ASTM B875-1996(2008) Standard Specification for Aluminum Diffusion Coating Applied by Pack Cementation Process《用于固体渗金属处理的铝扩散镀层的标准规范》.pdf

《ASTM B875-1996(2008) Standard Specification for Aluminum Diffusion Coating Applied by Pack Cementation Process《用于固体渗金属处理的铝扩散镀层的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM B875-1996(2008) Standard Specification for Aluminum Diffusion Coating Applied by Pack Cementation Process《用于固体渗金属处理的铝扩散镀层的标准规范》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B 875 96 (Reapproved 2008)Standard Specification forAluminum Diffusion Coating Applied by Pack CementationProcess1This standard is issued under the fixed designation B 875; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revisio

2、n, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers the requirements for aluminumdiffusion of metals by the pack cementation meth

3、od. Packdiffusion employs the chemical vapor deposition of a metalwhich is subsequently diffused into the surface of a substrate athigh temperature. The material to be coated (substrate) isimmersed or suspended in a powder containing aluminum(source), a halide salt (activator), and an inert diluent

4、such asalumina (filler). When the mixture is heated, the activatorreacts to produce an atmosphere of aluminum halides whichtransfers aluminum to the substrate for subsequent diffusion.The aluminum-rich surface enhances corrosion, thermal stabil-ity, and wear-resistant properties.1.2 This standard do

5、es not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Sta

6、ndards:2B 374 Terminology Relating to ElectroplatingB 487 Test Method for Measurement of Metal and OxideCoating Thickness by Microscopical Examination of CrossSectionB 602 Test Method for Attribute Sampling of Metallic andInorganic CoatingsB 697 Guide for Selection of Sampling Plans for Inspectionof

7、 Electrodeposited Metallic and Inorganic CoatingsB 762 Test Method of Variables Sampling of Metallic andInorganic CoatingsC 664 Test Methods for Thickness of Diffusion CoatingD 3951 Practice for Commercial Packaging3. Terminology3.1 Definitions used in this specification are in accordancewith Termin

8、ology B 374.3.2 Definitions of Terms Specific to This Standard:3.2.1 diffusion coatinga diffusion coating is one producedby causing an element to react with or diffuse into, or both, thesurface of a metallic substrate, thus, chemically altering thesurface of the substrate.3.2.2 retortscontainers in

9、which powder and parts arepacked for processing. They can be constructed of carbon,stainless, or high alloys and fabricated in all shapes and sizesto accommodate parts being processed.3.2.3 significant surfaceareas that are essential to theserviceability or function of the article. These surfaces mu

10、st beidentified on a drawing or marked-up sample of product. Areascan fall into one of three categories as follows:3.2.4 coating requiredthese surfaces must be in accor-dance with all quality requirements of this specification.3.2.5 no coating requiredthese surfaces are areas whereno coating is allo

11、wed due to a number of reasons includingdimensional, fabrication, and welding, as well as others.Materials used for masking are commercially available.3.2.6 optionalthese surfaces do not require coating, but atthe same time do not require masking.4. Classification4.1 There are three classes of alumi

12、num diffusion defined bybase (basis) metal category.4.1.1 Class ICarbon steel and low alloy.4.1.2 Class IIStainless steels.4.1.3 Class IIINickel-based alloys.5. Ordering Information5.1 In order to make the application of this specificationcomplete, the purchaser shall supply the following informatio

13、nto the vendor through a purchase order and drawings:5.1.1 Title, ASTM designation number, and date of issue ofthis specification.5.1.2 Deposit by classification (see Section 4).5.1.3 Composition and metallurgical condition of substrateto be coated.5.1.4 Location of significant surfaces (see 3.2.3).

