ASTM D1735-2004 Standard Practice for Testing Water Resistance of Coatings Using Water Fog Apparatus《用水雾仪进行涂层耐水性试验的标准规程》.pdf

《ASTM D1735-2004 Standard Practice for Testing Water Resistance of Coatings Using Water Fog Apparatus《用水雾仪进行涂层耐水性试验的标准规程》.pdf》由会员分享，可在线阅读，更多相关《ASTM D1735-2004 Standard Practice for Testing Water Resistance of Coatings Using Water Fog Apparatus《用水雾仪进行涂层耐水性试验的标准规程》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D 1735 04Standard Practice forTesting Water Resistance of Coatings Using Water FogApparatus1This standard is issued under the fixed designation D 1735; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last r

2、evision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 This practice covers the basic principles

3、and operatingprocedures for testing water resistance of coatings in anapparatus similar to that used for salt spray testing.1.2 This practice is limited to the methods of obtaining,measuring, and controlling the conditions and procedures ofwater fog tests. It does not specify specimen preparation,sp

4、ecific test conditions, or evaluation of results.NOTE 1Alternative practices for testing the water resistance ofcoatings include Practices D 870, D 2247, and D 4585.1.3 The values stated in SI units are to be regarded as thestandard. The values given in parentheses are for informationonly.1.4 This s

5、tandard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of whoever uses this standard to consult andestablish appropriate safety and health practices and deter-mine the applicability of regulatory limitations prior to use.2. Referenced

6、Documents2.1 ASTM Standards:2B117 Practice for Operating Salt Spray (Fog) ApparatusD 609 Practice for Preparation of Cold-Rolled Steel Panelsfor Testing Paint, Varnish, Conversion Coatings, andRelated Coating ProductsD 610 Test Method for Evaluating Degree of Rusting onPainted Steel SurfacesD 714 Te

7、st Method for Evaluating Degree of Blistering ofPaintsD 823 Practices for Producing Films of Uniform Thicknessof Paint, Varnish, and Related Products on Test PanelsD 870 Practice for Testing Water Resistance of CoatingsUsing Water ImmersionD 1193 Specification for Reagent WaterD 1654 Test Method for

8、 Evaluation of Painted or CoatedSpecimens Subjected to Corrosive EnvironmentsD 1730 Practices for Preparation of Aluminum andAluminum-Alloy Surfaces for PaintingD 2247 Practice for Testing Water Resistance of Coatings in100 % Relative HumidityD 2616 Test Method for Evaluation of Visual Color Differ-

9、ence With a Gray ScaleD 3359 Test Methods for Measuring Adhesion by Tape TestD 3363 Test Method for Film Hardness by Pencil TestD 4541 Test Method for Pull-Off Strength of CoatingsUsing Portable Adhesion TestersD 4585 Practice for Testing Water Resistance of CoatingsUsing Controlled Condensation3. S

10、ummary of Practice3.1 Coated specimens are placed in an enclosed chamber topermit free settling of fog on all specimens. The temperature ofthe chamber is usually maintained at 38C (100F). Theexposure condition is varied by selecting the duration of thetest. Water permeates the coating at rates that

11、are dependentupon the characteristics of the coating. Any effects such ascolor change, blisters, loss of adhesion, softening, or embrittle-ment are observed and reported.4. Significance and Use4.1 Water can cause the degradation of coatings, so knowl-edge of how a coating resists water is helpful in

12、 predicting itsservice life. Failure in water fog tests may be caused by anumber of factors, including a deficiency in the coating itself,contamination of the substrate, or inadequate surface prepara-tion. The test is therefore useful for evaluating coatings aloneor complete coating systems.4.2 Wate

13、r fog tests are used for research and development ofcoatings and substrate treatments, specification acceptance, andquality control in manufacturing. These tests usually result in apass or fail determination, but the degree of failure may also be1This practice is under the jurisdiction of ASTM Commi

14、ttee D01 on Paint andRelated Coatings, Materials, and Applications and is the direct responsibility ofSubcommittee D01.27 on Accelerated Testing.Current edition approved Nov. 1, 2004. Published December 2004. Originallyapproved in 1960. Last previous edition approved in 2002 as D 1735 02.2For refere

15、nced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West

16、Conshohocken, PA 19428-2959, United States.measured. A coating system is considered to pass if there is noevidence of water-related failure after a specified period oftime.4.3 Results obtained from the use of water fog tests inaccordance with this practice should not be represented asbeing equivalen

17、t to a period of exposure to water in the naturalenvironment, until the degree of quantitative correlation hasbeen established for the coating or coating system.4.4 The test apparatus is similar to that used in PracticeB117, and the conversion of the apparatus from salt spray towater fog testing is

18、feasible. Care should be taken to remove alltraces of the salt from the cabinet and reservoir when convert-ing from salt spray to water fog testing.5. Apparatus5.1 Descriptions for the Test Chamber, Test Specimen Sup-ports, and Fog Collecting Devices, are listed under ApparatusSection in Practice B1

19、17.5.2 Unless otherwise specified, provide for continuous re-cording, such as a chart recorder or data logger, of thetemperature within the chamber during the exposure period.6. Test Specimens6.1 This practice does not cover the preparation of testspecimens. The substrate composition and surface pre

