《ASTM C618-2017a Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete《混凝土用粉煤灰和生的或煅烧的天然火山灰的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM C618-2017a Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete《混凝土用粉煤灰和生的或煅烧的天然火山灰的标准规范》.pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: C618 17aStandard Specification forCoal Fly Ash and Raw or Calcined Natural Pozzolan for Usein Concrete1This standard is issued under the fixed designation C618; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year

2、of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope*1.1 This specification covers co

3、al fly ash and raw orcalcined natural pozzolan for use in concrete where cementi-tious or pozzolanic action, or both, is desired, or where otherproperties normally attributed to fly ash or pozzolans may bedesired, or where both objectives are to be achieved.NOTE 1Finely divided materials may tend to

4、 reduce the entrained aircontent of concrete. Hence, if a fly ash or natural pozzolan is added to anyconcrete for which entrainment of air is specified, provision should bemade to ensure that the specified air content is maintained by air contenttests and by use of additional air-entraining admixtur

5、e or use of anair-entraining admixture in combination with air-entraining hydrauliccement.1.2 The values stated in SI units are to be regarded asstandard. No other units of measurement are included in thisstandard.1.3 The text of this standard references notes and footnotes,which provide explanatory

6、 information. These notes and foot-notes (excluding those in tables and figures) shall not beconsidered as requirements of the standard.1.4 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principle

7、s for theDevelopment of International Standards, Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:2C125 Terminology Relating to Concrete and Concrete Ag-gregatesC311/C311M Test Methods for Sampling

8、 and Testing FlyAsh or Natural Pozzolans for Use in Portland-CementConcreteC1778 Guide for Reducing the Risk of Deleterious Alkali-Aggregate Reaction in Concrete3. Terminology3.1 Definitions:3.1.1 For definitions of terms used in this specification referto Terminology C125.4. Classification4.1 Class

9、 NRaw or calcined natural pozzolans that com-ply with the applicable requirements for the class as givenherein, such as some diatomaceous earths; opaline cherts andshales; tuffs and volcanic ashes or pumicites, calcined oruncalcined; and various materials requiring calcination toinduce satisfactory

10、properties, such as some clays and shales.4.2 Class FFly ash that meets the applicable requirementsfor this class as given herein. This class of fly ash haspozzolanic properties.4.3 Class CFly ash that meets the applicable requirementsfor this class as given herein. This class of fly ash, in additio

11、nto having pozzolanic properties, also has some cementitiousproperties.NOTE 2Class F fly ash is typically produced from burning anthraciteor bituminous coal, but may also be produced from subbituminous coaland from lignite. Class C fly ash is typically produced from burning ligniteor subbituminous c

12、oal, and may also be produced from anthracite orbituminous coal. Class C fly ashes typically have total calcium contents,expressed as calcium oxide (CaO), that are higher than Class F fly ashes.5. Ordering Information5.1 The purchaser shall specify any supplementary optionalphysical requirements.5.2

13、 The purchaser shall indicate which procedure, A or B,shall be used when specifying requirements for effectiveness incontribution to sulfate resistance under Table 3.6. Chemical Composition6.1 Fly ash and natural pozzolans shall conform to therequirements as to chemical composition prescribed in Tab

14、le 1.1This specification is under the jurisdiction of ASTM Committee C09 onConcrete and Concrete Aggregates and is the direct responsibility of SubcommitteeC09.24 on Supplementary Cementitious Materials.Current edition approved Dec. 15, 2017. Published January 2018. Originallyapproved in 1968. Last

15、previous edition approved in 2017 as C61817. DOI:10.1520/C0618-17A.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM we

16、bsite.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesThis international standard was developed in accordance with internationally recognized principles on standardizatio

17、n established in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.1NOTE 3The chemical component determinations and the limits placedon each do not predict the perfor

18、mance of the fly ash or natural pozzolanwith hydraulic cement in concrete, but collectively help describe compo-sition and uniformity of the material.7. Physical Properties7.1 Fly ash and natural pozzolans shall conform to thephysical requirements prescribed in Table 2. Supplementaryoptional physica

19、l requirements are shown in Table 3.8. Methods of Sampling and Testing8.1 Sample and test the fly ash or natural pozzolan inaccordance with the requirements of Test Methods C311/C311M.8.2 Use cement of the type proposed for use in the workand, if available, from the mill proposed as the source of th

20、ecement, in all tests requiring the use of hydraulic cement.9. Storage and Inspection9.1 The fly ash or natural pozzolan shall be stored in such amanner as to permit easy access for proper inspection andidentification of each shipment.9.2 Inspection of the material shall be made as agreed uponby the

21、 purchaser and the seller as part of the purchase contract.10. Rejection10.1 The purchaser has the right to reject material that failsto conform to the requirements of this specification. Rejectionshall be reported to the producer or supplier promptly and inwriting.10.2 The purchaser has the right t

22、o reject packages varyingmore than 5 % from the stated weight. The purchaser also hasthe right to reject the entire shipment if the average weight ofthe packages in any shipment, as shown by weighing 50packages taken at random, is less than that specified.10.3 The purchaser has the right to require

23、that material instorage prior to shipment for a period longer than 6 monthsafter testing be retested. The purchaser has the right to rejectsuch material if it fails to meet the fineness requirements.11. Packaging and Package Marking11.1 When the fly ash or natural pozzolan is delivered inpackages, t

24、he class, name, and brand of the producer, and theTABLE 1 Chemical RequirementsClassNF CSilicon dioxide (SiO2) plus aluminum oxide (Al2O3) plus iron oxide (Fe2O3),min, %70.0 70.0 50.0Sulfur trioxide (SO3), max, % 4.0 5.0 5.0Moisture content, max, % 3.0 3.0 3.0Loss on ignition, max, % 10.0 6.0A6.0ATh

