1、Designation: B 619 06Standard Specification forWelded Nickel and Nickel-Cobalt Alloy Pipe1This standard is issued under the fixed designation B 619; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A numbe
2、r in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification2covers welded pipe of nickel andnickel-cobalt alloys (UNS N10001; UNS N10242; UNSN10665; UNS N12160; UNS N10624; UNS N10
3、629; UNSN10675; UNS N10276; UNS N06455; UNS N06007; UNSN06975; UNS N08320; UNS N06002; UNS N06022; UNSN06035; UNS N06058; UNS N06059; UNS N06200; UNSN06985; UNS N06030; UNS R30556; UNS N08031; UNSN06230; UNS N06686; UNS N06210; and UNS R20033)* asshown in Table 1.1.2 This specification covers pipe i
4、n Schedules 5S, 10S,40S, and 80S through 8-in. nominal pipe size and larger as setforth in ANSI B36.19 (see Table 2).1.3 Two classes of pipe are covered as follows:1.3.1 Class IAs welded and solution annealed or weldedand sized and solution annealed.1.3.2 Class IIWelded, cold worked, and solution an
5、-nealed.1.4 All pipe shall be furnished in the solution annealed anddescaled condition. When atmosphere control is used, descal-ing is not necessary.1.5 The values stated in inch-pound units are to be regardedas the standard. The values given in parentheses are forinformation only.1.6 This standard
6、does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to become familiarwith all hazards including those identified in the appropriateMaterial Safety Data Sheet (MSDS) for this product/materialas provided by the m
7、anufacturer, to establish appropriatesafety and health practices, and determine the applicability ofregulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:3B 775 Specification for General Requirements for Nickeland Nickel Alloy Welded PipeB 899 Terminology Relating to Non-ferr
8、ous Metals andAlloysE 527 Practice for Numbering Metals and Alloys (UNS)2.2 ANSI Standards:4B36.19 Stainless Steel PipeB2.1 Pipe Threads2.3 ASME Boiler and Pressure Vessel Code5Section IX Welding and Brazing Qualifications3. Terminology3.1 For definitions of terms used in this standard refer toTermi
9、nology B 899.4. General Requirement4.1 Material furnished under this specification shall con-form to the applicable requirements of Specification B 775unless otherwise provided herein.5. Ordering Information5.1 It is the responsibility of the purchaser to specify allrequirements that are necessary f
10、or material ordered under thisspecification. Examples of such requirements include, but arenot limited to the following:5.1.1 Alloy (Table 1),5.1.2 Class (see 1.3),5.1.3 Quantity (feet or number of lengths),5.1.4 Size (nominal size or outside diameter and schedulenumber or average wall thickness),5.
11、1.5 LengthSpecify cut length or random,1This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02.07 on Refined Nickel and Cobalt and Their Alloys.Current edition approved June 1, 2006. Published June 2006. O
12、riginallyapproved in 1981. Last previous edition approved in 2005 as B 619 05.2For ASME Boiler and Pressure Vessel Code applications see related Specifi-cation SB-619 in Section II of that Code.* New designation established in accordance with Practice E 527 and SAEJ1086, Practice for Numbering Metal
13、s and Alloys (UNS).3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.4Available from American National Standard
14、s Institute (ANSI), 25 W. 43rd St.,4th Floor, New York, NY 10036.5Available from American Society of Mechanical Engineers (ASME), ASMEInternational Headquarters, Three Park Ave., New York, NY 10016-5990.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-29
15、59, United States.5.1.6 CertificationState if certification or a report of testresults is required,5.1.7 Purchaser InspectionState which tests or inspec-tions are to be witnessed,5.1.8 EndsPlain ends cut and deburred will be furnished,unless otherwise specified, and5.1.9 Samples for Product (Check)
16、AnalysisState whethersamples shall be furnished.6. Materials and Manufacture6.1 The pipe shall be made from flat-rolled alloy by anautomatic welding process with no addition of filler metal.6.2 Subsequent to welding and prior to final heat treatment,Class II pipes shall be cold worked either in both
17、 weld and basemetal or in weld metal only. The method of cold working maybe specified by the purchaser.7. Chemical Composition7.1 The material shall conform to the composition limitsspecified in Table 1.7.2 If a product (check) analysis is made by the purchaser,the material shall conform to the requ
18、irements specified inTable 1 subject to the permissible tolerances in SpecificationB 775.8. Mechanical Properties and Other Requirements8.1 Tension TestThe tensile properties of the material atroom temperature shall conform to those shown in Table 3.8.1.1 One tension test shall be made on each lot o
19、f pipe.8.2 Flattening TestOne flattening test shall be made on aspecimen from one end of one pipe from each lot.8.3 Transverse Guided Bend Test:8.3.1 At the option of the pipe manufacturer, the transverseguided bend test may be substituted in lieu of the flatteningtest. Two bend specimens shall be t
20、aken transversely from pipeor the test specimens may be taken from a test plate of the samematerial and heat as pipe, which is attached to the end of thecylinder and welded as a prolongation of the pipe longitudinalseam. Except as provided in 8.3.2, one shall be subjected to aface guided bend and a
21、second to a root guided bend test. Onespecimen shall be bent with the inside surface of the pipeagainst the plunger and the other with the outside surface of thepipe against the plunger. Guided bend test specimens shall beprepared and tested in accordance with Section IX, Part QW160 of theASME Boile
22、r and Pressure Vessel Code and shall beone of the types shown in QW462.2 and QW462.3 of that code.8.3.2 For specified wall thicknesses38 in. (9.5 mm) andover, but less than34 in. (19 mm) side bend tests may be madeinstead of the face and root bend tests. For specified wallthicknesses34 in. (19 mm) a
23、nd over, both specimens shall besubjected to the side bend tests. Side bend specimens shall bebent so that one of the side surfaces becomes the convexsurface of the bend specimen.8.3.3 The bend test shall be acceptable if no cracks or otherdefects exceeding18 in. (3 mm) in any direction be present i
24、nthe weld metal or between the weld and the pipe or plate metalafter bending. Cracks which originate along the edges of thespecimen during testing, and are less than14 in. (6.5 mm)measured in any direction shall not be considered.8.4 Hydrostatic or Nondestructive Electric TestEach pipeshall be subje
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ASTMB6192006STANDARDSPECIFICATIONFORWELDEDNICKELANDNICKELCOBALTALLOYPIPE 焊接 合金管 标准规范 PDF

链接地址:http://www.mydoc123.com/p-461761.html