of shear parallel to grain at 12 % moisture content takes into account the various subspecies of a particular wood species. The valuesfor shear parallel

44、 to grain may be found in Tables 4-3a through 44b of the Wood Handbook, Forest Products Society (1999 edition). Base the minimumallowable specific gravity on volume for wood at 12 % moisture content. For species not listed see Note 3. Adjustments for changes in moisture contentshall be made in accor

45、dance with formula 43 (page 434) found in the 1999 Wood Handbook.NOTE 2It has been documented that bonded shear specimens (Test Method D905 type specimen) on the average provide higher shear strength valuesthan solid wood specimens (Test Methods D143 type specimen). It may appear to be inconsistent

46、to compare shear strength data of bonded specimensto data based on 90 % of the solid wood shear strength found in the Wood Handbook. However, the goal of evaluating shear strength of adhesives inSpecification D2559 is to demonstrate the shear strength in a laminated product (tested using Test Method

47、 D905 type specimens) meets or exceeds thestrength of a solid wood beam when tested by standard procedures for solid wood (Test Methods D143 type specimen).NOTE 3For species not found in the 1999 Wood Handbook, values for shear parallel to grain at 12 % moisture content using solid wood are to beobt

48、ained on clear, straight-grained specimens following specific ASTM test methods and procedures. These include Test Methods D143 and D2555. TestMethods D143 testing is to be performed on a minimum of 28 shear strength specimens.SpeciesRequired Shear Strength, KPa (psi)AMinimum Allowable SpecificGravi

49、ty of Solid Wood Usedfor Each LaminationBMoisture Content of Wood at Test8% 12% 16%Douglas fir 7 600 (1 110) 7 000 (1 020) 6 500 (940) 0.43Hemlock, western 8 900 (1 290) 8 000 (1 160) 7 200 (1 050) 0.41Larch, western 9 400 (1 370) 8 400 (1 220) 7 600 (1 100) 0.55Oak, white 14 300 (2 080) 12 400 (1 800) 11 000 (1 560) 0.68Pine, southern 10 400 (1 510) 8 600 (1 250) 7 100 (1 040) 0.51Redwood 6 300 (910) 5 800 (850) 5 400 (790) 0.40ABased on 90 % of the shear strength parallel to grain at 12 % moisture content from Table 43 of the 1999 Wood Handbook. U