《ASTM C1530-2004 Standard Specification for Non-Asbestos Fiber-Cement Roofing Shakes Shingles and Slates with Designed Varying Profiles and Thicknesses《设计成可变轮廓和厚度的无石棉纤维水泥屋顶盖板、屋面板和石板.pdf》由会员分享，可在线阅读，更多相关《ASTM C1530-2004 Standard Specification for Non-Asbestos Fiber-Cement Roofing Shakes Shingles and Slates with Designed Varying Profiles and Thicknesses《设计成可变轮廓和厚度的无石棉纤维水泥屋顶盖板、屋面板和石板.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: C 1530 04Standard Specification forNon-Asbestos Fiber-Cement Roofing Shakes, Shingles, andSlates with Designed Varying Profiles and Thicknesses1This standard is issued under the fixed designation C 1530; the number immediately following the designation indicates the year oforiginal adop

2、tion or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers non-asbestos fiber-cementroofing shakes, shin

3、gles, and slates that are of designed varyingprofiles and thicknesses manufactured to provide the weather-exposed surfaces on roofs of buildings.1.2 The values stated are in SI units and are to be regardedas the standard. The values given in parenthesis (inch-poundunits) are provided for information

4、 only.1.3 This specification does not include details of productinstallation or system performance. Refer to the manufacturersinstallation literature for proper installation instructions, toSpecification C 1459 for roofing systems performance, and toTest Method E 108 for levels of fire resistance.1.

5、4 This specification is not applicable to asbestos-cementor fiber-cement products as specified in Specifications C 222and C 1225.1.5 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish

6、 appro-priate safety and health practices and determine the applica-bility of regulatory requirements prior to use.2. Referenced Documents2.1 ASTM Standards:2C 222 Specification for Asbestos-Cement Roofing ShinglesC 1154 Terminology for Non-Asbestos Fiber-ReinforcedCement ProductsC 1185 Test Methods

7、 for Sampling and Testing Non-Asbestos Fiber-Cement Flat Sheet, Roofing, and SidingShingles, and ClapboardsC 1225 Specification for Non-Asbestos Fiber-CementRoofing Shingles, Shakes, and SlatesC 1459 Specification for Performance of Non-AsbestosFiber-Reinforced Cement Shake, Shingle, and Slate Roof-

8、ing SystemsD 3359 Test Methods for Measuring Adhesion by Tape TestE 108 Test Method for Fire Tests of Roof CoveringsE 284 Terminology of AppearanceG 152 Practice for Operating Open Flame Carbon Arc LightApparatus for Exposure of Nonmetallic MaterialsG 153 Practice for Operating Enclosed Carbon Arc L

9、ightApparatus for Exposure of Nonmetallic MaterialsG 155 Practice for Operating Xenon Arc Light Apparatusfor Exposure of Nonmetallic Materials3. Terminology3.1 DefinitionsRefer to Terminology C 1154.3.2 Definitions of Terms Specific to This Standard:3.2.1 breaking load, nthe value of perpendicular f

10、orceexpressed in newtons (pound-force), as calculated from thebreaking load of a test specimen, loaded as a simple beam, withthe load applied to the center.4. Manufacture and Composition4.1 ManufactureThese products shall be formed eitherwith or without pressure and cured either under natural oracce

11、lerated conditions, to meet the physical requirements ofthis specification.4.2 CompositionThis specification is applicable to fiber-cement roofing products, consisting of an inorganic binder (forexample, Portland cement) reinforced by discrete non-asbestosfibers.NOTE 1Process aids, fillers, mineral

12、aggregates, and pigments arepermitted.5. Mechanical and Physical Properties5.1 Mechanical and physical properties, as defined in Sec-tion 9, shall be determined on uncoated and unsealed speci-mens, unless the coating is an integral part of the product.Where products are tested coated or sealed, the

13、results shall beidentified as pertaining to coated material. Coating surfacechanges as a consequence of mechanical testing shall not1This specification is under the jurisdiction of ASTM Committee C17 onFiber-Reinforced Cement Products and is the direct responsibility of SubcommitteeC17.02 on Non-Asb

14、estos Fiber Cement Products.Current edition approved June 1, 2004. Published July 2004. Originally approvedin 2002. Last previous edition approved in 2003 as C 153003.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual

15、Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.constitute a mechanical failure as long as such materials havepassed all the ph

