ASTM B737-2010(2015) Standard Specification for Hot-Rolled and or Cold-Finished Hafnium Rod and Wire《热轧和 或冷加工铪杆材和线材的标准规格》.pdf

《ASTM B737-2010(2015) Standard Specification for Hot-Rolled and or Cold-Finished Hafnium Rod and Wire《热轧和 或冷加工铪杆材和线材的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM B737-2010(2015) Standard Specification for Hot-Rolled and or Cold-Finished Hafnium Rod and Wire《热轧和 或冷加工铪杆材和线材的标准规格》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B737 10 (Reapproved 2015)Standard Specification forHot-Rolled and/or Cold-Finished Hafnium Rod and Wire1This standard is issued under the fixed designation B737; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year

2、 of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers hot- or cold-worked hafniumrod and wire.1.2 This specification contains two material gra

3、des, onespecifically for nuclear applications (Grade R1) and one forcommercial alloying applications (Grade R3).1.3 The products covered include the following:1.3.1 Rod38 to 1 in. (9.5 to 25 mm) in diameter.1.3.2 Wire less than38 in. (9.5 mm) in diameter.1.4 Unless a single unit is used, for example

4、, corrosion massgain in mg/dm2, the values stated in either inch-pound or SIunits are to be regarded separately as standard. The valuesstated in each system are not exact equivalents; therefore, eachsystem must be used independently of the other. SI valuescannot be mixed with inch-pound values.1.5 T

5、his standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Docume

6、nts2.1 ASTM Standards:2E8 Test Methods for Tension Testing of Metallic MaterialsE21 Test Methods for ElevatedTemperatureTensionTests ofMetallic MaterialsE29 Practice for Using Significant Digits in Test Data toDetermine Conformance with SpecificationsE2626 Guide for Spectrometric Analysis of Reactiv

7、e andRefractory Metals3. Terminology3.1 Definitions:3.1.1 rounds, flats, tubes, and wrought powder metallurgicalproducts (single definition, common to nuclear and non-nuclear standards) , na lot shall consist of a material of thesame size, shape, condition, and finish produced from the sameingot or

8、powder blend by the same reduction schedule and thesame heat treatment parameters. Unless otherwise agreedbetween manufacturer and purchaser, a lot shall be limited tothe product of an 8 h period for final continuous anneal, or toa single furnace load for final batch anneal.4. Ordering Information4.

9、1 Purchase orders for material under this specificationshall include the following information as required to ad-equately describe the desired material:4.1.1 Quantity (weight or number of pieces),4.1.2 Name of material,4.1.3 Form (rod, wire),4.1.4 Finish (Section 12),4.1.5 Applicable dimensions (dia

10、meter and length),4.1.6 Grade (Table 1),4.1.7 ASTM designation and year of issue,4.1.8 Zirconium analysis requirements (Table 1), and4.1.9 Workmanship standards (Section 13).NOTE 1A typical ordering description is as follows: 500 lb hafniumrod, annealed; mechanically descaled and pickled; 0.375 in.

11、diameter by 6in. minimum random lengths; Grade R1; ASTM Specification B737 - 01.4.2 In addition to the data specified in 4.1, the followingoptions and points of agreement between the manufacturer andthe purchaser shall be specified on the purchase order ifrequired:4.2.1 Mechanical test temperature (

12、see 8.1),4.2.2 Mechanical test requirements for Grade R3 (Section8),4.2.3 Straightness (Table 2),4.2.4 Special tests (Section 11),4.2.5 Inspection (Section 16),4.2.6 Hafnium isotopic composition and its analysis, (Table1),4.2.7 Metallurgical condition (Section 6),4.2.8 Corrosion test Grade 3 (9.3),4

13、.2.9 Rejected material return (Section 17), and4.2.10 Certification requirements (Section 19).1This specification is under the jurisdiction of ASTM Committee B10 onReactive and Refractory Metals and Alloys and is the direct responsibility ofSubcommittee B10.02 on Zirconium and Hafnium.Current editio

14、n approved May 1, 2015. Published May 2015. Originallyapproved in 1984. Last previous edition approved in 2010 as B737 10. DOI:10.1520/B0737-10R15.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandard

15、s volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States15. Materials and Manufacture5.1 Material covered by this specification shall be made byconventional

16、hot and cold working procedures, from ingotsproduced by vacuum melting in electron beam or consumablearc furnaces, or both, of a type conventionally used for reactivemetals.6. Metallurgical Condition6.1 All grades furnished under this specification shall be inthe recrystallization annealed condition

