ASTM C506M-2009 Standard Specification for Reinforced Concrete Arch Culvert Storm Drain and Sewer Pipe (Metric).pdf

《ASTM C506M-2009 Standard Specification for Reinforced Concrete Arch Culvert Storm Drain and Sewer Pipe (Metric).pdf》由会员分享，可在线阅读，更多相关《ASTM C506M-2009 Standard Specification for Reinforced Concrete Arch Culvert Storm Drain and Sewer Pipe (Metric).pdf（7页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: C 506M 09Standard Specification forReinforced Concrete Arch Culvert, Storm Drain, and SewerPipe (Metric)1This standard is issued under the fixed designation C 506M; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the y

2、ear of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 This specification covers rein

3、forced arch-shaped con-crete pipe to be used for the conveyance of sewage, industrialwastes, storm water, and for the construction of culverts.1.2 This specification is the SI companion to SpecificationC 506.NOTE 1This specification is a manufacturing and purchase specifica-tion only, and does not i

4、nclude requirements for bedding, backfill, or therelationship between field load condition and the strength classification ofpipe. However, experience has shown that the successful performance ofthis product depends upon the proper selection of the class of pipe, typeof bedding and backfill, and car

5、e that the installation conforms to theconstruction specifications. The owner of the reinforced concrete pipespecified herein is cautioned that he must correlate the field requirementswith the class of pipe specified and provide inspection at the constructionsite.2. Referenced Documents2.1 ASTM Stan

6、dards:2A 36/A 36M Specification for Carbon Structural SteelA 82/A 82M Specification for Steel Wire, Plain, for Con-crete ReinforcementA 185/A 185M Specification for Steel Welded Wire Rein-forcement, Plain, for ConcreteA 496/A 496M Specification for Steel Wire, Deformed, forConcrete ReinforcementA 49

7、7/A 497M Specification for Steel Welded Wire Rein-forcement, Deformed, for ConcreteA 615/A 615M Specification for Deformed and PlainCarbon-Steel Bars for Concrete ReinforcementA 706/A 706M Specification for Low-Alloy Steel De-formed and Plain Bars for Concrete ReinforcementC33 Specification for Conc

8、rete AggregatesC 150 Specification for Portland CementC 260 Specification for Air-Entraining Admixtures for Con-creteC 309 Specification for Liquid Membrane-Forming Com-pounds for Curing ConcreteC 494/C 494M Specification for Chemical Admixtures forConcreteC 497M Test Methods for Concrete Pipe, Manh

9、ole Sec-tions, or Tile MetricC 595 Specification for Blended Hydraulic CementsC 618 Specification for Coal Fly Ash and Raw or CalcinedNatural Pozzolan for Use in ConcreteC 822 Terminology Relating to Concrete Pipe and RelatedProductsC 989 Specification for Slag Cement for Use in Concreteand MortarsC

10、 1017/C 1017M Specification for Chemical Admixturesfor Use in Producing Flowing ConcreteC 1116 Specification for Fiber-Reinforced Concrete andShotcrete3. Terminology3.1 DefinitionsFor definitions of terms relating to con-crete pipe, see Terminology C 822.4. Classification4.1 Pipe manufactured accord

11、ing to this specification shallbe of three classes identified as ClassA-II,A-III, andA-IV. Thestrength requirements are prescribed in Table 1.5. Basis of Acceptance5.1 Unless otherwise designated by the owner at the time of,or before placing an order, there are two separate and alterna-tive bases of

12、 acceptance. Independent of the method ofacceptance, the pipe shall be designed to meet both the 0.01-in.crack and ultimate strength requirements.5.1.1 Acceptance on Basis of Plant Load Bearing Tests,Material Tests, and Inspection of Manufactured Pipe for VisualDefects and ImperfectionsAcceptability

13、 of the pipe in alldiameters and classes produced in accordance with 7.1 or 7.2shall be determined by the results of the three-edge-bearingtests as defined in 11.3.1; by such material tests as are required1This specification is under the jurisdiction of ASTM Committee C13 onConcrete Pipe and is the