16、ysical properties required.6. Supplementary Shapes6.1 Supplementary shapes such as starter pieces, hip andridge finishing pieces, and ridge rolls shall have the samegeneral characteristics as the products which they are designedto complement.7. Inspection and Acceptance7.1 Inspection of material sha

17、ll be at the point of shipmentat the manufacturing facility. The inspector, representing thepurchaser, shall have authorized access to the carriers beingloaded for shipment to the purchaser. The purchaser shall beafforded all reasonable and available facilities at the point ofshipment for sampling a

18、nd inspection of the material, whichshall be conducted so as not to interfere unnecessarily with theloading of the carriers.7.2 Third party certification, including inspections con-ducted either continuously or at regular intervals, shall berecognized as the alternative to lot inspection.7.3 The man

19、ufacturer shall set up a quality control programto inspect the product throughout the manufacturing process.Each production lot shall be marked or coded to identify thedate of manufacture. The Quality Control Program shall haveprovisions to identify and set aside any material or finishedproduct that

20、 appears defective and does not meet this specifi-cation.7.4 Third party inspection for Quality Control ProgramCertification shall be made at a minimum of once per quarter.These inspections shall occur without notice at anytime theplant is in operation. ISO 9000 Self Certification shall bepermitted

21、in lieu of a third party Quality Control InspectionProgram and quarterly inspections.7.5 Failure to conform with any of the requirements of thisspecification shall constitute grounds for non-acceptance.8. Production Quality Control Requirements8.1 Sampling:8.1.1 Breaking Load TestA minimum of one te

22、st speci-men per 500 m2(5382 ft2) exposed area of merchantablematerial produced shall be randomly selected from a consistentstage in the manufacturing process and tested for breaking loadas defined in 8.2.1.8.1.2 Water Absorption TestA minimum of one test speci-men per lot of merchantable material p

23、roduced shall berandomly selected from a consistent stage in the manufacturingprocess and tested for water absorption as defined in 8.3.8.2 Mechanical Requirements:8.2.1 Breaking Load Test ProcedureEach test specimenshall be centered on two parallel metal supports, having aradius of 13 mm (12 in.),

24、which shall be free to rotate (see Fig.1). The center-to-center distance between the supports shall be254 mm (10 in.). A load shall be applied at the center of thespan, with a metal bar of 13 mm (12 in.) radius, be parallel tothe two parallel metal supports, and be in contact with the testspecimen o

25、ver its entire width. The load shall be applied at auniform rate not exceeding 44.5 N (10 lbf) per second untilfailure. The failing load for each test specimen shall berecorded to the nearest9N(2lbf). Test results shall berecorded as N (lbf).8.2.2 Precision and Bias:8.2.2.1 PrecisionThe precision of

26、 the procedure in thisstandard for breaking load test is being determined.8.2.2.2 BiasSince there is no applicable reference mate-rial to determine bias for the breaking load test, no statement ofbias is being made.8.2.3 Condition of AcceptanceThe breaking load shall bea minimum of 312 N (70 lbf) fo

27、r a 305-mm (12-in.) widespecimen prior to shipping. If the manufacturer produces aproduct of widths other than 305 mm (12 in.), a force per unitwidth shall be calculated. The minimum force shall be 1.0N/mm (5.8 lb/in.).8.3 Water AbsorptionCalculate the amount of water ab-sorbed from the increase in

28、weight of the dried specimenduring submersion for a period of 48 h. Express waterabsorption as the percentage by weight when tested in accor-dance with Test Methods C 1185 on a full-sized specimen. Thevalues obtained are used for quality control purposes. Themaximum water absorption shall be 25 %.8.

29、4 Dimensions and Tolerances:8.4.1 Nominal Length, Width, and ThicknessThe shape,size, and thickness shall be specified by the manufacturer.Dimensions shall be determined as specified in Test MethodsC 1185.8.4.2 Length and Width ToleranceThe maximum varia-tion from the manufacturers specified lengths

30、 and widths shallbe 612 mm (12 in.) and 66mm(14 in.), respectively.8.4.3 Thickness ToleranceThe maximum variation fromthe manufacturers specified thickness shall be 625 % at thecenterline when cut at the middle of the test specimens length.8.4.4 Weight ToleranceThe maximum variation from themanufact

31、ures specified weight, on samples taken at a consis-tent point in the manufacturing process which are either asreceived or oven dried, shall be 610 %.8.5 Workmanship and Finish:8.5.1 WorkmanshipThe surface of the product to be ex-posed shall be free of defects that impair serviceability.8.5.2 Finish

