ASTM D713-2012(2017) Standard Practice for Conducting Road Service Tests on Fluid Traffic Marking Materials《路标漆进行路面使用的标准实施规程》.pdf

《ASTM D713-2012(2017) Standard Practice for Conducting Road Service Tests on Fluid Traffic Marking Materials《路标漆进行路面使用的标准实施规程》.pdf》由会员分享，可在线阅读，更多相关《ASTM D713-2012(2017) Standard Practice for Conducting Road Service Tests on Fluid Traffic Marking Materials《路标漆进行路面使用的标准实施规程》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D713 12 (Reapproved 2017)Standard Practice forConducting Road Service Tests on Fluid Traffic MarkingMaterials1This standard is issued under the fixed designation D713; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, th

2、e year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This practice covers the determination of the relativeservice life of fluid traffic marking materials such a

3、s paint,thermoplastic, epoxy, and polyester products under actual roadconditions using transverse test lines. Materials under test areapplied under prescribed conditions and periodic observationsare made using prescribed performance criteria.1.2 The values stated in SI units are to be regarded as th

4、estandard. The values given in parentheses are for informationonly.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety, health, and environmental practices and

5、deter-mine the applicability of regulatory limitations prior to use.1.4 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recom-me

6、ndations issued by the World Trade Organization TechnicalBarriers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:2D711 Test Method for No-Pick-Up Time of Traffic PaintD913 Practice for Evaluating Degree of Traffic MarkingLine WearD6628 Specification for Color of Pavement Marking

7、Mate-rialsE1710 Test Method for Measurement of RetroreflectivePavement Marking Materials with CEN-Prescribed Ge-ometry Using a Portable RetroreflectometerE2367 Test Method for Measurement of Nighttime Chroma-ticity of Pavement Marking Materials Using a PortableRetroreflection Colorimeter3. Significa

8、nce and Use3.1 This practice is an accelerated evaluation of beadretention, retroreflectivity, daytime color, night time color, andwear characteristics of fluid traffic marking materials. It is usedto determine the useful life of such markings in the field. Thesame procedures are applicable to evalu

9、ating longitudinal linesto determine service life.4. Type and Location of Pavement for Tests4.1 Select sections where traffic is moderate and free-rollingwith no grades, curves, intersections, or access points nearenough to cause excessive braking or turning movements,where wear is uniform with full

10、 exposure to the sun throughoutdaylight hours, and there is good drainage. Select surfaces thatare representative of the pavements upon which the fluid trafficmarking material will be used in practice. Such surfacesinclude portland cement concrete, sheet asphalt, bituminousconcrete, rock asphalt, an

11、d bituminous surface treatment.5. Conditions at Time of Application5.1 Clean the test area thoroughly of all foreign material.Follow the pavement marking manufacturers recommendationfor the application of the pavement marking to be tested. Thisshould include the recommendations for air and pavementt

12、emperature, material temperature, relative humidity, windchill, and wind speed. Application between 10 a.m. and 3 p.m.is recommended. During application record air and pavementtemperature, wind speed, and relative humidity hourly.6. Measurement of Wet Film Thickness6.1 To aid in obtaining the correc

13、t film thickness, a length ofroofing paper placed by the side of the road can be used. Placea rigid metal test panel on the roofing paper and in the path ofthe test line. A 300 by 300-mm (12 by 12-in.) metal panel 1.5mm (116 in.) in thickness is satisfactory. Immediately after thetest line is applie

14、d by the motorized striper, read the wet filmthickness. If the wet film thickness is not satisfactory, adjust thespray pressure and repeat until the target wet film thickness is1This practice is under the jurisdiction of ASTM Committee D01 on Paint andRelated Coatings, Materials, and Applications an

15、d is the direct responsibility ofSubcommittee D01.44 on Traffic Coatings.Current edition approved Dec. 1, 2017. Published December 2017. Originallyapproved in 1943. Last previous edition approved in 2012 as D713 12. DOI:10.1520/D0713-12R17.2For referenced ASTM standards, visit the ASTM website, www.