14、direct responsibility of Subcommittee C13.02 onReinforced Sewer and Culvert Pipe.Current edition approved June 1, 2009. Published June 2009. Originallyapproved in 1980. Last previous edition approved in 2008 as C 506M 08a.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontac

15、t ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.in accordance with 6.2,

16、6.3, 6.5, and 6.6, by an absorption testof the concrete from the wall of the pipe for each mix designthat is used on an order; and by visual inspection of the finishedpipe to determine its conformance with the accepted design andits freedom from defects.5.1.2 Acceptance on the Basis of Material Test

17、 and Inspec-tion of Manufactured Pipe for Defects and ImperfectionsAcceptability of the pipe in all diameters and classes producedin accordance with 7.1 or 7.2 shall be determined by the resultsof such material tests as are required in accordance with 6.2,6.3, 6.5, and 6.6; by crushing tests on conc

18、rete cores or curedconcrete cylinders; by an absorption test of the concrete fromthe wall of the pipe for each mix design that is used on anorder; and by inspection of the finished pipe, including amountand placement of reinforcement, to determine its conformancewith the accepted design and its free

19、dom from defects.5.1.3 When agreed upon by the owner and the manufacturer,any portion or any combination of the tests itemized in 5.1.1 or5.1.2 may form the basis of acceptance.5.2 Age for AcceptancePipe shall be considered ready foracceptance when they conform to the requirements as indicatedby the

20、 specified tests.6. Materials6.1 Reinforced ConcreteThe reinforced concrete shallconsist of cementitious materials, mineral aggregates, andwater, in which steel has been embedded in such a manner thatthe steel and concrete act together.6.2 Cementitious Materials:6.2.1 CementCement shall conform to t

21、he requirementsof Specification C 150, or shall be portland blast-furnace slagcement, or slag modified portland cement, or portland-pozzolan cement conforming to the requirements of Specifica-tion C 595, except that the pozzolan constituent in the Type IPportland pozzolan cement shall be fly ash and

22、 shall not exceed25 % by weight.TABLE 1 Strength Requirements for Reinforced Concrete PipeAApprox-imateEquivalentRoundSize,mmT,mmMini-mumRise,mmMini-mumSpan,mmf8cBMPaDouble Line ReinforcementCSingle LineReinforcementContinuous BasicReinforcement = AsDAdditional Reinforcement = AsDClass Inner Cage Ou

23、ter Cage“U ”(Inner Cage)“V ”(Outer Cage)A-II A-III A-IV A-II A-III A-IV A-II A-III A-IVDimen-sion,mmA-II A-III A-IVDimen-sion,mmA-II A-III A-IV A-II A-III A-IV375 57 280 460 27.6 27.6 27.6 . . . . . . . . . . . . . . 1.7 2.5 3.6450 63 345 560 27.6 27.6 27.6 . . . . . . . . . . . . . . 2.3 3.0 5.5525

24、 69 395 660 27.6 27.6 27.6 . . . . . . . . . . . . . . 2.8 3.6 6.1600 75 460 725 27.6 27.6 27.6 . . . . . . 660 . . . 735 . . . 3.4 4.6 6.8750 88 570 920 27.6 27.6 27.6 1.9 2.5 3.8 1.5 1.9 3.0 760 1.9 2.5 3.8 865 1.5 1.9 2.8 3.8 5.1 7.6900 100 675 1110 27.6 27.6 27.6 2.3 3.2 4.6 1.9 2.5 3.6 865 2.3

25、3.2 4.6 990 1.9 2.5 3.4 4.6 6.3 9.31050 113 795 1300 27.6 27.6 27.6 2.8 3.8 5.7 2.1 3.0 4.4 1065 2.8 3.8 5.7 1090 2.1 3.0 4.6 5.5 7.6 11.41200 125 915 1485 27.6 27.6 . 3.2 4.6 . 2.5 3.6 . 1220 3.2 4.6 . 1245 2.5 3.6 . 6.3 9.3 .1350 138 1015 1650 27.6 27.6 . 3.8 5.1 . 3.0 4.0 . 1320 3.8 5.1 . 1395 3.