20、paration,specimen preparation, and the number of specimens should beagreed upon prior to testing.NOTE 2Applicable methods for the preparation of test panels andsubstrates are given in Practices D 609 and D 1730. Practices D 823 coverapplication techniques of the production of uniform films.6.2 Its r

21、ecommended that a control specimen of a paintwith known durability be included with each test. Such controlspecimens can provide warning of changes in test severity in agiven apparatus, and can indicate variations in test severitybetween different apparatuses.6.3 Its recommended that at least two re

22、plicate specimensof each different coating be used, so as to compensate forvariations between specimens and variations in test conditionswithin the apparatus.7. Procedure7.1 Fill the reservoir with reagent water conforming to TypeIV or better of Specification D 1193.7.2 Heat the water to the desired

23、 temperature with thecirculating system in operation. If no temperature is specified,heat the water to 38 6 2C (100 6 4F). Maintain thetemperature throughout the test.7.3 Support or suspend specimens 15 from the vertical,with the plane of the specimen parallel to the direction of thefog flow. Slotte

24、d wood supports are suitable for flat specimens.Each specimen shall be placed to permit unencumbered expo-sure to the fog. A minimum spacing between specimens of 30mm is recommended. Arrange the specimens so that the waterfrom one specimen does not drip on other specimens.7.4 Place two containers wi

25、thin the chamber to collect fogfor measurement. Use collectors that have approximately thesame position within the chamber as the test specimens. Use aglass or plastic funnel with a diameter of area 80 cm2(area 100mm) with the stem of the funnel extending into the collectioncontainer. Locate one con

26、tainer within 10 cm of the fog nozzleand the other as far as possible from the nozzle. Place thecollectors so that they collect only the fog from the nozzle.Collection rates are to be measured every 24 h except onweekends. Record the collection rate in mL/h. Refer tocustomer specification for accept

27、able collection rates.7.4.1 Use at least four collectors for cabinets that have morethan one fogging nozzle. Position a collector 10 cm from eachnozzle. Place the other collectors at positions as far as possiblefrom each nozzle.7.4.2 It is recommended to map the collection rates withinthe exposure z

28、one of the cabinet once a year. Place collectorsthroughout the exposure zone to evaluate variations within thecabinet. Areas that are out of compliance should be taped offand specimens not tested there. Refer to manufacturers rec-ommendations to correct the problem.NOTE 3Collection rate mapping of a

29、 chamber throughout the expo-sure zone to ensure conformance to the collection rate requirements isrecommended as a means of reducing test variability.NOTE 4Larger cabinets that have more than one fogging nozzle, mayneed more than two collectors to obtain adequate collection information.Refer to man

30、ufacturers recommendations and customers requirementsfor specific requirements.7.5 To control for variability within the apparatus, reposi-tion the specimens on a regular basis so that all specimensspend equivalent amounts of time in the various areas of theapparatus (front, back, left, right, and c

31、enter).7.6 Adjust the atomizing air supply so that 1.0 to 3.0 mL ofwater/h is collected in a collector with a diameter of 100 mmbased on an average run of at least 16 h. The collection rateshould be agreed upon between the customer and the supplierbefore starting the test. The collection rate of the

32、 water shouldbe recorded daily.NOTE 5The fog rate specified in Practice B117is only 1.0 to 2.0mL/h for a collector with a diameter of 100 mm.7.7 Operate the test continuously with the test chamberclosed unless otherwise specified. Short interruptions to inspector remove specimens or to replenish the

33、 water supply arepermitted, but such interruptions should occur no more thanonce each day.7.8 Conclude the test after a specified period of time or aftereffects from exposure to water fog are observed.7.9 Wipe the test specimens dry. Rate specimens forchanges in color, blistering, etc. Evaluate spec

34、imens no lessthan 5 min and no more than 10 min after removal from test,as the effects from water exposure can change within a shorttime. Remove only as many specimens as can be rated withinthe specified time.NOTE 6The 0 to 10 scale described in the ASTM STP 5003ispreferred for rating. Relevant proc

35、edures for evaluating water effects aredescribed in Test Methods D 610, D 714, D 1654, D 2616, D 3359,D 3363, and D 4541.7.9.1 If possible, rate the specimens again after they havebeen removed from the test for a recovery period long enough3Paint and Coating Testing Manual, 14th ed., ASTM, 1995.D173

36、5042that moisture absorbed within the specimens dries out and thespecimens reach moisture equilibrium with room air. A recov-ery period of 12 from 24 h is generally sufficient. Thepost-recovery rating allows evaluation of the permanent effectsof the exposure as distinct from the transient effects, a

37、nd isespecially important for evaluation of color and gloss.8. Report8.1 Report the following information:8.1.1 Sample identification.8.1.2 Results of the evaluation(s).8.1.3 Reference to Practice D 1735.8.1.4 Hours of test duration.8.1.5 Test temperature.8.1.6 Rate of fog collection and pH of water

38、 collected.8.1.7 Special conditions of test or any deviations in testprocedure.9. Keywords9.1 adhesion; blistering; resistance-water; rust; water fogASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users

39、 of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every f

40、ive years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical

41、 committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).D1735043