ASTM D1735-2014 Standard Practice for Testing Water Resistance of Coatings Using Water Fog Apparatus《用水雾仪器测试喷粉表面防水性能的标准实施规程》.pdf
《ASTM D1735-2014 Standard Practice for Testing Water Resistance of Coatings Using Water Fog Apparatus《用水雾仪器测试喷粉表面防水性能的标准实施规程》.pdf》由会员分享,可在线阅读,更多相关《ASTM D1735-2014 Standard Practice for Testing Water Resistance of Coatings Using Water Fog Apparatus《用水雾仪器测试喷粉表面防水性能的标准实施规程》.pdf(4页珍藏版)》请在麦多课文档分享上搜索。
1、Designation: D1735 08D1735 14Standard Practice forTesting Water Resistance of Coatings Using Water FogApparatus1This standard is issued under the fixed designation D1735; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of
2、last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope Scope*1.1 This practice covers the
3、basic principles and operating procedures for testing water resistance of coatings in an apparatussimilar to that used for salt spray testing.1.2 This practice is limited to the methods of obtaining, measuring, and controlling the conditions and procedures of water fogtests. It does not specify spec
4、imen preparation, specific test conditions, or evaluation of results.NOTE 1Alternative practices for testing the water resistance of coatings include Practices D870, D2247, and D4585.1.3 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for informa
5、tion only.1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibilityof whoever uses this standard to consult and establish appropriate safety and health practices and determine the applicability ofregulatory limitations prior t
6、o use.2. Referenced Documents2.1 ASTM Standards:2B117 Practice for Operating Salt Spray (Fog) ApparatusD609 Practice for Preparation of Cold-Rolled Steel Panels for Testing Paint, Varnish, Conversion Coatings, and Related CoatingProductsD610 Practice for Evaluating Degree of Rusting on Painted Steel
7、 SurfacesD714 Test Method for Evaluating Degree of Blistering of PaintsD823 Practices for Producing Films of Uniform Thickness of Paint, Varnish, and Related Products on Test PanelsD870 Practice for Testing Water Resistance of Coatings Using Water ImmersionD1193 Specification for Reagent WaterD1654
8、Test Method for Evaluation of Painted or Coated Specimens Subjected to Corrosive EnvironmentsD1730 Practices for Preparation of Aluminum and Aluminum-Alloy Surfaces for PaintingD2247 Practice for Testing Water Resistance of Coatings in 100 % Relative HumidityD2616 Test Method for Evaluation of Visua
9、l Color Difference With a Gray ScaleD3359 Test Methods for Measuring Adhesion by Tape TestD3363 Test Method for Film Hardness by Pencil TestD4541 Test Method for Pull-Off Strength of Coatings Using Portable Adhesion TestersD4585 Practice for Testing Water Resistance of Coatings Using Controlled Cond
10、ensation3. Summary of Practice3.1 Coated specimens are placed in an enclosed chamber to permit free settling of fog on all specimens. The temperature of thechamber is usually maintained at 38C (100F). The exposure condition is varied by selecting the duration of the test. Water1 This practice is und
11、er the jurisdiction of ASTM Committee D01 on Paint and Related Coatings, Materials, and Applications and is the direct responsibility ofSubcommittee D01.27 on Accelerated Testing.Current edition approved Nov. 1, 2008June 15, 2014. Published December 2008July 2014. Originally approved in 1960. Last p
12、revious edition approved in 20022008 asD1735 04.D1735 08. DOI: 10.1520/D1735-08.10.1520/D1735-14.2 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Docume
13、nt Summary page on the ASTM website.This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM rec
14、ommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C
15、700, West Conshohocken, PA 19428-2959. United States1permeates the coating at rates that are dependent upon the characteristics of the coating.Any effects such as color change, blisters,loss of adhesion, softening, or embrittlement are observed and reported.4. Significance and Use4.1 Water can cause
16、 the degradation of coatings, so knowledge of how a coating resists water is helpful in predicting its servicelife. Failure in water fog tests may be caused by a number of factors, including a deficiency in the coating itself, contaminationof the substrate, or inadequate surface preparation. The tes
17、t is therefore useful for evaluating coatings alone or complete coatingsystems.4.2 Water fog tests are used for research and development of coatings and substrate treatments, specification acceptance, andquality control in manufacturing. These tests usually result in a pass or fail determination, bu
18、t the degree of failure may also bemeasured. A coating system is considered to pass if there is no evidence of water-related failure after a specified period of time.4.3 Results obtained from the use of water fog tests in accordance with this practice should not be represented as beingequivalent to
19、a period of exposure to water in the natural environment, until the degree of quantitative correlation has beenestablished for the coating or coating system.4.4 The test apparatus is similar to that used in Practice B117, and the conversion of the apparatus from salt spray to water fogtesting is fea
20、sible. Care should be taken to remove all traces of the salt from the cabinet and reservoir when converting from saltspray to water fog testing.5. Apparatus5.1 Descriptions for the Test Chamber, Test Specimen Supports, and Fog Collecting Devices, are listed underApparatus Sectionin Practice B117.5.2
21、 Unless otherwise specified, provide for continuous recording, such as a chart recorder or data logger, of the temperaturewithin the chamber during the exposure period.6. Test Specimens6.1 This practice does not cover the preparation of test specimens. The substrate composition and surface preparati
22、on, specimenpreparation, and the number of specimens should be agreed upon prior to testing.NOTE 2Applicable methods for the preparation of test panels and substrates are given in Practices D609 and D1730. Practices D823 cover applicationtechniques of the production of uniform films.6.2 Its recommen
23、ded that a control specimen of a paint with known durability be included with each test. Such controlspecimens can provide warning of changes in test severity in a given apparatus, and can indicate variations in test severity betweendifferent apparatuses.6.3 Its recommended that at least two replica
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ASTMD17352014STANDARDPRACTICEFORTESTINGWATERRESISTANCEOFCOATINGSUSINGWATERFOGAPPARATUS 水雾 仪器 测试 表面 防水
链接地址:http://www.mydoc123.com/p-510382.html