16、astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesThis int

17、ernational standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) C

18、ommittee.1attained. It is important that no glass beads or other interferingmaterials be present that would give a false wet film reading.When the wet film thickness is correct, apply a test line acrossa tared metal panel and weigh immediately. A balance must beimmediately available and be thoroughl

19、y shielded from windas well as be of 1500-g capacity with 0.1 g or better sensitivity.As a basis for determination of glass bead application (7.1) theweight of a paint line 100 by 300 mm (4 by 12 in.) (withoutconsideration for solvent loss) can be calculated as follows:W 5 0.0943 3 t 3 gwhere:W = we

20、ight of paint line, g,t = mil thickness, andg = weight per gallon, lb.6.2 Application of pavement markings by the spray processshall be by an appropriate spray applicator with traction driveand a spray nozzle similar to that used on normal markingequipment. The machine must be capable of setting and

21、maintaining a constant speed during the application process.Standard traffic paint shall be applied at a thickness of 15 mil(+ 1 mil).6.2.1 Application of other materials shall be accordancewith the manufacturers recommended procedures and assimilar as possible to that used on their normal markingeq

22、uipment. High build water bourne paints, epoxies, modifiedepoxies, polyurea, Methacrylate, and other exotic materialstested shall be applied at the rate recommended by themanufacturer with a 15 mil minimum. The minimum thicknessfor thermoplastic material tested shall be 30 mil. If thepavement markin

23、gs are applied by some other method thanspray, such as extrusion, it must be done with a piece ofequipment that will provide consistent material thicknessthroughout the test marking and be able to meet the manufac-turers requirements for the application of the pavementmarking.6.3 Test line for traff

24、ic paint and thermoplastic applied atless than 60 mil in thickness shall be 4 612 in. in width.Thermoplastic applied at more than 60 mil shall be 6 612 in.in width. For any other materials the applied width shall beaccording to the manufacturers recommendation.6.4 If the material is sprayable and ca

25、n be applied withtraction drive and a spray nozzle similar to that used on normalmarking equipment, thickness shall be checked by weight. Formaterials applied by any other means the thickness shall bechecked by instrument. Thickness will be determined by use ofa test panel and a micrometer or magnet

26、ic dry film thicknessgauge.7. Measurement of Glass Beads7.1 After the completion of 6.1, apply another test line to atared panel with the motorized striper, this time also adding theglass beads, and weigh immediately. The weight differencebetween this measurement and that in 6.1 gives the amount ofg

27、lass beads on the panel. Prior to weighing the panel, removeexcess glass beads which are not adhered to the pavementmarking from the panel to ensure an accurate representation ofthe bead rate. The process can be repeated if an adjustment inthe bead application rate is needed. The weight of applied g

28、lassbeads per gallon of pavement marking material can be calcu-lated as follows:W 5 1.418 3 B 3 T 15!where:W = weight of glass beads, g,B = glass beads per gallon of paint, lb., andT = thickness of paint being applied, mil.7.1.1 To calculate the bead rate in terms of weight per unitarea use the foll

29、owing calculation:Bead Rate lbs 100 ft2! 5 W A! * 100where:W = weight of glass beads, lb andA = area of pavement marking, ft2.7.2 Unless a manufacturer has requested to use a specialcoated bead, glass beads meeting requirements of AASHTOM247 for Type I Beads (identified at the time of application)wi

30、ll be applied to the pavement markings. The coating on thebeads shall be specified by the purchaser and shall be noted aspart of the test report. For standard traffic paint applied at 15wet mil the glass beads shall be applied at a rate of 6 poundsper gallon (6 lbs/100 ft2) and will be supplied by t

31、he testingagency. The testing agency will provide quality control testresults for the beads provided.7.3 Use of special beads or other retroreflective optics maybe applied at the manufacturers recommended application rateand method. If this is to be done the manufacturer shall providethe recommended

32、 application methodology, and applicationrate in the form of weight per unit area (such as lb/100 ft2) foreach bead or retroreflective optic that is to be used. Themanufacturer shall also provide the technical information forthe material being used to include such things as materialdescription, pert

33、inent specifications met, physical propertiessuch as size, roundness, chemical properties, and coatingcharacteristics. This information shall be available as part ofthe report.7.4 If the bead or reflective optic application can be con-trolled then the actual bead application rate shall be determined

