ASTM C441-2005 Standard Test Method for Effectiveness of Pozzolans or Ground Blast-Furnace Slag in Preventing Excessive Expansion of Concrete Due to the Alkali-Silica Reaction《在防止因.pdf

《ASTM C441-2005 Standard Test Method for Effectiveness of Pozzolans or Ground Blast-Furnace Slag in Preventing Excessive Expansion of Concrete Due to the Alkali-Silica Reaction《在防止因.pdf》由会员分享，可在线阅读，更多相关《ASTM C441-2005 Standard Test Method for Effectiveness of Pozzolans or Ground Blast-Furnace Slag in Preventing Excessive Expansion of Concrete Due to the Alkali-Silica Reaction《在防止因.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: C 441 05Standard Test Method forEffectiveness of Pozzolans or Ground Blast-Furnace Slag inPreventing Excessive Expansion of Concrete Due to theAlkali-Silica Reaction1This standard is issued under the fixed designation C 441; the number immediately following the designation indicates the

2、 year oforiginal adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method covers the determination of the e

3、ffec-tiveness of pozzolans or slag in preventing the excessiveexpansion caused by reaction between aggregates and alkaliesin portland cement mixtures. The evaluation is based on theexpansion developed in mortar bars by a combination ofportland cement and a pozzolan or slag, made with reactiveaggrega

4、tes (borosilicate glass), during storage under prescribedconditions of test.1.2 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determi

5、ne the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2C 125 Terminology Relating to Concrete and ConcreteAggregatesC 150 Specification for Portland CementC 227 Test Method for Potential Alkali Reactivity ofCement-Aggregate Combinations (Mortar-Bar Me

6、thod)C 618 Specification for Coal Fly Ash and Raw or CalcinedNatural Pozzolan for Use in ConcreteC 989 Specification for Ground Granulated Blast-FurnaceSlag for Use in Concrete and MortarsC 1240 Specification for Use of Silica Fume Used inCementitious MixturesC 1437 Test Method for Flow of Hydraulic

7、 Cement Mortar3. Terminology3.1 DefinitionsFor definitions of terms used in this testmethod, refer to Terminology C 125.4. Significance and Use4.1 This test method may be used as a preliminary orscreening test to evaluate the relative effectiveness of a numberof different materials being considered

8、for use to preventexcessive expansion due to alkali-silica reaction.4.2 This test method may also be used to evaluate materialsproposed for use on a particular job to prevent excessiveexpansion due to alkali-silica reaction, by testing in thequantity and in combination with the cement or cements to

9、beused on the job.4.3 This test method does not assess the suitability ofpozzolans or slag for use in concrete. These materials shouldcomply with Specification C 618, Specification C 989 orSpecification C 1240.5. Apparatus5.1 The apparatus shall be as described in Test MethodC 227.6. Materials6.1 Bo

10、rosilicate Glass3Borosilicate glass granulesgraded according to Table 1 or crushed Pyrex Glass No. 7740cullet or solid glass rod crushed and graded according to Table1. After the glass cullet or rod has been crushed and separatedinto the various sieve sizes, wash with a water spray over thesieve to

11、remove adhering dust and fine particles from theaggregate. Dry the portions retained on the various sieves and,unless used immediately, store each such portion individuallyin a clean container provided with a tight-fitting cover.6.2 High-Alkali CementFor the preparation of mortar barsfor the prelimi

12、nary or screening tests, use a blend of cement orcements that conform to Specification C 150 and containbetween 0.95 and 1.05 % total alkalies as sodium oxide (Na2O)1This test method is under the jurisdiction of ASTM Committee C09 onConcrete and Concrete Aggregates and is the direct responsibility o

13、f SubcommitteeC09.26 on Chemical Reactions .Current edition approved May 1, 2005. Published May 2005. Originallyapproved in 1959. Last previous edition approved in 2002 as C 44102a.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.or