32、The surface of the product to be exposedshall be smooth, grained, granulated, coated, or otherwisetextured.8.5.3 ColorThe exposed surface of the product shall bethe natural color of the product or be colored by the addition ofmineral pigments, pigmented coatings, veneers, or embeddedmineral granules

33、.FIG. 1 Breaking Load Test ApparatusC15300428.5.4 Holes for Nails and Supplemental FastenersWhenholes for nails and fasteners are provided in the units duringmanufacturing, they shall be located to provide the required lapand allow for proper application of necessary supplementalfasteners.8.5.5 Effl

34、orescenceEfflorescence that appears on fiber-cement products is not a serviceability defect.8.5.6 WeatheringNatural weather exposure, which canvary with site location, slope, and exposure, will affect acolored product. Any change in color does not in itself detractfrom the mechanical or physical pro

35、perties.9. Product Qualification Testing9.1 Product qualification testing shall consist of “once only”tests, with the manufacturers statement of results providedupon customers request. Changes in product formulation,design or manufacturing process, beyond the ranges allowed inthe manufacturers produ

36、ct specification, shall require appro-priate retesting and written concurrence by an independenttesting agency stating that the changes in formulation, designor manufacturing process are not detrimental to the require-ments of this specification.9.2 Frost Resistance Test (Freeze/Thaw)When tested ina

37、ccordance with Test Method C 1185 Section 16 (Freeze/Thawfor Roofing Products), the average ratio of retained strength forthe freeze/thaw specimens shall be categorized by grade asdefined in Table 1. Where freeze/thaw testing has not beendone, the product shall be assigned a rating of grade 1.9.3 Wa

38、rm Water TestMethods of testing shall be inaccordance with Test Method C 1185.9.3.1 Conditions of AcceptanceAfter testing, the speci-mens shall comply with the following:9.3.1.1 No additional visible cracks, structural alteration ordelamination shall be apparent.9.3.1.2 The mean breaking load per un

39、it width of the testspecimens after warm water exposure shall be at least 80percent of the mean breaking load per unit width of the wetcontrol specimens.9.4 Accelerated Weathering Test:9.4.1 Products shall be coated or uncoated as tested in 5.1.9.4.2 SampleTen representative and randomly selectedsam

40、ples of the product shall be used, of which five must beheld as controls.9.4.3 ApparatusTesting shall be performed using PracticeG 152, G 153, or G 155. The test method used shall bereported.9.4.4 ProcedureThe test shall be run for a period of 3000h on coated or uncoated material, as specified in th

41、e manufac-turers literature. It shall be reported whether the test wasperformed on coated or uncoated material.9.4.5 Conditions of AcceptanceSurface changes such ascracking, checking, crazing, erosion, or chalking shall bereported in accordance with Standard E 284. Loss of adhesionof the top surface

42、, as evaluated in accordance with TestMethods D 3359, shall constitute a failure.9.5 Water TightnessA full-sized, finished product speci-men, when completely framed and tested in accordance withTest Method C 1185, shall not be prohibited from showingmoisture on the underside, but in no instance shal

43、l there be anyfalling drops of water.9.6 Heat/Rain ResistanceThe specimens, when tested inaccordance with Test Methods C 1185, Section 15 on Heat/RainRoof Structures, for 25 cycles, shall not show visiblecracks or structural alteration of the roofing such as to affecttheir performance in use.10. Key

44、words10.1 accelerated weathering; breaking load; cement; efflo-rescence; fiber-cement; freeze/thaw test; frost resistance; inor-ganic fibers; mechanical properties; natural fiber; organicfibers; physical properties; roofing; shakes; shingles; slates;water tightness; weathering; weatherometer testTAB

45、LE 1 Frost Resistance ClassificationGradeNo. ofCyclesRetainedStrengthUseLimitations1 0 N/A Regions where the mean annual rainfall does not exceed 508 mm(20 in.) and the average of the daily lows for any month is at least2C (35F); Consult the manufacturer for geographicalrecommendations.2 25 75 % Reg

46、ions where the mean annual rainfall does not exceed 1016 mm(40 in.) and the average of the daily lows for any month is at least-1 C (30 F); Consult the manufacturer for geographicalrecommendations.3 100 75 % No regional limitations.C1530043ASTM International takes no position respecting the validity

47、 of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject

48、to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters

49、. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or