26、0 4.0 . 7.6 10.2 .1500 150 1145 1855 27.6 27.6 . 4.4 5.9 . 3.6 4.6 . 1525 4.4 5.9 . 1700 3.6 4.6 . 8.9 11.8 .1800 175 1370 2235 27.6 34.5 . 5.5 7.6 . 4.2 5.9 . 1725 5.5 7.6 . 1955 4.2 5.9 . 11.0 15.2 .2100 200 1575 2590 27.6 34.5 . 6.8 9.3 . 5.1 7.2 . . 6.8 9.3 . . 5.1 7.2 . 13.5 18.6 .2250 213 1830

27、 2920 . . . . . . . . . . . . . . . . . . . .2400 225 1960 3100 . . . . . . . . . . . . . . . . . . . .2700 250 2215 3505 . . . . . . . . . . . . . . . . . . . .3000 275 2460 3910 . . . . . . . . . . . . . . . . . . . .3300 250 2705 4285 . . . . . . . . . . . . . . . . . . . .D-Loads for 3Edge-Beari

28、ng MethodClass 0.3-mmCrackUltimateA-II 50.0 75.0A-III 65.0 100.0A-IV 100.0 150.0NoteTest load in newtons per linearmetre equals D-load 3 inside span inmillimetres.AFor modified or special designs, see 7.3.Bf 8c = minimum compressive strength of concrete in megapascals.CAs an alternative to designs r

29、equiring double line reinforcement, the reinforcement may be positioned and proportioned so that the total reinforcement of the inner cageplus the middle cage shall not be less than that specified for the inner cage continuous basic reinforcement, and the additional reinforcement “U ” and the totalr

30、einforcement of the outer cage plus the middle cage shall not be less than that specified for the outer cage continuous basic reinforcement and the additional reinforcement“V.”DAs= circumferential steel area in square millimetres per longitudinal centimetre of pipe barrel in each continuous basic ca

31、ge and additional cages in area denoted “U ”and “V.” Dimensions “U ” and “V ” are measured on the center line of the culvert wall.C506M0926.2.2 Ground Granulated Blast-Furnace Slag (GGBFS)GGBFS shall conform to the requirements of Grade 100 or 120of Specification C 989.6.2.3 Fly AshFly ash shall con

32、form to the requirements ofClass F or Class C of Specification C 618.6.2.4 Allowable Combinations of Cementitious MaterialsThe combination of cementitious materials used in the concreteshall be one of the following:6.2.4.1 Portland cement only,6.2.4.2 Portland blast furnace slag cement only,6.2.4.3

33、Slag modified portland cement only,6.2.4.4 Portland pozzolan cement only,6.2.4.5 A combination of portland cement and groundgranulated blast-furnace slag,6.2.4.6 A combination of portland cement and fly ash, or6.2.4.7 A combination of portland cement, ground granu-lated blast-furnace slag (not to ex

34、ceed 25 % of the totalcementitious weight) and fly ash (not to exceed 25 % of thetotal cementitious weight.6.3 AggregatesAggregates shall conform to SpecificationC33except that the requirement for gradation shall not apply.6.4 Admixtures and BlendsThe following admixtures andblends are allowable:6.4

35、.1 Air-entraining admixture conforming to SpecificationC 260;6.4.2 Chemical admixture conforming to SpecificationC 494/C 494M;6.4.3 Chemical admixture for use in producing flowingconcrete conforming to Specification C 1017/C 1017M; and6.4.4 Chemical admixture or blend approved by the owner.6.5 Steel

36、 ReinforcementReinforcement shall consist ofwire conforming to Specification A 82/A 82M or SpecificationA 496/A 496M; or of wire reinforcement conforming to Speci-fication A 185/A 185M or Specification A 497/A 497M;orofbars conforming to Specification A 36/A 36M, SpecificationA 615/A 615M Grade 40 o

37、r 60, or Specification A 706/A 706M Grade 60.6.6 Synthetic FibersCollated fibrillated virgin polypropy-lene fibers may be used, at the manufacturers option, inconcrete pipe as a nonstructural manufacturing material. OnlyType III synthetic fibers designed and manufactured specifi-cally for use in con