17、 unless otherwise speci-fied.7. Chemical Composition7.1 The material shall conform to the requirements forchemical composition as prescribed in Table 1.7.2 The manufacturers ingot analysis shall be consideredthe chemical analysis for material produced to this specifica-tion except for hydrogen and n

18、itrogen content which shall bedetermined on the finished product.7.3 Analysis shall be made using the manufacturers stan-dard methods.7.4 Sampling for chemical composition shall consist ofsamples taken at top, middle, and bottom of the ingot. Samplesfor hydrogen and nitrogen shall be taken as two ra

19、ndomsamples from each lot at final size.8. Mechanical Properties8.1 Grade R1 in rod form shall conform to the requirementsprescribed in Table 3 for room temperature mechanical prop-erties. Elevated temperature properties shall be used to deter-mine compliance only when specified in the purchase orde

20、r(see Test Methods E21).8.2 The yield strength shall be determined by the offset(0.2 %) method as prescribed in Test Methods E8.8.3 The tensile properties shall be determined using a strainrate of 0.003 to 0.007 in./in.mm/mm/min through the yieldstrength. After the yield strength has been exceeded,

21、thecross-head speed shall be increased to approximately 0.05in./in.mm/mm/min to failure.8.4 Requirements for mechanical properties do not apply towire.9. Corrosion Properties9.1 Two samples chosen at random from each lot shall becorrosion tested in water at 680F (360C), 2690 psi (18.5MPa) for 672 +

22、8 0 h using the manufacturers standardprocedure.9.2 Grade R1Coupons shall exhibit a weight gain of notmore than 10 mg/dm2.9.3 Grade R3Test for information only, if required bypurchase order.10. Permissible Variations in Dimensions10.1 Rod and wire shall conform to the dimensional require-ments for t

23、he specified product as prescribed in Table 2, Table4, and Table 5.TABLE 1 Chemical Requirements Maximum Impurity LevelComposition, Weight %ElementNuclear GradeAlloyingGradeGrade R1 Grade R3Aluminum 0.010 0.050Carbon 0.015 0.025Chromium 0.010 0.050Copper 0.010 .Hydrogen 0.0025 0.0050Iron 0.050 0.075

24、0Molybdenum 0.0020 .Nickel 0.0050 .Niobium 0.010 .Nitrogen 0.010 0.0150Oxygen 0.040 0.130Silicon 0.010 0.050Tantalum 0.020 .Tin 0.0050 .Titanium 0.010 0.050Tungsten 0.0150 0.0150Uranium 0.0010 .Vanadium 0.0050 .ZirconiumAAHafniumBbalance balanceAZirconium shall be reported. Acceptable levels shall b

25、e established by mutualagreement between purchaser and producer.BHafnium isotopic composition and analytical methods, if required, shall bemutually agreed upon by the purchaser and producer.TABLE 2 Permissible Variations in Straightness for StraightLengths Hot- or Cold-Finished Rod and WireADiameter

26、, in. (mm) Permissible VariationsUp to38 (9.5), incl332 in. (2.4 mm) in any 5 ft (1.5 m) but may notexceed332 in. (2.4 mm) (number of feet in length /5; number of meters in length / 1.52)Over38 to 1.0 (9.5 to 25)116 in. (1.6 mm) in any 5 ft (1.5 m) but may notexceed116 in. (1.6 mm) (number of feet i

27、n length /5; number of meters in length / 1.52)AThe measurement is taken on the concave side of the bar with a straight- edge.Unless otherwise specified, hot- or cold-finished bars for machining purposes arefurnished machine straightened to the tolerances specified in the table.TABLE 3 Mechanical Pr

28、opertiesGrade Condition Test TemperatureTensile Strength, minksi (MPa)Yield Strength, minksi (MPa)Elongation in 2 in.or 50 mm, min, %AR1 annealed RT 58 (400) 22 (150) 22annealed 600F (315C) 25 (170) 11 (75) 32AWhen a sub-size specimen is used, the gage length shall be as specified in Test Methods E8

29、.B737 10 (2015)211. Special Tests11.1 Additional tests may be specified in the purchase order.The test method and standards shall be agreed upon in advancebetween manufacturer and purchaser.12. Finish12.1 Rods shall be furnished with one of the followingsurface finishes as designated in the purchase