14、1This specification is under the jurisdiction of ASTM Committee B08 onMetallic and Inorganic Coatings and is the direct responsibility of SubcommitteeB08.08.01 on Engineering Coatings.Current edition approved Aug. 1, 2008. Published September 2008. Originallyapproved in 1996. Last previous edition a

15、pproved in 2003 as B 875 96 (2003).2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM Internatio

16、nal, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.5.1.5 Samples for destructive metallurgical test (see 8.1).5.1.6 Any post heat treatment required.5.1.7 Acceptance inspection procedure to be used (seeSection 9).5.1.8 Any requirement for certification (see Sect

17、ion 11).6. Processing Requirements6.1 Substrate PreparationThe metal to be aluminizedshall be free of flaws and defects that will be detrimental to thecoating. Thorough cleaning is essential to ensure satisfactorydiffusion. Materials used for cleaning should not damage thebase metal. Oils, dirt, gre

18、ase, and stains must be removed.When blasting is also required, use aluminum oxide (90 to 220mesh) at 60 to 80 psi from 4 to 6 in. standoff.6.2 Pack MixCan be categorized by the following:6.2.1 Types of Activity:6.2.1.1 High ActivityDeposit aluminum rapidly and per-form at temperatures (1000 to 1500

19、F). This is usually fol-lowed by a diffusion heat treatment at (1900 to 2000F).6.2.1.2 Low ActivityDeposit aluminum slowly and per-form at temperatures in excess of 1650F.6.2.2 Materials:6.2.2.1 Masteralloy with 50 to 100 % Pure AluminumSold under a number of trade names in various mesh sizes.Percen

20、tage in mix depends on material being processed.6.2.2.2 ActivatorMost commonly used is ammoniumchloride, but many others are available. Percentage in mixdepends on material and type of activity.6.2.2.3 Inert FillerAluminum oxide or calcined aluminais used and commercially available in numerous mesh

21、sizes.Percentage in mix depends on material being processed andmesh size being used.NOTE 1It is important that both proper equipment is used and timeestablished to guarantee uniform blend of pack mix.NOTE 2It is common practice to rejuvenate used mixes by addition ofcoating elements, alloys, and act

22、ivators. Chemical analysis of used mixesfacilitates control of critical constituents. Disposal of used mixes must beperformed in compliance with environmental regulations.6.3 LoadingPlace pack mix and parts in retorts. Retortsize is limited by dimensions of furnace used for processing.6.4 Furnace Cy

23、cle:6.4.1 High-activity packs are heated to a temperature be-tween 1100 and 1500F and held for the amount of time neededto produce a sufficient deposit of aluminum which after ahigh-temperature diffusion cycle meets thickness requirements.Time is also dependent on activator(s) being used.6.4.2 Low-a

24、ctivity packs are heated to a temperature be-tween 1650 and 2100F and held for the amount of time neededto produce the desired depth of diffusion.NOTE 3Due to the high temperature of the process, a positive pressureof an inert gas, usually argon, must be maintained in retorts throughout theentire fu

25、rnace cycle.6.5 Post-CleaningRetorts should be allowed to cool suf-ficiently before opening. When parts are removed from retorts,residual pack mix is removed from surfaces by a supplier-approved method.6.6 Diffusion Heat TreatmentParts processed in high ac-tivity packs are placed in the retort and u

26、nder inert atmosphereof argon or hydrogen are heated to 1900 to 2000F and held forthe amount of time needed to produce the desired level ofdiffusion.6.7 Post-StraighteningLong tubes may have distortiondue to the high temperature of process. Use rotary straighteneror hydraulic press to restore straig

27、htness and ovality.6.8 Visual InspectionInspect in accordance with 7.3.6.9 Marking and PackagingTo be defined by the pur-chaser in the purchase order. Parts processed for the U.S.government and military, including subcontracts, shall bepackaged in accordance with Practice D 3951.7. Coating Requireme

28、nts7.1 Diffusion ThicknessThe following are minimums forthe different classes of materials based on standard processparameters. Thicker coatings require special processing andmust be called out for in the purchase order if required.Class Minimum, in.Class I (carbon and low alloy) 0.005Class II (stai

29、nless steels) 0.003Class III (nickel-base alloys) 0.0017.2 Aluminum ContentThe outer 15 % of coating shallcontain a minimum of 28 % (by weight) aluminum.7.3 AppearanceThe diffusion zone shall be nonporousand adherent to the base metal and shall have a uniform surfacefree from objectionable imperfect

30、ions. Minor variations incolor and surface appearance shall be considered acceptable,providing the requirements of 7.1 and 7.2 are met (see 8.6).8. Test Methods8.1 Special Test Specimens:8.1.1 The permission or the requirements to use special testspecimens, the number to be used, the material from w

