《ASTM B752-2006(2011)e2 Standard Specification for Castings Zirconium-Base Corrosion Resistant for General Application 《通用耐腐蚀锆基铸件的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM B752-2006(2011)e2 Standard Specification for Castings Zirconium-Base Corrosion Resistant for General Application 《通用耐腐蚀锆基铸件的标准规格》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B752 06 (Reapproved 2011)2Standard Specification forCastings, Zirconium-Base, Corrosion Resistant, for GeneralApplication1This standard is issued under the fixed designation B752; the number immediately following the designation indicates the year oforiginal adoption or, in the case of

2、revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1NOTEMethod E 142 was removed editorially from Section 2 and X1.1.2 was corrected in April 2011.2NOTESI unit

3、s were removed editorially from Elongation heading in Table S6.1 in March 2012.1. Scope1.1 This specification covers zirconium and zirconium-alloycastings for general corrosion-resistant and industrial applica-tions.1.2 The values stated in inch-pound units are to be regardedas standard. The values

4、given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.2. Referenced Documents2.1 ASTM Standards:2A802/A802M Practice for Steel Castings, Surface Accep-tance Standards, Visual ExaminationE8 Test Methods for Tension Testing o

5、f Metallic MaterialsE10 Test Method for Brinell Hardness of Metallic MaterialsE18 Test Methods for Rockwell Hardness of Metallic Ma-terialsE23 Test Methods for Notched Bar Impact Testing ofMetallic MaterialsE94 Guide for Radiographic ExaminationE165 Practice for Liquid Penetrant Examination for Gene

6、ralIndustryE446 Reference Radiographs for Steel Castings Up to 2 in.(50.8 mm) in Thickness3. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 pour, nshall consist of all material melted and castat one time.3.2 Lot Definitions:3.2.1 castings, na lot shall consist of all castings pr

7、oducedfrom the same pour.4. Ordering Information4.1 Orders for castings to this specification shall include thefollowing, as required to describe the requirements adequately.4.1.1 Description of the castings by pattern number ordrawing (dimensional tolerances shall be included on thecasting drawing)

8、,4.1.2 Quantity,4.1.3 Grade Designation (see Table 1),4.1.4 Options in the specification, and4.1.5 Supplementary requirements desired, including thestandards of acceptance.5. Materials and Manufacture5.1 Material for this specification shall be melted by con-ventional processes used for reactive met

9、als. Typical methodsinclude the consumable electrode and inductoslag meltingprocesses.6. Chemical Composition6.1 Pour AnalysisAn analysis of each pour shall be madeby the producer from a sample such as a casting or test bar thatis representative of the pour. The chemical composition deter-mined shal

10、l conform to the requirements specified for therelevant grade in Table 1.6.1.1 The elements listed in Table 1 are intentional alloyingadditions of elements which are inherent to the manufacture ofprimary zirconium, zirconium sponge, mill product or castings.6.1.1.1 Elements other than those listed i

11、n Table 1 aredeemed to be capable of occurring in the grades listed in Table1 by and only by way of unregulated or unanalyzed scrap1This specification is under the jurisdiction of ASTM Committee B10 onReactive and Refractory Metals and Alloys and is the direct responsibility ofSubcommittee B10.02 on

12、 Zirconium and Hafnium.Current edition approved April 1, 2011. Published April 2011. Originallyapproved in 1985. Last previous edition approved in 2006 as B752 06. DOI:10.1520/B0752-06R11E02.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serv

13、iceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.additions to the pour. Therefore, pour analysis for ele

14、ments notlisted in Table 1 shall be considered to be in excess of the intentof this specification.6.2 When agreed upon by producer and purchaser andrequested by the purchaser in his written purchase order,chemical analysis shall be completed for specific residualelements not listed in this specifica

15、tion.6.3 Product AnalysisA product analysis may be made bythe purchaser on a representative casting from any lot. Becauseof the possibility of oxygen or other interstitial contamination,samples for oxygen, carbon, hydrogen, and nitrogen analysisshall be taken no closer than14 in. (6.3 mm) to a cast

16、surfaceexcept that castings too thin for this shall be analyzed onrepresentative material. The chemical composition determinedshall conform to the analysis in Table 1 within the checkanalysis variations shown in Table 2 or shall be subject torejection by the purchaser.6.4 In the event of disagreemen

17、t between the manufacturerand the purchaser on the conformance of the material to therequirements of this specification or any special test specifiedby the purchase, a mutually acceptable referee shall performthe tests in question. The results of the referees testing shall beused in determining conf

18、ormance of the material to thisspecification.7. Heat Treatment7.1 Unless otherwise specified in the contract, all castingswill be supplied in the as-cast condition except when post-weldheat treatment is required.7.2 If post-weld heat treatment is required, it shall consist ofa stress relief performe