38、crete and conforming to the requirements ofSpecification C 1116 shall be accepted.7. Design7.1 Size and DimensionsThe standard sizes of arch pipeare listed in Table 1. The internal dimensions for each standardsize shall be as defined in Fig. 1, subject to the permissiblevariations of Section 12.Appr

39、oximateEquivalentRound Size,mmWater Area, m2Rise, mm Span, mm A,mm B,mm C,mm R1,mm R2,mm R3,mm375 0.10 280 460 10 121 128 580 270 102450 0.15 345 560 5 153 145 700 350 135525 0.20 395 660 20 158 195 900 375 135600 0.26 460 725 90 153 248 1035 370 115750 0.41 570 920 95 194 305 1300 475 155900 0.59 6

40、75 1110 105 218 395 1575 570 1601050 0.82 795 1300 130 258 460 1855 665 1901200 1.06 915 1485 155 297 522 2135 760 2201350 1.33 1015 1650 170 330 575 2350 850 2501500 1.64 1145 1855 190 373 642 2670 955 2851800 2.38 1370 2235 225 428 798 3200 1145 3202100 3.21 1575 2590 255 475 940 4130 1320 3552250

41、 4.13 1830 2920 330 604 970 4650 1500 4902400 4.80 1960 3100 385 616 1040 5535 1575 5102700 6.13 2215 3505 435 681 1182 6835 1780 5703000 7.60 2460 3910 480 740 1345 7655 1980 6103300 9.21 2705 4285 530 835 1458 8355 2175 685FIG. 1 Cross-Sectional Shape of Arch PipeC506M0937.2 Design TablesThe wall

42、thickness, compressivestrength of concrete, and the area of circumferential reinforce-ment shall be as prescribed in Table 1, subject to the provisionsof 7.3, 11.4, and Section 12.7.2.1 Footnotes to the tables herein are intended to beamplifications of the tabulated requirements and are to beconside

43、red applicable and binding as if they were contained inthe body of the specification.7.3 Modified and Special Designs:7.3.1 If permitted by the owner, the manufacturer mayrequest approval by the owner of modified designs that differfrom the designs in this Section 7 or special designs for sizesand l

44、oads beyond those shown in Table 1, or special designs forpipe sizes that do not have steel reinforcement areas shown inTable 1.7.3.2 Such modified or special designs shall be based onrational or empirical evaluations of the ultimate strength andcracking behavior of pipe and shall fully describe to

45、the ownerany deviations from the requirements of this Section 7. Thedescriptions of modified or special designs shall include thewall thickness, the concrete strength, and the area, type,placement, number of layers, and strength of the steel rein-forcement.7.3.3 The manufacturer shall submit to the

46、owner proof ofthe adequacy of the proposed modified or special design. Suchproof may comprise the submission of certified three-edge-bearing tests already made, which are acceptable to the owneror, if such three-edge-bearing tests are not available or accept-able, the manufacturer may be required to

47、 perform proof testson sizes and classes selected by the owner to demonstrate theadequacy of the proposed design.7.3.4 Such pipe must meet all of the test and performancerequirements specified by the owner in accordance withSection 5.7.4 AreaIn this specification, when the word area is notdescribed

48、by adjectives, such as cross-sectional or single wire,it shall be understood to be the cross-sectional area ofreinforcement per unit lengths of pipe.8. Reinforcement8.1 Circumferential ReinforcementA line of circumferen-tial reinforcement for any given total area may be composed oftwo layers for pip

49、e with wall thicknesses of less than 180 mmor three layers for pipe with wall thicknesses of 180 mm orgreater. The layers shall not be separated by more than thethickness of one longitudinal plus 6 mm. The multiple layersshall be fastened together to form a single cage. All otherspecification requirements such as laps, welds, and tolerancesof placement in the wall of the pipe, etc., shall apply to thismethod of fabricating a line of reinforcement.8.1.1 Where one line of reinforcement is used, it shall beplaced so that the cover of the concrete over the circum