14、g. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3The sole source of supply of borosilicate glass granules in the specific sizescalled for in this test method known to the committee at this time is EnviroglassInternational, Caldw

15、ell, ID, http:/ If you are aware ofalternative suppliers, please provide this information to ASTM InternationalHeadquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee,1which you may attend.1Copyright ASTM International, 100 Barr Harbor Drive,

16、 PO Box C700, West Conshohocken, PA 19428-2959, United States.calculated as % Na2O + 0.658 3 % potassium oxide (K2O). Ifblending is needed, introduce the individual cements into thebatch separately.7. Proportioning and Consistency of Mortar7.1 Control MixtureThe quantities of dry materials for theco

17、ntrol mixture shall be 400 g of high-alkali cement and 900 gof glass aggregate made by recombining the portions retainedon the various sieves in the prescribed grading (Table 1). Testspecimens made from the control mixture shall have a 14-dayincrease in length of at least 0.250 %.7.2 Test Mixture Us

18、ing PozzolansThe quantities of drymaterials for the test mixture shall be 300 g of high-alkalicement, a mass of pozzolan having an absolute volume equal tothe absolute volume of 100 g of portland cement (100 3 den-sity of pozzolan/3.15) and 900 g of glass aggregate made asdescribed for the control m

19、ixture.7.3 Test Mixture Using SlagThe quantities of dry materi-als for this test mixture shall be 200 g of high-alkali cement, amass of slag having an absolute volume of 200 g of portlandcement (200 3 density of slag/3.15) and 900 g of glass made inaccordance with 7.1.7.4 A smaller quantity of the p

20、ozzolan or slag and aproportionately large quantity of cement may be used if thereis evidence that it is unusually effective in reducing expansiondue to the alkali-silica reaction and that the use of a smallerquantity is likely to produce a large reduction of expansion ofthe test mixture as compared

21、 to that of the control mixture.7.5 Job MixtureThe quantities of dry materials used forthe job mixture shall be in accordance with the requirementsgiven above, except that the cement or cements to be used onthe job shall be used instead of the high-alkali cement. Also,the quantity of pozzolan or sla

22、g, by mass, used with theportland cement shall be equivalent to that proposed for use onthe job.7.6 FlowThe amount of mixing water, measured in mil-lilitres, shall be such as to produce a flow of between 100 and115 as determined in accordance with Test Method C 1437.8. Temperature and Humidity8.1 Th

23、e temperature of the dry materials, water, moldingroom, and moist cabinet and the humidity of the laboratory andmoist cabinet shall conform to the requirements of Test MethodC 227.9. Test Specimen9.1 Preparation of MoldsPrepare the molds as specifiedin Test Method C 227.9.2 Mixing of MortarMix the m

24、ortar as specified in TestMethod C 227, except add the admixture or slag with thecement to the water.9.3 Molding Test SpecimensMold the specimens as speci-fied in Test Method C 227.9.4 Dimensions and Number of Test SpecimensMakethree 1 by 1 by 1114-in. or 25 by 25 by 285-mm test specimenshaving an e

25、ffective gage length of 10 6 0.1 in. or 254 6 2.5mm from each batch of each mortar mixture. One set of threespecimens shall represent each test mixture or each jobmixture. On the same day that the test specimens are made,make one set of three specimens representing the controlmixture and store in th

26、e same container with the correspondingtest specimens. Make all specimens stored in a given containeron the same day. If more specimens from test or job mixtures,or both, are made on a given day than can be stored in a singlecontainer with the specimens from the control mixture made onthat day, make

27、 additional control mixture specimens for eachadditional storage container used.10. Procedure10.1 Store and measure the test specimens in accordancewith the applicable requirements of Test Method C 227.11. Calculation11.1 For tests of mixtures proportioned as prescribed, cal-culate the reduction of

28、mortar expansion resulting from the useof a pozzolan or slag and report the result to the nearest 0.1 %as follows.Re5Er2 Et!3100/Erwhere:Re= reduction of mortar expansion, %,Et= average increase in length of mortar bars from the testmixture, andEr= average increase in length of mortar bars from thec