25、e use of Class F pozzolan containing up to 12.0 % loss on ignition may be approved by the user if either acceptable performance records or laboratory test resultsare made available.TABLE 2 Physical RequirementsClassNFCFineness:Amount retained when wet-sieved on 45 m (No. 325) sieve, max, % 34 34 34S

26、trength activity index:AWith portland cement, at 7 days, min, percent ofcontrol75B75B75BWith portland cement, at 28 days, min, percent ofcontrol75B75B75BWater requirement, max, percent of control 115 105 105Soundness:CAutoclave expansion or contraction, max, % 0.8 0.8 0.8Uniformity requirements:The

27、density and fineness of individual samplesshall not vary from the average established by theten preceding tests, or by all preceding tests if thenumber is less than ten, by more than:Density, max variation from average, % 5 5 5Percent retained on 45-m (No. 325), max variation,percentage points from

28、average55AThe strength activity index with portland cement is not to be considered a measure of the compressive strength of concrete containing the fly ash or natural pozzolan.The mass of fly ash or natural pozzolan specified for the test to determine the strength activity index with portland cement

29、 is not considered to be the proportionrecommended for the concrete to be used in the work. The optimum amount of fly ash or natural pozzolan for any specific project is determined by the required propertiesof the concrete and other constituents of the concrete and is to be established by testing. S

30、trength activity index with portland cement is a measure of reactivity with a givencement and is subject to variation depending on the source of both the fly ash or natural pozzolan and the cement.BMeeting the 7 day or 28 day strength activity index will indicate specification compliance.CIf the fly

31、 ash or natural pozzolan will constitute more than 20 % by mass of the cementitious material in the project mixture, the test specimens for autoclave expansionshall contain that anticipated percentage. Excessive autoclave expansion is highly significant in cases where water to cementitious material

32、ratios are low, for example,in block or shotcrete mixtures.C618 17a2weight of the material contained therein, shall be plainlymarked on each package. Similar information shall be providedin the shipping invoices accompanying the shipment of pack-aged or bulk material.12. Suppliers Certification12.1

33、Upon request of the purchaser, in the contract or theorder, a suppliers report shall be furnished stating the resultsof tests made on samples of the material and certifying theproduct conforms to all applicable requirements of this speci-fication. In addition, the report shall include the percentage

34、s ofmagnesium oxide (MgO), sodium oxide (Na2O), potassiumoxide (K2O), and calcium oxide (CaO), all determined asdescribed in Test Methods C311/C311M. The report shall alsoinclude the total alkali content of the material, expressed asequivalent percentage of sodium oxide (Na2Oe).NOTE 4Guidance on pre

35、paring the suppliers report is provided inAppendix X1.13. Keywords13.1 fly ash; natural pozzolan; pozzolansAPPENDIXES(Nonmandatory Information)X1. SUPPLIERS CERTIFICATION REPORTX1.1 To provide uniformity for reporting the results of testsperformed on pozzolans under this specification, and affirming

36、compliance to the applicable limits of this standard, an ex-ample report of analysis is shown in Fig. X1.1.X2. EFFECTIVENESS OF FLY ASH OR NATURAL POZZOLAN IN PREVENTING EXCESSIVE EXPANSION OF CONCRETEDUE TO ALKALI SILICA REACTIONX2.1 If properly proportioned in concrete mixtures, both flyash and na

37、tural pozzolan have been shown to prevent excessiveexpansion due to alkali silica reaction. The quantity of fly ashor natural pozzolan required to mitigate alkali silica reaction,measured in terms of portland cement replacement, is depen-dent on the properties of the fly ash or pozzolan, reactivity

38、ofthe aggregate and the alkali loading of the concrete. Forinformation on ASR mitigation, including test methods, seeGuide C1778.TABLE 3 Supplementary Optional Physical RequirementsNOTE 1These optional requirements apply only when specifically requested.ClassNFCIncrease of drying shrinkage of mortar

39、 bars at 28 days, max, difference, in %,over controlA0.03 0.03 0.03Uniformity Requirements:In addition, when air-entraining concrete is specified, the quantity of air-entraining agent required to produce an air content of 18.0 vol % of mortarshall not vary from the average established by the ten pre

40、ceding tests or by allpreceding tests if less than ten, by more than, %20 20 20Effectiveness in Contributing to Sulfate Resistance:BProcedure A:Expansion of test mixture:For moderate sulfate exposure after 6 months exposure, max, % 0.10 0.10 0.10For high sulfate exposure after 6 months exposure, max

41、, % 0.05 0.05 0.05Procedure B:Expansion of test mixture as a percentage of sulfate resistance cementcontrol after at least 6 months exposure, max,%100 100 100ADetermination of compliance or noncompliance with the requirement relating to increase in drying shrinkage will be made only at the request o

42、f the purchaser.BFly ash or natural pozzolan shall be considered effective only when the fly ash or natural pozzolan is used at percentages, by mass, of the total cementitious materialwithin 2 % of those that are successful in the test mixtures or between two percentages that are successful, and whe

43、n the C3A content of the project cement is less than,or equal to, that which was used in the test mixtures. See Appendix X2 of Test Method C311/C311M.C618 17a3FIG. X1.1 Example of a Suppliers ReportC618 17a4SUMMARY OF CHANGESCommittee C09 has identified the location of selected changes to this speci

44、fication since the last issue,C618 17, that may impact the use of this specification. (Approved Dec. 15, 2017)(1) Revised Section 3.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard

45、 are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif n

46、ot revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which

47、 you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,Uni

48、ted States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 17a5