ASTM D449 D449M-2003(2014)e1 Standard Specification for Asphalt Used in Dampproofing and Waterproofing《防潮和防水用沥青的标准规格》.pdf

《ASTM D449 D449M-2003(2014)e1 Standard Specification for Asphalt Used in Dampproofing and Waterproofing《防潮和防水用沥青的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM D449 D449M-2003(2014)e1 Standard Specification for Asphalt Used in Dampproofing and Waterproofing《防潮和防水用沥青的标准规格》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D449/D449M 03 (Reapproved 2014)1Standard Specification forAsphalt Used in Dampproofing and Waterproofing1This standard is issued under the fixed designation D449/D449M; the number immediately following the designation indicates the yearof original adoption or, in the case of revision, t

2、he year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1NOTEUnits information was editor

3、ially corrected in January 2014.1. Scope1.1 This specification covers three types of asphalt suitablefor use as a mopping coat in dampproofing; or as a plying ormopping cement in the construction of membrane waterproof-ing systems with felts in accordance with Specification D226;fabrics in accordanc

4、e with Specifications D173 or D1668(asphalt types); asphalt-impregnated glass mat in accordancewith Specifications D2178; and with primer in accordance withSpecification D41.1.2 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard. The values stated ineac

5、h system may not be exact equivalents; therefore, eachsystem should be used independently of the other. Combiningvalues from the two systems may result in non-conformancewith the standard.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is

6、theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2D5 Test Method for Penetration of Bituminous MaterialsD36 Test Method for Softening

7、Point of Bitumen (Ring-and-Ball Apparatus)D41 Specification for Asphalt Primer Used in Roofing,Dampproofing, and WaterproofingD92 Test Method for Flash and Fire Points by ClevelandOpen Cup TesterD113 Test Method for Ductility of Bituminous MaterialsD140 Practice for Sampling Bituminous MaterialsD173

8、 Specification for Bitumen-Saturated Cotton FabricsUsed in Roofing and WaterproofingD226 Specification for Asphalt-Saturated Organic Felt Usedin Roofing and WaterproofingD1668 Specification for Glass Fabrics (Woven and Treated)for Roofing and WaterproofingD2042 Test Method for Solubility of Asphalt

9、Materials inTrichloroethyleneD2178 Specification for Asphalt Glass Felt Used in Roofingand WaterproofingD3461 Test Method for Softening Point of Asphalt and Pitch(Mettler Cup-and-Ball Method)3. Classification3.1 Asphalts covered by this specification include threetypes:3.1.1 Type IA soft, adhesive,

10、“self-healing” asphalt thatflows easily under the mop and is suitable for use below gradeunder uniformly moderate temperature conditions both duringthe process of installation and during service.NOTE 1Type I asphalt is suitable for foundations, tunnels, subways,and so forth.3.1.2 Type IIA somewhat l

11、ess susceptible asphalt thanType I, with good adhesive and “self-healing” properties,suitable for use above grade where it will not be exposed totemperatures exceeding 50C 122F.NOTE 2Type II asphalt is suitable for railroad bridges, culverts,retaining walls, tanks, dams, conduits, spray decks, and s

12、o forth.3.1.3 Type IIIAn asphalt less susceptible to temperaturethan Type II, with good adhesive properties, and suitable foruse above grade on vertical surfaces exposed to direct sunlightor temperatures above 50C 122F.4. Materials and Manufacture4.1 The asphalt shall be prepared from crude petroleu

13、m bysuitable refining processes to conform to the applicable physi-cal requirements for each type.1This specification is under the jurisdiction of ASTM Committee D08 onRoofing and Waterproofing and is the direct responsibility of Subcommittee D08.03on Surfacing and Bituminous Materials for Membrane

14、Waterproofing and Built-upRoofing.Current edition approved May 1, 2008. Published January 2014. Originallyapproved in 1937. Last previous edition approved in 2008 as D449 03 (2008).DOI: 10.1520/D0449_D0449M-03R14E01.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM

15、 Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States15. Physical Requirements5.1 The

16、 asphalt shall be homogeneous and free of water.5.2 Each type shall conform to the appropriate requirementsprescribed in Table 1.6. Sampling and Test Methods6.1 Sample the material and determine the properties enu-merated in this specification in accordance with the followingmethods:6.1.1 SamplingPr

17、actice D140.6.1.2 Softening PointTest Methods D36 and D3461.6.1.3 Flash PointTest Method D92.6.1.4 PenetrationTest Method D5.6.1.5 DuctilityTest Method D113.6.1.6 Solubility in TrichloroethyleneTest Method D2042.7. Inspection and Certification7.1 Inspection and certification of the material shall be

18、 asagreed upon between the purchaser and the seller. Specificrequirements shall be made part of the purchase contract.8. Rejection and Rehearing8.1 If the results of any test do not conform to the require-ments of this specification, retesting to determine conformitymay be performed as agreed upon b

19、etween the purchaser andthe seller.9. Packaging and Marking9.1 The material shall be suitably packaged to permitacceptance by the carrier and to afford adequate protectionfrom the normal hazards of handling and shipment.9.2 Each container shall be plainly marked with the nameand brand of the manufac

20、turer or seller.10. Keywords10.1 asphalt; dampproofing; fabrics; waterproofingASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the valid

21、ity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comme

22、nts are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have n

23、ot received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple co

24、pies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/CO

25、PYRIGHT/).TABLE 1 Physical Requirements of Asphalt Used in Dampproofing and WaterproofingType I Type II Type IIIMin Max Min Max Min MaxSoftening point (ring-and-ball), C F 46 115 60 140 63 145 77 170 82 180 93 200Flash point (Cleveland open cup), C F 232 450 . 232 450 . 246 475 .Penetration:0C 32F, 200 g, 60 s; 0.1 mm 5 . 10 . 10 .25C 77F, 100 g, 5 s; 0.1 mm 50 100 25 50 20 4046C 115F, 50 g, 5 s; 0.1 mm 100 . . 130 . 100Ductility at 25C 77F, cm 30 . 10 . 2 .Solubility in trichloroethylene, % 99 . 99 . 99 .D449/D449M 03 (2014)12