29、ontrol mixture.11.2 For test mixtures proportioned in accordance with thejob mixture procedure, report the average length increase of themortar bars as the length increase of the combination proposedfor use in the work. Indicate contraction (length decrease) byprefixing a minus sign to the value of

30、the length changereported.12. Interpretation12.1 Information pertaining to this procedure and to thesignificance of the results obtained has been published4,5,6,74Moran, W. T., and Gilliland, J. L., “Summary of Methods for DeterminingPozzolanic Activity,” Symposium on Use of Pozzolanic Materials in

31、Mortars andConcretes, ASTM STP 99, ASTM International, 1950, p. 109.5Gilliland, J. L., and Bartley, T. R., “Water-Solubility of Alkalies in PortlandCement,” Journal of the American Concrete Institute, American Concrete Institute,Vol 47, 1951, p. 153 (especially Fig. number 2 and Table number 3).6Mie

32、lenz, R. C., Greene, K. T., Benton, E. J., and Geier, F. H., “Chemical Testfor Alkali Reactivity of Pozzolans,” Proceedings, ASTM International, Vol 52,1952, p. 1128.7Pepper, L., and Mather, B., “Effectiveness of MineralAdmixtures in PreventingExcessive Expansion of Concrete Due to Alkali-Aggregate

33、Reaction,” Proceedings,ASTM International, Vol 59, 1959, p. 11781203.TABLE 1 Grading RequirementsSieve SizeMass, %Passing Retained on4.75-mm (No. 4) 2.36-mm (No. 8) 102.36-mm (No. 8) 1.18-mm (No. 16) 251.18-mm (No. 16) 600-m (No. 30) 25600-m (No. 30) 300-m (No. 50) 25300-m (No. 50) 150-m (No. 100) 1

34、5C441052and should be reviewed before results of the test are used as abasis for conclusions and recommendations concerning theproperties and use of pozzolans, or slag combinations forconcrete.12.2 Minimum values for the reduction of mortar expansion(Re) have been selected for use in specifications

35、as a basis foracceptance of pozzolan or slag proposed for use in combinationwith high-alkali cement and an aggregate known to be poten-tially deleteriously alkali reactive.13. Report13.1 Report the following information:13.1.1 Type and source of glass used.13.1.2 The type of portland cement used and

36、 its total alkalicontent as Na2O in percent. If the test is applied to acement-pozzolan or cement-slag combination to be used inspecific work, the type, brand, and manufacturing plant of thecement.13.1.3 The type and proportion of pozzolan or slag used. Ifthe test is applied to a cement-pozzolan or

37、cement-slagcombination to be used in specific work, the type, brand,source, proportion, and the nature of the pozzolan or slag.13.1.4 If the control mixture and the test mixture areprepared as specified, the average increase in length of themortar bars prepared from the control mixture and the avera

38、geincrease in length of the mortar bars from the test mixture, inpercent. Also, the reduction in mortar length change resultingfrom the use of the pozzolan or slag (Re), in percent.13.1.5 The average increase in length of the mortar barsprepared from the job mixtures, in percent.14. Precision and Bi

39、as14.1 PrecisionRepeatability shall be considered satisfac-tory if the percentage length increase of each specimen madefrom the same cement-aggregate combination is within 0.003of the average, except that, if the average length increaseexceeds 0.02 %, the repeatability shall be considered satisfac-t

40、ory if the percentage length increase of each specimen moldedfrom the same cement-aggregate combination is within 15 %of the average.14.2 BiasThis procedure has no bias because the effec-tiveness is defined in terms of this test method.15. Keywords15.1 alkali-silica reaction; concrete; expansion; fl

41、y ash;ground blast-furnace slag; mortar; pozzolan; silica fumeASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such

42、patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited

43、either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fa

44、ir hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).C441053