34、and included as part of the report. If the rate cannot beconsistently controlled then the beads or reflective opticsshould be applied in such a manner to fully saturate (flood) themarking and this should be reflected in the report.8. Application Procedure8.1 Apply the test stripes at the required wi

35、dth and trans-versely on the road. At the option of the purchaser, the teststripes may be applied to the pavement at an angle of 45 to thedirection of the traffic, or longitudinally in each wheel path, inorder to increase the area of contact with traffic. If the markingsare to be applied in a longit

36、udinal pattern then the patternshould be discussed and agreed to prior to conducting the fieldtest.8.2 Apply test stripes (trained personnel under the supervi-sion of the purchaser) by using a pavement-marking machinesimilar to the production pavement marking equipment. ApplyD713 12 (2017)2the test

37、stripes to at least two sections of each road surfaceselected to ensure against undetected road surface problems.When more than one specimen is tested at more than onelocation, change the sequence of placement to minimize theeffect of time of day and time period before the test deck isopened to traf

38、fic.8.3 Apply at least two lines of each specimen in eachsection for better statistical reliability. A tared panel as used inthe measurement of glass beads (see 7.1) should be placedbetween the wheel track of one lines application as a doublecheck for material and glass bead application rates. Weigh

39、tsbetween this reading and that found in 7.1 should agree within0.5 g. The purchaser may wish to place another smaller panelbetween the wheel tracks to retain for future reference. Thethickness of samples shall be checked within the first three footsection of the test lines.8.4 For standard traffic

40、paint the road surface test linesshould have a wet film thickness within 61.0 mil of thatrequired by the purchaser.NOTE 1If no wet film thickness is specified, 15.0 mil is recom-mended.8.5 High build waterborne paints, epoxies, modifiedepoxies, polyurea, Methacrylate, and other exotic materialsteste

41、d shall be applied at the rate recommended by themanufacturer with a 15 mil minimum. The minimum milthickness for thermoplastic material tested shall be 30 mil. Ifthe pavement markings are applied by some other method thanspray, such as extrusion, it must be done with a piece ofequipment that will p

42、rovide consistent material thicknessthroughout the test marking and be able to meet the manufac-turers requirements for the application of the pavementmarking.8.6 A fluid marking material with which the purchaser hashad considerable production experience is recommended to beadded to the test series

43、as a control to gauge the relativeperformance for materials applied under the road service testconditions for a particular test series.8.7 For standard traffic paint that utilizes the standard glassbeads (AASHTO Type 1) for drop on application, the glassbeads are placed in the paint film within 60.5

44、 lb/gal of thatrequired by the purchaser. The standard glass beads aresupplied by the purchaser.NOTE 2If no bead application rate is specified, 6.0 lb/gal (6 lb/100 ft2)of paint that is applied at 15 mil is recommended.8.8 If special beads or other retroreflective optics are usedper the manufacturer

45、s recommendations the application shallbe made according to the manufacturers recommended appli-cation methodology, and application rate for each bead orretroreflective optic that is to be used. The application rate shallbe of each type of bead or other retroreflective optic shall beincluded in the

46、report.9. Performance Criteria9.1 Unless otherwise stated all evaluations shall be per-formed in one or both of the following areas; the center of theleft wheel path and in the skip line area. The evaluations willbe made at the eighteen (18) in. length of line centered on theleft wheel track area (w

47、heel track) and nine (9) in. from theskip line area (centerline). The centerline can further be locatedas the area to the left of the left wheel path in the last nine (9)in. of the line.9.2 Auto-No-Track TimeThe auto no-track time is deter-mined by passing over the freshly applied line in a simulate

48、dpassing maneuver with a standard size passenger car withregular treads (no snow treads). A line showing no visualpick-up and redeposition of the materials onto the pavementsurface when viewed from a distance of 15 m (50 ft) in thehighway direction is considered as showing no pick-up andconforming t

49、o the drying time requirements.9.2.1 The test line is applied at the same temperature, thesame wet film thickness, and the same rate of glass beads aswill be specified by the purchaser in production application.9.2.2 The no-track maximum time is measured when thepavement temperature is from 15 to 50C (60 to 120F) andunder local humidity conditions, providing that the pavement isdry.9.3 AppearanceThe impression of the observer of thegeneral condition of the test lines when viewed without anydetailed inspection, from a distance of at least 10 ft. It is ameas