19、d at 1050 6 50F (565 6 25C) for aminimum of12 h at temperature plus an additional12 hattemperature per inch of thickness for section sizes greater than1 in. (25 mm). After heat treatment, the castings should becooled in air or in the furnace to ambient temperature unlessotherwise agreed upon between

20、 the purchaser and producer.8. Workmanship, Finish and Appearance8.1 All castings shall be made in a workmanlike manner andshall conform to the dimensions in drawings furnished by thepurchaser before manufacturing is started. If the pattern issupplied by the purchaser, the dimensions of the casting

21、shallbe as predicted by the pattern.8.2 The surface of the casting shall be free of adhering moldmaterial, scale, cracks, and hot tears as determined by visualexamination. Other surface discontinuities shall meet the visualacceptance standards specified in the order. Practice A802/A802M or other vis

22、ual standards may be used to defineacceptable surface discontinuities and finish. Unacceptablesurface discontinuities shall be removed, and their removalverified by visual examination of the resultant cavities.9. Repair by Welding9.1 If repairs are required, these shall be made using awelding proced

23、ure and operators certified to quality require-ments established by the producer. The procedures developedshall be consistent with standard practices recommended forreactive metal alloys. The producer shall maintain documenta-tion on procedure and welder qualifications. Procedure modi-fications or s

24、pecial arrangements shall be as agreed uponbetween the producer and purchaser.9.2 Weld repairs shall be considered major in the case of acasting that has leaked on a hydrostatic test or when the depthof the cavity after preparation for repair exceeds 20 % of theactual wall thickness or 1 in. (25 mm)

25、, whichever is smaller, orwhen the surface area of the cavity exceeds approximately 10in.2(6500 mm2). All other weld repairs shall be consideredminor. Major and minor repairs shall be subject to the samequality standards as are used to inspect the castings.9.3 The composition of the deposited weld m

26、etal shall bewithin the chemical requirements for each grade established inTable 1.9.4 All castings with major weld repairs shall be stressrelieved after repair in accordance with 7.2. Stress relief afterminor repairs is not required for grades 702C and 704C exceptby agreement between the producer a

27、nd the purchaser. Grade705C must be stress relieved after any weld repair.10. Inspection10.1 The producer shall afford the purchasers inspector allreasonable facilities necessary to satisfy him that the materialTABLE 1 Chemical RequirementsAGrade Designation,Composition, %702C 704C 705CZirconium and

28、 hafnium,min.98.8 97.1 95.1Hafnium, maxIron and chro-mium, max4.50.34.50.34.50.3Hydrogen, max 0.005 0.005 0.005Nitrogen, max 0.03 0.03 0.03Carbon, max 0.1 0.1 0.1Oxygen, max 0.25 0.3 0.3Phosphorus, max 0.01 0.01 0.01Tin . 1.0 to 2.0 .Niobium . . 2.0 to 3.0ABy agreement between the purchaser and the

29、producer, analysis may berequired and limits established for elements and compounds not specified in thistable.TABLE 2 Check Analysis TolerancesElementMaximumof Range,Weight, %PermissibleVariationin CheckAnalysisNitrogen 0.03 +0.006Carbon 0.10 +0.02Hydrogen 0.005 +0.001Iron and chromium 0.30 +0.06Ox

30、ygen 0.25 +0.05Hafnium 4.50 +0.50Phosphorus 0.010 +0.003Tin 1.0 to 2.0 60.02Niobium 2.0 to 3.0 60.015Residuals 0.10 +0.02B752 06 (2011)22is being produced and furnished in accordance with thisspecification. Foundry inspection by the purchaser shall notinterfere unnecessarily with the producers opera

31、tions.All testsand inspections, with the exception of product analysis (6.3),shall be made at the place of manufacture, testing, or inspectionunless otherwise agreed upon.11. Rejection11.1 Any rejection based on test reports shall be reported tothe producer within 60 days from the receipt of the tes

32、t reportsby the purchaser.11.2 Material that shows unacceptable discontinuities asdetermined by the acceptance standards specified on the order,subsequent to acceptance at the producers works, will berejected, and the producer shall be notified within 60 days, oras otherwise agreed upon.12. Product

33、Marking12.1 Unless otherwise specified, the following shall apply:12.1.1 Castings shall be marked for material identificationwith the ASTM specification number (B752) and grade sym-bol, that is, 702C, 704C, or 705C.12.1.2 The producers name or identification mark and thepattern number shall be cast

34、or stamped using low stressstamps on all castings. Small size castings may be such thatmarking must be limited consistent with the available area.12.1.3 The marking of lot numbers on individual castingsshall be agreed upon between the producer and the purchaser.12.1.4 Marking shall be in such a posi

35、tion as not to injurethe usefulness of the casting.13. Keywords13.1 castings; corrosion-resistant; zirconium; zirconiumalloysSUPPLEMENTARY REQUIREMENTSSupplementary requirements shall be applied only when specified by the purchaser. Details of thesupplementary requirements shall be agreed upon betwe

36、en the producer and purchaser. The specifiedtests shall be performed by the producer prior to shipment of the castings.S1. Radiographic ExaminationS1.1 The castings shall be examined for internal defects bymeans of X rays or gamma rays. The procedure shall be inaccordance with Guide E94 and types an

37、d degrees of discon-tinuities shall be judged by Reference Radiographs E446. Theextent of examination and basis for acceptance shall be agreedupon between the producer and purchaser.S2. Liquid Penetrant ExaminationS2.1 The castings shall be examined for surface disconti-nuities by means of liquid pe

38、netrant examination. The exami-nation shall be in accordance with Test Method E165. Areas tobe inspected, methods and types of liquid penetrants to be used,developing procedure, and basis for acceptance shall be agreedupon between the producer and purchaser.S3. Examination of Weld PreparationS3.1 Ca

39、vities prepared for welding as a result of surfacediscontinuities, such as cracks, open porosity, and so forth shallbe examined by means of liquid penetrant examination in orderto verify removal of such discontinuities.S3.2 Weld repairs that are made to eliminate discontinuitiesthat are detected by

40、radiography shall be re-radiographed toverify that unacceptable discontinuities have been removed.S4. CertificationS4.1 A test report shall be furnished. The test report shallcontain the results of the actual chemical analysis and othertests specified by the purchaser.S4.2 Each test report shall be

41、signed by an authorized agentof the seller or producer.S4.3 The test report shall be furnished within 5 days ofshipment of the castings.S5. Prior Approval of Major Weld RepairsS5.1 Major weld repairs as defined and agreed upon be-tween the producer and purchaser shall be subject to the priorapproval

42、 of the purchaser.S6. Tension TestS6.1 Tensile properties shall be determined on materialrepresenting each pour. Properties shall be determined in theas-cast condition unless the purchase order requires the prop-erties be determined in the final condition after all heattreatments (including isostati

43、c pressing) have been completedor unless otherwise specified in the purchase order. The resultsshall conform to the requirements specified in Table S6.1.S6.2 Test bars may be obtained from special test blocks castfor that purpose or cut from castings processed with a lot.TABLE S6.1 Tensile and Hardn

44、ess RequirementsGradeTensileStrength,minYieldStrength, 0.2 %Offset, minElongationin1in.length, min, %Hardness,HB, maxHardness,Rockwell,maxksi MPa ksi MPa702C 55 (380) 40 (276) 12 210 B96704C 60 (413) 40 (276) 10 235 B99705C 70 (483) 50 (345) 12 235 B99B752 06 (2011)23S6.3 Tensile tests shall be made

45、 in accordance with therequirements of Test Methods E8. Tensile properties shall bedetermined using a strain rate of 0.003 to 0.007 in./in./min(0.005 to 0.007 mm/mm/min) through the yield strength.S6.4 If any test specimen shows defective machining ordevelops flaws, it may be discarded and another s

46、pecimensubstituted from the same pour.S7. Hardness TestS7.1 Hardness shall be determined on each lot. Hardnessshall be determined in the as-cast condition unless the purchaseorder requires the hardness be determined in the final conditionafter all heat treatments (including isostatic pressing) haveb

47、een completed or unless otherwise specified in the purchaseorder. The results shall conform to the requirements specifiedin Table S6.1.S7.2 Hardness shall be determined on a sample cast for thatpurpose, or on a casting randomly selected from a lot. If acasting is used for a hardness sample, indentat

48、ions shall bemade in a surface that will not be subsequently machined.Hardness values reported shall be representative of the basemetal of the castings and not of any surface contaminationcaused by mold-metal interactions.S7.3 Hardness tests shall be made in accordance with therequirements of Test M

49、ethods E10 or E18.S8. Hot Isostatic Pressing (HIP)S8.1 Hot Isostatic Pressing (HIP) shall be used to improveas-cast properties or remove internal defects, or both. Tempera-ture, time at temperature, and atmosphere shall be agreed uponbetween supplier and purchaser.S8.2 HIP may be substituted for required thermal treatmentprovided all requirements for that treatment are met andtemperatures detrimental to the material properties are notreached.S9. Charpy Impact TestS9.1 Charpy impact test properties shall be determined onmaterial representing each lot. Three Cha