ASTM D865-2011(2018) Standard Test Method for Rubber&x2014 Deterioration by Heating in Air (Test Tube Enclosure).pdf
《ASTM D865-2011(2018) Standard Test Method for Rubber&x2014 Deterioration by Heating in Air (Test Tube Enclosure).pdf》由会员分享,可在线阅读,更多相关《ASTM D865-2011(2018) Standard Test Method for Rubber&x2014 Deterioration by Heating in Air (Test Tube Enclosure).pdf(5页珍藏版)》请在麦多课文档分享上搜索。
1、Designation: D865 11 (Reapproved 2018)Standard Test Method forRubberDeterioration by Heating in Air (Test TubeEnclosure)1This standard is issued under the fixed designation D865; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the
2、year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope1.1 This test method covers
3、a procedure to determine thedeterioration induced by heating rubber specimens in indi-vidual test tube enclosures with circulating air. This isolationprevents cross contamination of compounds due to loss ofvolatile materials (for example, antioxidants) and their subse-quent migration into other rubb
4、er compounds (specimens). Theabsorption of such volatile materials may influence the degra-dation rate of rubber compounds.1.2 The values stated in SI units are to be regarded as thestandard. The values given in parentheses are for informationonly.1.3 This standard does not purport to address all of
5、 thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety, health, and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.4 This international standard was developed in ac
6、cor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade (TBT) Committee.2. Referenced Documents2.1 A
7、STM Standards:2D412 Test Methods for Vulcanized Rubber and Thermoplas-tic ElastomersTensionD573 Test Method for RubberDeterioration in an AirOvenD1349 Practice for RubberStandard Conditions for Test-ingD2240 Test Method for Rubber PropertyDurometer Hard-nessD3182 Practice for RubberMaterials, Equipm
8、ent, and Pro-cedures for Mixing Standard Compounds and PreparingStandard Vulcanized SheetsD3183 Practice for RubberPreparation of Pieces for TestPurposes from ProductsD4483 Practice for Evaluating Precision for Test MethodStandards in the Rubber and Carbon Black ManufacturingIndustries3. Summary of
9、Test Methods3.1 Specimens of vulcanized rubber are exposed to thedeteriorating influence of air at specified elevated temperaturefor known periods of time, after which their physical propertiesare determined. These are compared with the properties deter-mined on the original unexposed specimens and
10、the changesnoted.3.2 Unless otherwise specified, the determination of thephysical properties shall be carried out in accordance with testmethods in Test Methods D412.3.3 Except as may be otherwise specified in this testmethod, the requirements of Practices D3182 and D3183 shallbe complied with and a
11、re made part of this test method.3.4 In case of conflict between the provisions of this testmethod and those of detailed specifications or test methods fora particular material, the latter shall take precedence or ifotherwise agreed upon between customer and supplier orbetween laboratories.4. Signif
12、icance and Use4.1 Rubber and rubber products must resist the deteriorationof physical properties with time caused by oxidative andthermal ageing. This test method determines these character-istics in a way that is free of some of the complications inherentin community-type ageing devices, that is wh
13、ere numerouscompounds (specimens) are aged in the same enclosure.1This test method is under the jurisdiction of ASTM Committee D11 on Rubberand Rubber-like Materials and is the direct responsibility of Subcommittee D11.15on Degradation Tests.Current edition approved July 1, 2018. Published August 20
14、18. Originallyapproved in 1946. Last previous edition approved in 2011 as D865 11. DOI:10.1520/D0865-11R18.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the stand
15、ards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Deci
16、sion on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.14.2 The isolation of compounds (specimens) by the use ofindividual circulating air test tube enclosures prevents crossconta
17、mination from volatile products and permits a morerepresentative assessment of ageing performance.4.3 Please refer to the Annex in Test Method D573 forimportant information on standard compounds used for preci-sion testing for accelerated test ageing evaluation.5. Apparatus5.1 The apparatus for heat
18、 ageing shall consist of borosili-cate glass test tubes 38 mm (1.52 in.) in diameter and 300 mm(12 in.) in length heated uniformly in suitable equipment suchas an oil or water bath or metal block (see Fig. 1) so arrangedas to comply with the following requirements:5.1.1 No more than three specimens
19、shall be exposed ineach test tube, and all specimens in a single tube shall be froma single compound.5.1.2 Provisions shall be made for vertical suspension of thespecimens as near the bottom of the test tube as possiblewithout touching each other or the sides of the test tube duringthe test.Asuggest
20、ed means for holding the specimens is shownin Fig. 2.5.1.3 The test tubes shall be provided with a tight-fittingcork or nonreactive composition stopper through which an inletand an outlet tube shall be placed as shown in Fig. 2.5.1.4 The heating equipment shall be provided with athermostatic control
21、 that will maintain the temperature at thelocation of the specimens in the test tube within 61C(61.8F) of the prescribed temperature. If a liquid medium isused, suitable stirring or circulation shall be provided to assureuniformity of temperature.5.1.5 The temperature should be automatically recorde
22、dover the entire test period using a temperature-measuringdevice capable of measuring at the specified temperaturewithin 61C (61.8F). Apparatus that is not equipped withautomatic recording capabilities, the temperature shall bemeasured with sufficient frequency to assure compliance withthe temperatu
23、re limits specified in 10.1.5.1.6 Prior to commencing a test, or series of tests, a checkof the actual temperature within the test tube shall be made byplacing a thermometer in the tube with the bulb in the locationordinarily occupied by the specimens. Alternatively, a digitaltemperature measuring d
24、evice may be used in place of aliquid-in-glass thermometer, wherein the probe is placed in aposition ordinarily occupied by the specimens. The thermom-eter or probe shall be inserted through either the tubes orthrough a third hole in the stopper which shall be securelyclosed during the test.5.1.7 Th
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ASTMD86520112018STANDARDTESTMETHODFORRUBBERX2014DETERIORATIONBYHEATINGINAIRTESTTUBEENCLOSUREPDF
链接地址:http://www.mydoc123.com/p-512352.html