30、 order:12.1.1 Mechanically descaled and pickled,12.1.2 Centerless ground and pickled, or12.1.3 Centerless ground, pickled, and oxidized.12.2 Wire shall be furnished with one of the followingsurface finishes as designated in the purchase order:12.2.1 Conditioned and pickled, or12.2.2 Conditioned, pic

31、kled, and oxidized.13. Workmanship13.1 Cracks, seams, slivers, blisters, burrs, and other inju-rious imperfections shall not exceed standards of acceptabilityagreed upon by the manufacturer and the purchaser.14. Number of Test and Retests14.1 Two random samples shall be taken from each lot.14.2 If a

32、ny sample or specimen exhibits obviouscontamination, improper preparation, or flaws disqualifying itas a representative sample, it shall be discarded and a newsample or specimen substituted.14.3 If the results of any test lot are not in conformance withthe requirements of this specification, the lot

33、 may be retested atthe option of the manufacturer. The frequency of the retest willbe double the initial number of tests and if the results of theretest conform to the specification, then the retest values willbecome the test values for certification.All test values, originaland retest, shall be rep

34、orted to the purchaser.15. Significance of Numerical Limits15.1 For the purpose of determining compliance with thespecified limits for requirements of the properties listed in thefollowing table, an observed value or a calculated value shallbe rounded as indicated in accordance with the roundingmeth

35、ods of Practice E29.PropertyRounded Unit for Observedor Calculated ValueChemical composition, andtolerances (when expressed asdecimals)nearest unit in the last right-hand place offigures of the specified limitTensile strength and yieldstrengthnearest 1000 psi (10 MPa)Elongation nearest 1 %16. Inspec

36、tion16.1 The manufacturer shall inspect the material covered bythis specification prior to shipment. If so specified in thepurchase order, the purchaser or his representative may witnessthe testing and inspection of the material at the place ofmanufacture. In such cases, the purchaser shall state in

37、 hispurchase order which test he desires to witness. The manufac-turer shall give notice to the purchaser as to the time and placeof the designated tests. If the purchasers representative doesnot present himself at the time agreed upon for the testing, themanufacturer shall consider the requirement

38、for purchasersinspection at place of manufacture to be waived.16.2 The manufacturer shall afford the inspector represent-ing the purchaser, without charge, all reasonable facilities tosatisfy him that the material is being furnished in accordancewith this specification. This inspection shall be so c

39、onducted asnot to interfere unnecessarily with the operation of the works.17. Rejection17.1 Rejection for failure of the material to meet therequirements of this specification shall be reported to themanufacturer within 60 calendar days from the receipt of thematerial by the purchaser. Unless otherw

40、ise specified, rejectedmaterial may be returned to the manufacturer at the manufac-turers expense, unless the purchaser receives, within 3 weeksof the notice of rejection, other instructions for disposition.18. Referee18.1 In the event of disagreement between the manufacturerand the purchaser on the

41、 conformance of the material to therequirements of this specification or any special test specifiedby the purchaser, a mutually acceptable referee shall performthe tests in question. The results of the referees testing shall beused in determining conformance of the material to thisspecification.19.

42、Certification19.1 A producers or suppliers certification shall be fur-nished to the purchaser that the material was manufactured,sampled, tested, and inspected in accordance with this speci-fication and has been found to meet the requirements. Thecertificate shall include a report of the test result

43、s.20. Packaging and Package Marking20.1 Each shipment shall be legibly and conspicuouslymarked or tagged with the following information:20.1.1 Purchase order or contract number,20.1.2 Name of material,20.1.3 Grade,20.1.4 Size,20.1.5 Lot, heat or ingot number,TABLE 4 Permissible Variations in Diamete

44、r for Hot- or Cold-Finished Rod and WireDiameters, in. (mm)PermissibleVariations, in. (mm)AUp to316 (4.8), incl 0.002 (0.05)Over316 to58 (4.8 to 16), incl 0.003 (0.08)Over58 to34 (16 to 19), incl 0.004 (0.10)Over34 to 1.0 (19 to 25), incl 0.005 (0.13)AWhen it is necessary to heat treat or heat treat

45、 and pickle after cold finishing,because of special hardness, surface or mechanical property requirements,tolerances are double those shown in the table.B737 10 (2015)320.1.6 Condition,20.1.7 Gross, net, and tare weights, and20.1.8 ASTM specification designation number.20.2 All material shall be pac

46、kaged in such a manner as toensure safe delivery to its destination when properly trans-ported by any common carrier.21. Keywords21.1 hafnium; hafnium alloy; rod; wireASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin th

47、is standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must b

48、e reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theres

49、ponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-