31、hichthey are to be made, and their shape and size shall be stated bythe purchaser.NOTE 4Test specimens are often used to represent coated articles in atest if these articles are of a size, shape, or material that is not suitable forthe test, or if it is preferred not to submit articles to a destruct

32、ive test,because, for example, the articles are expensive or few in number. Thespecimen should duplicate the characteristics of the article that influencethe property being tested.8.1.2 Special test specimens used to represent articles in anadhesion, weldability, corrosion resistance, or appearance

33、testshall be made of the same material, shall be in the samemetallurgical condition, and shall have the same surfacecondition as the articles they represent, and they shall be placedand processed in the production lot along with the articles theyrepresent.8.2 ThicknessPerform the destructive test on

34、 samples inaccordance with Test Methods C 664. Read and record theresults in accordance with Test Method B 487.8.3 Aluminum ContentShall be performed by beta back-scatter or X-ray fluorescence.8.4 Mechanical Properties (if required)Tensile testing onsamples from each process batch.8.5 Hardness Testi

35、ng (if required)Macrohardness and mi-crohardness testing are both acceptable means.8.6 AppearanceThe coating can be examined at up to 53magnification for conformance to appearance requirements.B 875 96 (2008)29. Sampling9.1 The sampling plan used for inspection of a quantity ofcoated articles shall

36、be agreed upon by the purchaser and thesupplier.NOTE 5Usually, when a collection of coated articles, the inspectionlot (9.2), is examined for compliance with the requirements placed on thecoating, a relatively small number of the articles, the sample, is selectedat random and is inspected. The inspe

37、ction lot is then classified ascomplying or not complying with the requirements based on the results ofthe inspection of the sample. The size of the sample and the criteria ofcompliance are determined by the application of statistics. This procedureis known as sampling inspection. Three standards, T

38、est Method B 602,Guide B 697, and Method B 762, contain sampling plans that are designedfor the sampling inspection of coatings.Test Method B 602 contains four sampling plans, three for use with teststhat are nondestructive and one for tests that are destructive. The buyerand seller may agree on the

39、 plan or plans to be used. If they do not, TestMethod B 602 designates the plan to be used.Guide B 697 provides a large number of plans and also gives guidancein the selection of a plan. When Guide B 697 is specified, the buyer andthe seller need to agree on the plan to be used.Method B 762 can be u

40、sed only for coating requirements that have anumerical limit, such as a coating thickness. The test must yield anumerical value, and certain statistical requirements must be met. MethodB 762 contains several plans and also gives instructions for designatingplans to meet special needs. The buyer and

41、the seller may agree on theplan or plans to be used. If they do not, Method B 762 designates the planto be used.NOTE 6When both destructive and nondestructive tests exist for themeasurement of a characteristic, the purchaser needs to state which one isto be used so that the proper sampling plan is s

42、elected. A test may destroythe coating, but in a noncritical area; or, although it may destroy thecoating, a tested part may be reclaimed by stripping and recoating. Thepurchaser needs to state whether the test is to be considered destructive ornondestructive.9.2 An inspection lot shall be defined a

43、s a collection ofcoated articles of the same kind that have been produced to thesame specifications, coated by a single supplier at one time orapproximately the same time under essentially identical con-ditions, and that are submitted for acceptance or rejection as agroup.9.3 If special test specime

44、ns are used to represent the coatedarticles in a test, the number used shall be that required in 8.1.1.10. Rejection and Rehearing10.1 Parts that fail to conform to the requirements of thisspecification may be rejected. Rejection shall be reported to theproducer promptly in writing. In the case of d

45、issatisfactionwith the results of a test, the producer may make a claim for arehearing. Coatings that show imperfections may be rejected.11. Certification11.1 When specified in the purchase order or contract, thepurchaser shall be furnished with certifications that the samplesrepresenting each lot h

46、ave been either tested or inspected asdirected by this specification and the requirements have beenmet. When specified in the purchase order or contract, a reportof the test results must be furnished.12. Record Retention12.1 The seller is to maintain all job records and samples fora period of two ye

47、ars unless the purchaser requires a longerperiod.13. Keywords13.1 aluminizing; corrosion-resistant coatings; diffusioncoating; pack cementationASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of th

48、is standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five ye

49、ars andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr